CN109735187A - 一种白色uv纳米金属卷材涂料 - Google Patents
一种白色uv纳米金属卷材涂料 Download PDFInfo
- Publication number
- CN109735187A CN109735187A CN201811646795.8A CN201811646795A CN109735187A CN 109735187 A CN109735187 A CN 109735187A CN 201811646795 A CN201811646795 A CN 201811646795A CN 109735187 A CN109735187 A CN 109735187A
- Authority
- CN
- China
- Prior art keywords
- white
- nano metal
- coil coating
- modified
- metal coil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种白色UV纳米金属卷材涂料，属于涂料技术领域。按重量百分比计原料组成：改性纯丙烯酸树脂：10％～30％，改性聚酯丙烯酸酯：5％～20％，改性聚氨酯丙烯酸酯：10％～25％，改性环氧丙烯酸酯：5％～10％，TPGDA三丙二醇二丙烯酸酯：5％～15％，TMPTA三丙烯酸丙烷三甲醇酯：5％～15％，光引发剂：3％～6％，消泡剂：0.1％～0.8％，流平剂：0.1％～0.8％，纳米氧化锆：0.3％～1％，白色膏UJ‑100及不可避免的杂质：余量。优点在于：添加了可提高金属表面附着力的改性聚氨酯丙烯酸酯，以及可提高固化膜柔韧性及对颜料润湿性好的树脂、光引发剂和各种助剂，这些物质通过发生聚合反应形成交联网格再固化成膜，增强了对金属表面的附着力，同时改善了漆膜的柔韧性以及提高了彩色涂层的鲜艳度。
Description
技术领域
本发明属于涂料技术领域，具体涉及一种白色UV纳米金属卷材涂料。
背景技术
UV纳米金属卷材涂料用于钢材防锈、彩涂钢板、铝合金门窗保护及金属饰板制造等方面。金属表面涂装UV涂料以后既美观又可以保护金属基材表面。由于金属自身易腐蚀且易受外部环境磨损、刮伤等系列问题，所以通过使用UV纳米金属卷材涂料可以改善以上出现的问题。
发明内容
本发明的目的是提供一种白色UV纳米金属卷材涂料，具有高附着力及柔韧性。
本发明的白色UV纳米金属卷材涂料，按重量百分比计，由以下原料组成：
优选的，按重量百分比计，由以下原料组成：
更为优选的，按重量百分比计，由以下原料组成：
其中，所述改性环氧丙烯酸酯采用胺改性环氧丙烯酸酯、脂肪酸改性环氧丙烯酸酯、磷酸改性环氧丙烯酸酯、聚氨酯改性环氧丙烯酸酯、有机硅改性环氧丙烯酸酯中的一种；
其中，所述光引发剂采用Irgacure-1000、KIP-150、BP、1173、184、中的一种；
其中，所述消泡剂采用Foamex-810、Foamex-N、Airex-920、Efka-2720中的一种；
其中，所述流平剂采用德谦-488、迪高-435、BYK-333、BYK-361中的一种。
它包括如下制备步骤：先将上述重量百分比的改性纯丙烯酸酯、改性聚酯丙烯酸酯、改性聚氨酯丙烯酸酯、改性环氧丙烯酸脂、TPGDA(三丙二醇二丙烯酸酯)、TMPTA(三丙烯酸丙烷三甲醇酯)加入到容器中，充分搅拌，再加入上述重量百分比的光引发剂、消泡剂、流平剂、纳米氧化锆，充分搅拌，最后加入适量的白色膏UJ-100，充分搅拌后再用纳米球磨机进行球磨细化即得一种白色的UV纳米金属卷材涂料。
改性聚酯丙烯酸酯，具有低气味、低刺激性、较好的柔韧性和颜料润湿性，适用于彩色涂料。
改性聚氨酯丙烯酸酯，其耐黄变性佳、拉伸伸长率极佳，主要提高固化膜的柔韧性，而且对促进附着力也起到一定作用。
改性纯丙烯酸树脂，具有极好的耐变黄性、良好的柔韧性，对各种基材都有较好的附着力，配合其它树脂来增进对基材的附着力和涂层间的附着力。
改性环氧丙烯酸酯，可提高光固化速率，改善涂层脆性、附着力和对颜料的润湿性。
流平剂和消泡剂，是涂料调配中不可缺少的助剂。
本发明的有益效果为：本发明的UV纳米金属卷材涂料中添加了可提高金属表面附着力的改性聚氨酯丙烯酸酯，以及可提高固化膜柔韧性及对颜料润湿性好的树脂、光引发剂和各种助剂，这些物质通过发生聚合反应形成交联网格再固化成膜，增强了对金属表面的附着力，同时改善了漆膜的柔韧性以及提高了彩色涂层的鲜艳度。
具体实施方式：
下面结合实施例多本发明作进一步说明。
实施例1：
一种白色UV纳米金属卷材涂料其组分及其重量百分比为：
它的制备过程如下：先将上述重量百分比的改性纯丙烯酸酯、改性聚酯丙烯酸酯、改性聚氨酯丙烯酸酯、磷酸改性环氧丙烯酸脂、TPGDA(三丙二醇二丙烯酸酯)、TMPTA(三丙烯酸丙烷三甲醇酯)加入到容器中，充分搅拌，再加入上述重量百分比的光引发剂(Irgacure-1000)、消泡剂(Foamex-810)、流平剂(德谦-488)、纳米氧化锆，充分搅拌，最后加入适量的白色膏UJ-100，充分搅拌后再用纳米球磨机进行球磨细化即得一种白色的UV纳米金属卷材涂料。
以上所述仅为本发明较佳的实施方式，但本发明的保护范围并不局限于此。
Claims (5)
1.一种白色UV纳米金属卷材涂料，其特征在于，按重量百分比计，由以下原料组成：
2.根据权利要求1所述的优选的白色UV纳米金属卷材涂料，其特征在于，按重量百分比计，由以下原料组成：
3.根据权利要求1所述的优选的白色UV纳米金属卷材涂料，其特征在于，按重量百分比计，由以下原料组成：
4.根据权利要求1-3任意一项所述的优选的白色UV纳米金属卷材涂料，其特征在于，
所述改性环氧丙烯酸酯采用胺改性环氧丙烯酸酯、脂肪酸改性环氧丙烯酸酯、磷酸改性环氧丙烯酸酯、聚氨酯改性环氧丙烯酸酯、有机硅改性环氧丙烯酸酯中的一种；
所述光引发剂采用Irgacure-1000、KIP-150、BP、1173、184、中的一种；
所述消泡剂采用Foamex-810、Foamex-N、Airex-920、Efka-2720中的一种；
所述流平剂采用德谦-488、迪高-435、BYK-333、BYK-361中的一种。
5.根据权利要求1所述的优选的白色UV纳米金属卷材涂料，其特征在于，该涂料制备步骤：先将上述重量百分比的改性纯丙烯酸酯、改性聚酯丙烯酸酯、改性聚氨酯丙烯酸酯、改性环氧丙烯酸脂、TPGDA三丙二醇二丙烯酸酯、TMPTA三丙烯酸丙烷三甲醇酯加入到容器中，搅拌，再加入上述重量百分比的光引发剂、消泡剂、流平剂、纳米氧化锆，充分搅拌，最后加入适量的白色膏UJ-100，搅拌后再用纳米球磨机进行球磨细化即得一种白色的UV纳米金属卷材涂料。