CN110157337A - 凹凸不平曲面花岗岩的翻新抛光粉及其翻新抛光的方法 - Google Patents
凹凸不平曲面花岗岩的翻新抛光粉及其翻新抛光的方法 Download PDFInfo
- Publication number
- CN110157337A CN110157337A CN201910561437.5A CN201910561437A CN110157337A CN 110157337 A CN110157337 A CN 110157337A CN 201910561437 A CN201910561437 A CN 201910561437A CN 110157337 A CN110157337 A CN 110157337A
- Authority
- CN
- China
- Prior art keywords
- granite
- renovation
- curved surface
- polishing
- uneven curved
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及翻新领域,涉及凹凸不平曲面花岗岩的翻新抛光粉其及翻新抛光的方法。按重量比例,其包括:生灰粉20‑40%、磨粒60‑80%,混合均匀制成花岗岩翻新粉,通过在花岗岩翻新粉中加入2至5倍水制成花岗岩翻新膏,花岗岩翻新膏均匀涂抹在被翻新抛光的凹凸不平曲面花岗岩的表层面,用安装在水磨机上的圆盘刷施压和快速旋转花岗岩翻新膏,对凹凸不平曲面花岗岩的表面层进行研磨抛光处理。本发明,可以解决花岗岩表面是凹凸不平,而且是曲面的情况下,进行翻新、抛光、保养的处理。
Description
技术领域
本发明涉及翻新领域,更具体地说,它涉及凹凸不平曲面花岗岩的翻新抛光粉及其翻新抛光的方法。
背景技术
室外饰品、建筑物裸露在外的部分、城市标志、大型室外雕像等,常常会使用花岗岩材料。
花岗岩是天然材料,不是人工合成的材料,具有生命特性,它会根据周围环境、空气、磁场、阳光、雨水等情况而发生颜色变化,这种颜色变化,有时是有利的,有时却是不利的,譬如:雕像眼睛里的雨水积存时间长了,吸收空气中二氧化碳、二氧化硫、氮的氧化物等物质,生成亚硫酸SO2 + H2O = H2SO3,亚硫酸不稳定,被空气中的氧气氧化生成硫酸2H2SO3 + O2 = 2H2SO4,硫酸是强酸,酸性较强。硫酸和亚硫酸从雕像眼睛流出,使雕像脸部形成垂直流痕,特别象雕像在流泪哭泣,使信仰、崇敬、喜欢这个雕像的人们,心里特别难受。
对于花岗岩不利的颜色变化,需要处理,最好的办法是翻新,就是将变化了的颜色层面清除掉,露出新的层面。但花岗岩具有生命特征,采用化学方法进行处理后,往往会留下后遗症。
对于平面型花岗岩的表面层的清除和抛光,可用砂轮、抛光片进行研磨和抛光,但是,如果花岗岩表面是凹凸不平的,而且是曲面的,目前没有什么方法进行处理。譬如雕像眼睛、鼻子、嘴巴、耳朵处的颜色清除和抛光。
因此,发明一种可以清除和抛光凹凸不平,而且是曲面的花岗岩材料的表面层的翻新抛光粉及其翻新抛光的方法,显得非常必要。
发明内容
本发明的目的是提供凹凸不平曲面花岗岩的翻新抛光粉其及翻新抛光的方法,其目的在于,清除和抛光凹凸不平,而且是曲面的花岗岩材料的表面层。
