CN110091128A - 一种轴承套圈的加工方法 - Google Patents
一种轴承套圈的加工方法 Download PDFInfo
- Publication number
- CN110091128A CN110091128A CN201910348488.XA CN201910348488A CN110091128A CN 110091128 A CN110091128 A CN 110091128A CN 201910348488 A CN201910348488 A CN 201910348488A CN 110091128 A CN110091128 A CN 110091128A
- Authority
- CN
- China
- Prior art keywords
- bearing
- material base
- ring
- bearing ring
- carried out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种轴承套圈的加工方法，包括以下步骤：步骤一：对现有的轴承钢材料，进行检验，挑选质量合格的，备用；步骤二：根据所需轴承套圈的尺寸，对步骤一种合格的轴承钢材料进行下料得到料坯；步骤三：对步骤二中的料坯进行超声波探伤；步骤四：对步骤三中经过超声波探伤的料坯进行退火处理，去除锻造能力；步骤五：对退火处理后的料坯进行碾环得到轴承套圈毛坯；步骤六：对步骤五中的轴承套圈毛坯进行车削加工；步骤七：对车削后的轴承套圈毛坯进行热处理；步骤八：对热处理后的轴承套圈毛坯进行磨削；步骤九：对磨削后的套圈进行清洗、检验即得成品。本发明可以缩短轴承套圈的生产周期，降低轴承套圈的生产成本。
Description
技术领域
本发明涉及一种轴承，具体是一种轴承套圈的加工方法，属于轴承生产技术领域。
背景技术
轴承是当代机械设备中一种重要零部件，它的主要功能是支撑机械旋转体，降低其运动过程中的摩擦系数，并保证其回转精度。
轴承套圈是轴承的基本组成部分，其加工质量和加工效率决定着轴承的质量和效率，现有的加工轴承套圈的存在着加工工艺复杂、加工时间长、制造成本高的问题。
发明内容
针对现有技术的不足，提供本发明一种轴承套圈的加工方法，可以缩短轴承套圈的生产周期，降低轴承套圈的生产成本。
一种轴承套圈的加工方法，其特征在于，包括以下步骤：
步骤一：对现有的轴承钢材料，进行检验，挑选质量合格的，备用；
步骤二：根据所需轴承套圈的尺寸，对步骤一种合格的轴承钢材料进行下料得到料坯；
步骤三：对步骤二中的料坯进行超声波探伤；
步骤四：对步骤三中经过超声波探伤的料坯进行退火处理，去除锻造能力；
步骤五：对退火处理后的料坯进行碾环得到轴承套圈毛坯；
步骤六：对步骤五中的轴承套圈毛坯进行车削加工；
步骤七：对车削后的轴承套圈毛坯进行热处理；
步骤八：对热处理后的轴承套圈毛坯进行磨削；
步骤九：对磨削后的套圈进行清洗、检验即得成品。
步骤四中退火的温度在180-220℃。
步骤五中碾环的温度为1100-1250℃。
有益效果：本发明可以缩短轴承套圈的生产周期，降低轴承套圈的生产成本，并且可以沿长轴承套圈的使用寿命。
具体实施方式
下面通过实施例对本发明做进一步详细说明。
一种轴承套圈的加工方法，包括以下步骤：
步骤一：对现有的轴承钢材料，进行检验，挑选质量合格的，备用；
步骤二：根据所需轴承套圈的尺寸，对步骤一种合格的轴承钢材料进行下料得到料坯；
步骤三：对步骤二中的料坯进行超声波探伤；
步骤四：对步骤三中经过超声波探伤的料坯进行退火处理，去除锻造能力；
步骤五：对退火处理后的料坯进行碾环得到轴承套圈毛坯；
步骤六：对步骤五中的轴承套圈毛坯进行车削加工；
步骤七：对车削后的轴承套圈毛坯进行热处理；
步骤八：对热处理后的轴承套圈毛坯进行磨削；
步骤九：对磨削后的套圈进行清洗、检验即得成品。
步骤四中退火的温度在180-220℃。
步骤五中碾环的温度为1100-1250℃。
Claims (3)
1.一种轴承套圈的加工方法，其特征在于，包括以下步骤：
步骤一：对现有的轴承钢材料，进行检验，挑选质量合格的，备用；
步骤二：根据所需轴承套圈的尺寸，对步骤一种合格的轴承钢材料进行下料得到料坯；
步骤三：对步骤二中的料坯进行超声波探伤；
步骤四：对步骤三中经过超声波探伤的料坯进行退火处理，去除锻造能力；
步骤五：对退火处理后的料坯进行碾环得到轴承套圈毛坯；
步骤六：对步骤五中的轴承套圈毛坯进行车削加工；
步骤七：对车削后的轴承套圈毛坯进行热处理；
步骤八：对热处理后的轴承套圈毛坯进行磨削；
步骤九：对磨削后的套圈进行清洗、检验即得成品。
2.如权利要求1所述的一种轴承套圈的加工方法，其特征在于，步骤四中退火的温度在180-220℃。
3.如权利要求2所述的一种轴承套圈的加工方法，其特征在于，步骤五中碾环的温度为1100-1250℃。