CN109735185A - A kind of novel water-in-water multicolor coating and preparation method thereof - Google Patents
A kind of novel water-in-water multicolor coating and preparation method thereof Download PDFInfo
- Publication number
- CN109735185A CN109735185A CN201811614344.6A CN201811614344A CN109735185A CN 109735185 A CN109735185 A CN 109735185A CN 201811614344 A CN201811614344 A CN 201811614344A CN 109735185 A CN109735185 A CN 109735185A
- Authority
- CN
- China
- Prior art keywords
- water
- gras
- deionized water
- multicolor coating
- pregel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of novel water-in-water multicolor coating, the water-in-water multicolor coating is comprised the following components in parts by weight: (1) A expects: deionized water 1~2, preservative 0.2~0.4, ethylene glycol 1~1.4, coalescing agent 0.3~0.7, silicone acrylic emulsion 13~17, defoaming agent 0.1~0.3, multifunctional assistant 0.1~0.2；(2) B expects: deionized water 1~1.5, alkali swollen thickener 0.05~0.1；(3) C expects: particle mixed liquor 75~85.A kind of preparation method of novel water-in-water multicolor coating, a kind of preparation method of novel water-in-water multicolor coating include the following steps: that (1) prepares GRAS B pregel；(2) color-mixed base paint is prepared；(3) particle mixed liquor is prepared；(4) with paint.The present invention can solve that the existing water-water coating shelf-life is shorter, and viscosity is unstable, there are problems that rear thickening behavior.
Description
Technical field
The invention belongs to technical field of coatings more particularly to a kind of novel water-in-water multicolor coating and preparation method thereof.
Background technique
Raising with the fast development and people of Architectural Paint in China industry to finishing requirements, water-in-water multicolor coating by
To more and more concerns, multicolor finish can replace the stone materials such as granite as exterior coating, reduce the exploitation to lithotome,
It plays a protective role to environment, the demand of development is met with the characteristics of " environmental protection, energy conservation are graceful ".In addition, the colorful painting of water-water
Expect complete Water-borne modification, VOC content is low, and the color grain of different colours and size can be configured according to the demand of people, and spraying can
Obtain different marmorean decorative pattern figure effects.
There are many systems for water-in-water multicolor coating, and current most popular system is cellulose ether speciality viscosity system.
But the selection of the cellulose dosage of water-in-water multicolor coating, molecular weight height and different protective glue is to color grain form, size,
Bleeding and the rear thickening of multicolor finish have a great impact, stable seldom of domestic existing water-water formulation for coating material, at present industry
In multicolor finish because its shelf life of products is short, the general water-water coating shelf-life only 3~6 months, be more than shelf-life product
It is unstable to will appear viscosity, system viscosity becomes larger as the time increases, and it is serious to thicken, to influence its use, cause water packet
Water paint Sales Channel extremely limits to, and can not carry out retail sales, can only sell for engineering, and engineering client is wanted
Goods will also show enquiry and now produce, the popularization of limit product.
Summary of the invention
It is an object of the invention to: shorter for the above-mentioned existing water-water coating shelf-life, viscosity is unstable, increases after existing
The problem of thick phenomenon, the present invention provide a kind of novel water-in-water multicolor coating and preparation method thereof.
The technical solution adopted by the invention is as follows:
A kind of novel water-in-water multicolor coating, the water-in-water multicolor coating comprise the following components in parts by weight:
(1) A expects: deionized water 1~2, preservative 0.2~0.4, ethylene glycol 1~1.4, coalescing agent 0.3~0.7, silicon third
Lotion 13~17, defoaming agent 0.1~0.3, multifunctional assistant 0.1~0.2；
(2) B expects: deionized water 1~1.5, alkali swollen thickener 0.05~0.1；
(3) C expects: particle mixed liquor 75~85.
Further, the particle mixed liquor includes deionized water, anti-settling agent, GRAS B pregel, color-mixed base paint；Institute
State deionized water, anti-settling agent, GRAS B pregel, color-mixed base paint weight ratio are as follows: 5~9:1~3:6~12:55~65.
Further, the color-mixed base paint comprises the following components in parts by weight:
(1) D expects: deionized water 64~66, cellulose 0.6~1.0, defoaming agent 0.1~0.3, dedicated wetting agent 0.2~
0.4, titanium dioxide 0.8~1.2, kaolin 2~4, multifunctional assistant 0.1~0.3；
(2) E expect: preservative 0.2~0.4, lotion 18~22, coalescing agent 0.5~0.7, defoaming agent 0.1~0.3, go from
Sub- water 1~3, alkali swollen thickener 0.2~0.4；
(3) F expects: GRAS B pregel 6~12.