本发明的上述技术目的是通过以下技术方案得以实现的。
一种翻新抛光凹凸不平曲面花岗岩的翻新粉,可对花岗岩表面进行物理方式的翻新抛光处理,磨料选用硬度大于花岗岩硬度的金刚石材料,或者碳化硅材料,或者刚玉材料。
所述花岗岩翻新粉,按重量比例,其包括:生灰粉20-40%、磨粒60-80%。
花岗岩硬度在摩氏硬度在6度至7度之间,所述磨粒采用硬度大于花岗岩硬度的材料,如金刚石材料、碳化硅材料、刚玉材料。
花岗岩翻新粉的配制方法:将生灰粉和磨粒按比例混合均匀,生灰粉和磨粒的目数大小相同,以便于均匀混合。
优选的,翻新花岗岩时,所述磨粒为46目至120目的磨粒。
优选的,抛光花岗岩时,所述磨粒为240目至800目的磨料微粉。
通过采用上述技术方案,可以让硬于花岗岩的磨料颗粒,或磨料微粉均匀到达凹凸不平曲面花岗岩的表面层,从而可以抛光或研磨凹凸不平曲面花岗岩的表面层。
本发明的另一个目的是提供凹凸不平曲面花岗岩的翻新抛光方法,包括以下步骤。
步骤一:将翻新抛光凹凸不平曲面花岗岩的翻新粉,加入它的2至5重量倍数的水,调合成膏状物,制成翻新抛光凹凸不平曲面花岗岩的翻新膏,水的用量比例根据被翻新抛光的花岗岩的表面情况而定,花岗岩表面凹凸差大的,加水量大,粘稠度小,使所述翻新膏能到达凹底,花岗岩表面凹凸差小的,加水量小,粘稠度大,使翻新膏能粘结在凸顶,而不会滑脱下来。
步骤二:将步骤一所述翻新膏,均匀涂抹在被翻新抛光的凹凸不平曲面花岗岩表层面。
步骤三:将圆盘刷安装在水磨机上,手持水磨机对步骤二涂抹了翻新抛光凹凸不平曲面花岗岩的翻新膏的地方,进行翻新抛光。
因离心力的作用,当所述翻新膏越用越少时,可重复步骤二的过程。
操作人员一边手持水磨机对花岗岩进行翻新抛光处理,一边打开水磨机的水龙头,在工作面上加入适量水,起到降温与补水的功效。
如果花岗岩表面凹凸差比较大,圆盘刷的刷丝采用长短参差不齐的形态,以使圆盘刷的刷丝的动力能传达到花岗岩表面的凹底处。
步骤四:待花岗岩表面的凹底处翻新抛光完成后,完全打开手持水磨机的水龙头,通过圆盘刷的转动和水的冲力,对花岗岩表面进行清洗。
本发明的工作原理:通过以上所述翻新粉的配方、翻新粉制成翻新膏技术,可以让磨料均匀涂抹在花岗岩的曲面处,可以让磨料到达花岗岩凹凸面的凹底。用安装在水磨机上圆盘刷施压和快速旋转花岗岩翻新膏,使磨粒在花岗岩的表面层移动,对凹凸不平曲面花岗岩的表面层的各个地方,进行研磨抛光处理,不会产生遗漏的点和面。
花岗岩表面层翻新后,或者抛光完成后,花岗岩新层面直接曝露在空气中、阳光中、雨水中,从而发生颜色变化,为了延长花岗岩新层面的新鲜时间,需要对花岗岩新层面进行防护处理。
硅油具用抗氧化、闪点高、挥发性小、对金属无腐蚀、无毒等特点。
凹凸不平曲面花岗岩的保养方法:
步骤一:将硅油,涂抹在被保养的凹凸不平曲面花岗岩表层面。
步骤二:将圆盘刷安装在水磨机上,手持水磨机对涂抹了硅油的地方,用圆盘刷的高速旋转,将硅油均匀涂抹在花岗岩表层曲面的凹底和凸顶。
通过所述凹凸不平曲面花岗岩的保养方法,使凹凸不平曲面花岗岩表层面覆盖上一层硅油,阻挡了花岗岩与空气、雨水,并且不会产生遗漏的点和面,从而延长花岗岩表面的新鲜时间。
综上所述,本发明具有以下有益效果:
