CN1098284A - 透明弹性理疗罐及其制造方法 - Google Patents
透明弹性理疗罐及其制造方法 Download PDFInfo
- Publication number
- CN1098284A CN1098284A CN 94105777 CN94105777A CN1098284A CN 1098284 A CN1098284 A CN 1098284A CN 94105777 CN94105777 CN 94105777 CN 94105777 A CN94105777 A CN 94105777A CN 1098284 A CN1098284 A CN 1098284A
- Authority
- CN
- China
- Prior art keywords
- parts
- districts
- transparent
- cup
- lubricant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于用高聚合度PVC、SBS、硅橡胶等透
明弹性体制成供理疗用的理疗罐,其特点为罐体柔
软,不用点火就可产生负压,故绝不会造成烫伤,负压
可通过变形量的大小有效调节;另外,本发明透明,使
用时医生可清晰地观察到患部瘀血情况,与传统玻
璃、陶、竹等罐相比,不会烫伤,也不会划伤,操作方
便、安全。
Description
本发明属于用高聚合度PVC、SBS、硅橡胶等透明弹性体制成的供理疗用的理疗罐。
拔火罐是祖国医学的优秀遗产之一,是利用在竹、陶、玻璃罐内点火消耗氧气造成负压而吸附在人体一定部位(穴位)使局部产生瘀血现象而达到理疗效果。俗话说“扎针拔罐,病好一半”,拔罐能改进局部血循环,促进病理分泌物的吸收,可治疗局部慢性炎症,软组织劳损、胃肠疾病、哮喘以及痛经等20多种疾病(详见《中医学》)。它施用方便,费用低廉,在民间流传已久,而在医疗费用日趋高昂的今天更具现实意义。
但是传统的拔火罐也存其严重缺陷,即负压之产生必须通过在罐内点火,造成操作不便,易产生烫伤、划伤等,尤其用玻璃制成的罐体,更易产生破口对人体造成伤害,这就限制了“负压理疗”这一祖国医学瑰宝的进一步发扬光大。
本发明的目的就是针对现有技术的不足之处,设计一种透明弹性理疗罐,利用其罐体的弹性变形排出空气而形成负压,吸附到穴位上从而达到理疗效果。
本发明的技术解决方案是利用高聚合度PVC、SBS硅橡胶等透明弹性体制成的理疗罐,配方如下(以重量份计):
一、用PVC生产理疗罐
高聚合度PVC 100份
MBS 6~20份
DOP(邻苯二甲酸二辛酯) 80~150份
DBP(邻苯二甲酸二丁酯) 0~70份
透明稳定剂 2~6份
加工助剂 0~3份
润滑剂 0.5~2份
着色剂 0~0.1份
二、用SBS生产理疗罐
SBS 100份
环烧油 0~50份
PS 0~30份
抗氧剂 0~1份
润滑剂 0.1~1份
造粒温度一区80℃~100℃,二区130℃~150℃,三区170℃~180℃,四区170℃~185℃,机头170℃~180℃,造粒机转速15~50rpm;成型各区温度用PVC生产比造粒温度高20℃~30℃,用SBS生产比造粒温度高10℃。
本发明的基本形状仍为口小腹大的中空结构。
本发明由于采用透明弹性体原料制成,故罐体柔软,不用点火就可产生负压,且绝不会造成烫伤,负压可通过变形量的大小有效调节。由于本发明是透明的,使用时医生可清晰地观察到患部的瘀血情况,正确地掌握治疗程度,因此本发明与传统玻璃、陶、竹、等罐相比,有不会烫伤,不会划(割)伤,操作简便、安全,负压可调,可观察治疗进度等诸多优点。
本发明实施例:
一、用PVC生产理疗罐
例1.PVC【P(平均聚合度)=4000】 100份
MBS(BTA) 8份
DOP 80份
DBP 70份
透明稳定剂(有机锡) 5份
加工稳定剂(ACR-201) 3份
润滑剂(G-16) 0.3份
润滑剂(EBS) 0.8份
着色剂(群青) 0.01份
将上述物料在高速混合机中混合,至温度达110℃出料,在转速为20rpm单螺杆造粒机中造粒,造粒温度为一区80℃,二区130℃,三区170℃,四区170℃,机头170℃,经切粒,风冷后进行中空吹塑成型,成型温度一区100℃,二区150℃,三区190℃,四区190℃,机头190℃,检验,成品。
例2.PVC(P=4000) 100份
MBS(BTA) 20份
DOP 140份
DBP 10份
透明稳定剂(金属皂) 6份
加工助剂(ACR-201) 3份
润滑剂(G-16) 0.3份
润滑剂(EBS) 0.8份
着色剂(群青) 0.01份
将上述物料在高速混合机中混合,至温度达110℃出料,在转速为50rpm双螺杆造粒机中造粒,造粒温度为一区100℃,二区150℃,三区180℃,四区185℃,机头180℃,经切粒,风冷后进行注塑成型,成型温度一区130℃,二区180℃,三区210℃,四区215℃,机头温度200℃,检验,成品。
二、用SBS生产理疗罐
例3.SBS(YH-792) 100份
环烷油 50份
PS(透明) 15份
抗氧剂(B215) 0.5份
润滑剂(EBS) 1.0份
工艺步骤同例1,造粒温度一区90℃,二区140℃,三区175℃,四区180℃,机头175℃,经切粒,风冷后进行中空吹塑机成型,成型温度一区100℃,二区150℃,三区185℃,四区190℃,机头185℃,检验,成品。
Claims (3)
1、一种透明弹性理疗罐,其特征在于配方成份如下(以重量计):
(1)高聚合度PVC(P=4000) 100份
MBS 6~20份
DOP 80~150份
DBP 0~70份
透明稳定剂 2~6份
加工助剂 0~3份
润滑剂 0.5~2份
着色剂 0~0.1份
(2)SBS 100份
环烷油 0~50份
PS 0~30份
抗氧剂 0~1份
润滑剂 0.1~1份
2、根据权利要求1所述的理疗罐,其特征在于透明稳定剂为有机锡和金属皂,润滑剂为EBS。
3、一种透明弹性理疗罐的制备方法,其特征在于工艺流程为:原料称量→混合→造粒→切粒、风冷→成型(中空吹塑、注塑)→检验→成品。
造粒温度一区80℃~100℃,二区130℃~150℃,三区170℃~180℃,四区170℃~185℃,机头170℃~180℃,造粒机转速15~50rpm;成型各区温度用PVC生产比造粒温度高20℃~30℃,用SBS生产比造粒温度高10℃。