CN110038583B - 一种加氢精制催化剂的制备方法 - Google Patents
一种加氢精制催化剂的制备方法 Download PDFInfo
- Publication number
- CN110038583B CN110038583B CN201810037417.3A CN201810037417A CN110038583B CN 110038583 B CN110038583 B CN 110038583B CN 201810037417 A CN201810037417 A CN 201810037417A CN 110038583 B CN110038583 B CN 110038583B
- Authority
- CN
- China
- Prior art keywords
- catalyst
- mixed solution
- aging
- weight
- reaction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
催化剂编号 | A | B | C | D | E | F | G | H |
Ni,以NiO计,wt% | 19 | 24 | 16 | 20 | 19 | 19 | 19 | 19 |
W,以WO<sub>3</sub>计,wt% | 35 | 32 | 36 | 32 | 35 | 35 | 35 | 35 |
Mo,以MoO<sub>3</sub>计,wt% | 18 | 16 | 20 | 17 | 18 | 18 | 18 | 18 |
Al,以Al<sub>2</sub>O<sub>3</sub>计,wt% | 余量 | 余量 | 余量 | 余量 | 余量 | 余量 | 余量 | 余量 |
其它/wt% | - | ZrO<sub>2</sub>/3.0 | - | - | - | - | - | - |
比表面积,m<sup>2</sup>/g | 205 | 199 | 192 | 203 | 175 | 179 | 219 | 225 |
孔容,mL/g | 0.314 | 0.301 | 0.297 | 0.303 | 0.271 | 0.273 | 0.325 | 0.334 |
机械强度,N/mm | 17.6 | 17.9 | 17.8 | 17.6 | 16.7 | 17.2 | 15.8 | 14.7 |
催化剂编号 | 平均堆叠层数N<sub>A</sub> | 平均长度L<sub>A</sub>,nm |
A | 8.41 | 4.92 |
B | 8.32 | 4.95 |
C | 8.35 | 4.95 |
D | 8.30 | 4.97 |
E | 4.88 | 7.92 |
F | 5.03 | 8.01 |
G | 5.97 | 7. 85 |
H | 5.93 | 7. 62 |
催化剂编号 | A | B | C | D | E | F | G | H |
片层数分布,% | ||||||||
<4.0层 | 4.09 | 4.52 | 4.71 | 4.58 | 30.22 | 32.56 | 24.98 | 20.56 |
4.0至小于7.0层 | 10.05 | 10.57 | 10.22 | 10.16 | 66.22 | 64.98 | 71.26 | 74.26 |
7.0~9.0层 | 74.65 | 74.18 | 74.33 | 74.41 | 3.56 | 2.46 | 3.76 | 5.18 |
>9.0层 | 11.21 | 10.63 | 10.74 | 10.85 | - | - | - | - |
长度分布,% | ||||||||
<2.0nm | 6.48 | 6.31 | 6.38 | 6.74 | 1.19 | 1.23 | 1.09 | 1.54 |
2.0至小于4.0nm | 13.58 | 13.46 | 13.24 | 13.37 | 4.58 | 5.26 | 4.98 | 4.74 |
4.0~6.0nm | 74.67 | 74.61 | 74.66 | 74.83 | 8.27 | 8.56 | 8.69 | 8.19 |
大于6.0至8.0nm | 4.35 | 4.52 | 4.84 | 4.11 | 65.17 | 64.21 | 65.59 | 66.58 |
>8.0nm | 0.92 | 1.10 | 0.88 | 0.95 | 20.79 | 20.74 | 19.65 | 18.95 |
项目 | 分析结果 |
密度(20℃),g/cm<sup>3</sup> | 0.9025 |
馏程范围,℃ | 162-375 |
S,µg/g | 5026 |
N,µg/g | 1024 |
催化剂编号 | A | B | C | D |
生成油密度(20℃),g/cm<sup>3</sup> | 0.8695 | 0.8697 | 0.8701 | 0.8699 |
馏程范围,℃ | 171-371 | 170-371 | 172-372 | 173-372 |
S,µg/g | 7.9 | 8.3 | 8.4 | 8.6 |
N,µg/g | 8.1 | 8.5 | 8.7 | 8.8 |
催化剂编号 | E | F | G | H |
生成油密度(20℃),g/cm<sup>3</sup> | 0.8856 | 0.8883 | 0.8804 | 0.8812 |
馏程范围,℃ | 173-374 | 172-374 | 176-373 | 175-373 |
S,µg/g | 265.6 | 260.2 | 217.5 | 228.6 |
N,µg/g | 78.2 | 74.8 | 60.9 | 62.1 |
催化剂编号 | A | B | C | D | E |
加氢精制油中硫含量,µg/g | 7.9 | 8.3 | 8.4 | 8.6 | 265.6 |
C<sub>1</sub>-DBT,µg/g | 0 | 0 | 0 | 0 | 48.3 |
4- BMDBT,µg/g | 1.7 | 1.8 | 1.8 | 1.8 | 69.2 |
6-BMDBT,µg/g | 1.9 | 2.0 | 2.0 | 2.1 | 65.6 |
4,6- BMDBT,µg/g | 4.3 | 4.5 | 4.6 | 4.7 | 82.5 |
催化剂编号 | F | G | H |
加氢精制油中硫含量,µg/g | 260.2 | 217.5 | 228.6 |
C<sub>1</sub>-DBT,µg/g | 40.7 | 33.4 | 37.8 |
4- BMDBT,µg/g | 61.5 | 54.9 | 56.5 |
6-BMDBT,µg/g | 68.4 | 56.3 | 60.3 |
4,6- BMDBT,µg/g | 89.6 | 72.9 | 74.0 |
催化剂编号 | A | B | C | D | E |
加氢精制油中氮含量,µg/g | 8.1 | 8.5 | 8.7 | 8.8 | 78.2 |
1- MCB,µg/g | 1.6 | 1.7 | 1.7 | 1.7 | 28.3 |
1,8-BMCB,µg/g | 2.3 | 2.4 | 2.5 | 2.5 | 34.9 |
1,4,8- TMCB,µg/g | 4.2 | 4.4 | 4.5 | 4.6 | 15.0 |
催化剂编号 | F | G | H |
加氢精制油中氮含量,µg/g | 74.8 | 60.9 | 62.1 |
1-MCB,µg/g | 24.2 | 18.1 | 17.8 |
1,8-BMCB,µg/g | 35.3 | 28.3 | 29.5 |
1,4,8-TMCB,µg/g | 15.3 | 14.5 | 14.8 |
Claims (37)