Further, the GRAS B pregel includes deionized water, preservative, GRAS B protection rubber powder；It is described go from
The weight ratio of sub- water, preservative, GRAS B protection rubber powder are as follows: 90~92:0.1~0.2:6~10.
Further, in the anti-settling agent containing 0.3~0.8% preservative.By the way that preservative is added in anti-settling agent,
It can prevent from reducing viscosity, dispersion is until be completely dissolved no agglomerate under high velocity agitation.
A kind of preparation method of novel water-in-water multicolor coating, includes the following steps:
(1) it prepares GRAS B pregel: preservative, GRAS B protection rubber powder being added in deionized water and carry out high-speed stirring
It mixes, mixing time is 50~70min, obtains GRAS B pregel；
(2) it prepares color-mixed base paint: D being expected that mixing carries out high-speed stirred, mixing time is 15~30min；Then it adjusts
To stir at low speed, E material is added, mixing time is 5~8min；It is eventually adding GRAS B pregel, is adjusted to moderate-speed mixer, is stirred
Time is 10~20min, obtains color-mixed base paint；
(3) it prepares particle mixed liquor: deionized water, anti-settling agent, GRAS B pregel is added to the toning base prepared
High-speed stirred is carried out in plinth paint, mixing time is 5~10min；Then it being adjusted to stir at low speed, mixing time is 5~10min,
It is granulated simultaneously with pelletizer, obtains particle mixed liquor；
(4) with paint: A material being stirred in blender, carries out high-speed stirred, mixing time is 5~10min, then
The amount that half is added in B material after mixing uses dispersion impeller instead into A material, is adjusted to Ultra-Low Speed stirring, it is mixed to be slowly added to particle
It closes liquid to be uniformly mixed, is further continued for putting into the other half uniformly mixed B material, continues to be stirred up to water-in-water multicolor coating.
Further, the revolving speed of the high-speed stirred is 1500~1800r/min, the revolving speed of moderate-speed mixer is 800~
1000r/min, the revolving speed stirred at low speed are 400~500r/min, and the revolving speed of Ultra-Low Speed stirring is 150~250r/min.
Further, the deionized water in the step (2) in E material and alkali swollen thickener be pre-mixed
It is even.By the way that deionized water and alkali swollen thickener to be pre-mixed, the viscosity of the color-mixed base paint after can making preparation exists
Preferable use state prevents the excessive effect for influencing post-coatings of viscosity.
Further, the particle size after being granulated in the step (3) by pelletizer is 0.1~0.3mm.
In conclusion by adopting the above-described technical solution, the beneficial effects of the present invention are:
1. the novel water-in-water multicolor coating finished product of the present invention does not have rear thickening behavior, product viscosity is 75 after storage nine months
Between~80KU, and the flexibility and good leveling property of coating color dot, color dot is not allowed frangible in spraying process, and color dot is in basal plane energy
More preferable drawout, coating weight are reduced；
2. water-water coating when novel water-in-water multicolor coating liquid of the invention can manually be sprayed with multicolor spray equipment
It applies, construction is primary to be formed, time and labour saving material-saving；Water-water coating after film-forming has graceful, ventilative, waterproof, decoration
Etc. functions.
Detailed description of the invention
Examples of the present invention will be described by way of reference to the accompanying drawings, in which:
Fig. 1 is a kind of novel water-in-water multicolor coating different time viscosity change curve graph of the present invention.
Specific embodiment
All features disclosed in this specification or disclosed all methods or in the process the step of, in addition to mutually exclusive
Feature and/or step other than, can combine in any way.
It elaborates below with reference to Fig. 1 to the present invention.
Embodiment 1
A kind of novel water-in-water multicolor coating, the water-in-water multicolor coating comprise the following components in parts by weight:
(1) A expect: deionized water 1, preservative 0.2, ethylene glycol 1, coalescing agent 0.3, silicone acrylic emulsion 13, defoaming agent 0.1,
Multifunctional assistant 0.1；
(2) B expects: deionized water 1, alkali swollen thickener 0.05；
(3) C expects: particle mixed liquor 75.