本发明,可以解决花岗岩表面在凹凸不平,而且是曲面的情况下,进行翻新抛光处理,完全利用物理方式,避免了化学方式对花岗岩石造成的二次污染。本明中所采用的材料、工具、步骤在本发明中的具体有益效果为:
1、比花岗岩硬的金刚石、碳化硅磨料、刚玉磨料,可以清除掉花岗岩表面的老化层,露出新层,可以翻新和抛光花岗岩表面层。
2、生灰粉制成熟石灰膏,可以让磨料均匀粘结在花岗岩表面,使凸顶、凹底都有磨料附在上面,解决现有技术中磨料无法均匀到达曲面的各处、无法到达花岗岩表面层的凹底。并且熟石灰膏可以被水轻易冲洗干净,不会对花岗岩造成二次污染。
3、圆盘刷和手持水磨机,可以施力于花岗岩表面的曲面的各处、表面层的凸顶、表面层的凹底,可以高速移动磨粒,使磨粒发挥作用。
4、水可以为翻新抛光过程中降温,并可以在完成翻新抛光后的清洗工作。
5、生灰粉、熟石灰膏、磨料不与花岗岩发生化物反应,只是通过物理手段进行翻新抛光处理,花岗岩不会在翻新抛光过程中和翻新抛光后,产生不良的化学反应。
6、硅油阻隔了氧气、雨水,以及生成的亚硫酸与翻新抛光后的花岗岩的接触,从而延长花岗岩的新鲜感时间。
附图说明
图1是翻新膏涂抹在花岗岩曲面上的示意图。
图2是圆盘刷上的刷丝触及花岗岩表面上的凸顶和凹底的示意图。
图中:1、花岗岩,2、翻新膏,3、圆盘刷,31、刷丝。
具体实施方式
以下结合附图对本发明作进一步详细说明。
如图1所示,翻新膏2涂抹在花岗岩1曲面上的示意图,因花岗岩表面凸凹不平,又因翻新膏为糊膏状,所以翻新膏可以涂附在花岗岩1的层面上。
如图2所示,圆盘刷3上的刷丝31制成长短不一样的状态,刷丝31可弯曲,圆盘刷3在花岗岩表面上移动时,长短不一样并可弯曲的刷丝31可触及花岗岩表面凹底,起到对花岗岩表面凹底处的翻新和抛光处理。
实施例一:翻新凹凸不平曲面花岗岩表面层采用的花岗岩翻新膏的配制工艺。
一种翻新抛光凹凸不平曲面花岗岩的翻新粉,可对花岗岩表面进行物理方式的翻新处理,磨料选用碳化硅磨粒。
花岗岩翻新粉的配制方法:所述花岗岩翻新粉,按重量比例,其包括:生灰粉50%、碳化硅磨粒50%。
按重量比例,将50%生灰粉和50%碳化硅磨粒按比例混合均匀,生灰粉的目数为80目,磨粒的目数为80目,均匀混合后,装入容器。
花岗岩翻新膏2的配制方法:在使用前,将两倍于花岗岩翻新粉重量的水加入到花岗岩翻新粉中,调制成糊膏状,制成花岗岩翻新膏2。
将花岗岩翻新膏2均匀涂附到凹凸不平曲面花岗岩1的表面上。
实施例二:抛光凹凸不平曲面花岗岩表面层采用的花岗岩翻新膏的配制工艺。
将实施例一中的生灰粉的目数换成300目生灰粉,磨粒的目数换成300目的磨粒。
实施例三:翻新花岗岩材质的炎黄二帝雕像面部。
所述炎黄二帝雕像面部,由花岗岩材料制成。
翻新方法,包括以下步骤。
步骤一:将实施例一中的花岗岩翻新粉,按重量比,加入两倍水,调合成膏状物,制成翻新抛光凹凸不平曲面花岗岩的翻新膏2。
步骤二:将步骤一所述翻新膏2,均匀涂抹在炎黄二帝雕像面部表面层。
步骤三:将圆盘刷安装在水磨机上,手持水磨机, 圆盘刷高速旋转,对步骤二涂抹了炎黄二帝雕像面部表面层,进行翻新处理。
因离心力的作用,当所述翻新膏越用越少时,可重复步骤二的过程。
操作人员一边手持水磨机对花岗岩进行翻新抛光处理,一边打开水磨机的水龙头加水至工作面,起到降温与补水的功效。
