CN109928633A - 一种高温陶瓷透明釉 - Google Patents
一种高温陶瓷透明釉 Download PDFInfo
- Publication number
- CN109928633A CN109928633A CN201711355844.8A CN201711355844A CN109928633A CN 109928633 A CN109928633 A CN 109928633A CN 201711355844 A CN201711355844 A CN 201711355844A CN 109928633 A CN109928633 A CN 109928633A
- Authority
- CN
- China
- Prior art keywords
- clear frit
- refractory ceramics
- ceramics clear
- high temperature
- ingredient
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种高温陶瓷透明釉,其特征在于:采用天然矿物原料及工业化工原料,按照化学组成百分比:SiO2 52.89%、Al2O3 15.09%、B2O3 18.45%、Li2O 1.19%、Na2O 3.16%、K2O 2.13%、MgO 2.40%、CaO 2.52%、ZnO 2.17%,经配料、研磨、高温熔制、淬冷、球磨、过筛工序获得高温陶瓷透明釉。本发明通过成分的配比控制,解决了化学稳定性、光泽度、表面张力、膨胀系数等问题,得到了光亮平整、流动效果良好,且与瓷胎匹配良好的高温陶瓷透明釉。
Description
技术领域
本发明属无机非金属材料(陶瓷)领域,具体涉及一种高温陶瓷透明釉。
背景技术
传统高温陶瓷透明釉的主要熔剂是铅粉、牙硝(硝酸钾);氧化铅、硝酸钾是良好的助熔剂,不仅具有高折射率可提高釉面光泽度,同时其高温粘度小,使釉面光亮平整、色彩鲜明亮丽,流动效果良好,具艺术机理效果。但传统高温陶瓷透明釉含有大量对人体有害的铅元素等,面对当今国内外对陶瓷产品铅、镉溶出量限制越来越严的要求,将无法满足新的需求。
发明内容
本发明要解决的技术问题是提供一种工艺简单、绿色环保、耐酸、耐碱性优良、光泽度高的高温陶瓷透明釉。
本发明通过以下技术方案予以实现:一种高温陶瓷透明釉,采用天然矿物原料及工业化工原料,按照化学组成百分比:SiO2 52.89%、Al2O3 15.09%、B2O3 18.45%、Li2O1.19%、Na2O 3.16%、K2O 2.13%、MgO 2.40%、CaO 2.52%、ZnO 2.17%,经配料、研磨、高温熔制、淬冷、球磨、过筛工序获得高温陶瓷透明釉。
所述高温熔制工序的参数为:升温速率为5℃/min,最高熔制温度为1300℃,保温时间为30min。
所述过筛工序为:过300目筛,筛余为0。
故本发明采用不含对人体有毒害的铅、镉、砷、铋等元素的天然矿物原料及工业化工原料,用硼与钾等碱金属复合替代铅,引入降低膨胀系数的氧化物组分及提高折射率的氧化物组分,解决了化学稳定性、光泽度、表面张力、膨胀系数等问题,得到了光亮平整、流动效果良好,且与瓷胎匹配良好的高温陶瓷透明釉,具有广阔的应用前景。
具体实施方式
为更进一步阐述本发明、为达成预定发明目的所采取的技术手段及功效,以下结合较佳实施例,对本发明进行详细说明:
实施例1
步骤一:按化学组成百分比:SiO2 52.89%、Al2O3 15.09%、B2O3 18.45%、Li2O 1.19%、Na2O 3.16%、K2O 2.13%、MgO 2.40%、CaO 2.52%、ZnO 2.17%,进行配料;
步骤二:将步骤一的原料混合并研磨均匀后,装入刚玉坩埚中;
步骤三:将刚玉坩埚放入电炉中,按5℃/min的速率升温,升温至1300℃,并保温30min;
步骤四:将淬冷后的颗粒状熔块放入球磨罐中,球磨后过300目筛,筛余为0,经干燥后获得高温陶瓷透明釉粉末备用;
步骤五:将高温陶瓷透明釉粉末与水按重量比2:1拌合均匀后,按厚度0.7mm涂覆在平瓷板上,干燥后放入电炉彩烤,按5℃/min的速率升温,升温至1290℃,经自然冷却获得样品,彩烤后样品经检测,其光泽度为85.9%;耐酸、耐碱性能为A级;铅含量、镉含量低于标准。
Claims (3)
1.一种高温陶瓷透明釉,其特征在于:采用天然矿物原料及工业化工原料,按照化学组成百分比:SiO2 52.89%、Al2O3 15.09%、B2O3 18.45%、Li2O 1.19%、Na2O 3.16%、K2O 2.13%、MgO 2.40%、CaO 2.52%、ZnO 2.17%,经配料、研磨、高温熔制、淬冷、球磨、过筛工序获得高温陶瓷透明釉。
2.根据权利要求1所述的高温陶瓷透明釉,其特征在于:所述高温熔制工序的参数为:升温速率为5℃/min,最高熔制温度为1300℃,保温时间为30min。
3.根据权利要求1所述的高温陶瓷透明釉,其特征在于:所述过筛工序为:过300目筛,筛余为0。