CN107915406A - 一种耐磨低收缩率釉料 - Google Patents

一种耐磨低收缩率釉料 Download PDF

Info

Publication number
CN107915406A
CN107915406A CN201711234443.7A CN201711234443A CN107915406A CN 107915406 A CN107915406 A CN 107915406A CN 201711234443 A CN201711234443 A CN 201711234443A CN 107915406 A CN107915406 A CN 107915406A
Authority
CN
China
Prior art keywords
parts
glaze
wear
colorant
shrinkage
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711234443.7A
Other languages
English (en)
Inventor
黄军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201711234443.7A priority Critical patent/CN107915406A/zh
Publication of CN107915406A publication Critical patent/CN107915406A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐磨低收缩率釉料，由以下重量份的各组分组成:钾长石 25‑38份；方解石 10‑15份；铝粉 7‑12份；色料 3‑5份；气相二氧化硅 13‑20份；碳化硅 3‑6份；铝矾土 2‑4份；膨润土 21‑26份；本发明釉料根据需要与适当的水混合调成泥状釉料通过蘸釉、荡釉、浇釉、刷釉、喷釉等工序涂覆在陶瓷坯体上烧结，具有耐磨、低收缩率的特点。

Description

一种耐磨低收缩率釉料
技术领域
本发明涉及一种耐磨低收缩率釉料。
背景技术
釉是覆盖在瓷制品表面的无色或有色的玻璃质薄层或者是玻璃体与晶体的混合层，是通过釉料基础配方和水、色料等制 成的具有高强度和高粘度的材料。釉附着在瓷制品表面，可改善瓷制品性能，如能增加瓷制品的机械强度、热稳定性和电介强度等。
釉的种类很多，按坯体类分，可分为瓷釉、陶釉及火石器釉等，按烧成温度可分为高温釉、低温釉，按外表特征可分为 透明釉、乳浊釉、颜色釉、有光釉、无光釉、裂纹釉(开片)、 结晶釉等，按釉料组成可分为石灰釉、长石釉、铅釉、无铅釉、 硼釉、铅硼釉等。
目前现有的釉料作存在的缺点是耐磨性差，收缩率大，影响瓷器的耐用性及良品率。
发明内容
本发明所要解决的技术问题是，克服以上现有技术的缺点：提供一种低收缩率、耐磨的釉料。
本发明的技术解决方案如下：一种耐磨低收缩率釉料，由以下重量份的各组分组成:
钾长石 25-38份；
方解石 10-15份；
铝粉 7-12份；
色料 3-5份；
气相二氧化硅 13-20份；
碳化硅 3-6份；
铝矾土 2-4份；
膨润土 21-26份。
作为最优配比，其由以下重量份的各组分组成:
钾长石 30份；
方解石 12份；
铝粉 7份；
色料 3份；
气相二氧化硅 20份；
碳化硅 3份；
铝矾土 2份；
膨润土 26份。
其配制方法为：按上述重量份比例将钾长石 、方解石 、铝粉 、色料、气相二氧化硅、碳化硅 、铝矾土 、膨润土混合球磨至360-500目即可。
所述色料为粉末状陶瓷色料。
本发明的有益效果是：本发明釉料根据需要与适当的水混合调成泥状釉料通过蘸釉、荡釉、浇釉、刷釉、喷釉等工序涂覆在陶瓷坯体上烧结，具有耐磨、低收缩率的特点。
具体实施方式
下面用具体实施例对本发明做进一步详细说明，但本发明不仅局限于以下具体实施例。
实施例一
一种耐磨低收缩率釉料，由以下重量份的各组分组成:
钾长石 25份；
方解石 10份；
铝粉 7份；
色料 3份；
气相二氧化硅 13份；
碳化硅 3份；
铝矾土 2份；
膨润土 21份。
其配制方法为：按上述重量份比例将钾长石 、方解石 、铝粉 、色料、气相二氧化硅、碳化硅 、铝矾土 、膨润土混合球磨至360-500目即可。
实施例二
一种耐磨低收缩率釉料，由以下重量份的各组分组成:
钾长石 38份；
方解石 15份；
铝粉 12份；
色料 5份；
气相二氧化硅 20份；
碳化硅 6份；
铝矾土4份；
膨润土 26份。
其配制方法为：按上述重量份比例将钾长石 、方解石 、铝粉 、色料、气相二氧化硅、碳化硅 、铝矾土 、膨润土混合球磨至360-500目即可。
实施例三
一种耐磨低收缩率釉料，由以下重量份的各组分组成:
钾长石 30份；
方解石 15份；
铝粉 7份；
色料 5份；
气相二氧化硅20份；
碳化硅 3份；
铝矾土 2份；
膨润土 26份。
其配制方法为：按上述重量份比例将钾长石 、方解石 、铝粉 、色料、气相二氧化硅、碳化硅 、铝矾土 、膨润土混合球磨至360-500目即可。
实施例四
一种耐磨低收缩率釉料，由以下重量份的各组分组成:
钾长石 30份；
方解石 12份；
铝粉 7份；
色料 3份；
气相二氧化硅 20份；
碳化硅 3份；
铝矾土 2份；
膨润土 26份。
其配制方法为：按上述重量份比例将钾长石 、方解石 、铝粉 、色料、气相二氧化硅、碳化硅 、铝矾土 、膨润土混合球磨至360-500目即可。
实施例五
一种耐磨低收缩率釉料，由以下重量份的各组分组成:
钾长石 30份；
方解石 12份；
铝粉 8份；
色料 4份；
气相二氧化硅 15份；
碳化硅 3份；
铝矾土 3份；
膨润土 25份。
其配制方法为：按上述重量份比例将钾长石 、方解石 、铝粉 、色料、气相二氧化硅、碳化硅 、铝矾土 、膨润土混合球磨至360-500目即可。
所述色料为粉末状陶瓷色料。
使用时根据需要与重量百分比20-35%水混合调成泥状釉料通过蘸釉、荡釉、浇釉、刷釉、喷釉等工序涂覆在陶瓷坯体上烧结，本发明的适合烧结温度为1020-1100℃，具有低脆性、低收缩率的特点。
以上仅是本发明的特征实施范例，对本发明保护范围不构成任何限制。凡采用同等交换或者等效替换而形成的技术方案，均落在本发明权利保护范围之内。

Claims (4)

1.一种耐磨低收缩率釉料，其特征在于：由以下重量份的各组分组成:
钾长石 25-38份；
方解石 10-15份；
铝粉 7-12份；
色料 3-5份；
气相二氧化硅 13-20份；
碳化硅 3-6份；
铝矾土 2-4份；
膨润土 21-26份。
2.根据权利要求1所述的耐磨低收缩率釉料，其特征在于：由以下重量份的各组分组成:
钾长石 30份；
方解石 12份；
铝粉 7份；
色料 3份；
气相二氧化硅 20份；
碳化硅 3份；
铝矾土 2份；
膨润土 26份。
3.根据权利要求1所述的耐磨低收缩率釉料，其特征在于： 其配制方法为：按上述重量份比例将钾长石 、方解石 、铝粉 、色料、气相二氧化硅、碳化硅 、铝矾土 、膨润土混合球磨至360-500目即可。
4.根据权利要求1所述的耐磨低收缩率釉料，其特征在于：所述色料为粉末状陶瓷色料。
CN201711234443.7A 2017-11-30 2017-11-30 一种耐磨低收缩率釉料 Pending CN107915406A (zh)