在翻新炎黄二帝雕像的眼部、耳部、鼻孔部时,将圆盘刷的刷丝剪成长短参差不齐的形态,以使圆盘刷的刷丝的动力能传达到花岗岩1表面层的凹底处。
优选的,所述圆盘刷丝,具体材料采用锦纶高强耐磨尼龙丝浸泡了高耐磨热塑性丙烯酸树脂的刷丝,刷丝粗细度为80目。
步骤四:待花岗岩1表面的凹底处翻新抛光完成后,完全打开手持水磨机的水龙头,通过圆盘刷的旋转和水的冲洗,对炎黄二帝雕像面部进行清洗。
实施例四:抛光花岗岩材质的盘古袓始雕像面部。
所述盘古袓始雕像面部,由花岗岩材料制成。
将实施例三中的生灰粉的粒度目数换成300目的生灰粉,磨粒的粒度目数换成300目的磨粒。
所述圆盘刷丝,材料采用锦纶高强耐磨尼龙丝浸泡了高耐磨热塑性丙烯酸树脂的刷丝,刷丝粗细度为180目。
实施例五:盘古袓始雕像面部的保养方法:
所述盘古袓始雕像面部,由花岗岩材料制成。
步骤一:将硅油,涂抹在已经翻新抛光了的盘古袓始雕像面部;
步骤二:将圆盘刷安装在水磨机上,手持水磨机对涂抹了硅油的地方,用圆盘刷的高速旋转,将硅油均匀涂抹在盘古袓始雕像面部表层面的凹底和凸顶。
优选的,所述圆盘刷丝,材料采用麻丝,刷丝粗细度为300目。
优选的,所述硅油具体采用甲基硅油。
以上所述仅是本发明的优选实施方式,本发明的保护范围并不仅局限于上述实施例,凡属于本发明思路下的技术方案均属于本发明的保护范围。应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理前提下的若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (6)
1.凹凸不平曲面花岗岩的翻新抛光粉,其特征在于,按重量比例,其包括:生灰粉20-40%、磨粒60-80%,将生灰粉和磨粒按比例混合均匀,生灰粉和磨粒的目数大小相同。
2.根据权利要求1所述的凹凸不平曲面花岗岩的翻新抛光粉,其特征在于,所述磨粒所用材料的硬度大于花岗岩的硬度。
3.根据权利要求1所述的凹凸不平曲面花岗岩的翻新抛光粉,其特征在于,翻新花岗岩时,所述磨粒粒度为46目至120目的磨粒;抛光花岗岩时,所述磨粒粒度为240目至800目的磨料微粉。
4.根据权利要求1所述的翻新抛光粉的翻新抛光的方法,其特征在于,其包括以下步骤:
步骤一:在凹凸不平曲面花岗岩的翻新粉中,加入2至5倍水,调合成膏状物,制成翻新抛光凹凸不平曲面花岗岩的翻新膏;
步骤二:将步骤一所述翻新膏,均匀涂抹在被翻新抛光的凹凸不平曲面花岗岩的表层面;
步骤三:将圆盘刷安装在水磨机上,手持水磨机对步骤二涂抹了凹凸不平曲面花岗岩的翻新膏的地方,进行翻新抛光,同时打开水磨机的水龙头,加水到工作面上;
步骤四:待花岗岩表面的凹底处翻新抛光完成后,完全打开手持水磨机的水龙头,水磨机带动圆盘刷转动,对花岗岩表面进行刷洗。
5.根据权利要求4所述的凹凸不平曲面花岗岩的翻新抛光粉的翻新抛光的方法,其特征在于,所述圆盘刷的刷丝采用长短参差不齐的形态。
6.凹凸不平曲面花岗岩的保养方法,其特征在于,其包括以下步骤:
步骤一:将硅油,涂抹在已经翻新抛光的凹凸不平曲面花岗岩表层面;
步骤二:将圆盘刷安装在水磨机上,手持水磨机对涂抹了硅油的地方,在圆盘刷的旋转情况下,将硅油均匀涂抹在花岗岩表层面的凹底和凸顶。