Further, the particle mixed liquor includes deionized water, anti-settling agent, GRAS B pregel, color-mixed base paint；Institute
State deionized water, anti-settling agent, GRAS B pregel, color-mixed base paint weight ratio are as follows: 5:1:6:55.
Further, the color-mixed base paint comprises the following components in parts by weight:
(1) D expects: deionized water 64, cellulose 0.6, defoaming agent 0.1, dedicated wetting agent 0.2, titanium dioxide 0.8, kaolin
2, multifunctional assistant 0.1；
(2) E expects: preservative 0.2, lotion 18, coalescing agent 0.5, defoaming agent 0.1, deionized water 1, alkali swollen thickener
0.2；
(3) F expects: GRAS B pregel 6.
Further, the GRAS B pregel includes deionized water, preservative, GRAS B protection rubber powder；It is described go from
The weight ratio of sub- water, preservative, GRAS B protection rubber powder are as follows: 90:0.1:6.
Further, in the anti-settling agent in the step (3) containing 0.3% preservative.By being added in anti-settling agent
Preservative can prevent from reducing viscosity, and dispersion is until be completely dissolved no agglomerate under high velocity agitation.
Further, the GRAS B that preservative k14, the GRAS B protection rubber powder that the preservative is Te Nuoyi is Ge Ruite
Rubber powder is protected, dedicated wetting agent is the dedicated wetting agent DC803 of Ge Ruite, and lotion is the lotion 4930 of Japanese Showa, and alkali soluble is swollen
Thickener is the alkali swollen thickener HS1152 of BASF, and coalescing agent is the coalescing agent of TEXNOAL, and multifunctional assistant is the U.S.
The AMP95 of Tao Shi.
A kind of preparation method of novel water-in-water multicolor coating, includes the following steps:
(1) it prepares GRAS B pregel: preservative, GRAS B protection rubber powder being added in deionized water and carry out high-speed stirring
It mixes, mixing time is 50~70min, obtains GRAS B pregel, which can store half a year or more without becoming
Change；
(2) it prepares color-mixed base paint: D is expected that mixing carries out high-speed stirred, mixing time 15min；Then it is adjusted to low
E material, mixing time 5min is added in speed stirring；It is eventually adding GRAS B pregel, is adjusted to moderate-speed mixer, mixing time is
10min obtains color-mixed base paint；
(3) it prepares particle mixed liquor: deionized water, anti-settling agent, GRAS B pregel is added to the toning base prepared
High-speed stirred, mixing time 5min are carried out in plinth paint；Then it is adjusted to stir at low speed, mixing time 5min, while with making
Grain machine is granulated, and obtains particle mixed liquor；
(4) with paint: A material being stirred in blender, carries out high-speed stirred, then mixing time 5min expects B
The amount of half is added after mixing into A material, uses dispersion impeller instead, is adjusted to Ultra-Low Speed stirring, is slowly added to particle mixed liquor
It is uniformly mixed, is further continued for putting into the other half uniformly mixed B material, continues to be stirred up to water-in-water multicolor coating.
Further, the revolving speed of the high-speed stirred is 1500r/min, and the revolving speed of moderate-speed mixer is 800r/min, low speed
The revolving speed of stirring is 400r/min, and the revolving speed of Ultra-Low Speed stirring is 150r/min.
Further, the deionized water in the step (2) in E material and alkali swollen thickener be pre-mixed
It is even.By the way that deionized water and alkali swollen thickener to be pre-mixed, the viscosity of the color-mixed base paint after can making preparation exists
Preferable use state prevents the excessive effect for influencing post-coatings of viscosity.
Further, the particle size after being granulated in the step (3) by pelletizer is 0.1mm.
The novel water-in-water multicolor coating finished product of the present invention does not have rear thickening behavior, and product viscosity is after storage nine months
75KU, and the flexibility and good leveling property of coating color dot, color dot is not allowed frangible in spraying process, and color dot can more preferably be spread in basal plane
Expansion, coating weight are reduced.
Embodiment 2
A kind of novel water-in-water multicolor coating, the water-in-water multicolor coating comprise the following components in parts by weight:
(1) A expects: deionized water 2, preservative 0.4, ethylene glycol 1.4, coalescing agent 0.7, silicone acrylic emulsion 17, defoaming agent 0.1
~0.3, multifunctional assistant 0.2；
(2) B expects: deionized water 1.5, alkali swollen thickener 0.1；
(3) C expects: particle mixed liquor 85.
Further, the particle mixed liquor includes deionized water, anti-settling agent, GRAS B pregel, color-mixed base paint；Institute
State deionized water, anti-settling agent, GRAS B pregel, color-mixed base paint weight ratio are as follows: 9:3:12:65.
Further, the color-mixed base paint comprises the following components in parts by weight:
(1) D expects: deionized water 66, cellulose 1.0, defoaming agent 0.3, dedicated wetting agent 0.4, titanium dioxide 1.2, kaolin
4, multifunctional assistant 0.3；
(2) E expects: preservative 0.4, lotion 22, coalescing agent 0.7, defoaming agent 0.3, deionized water 3, alkali swollen thickener
0.4；
(3) F expects: GRAS B pregel 12.
Further, the GRAS B pregel includes deionized water, preservative, GRAS B protection rubber powder；It is described go from
The weight ratio of sub- water, preservative, GRAS B protection rubber powder are as follows: 92:0.2:10.
Further, the GRAS B that preservative k14, the GRAS B protection rubber powder that the preservative is Te Nuoyi is Ge Ruite
Rubber powder is protected, dedicated wetting agent is the dedicated wetting agent DC803 of Ge Ruite, and lotion is the lotion 4930 of Japanese Showa, and alkali soluble is swollen
Thickener is the alkali swollen thickener HS1152 of BASF, and coalescing agent is the coalescing agent of TEXNOAL, and multifunctional assistant is the U.S.
The AMP95 of Tao Shi.
A kind of preparation method of novel water-in-water multicolor coating, includes the following steps:
(1) it prepares GRAS B pregel: preservative, GRAS B protection rubber powder being added in deionized water and carry out high-speed stirring
It mixes, mixing time is 50~70min, obtains GRAS B pregel, which can store half a year or more without becoming
Change；
(2) it prepares color-mixed base paint: D is expected that mixing carries out high-speed stirred, mixing time 30min；Then it is adjusted to low
E material, mixing time 8min is added in speed stirring；It is eventually adding GRAS B pregel, is adjusted to moderate-speed mixer, mixing time is
20min obtains color-mixed base paint；
(3) it prepares particle mixed liquor: deionized water, anti-settling agent, GRAS B pregel is added to the toning base prepared
High-speed stirred, mixing time 10min are carried out in plinth paint；Then it is adjusted to stir at low speed, mixing time 10min is used simultaneously
Pelletizer is granulated, and obtains particle mixed liquor；
(4) with paint: A material being stirred in blender, carries out high-speed stirred, mixing time 10min, then by B
The amount of half is added into A material in material after mixing, uses dispersion impeller instead, is adjusted to Ultra-Low Speed stirring, is slowly added to particle mixing
Liquid is uniformly mixed, and is further continued for putting into the other half uniformly mixed B material, is continued to be stirred up to water-in-water multicolor coating.
Further, the revolving speed of the high-speed stirred is 1800r/min, and the revolving speed of moderate-speed mixer is 1000r/min, low speed
The revolving speed of stirring is 500r/min, and the revolving speed of Ultra-Low Speed stirring is 250r/min.
Further, the deionized water in the step (2) in E material and alkali swollen thickener be pre-mixed
It is even.By the way that deionized water and alkali swollen thickener to be pre-mixed, the viscosity of the color-mixed base paint after can making preparation exists
Preferable use state prevents the excessive effect for influencing post-coatings of viscosity.
Further, in the anti-settling agent in the step (3) containing 0.8% preservative.By being added in anti-settling agent
Preservative can prevent from reducing viscosity, and dispersion is until be completely dissolved no agglomerate under high velocity agitation.
Further, the particle size after being granulated in the step (3) by pelletizer is 0.3mm.
The novel water-in-water multicolor coating finished product of the present invention does not have rear thickening behavior, and product viscosity is after storage nine months
80KU, and the flexibility and good leveling property of coating color dot, color dot is not allowed frangible in spraying process, and color dot can more preferably be spread in basal plane
Expansion, coating weight are reduced.
Embodiment 3
A kind of novel water-in-water multicolor coating, the water-in-water multicolor coating comprise the following components in parts by weight:
(1) A expects: deionized water 1.5, preservative 0.3, ethylene glycol 1.2, coalescing agent 0.5, silicone acrylic emulsion 15, defoaming agent
0.2, multifunctional assistant 0.15；
(2) B expects: deionized water 1.2, alkali swollen thickener 0.08；
(3) C expects: particle mixed liquor 80.
Further, the particle mixed liquor includes deionized water, anti-settling agent, GRAS B pregel, color-mixed base paint；Institute
State deionized water, anti-settling agent, GRAS B pregel, color-mixed base paint weight ratio are as follows: 7:2:10:60.
Further, the color-mixed base paint comprises the following components in parts by weight:
(1) D expects: deionized water 65, cellulose 0.8, defoaming agent 0.2, dedicated wetting agent 0.3, titanium dioxide 1.0, kaolin
3, multifunctional assistant 0.2；
(2) E expects: preservative 0.3, lotion 20, coalescing agent 0.6, defoaming agent 0.2, deionized water 2, alkali swollen thickener
0.3；
(3) F expects: GRAS B pregel 8.
Further, the GRAS B pregel includes deionized water, preservative, GRAS B protection rubber powder；It is described go from
The weight ratio of sub- water, preservative, GRAS B protection rubber powder are as follows: 91:0.2:8.
Further, the GRAS B that preservative k14, the GRAS B protection rubber powder that the preservative is Te Nuoyi is Ge Ruite
Rubber powder is protected, dedicated wetting agent is the dedicated wetting agent DC803 of Ge Ruite, and lotion is the lotion 4930 of Japanese Showa, and alkali soluble is swollen
Thickener is the alkali swollen thickener HS1152 of BASF, and coalescing agent is the coalescing agent of TEXNOAL, and multifunctional assistant is the U.S.
The AMP95 of Tao Shi.
A kind of preparation method of novel water-in-water multicolor coating, includes the following steps:
(1) it prepares GRAS B pregel: preservative, GRAS B protection rubber powder being added in deionized water and carry out high-speed stirring
It mixes, mixing time is 50~70min, obtains GRAS B pregel, which can store half a year or more without becoming
Change；
(2) it prepares color-mixed base paint: D is expected that mixing carries out high-speed stirred, mixing time 20min；Then it is adjusted to low
E material, mixing time 7min is added in speed stirring；It is eventually adding GRAS B pregel, is adjusted to moderate-speed mixer, mixing time is
15min obtains color-mixed base paint；
(3) it prepares particle mixed liquor: deionized water, anti-settling agent, GRAS B pregel is added to the toning base prepared
High-speed stirred, mixing time 8min are carried out in plinth paint；Then it is adjusted to stir at low speed, mixing time 8min, while with making
Grain machine is granulated, and obtains particle mixed liquor；
(4) with paint: A material being stirred in blender, carries out high-speed stirred, then mixing time 8min expects B
The amount of half is added after mixing into A material, uses dispersion impeller instead, is adjusted to Ultra-Low Speed stirring, is slowly added to particle mixed liquor
It is uniformly mixed, is further continued for putting into the other half uniformly mixed B material, continues to be stirred up to water-in-water multicolor coating.
Further, the revolving speed of the high-speed stirred is 1600r/min, and the revolving speed of moderate-speed mixer is 900r/min, low speed
The revolving speed of stirring is 450r/min, and the revolving speed of Ultra-Low Speed stirring is 200r/min.
Further, the deionized water in the step (2) in E material and alkali swollen thickener be pre-mixed
It is even.By the way that deionized water and alkali swollen thickener to be pre-mixed, the viscosity of the color-mixed base paint after can making preparation exists
Preferable use state prevents the excessive effect for influencing post-coatings of viscosity.
Further, in the anti-settling agent in the step (3) containing 0.5% preservative.By being added in anti-settling agent
Preservative can prevent from reducing viscosity, and dispersion is until be completely dissolved no agglomerate under high velocity agitation.
Further, the particle size after being granulated in the step (3) by pelletizer is 0.2mm.
The novel water-in-water multicolor coating finished product of the present invention does not have rear thickening behavior, and product viscosity is after storage nine months
78KU, and the flexibility and good leveling property of coating color dot, color dot is not allowed frangible in spraying process, and color dot can more preferably be spread in basal plane
Expansion, coating weight are reduced.
Experimental section
Choose three groups of water-water coating in each embodiment different time (0 day, 15 days, 30 days, 60 days, 90 days,
180 days, 270 days) viscosity measurements are carried out, three groups of water burnt-in sand coating in each embodiment are calculated after detection in different time points
The average value of viscosity, then the average value is made into curve graph.
It can be seen that the water-water coating of three embodiments with the growth of time from Fig. 1 curve graph, viscosity becomes without obvious
Change, thickening behavior after not occurring has preferable stability.
Claims (9)
1. a kind of novel water-in-water multicolor coating, which is characterized in that the water-in-water multicolor coating includes the group of following parts by weight
Point:
(1) A expects: deionized water 1~2, preservative 0.2~0.4, ethylene glycol 1~1.4, coalescing agent 0.3~0.7, silicone acrylic emulsion
13~17, defoaming agent 0.1~0.3, multifunctional assistant 0.1~0.2；
(2) B expects: deionized water 1~1.5, alkali swollen thickener 0.05~0.1；
(3) C expects: particle mixed liquor 75~85.
2. a kind of novel water-in-water multicolor coating according to claim 1, which is characterized in that the particle mixed liquor includes
Deionized water, anti-settling agent, GRAS B pregel, color-mixed base paint；The deionized water, anti-settling agent, GRAS B pregel, toning
The weight ratio of base paint are as follows: 5~9:1~3:6~12:55~65.
3. a kind of novel water-in-water multicolor coating according to claim 2, which is characterized in that the color-mixed base paint includes
Following parts by weight component:
(1) D expects: deionized water 64~66, cellulose 0.6~1.0, defoaming agent 0.1~0.3, dedicated wetting agent 0.2~0.4, titanium
White powder 0.8~1.2, kaolin 2~4, multifunctional assistant 0.1~0.3；
(2) E expects: preservative 0.2~0.4, lotion 18~22, coalescing agent 0.5~0.7, defoaming agent 0.1~0.3, deionized water
1~3, alkali swollen thickener 0.2~0.4；
(3) F expects: GRAS B pregel 6~12.
4. a kind of novel water-in-water multicolor coating according to claim 3, which is characterized in that the GRAS B pregel packet
Include deionized water, preservative, GRAS B protection rubber powder；The weight ratio of the deionized water, preservative, GRAS B protection rubber powder
Are as follows: 90~92:0.1~0.2:6~10.
5. a kind of novel water-in-water multicolor coating according to claim 2, which is characterized in that contain in the anti-settling agent
0.3~0.8% preservative.
6. a kind of preparation method of novel water-in-water multicolor coating, which comprises the steps of:
(1) it prepares GRAS B pregel: preservative, GRAS B protection rubber powder being added in deionized water and carry out high-speed stirred,
Mixing time is 50~70min, obtains GRAS B pregel；
(2) it prepares color-mixed base paint: D being expected that mixing carries out high-speed stirred, mixing time is 15~30min；Then it is adjusted to low
Speed stirring, is added E material, and mixing time is 5~8min；It is eventually adding GRAS B pregel, is adjusted to moderate-speed mixer, mixing time
For 10~20min, color-mixed base paint is obtained；
(3) it prepares particle mixed liquor: deionized water, anti-settling agent, GRAS B pregel is added to the color-mixed base paint prepared
Interior carry out high-speed stirred, mixing time are 5~10min；Then it is adjusted to stir at low speed, mixing time is 5~10min, simultaneously
It is granulated with pelletizer, obtains particle mixed liquor；
(4) with paint: A material being stirred in blender, carries out high-speed stirred, mixing time is 5~10min, then expects B
The amount of half is added after mixing into A material, uses dispersion impeller instead, is adjusted to Ultra-Low Speed stirring, is slowly added to particle mixed liquor
It is uniformly mixed, is further continued for putting into the other half uniformly mixed B material, continues to be stirred up to water-in-water multicolor coating.
7. a kind of preparation method of novel water-in-water multicolor coating according to claim 6, which is characterized in that the high speed
The revolving speed of stirring is 1500~1800r/min, and the revolving speed of moderate-speed mixer is 800~1000r/min, and the revolving speed stirred at low speed is
400~500r/min, the revolving speed of Ultra-Low Speed stirring are 150~250r/min.
8. a kind of preparation method of novel water-in-water multicolor coating according to claim 6, which is characterized in that the step
(2) deionized water and alkali swollen thickener in E material be pre-mixed uniformly.
9. a kind of preparation method of novel water-in-water multicolor coating according to claim 6, which is characterized in that the step
(3) particle size after being granulated in by pelletizer is 0.1~0.3mm.