CN107142020B - A kind of environment-friendly imitation stone texture artistic floors coating and preparation method thereof - Google Patents
A kind of environment-friendly imitation stone texture artistic floors coating and preparation method thereof Download PDFInfo
- Publication number
- CN107142020B CN107142020B CN201710350534.0A CN201710350534A CN107142020B CN 107142020 B CN107142020 B CN 107142020B CN 201710350534 A CN201710350534 A CN 201710350534A CN 107142020 B CN107142020 B CN 107142020B
- Authority
- CN
- China
- Prior art keywords
- coating
- base
- parts
- environment
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of environment-friendly imitation stone texture artistic floors coatings and preparation method thereof.After the coating is mixed by colored base-material and curing agent by weight 5-20:1 respectively, sprayed with specific spraying method.Colored base-material is then made of base paint plus various mill bases.Distortion melting of the environment-friendly imitation stone texture artistic floors coating analog stone material obtained by the present invention in process of crustal movement such as is interpenetrated at the variations of generations, and texture exquisiteness is changeable, there is color gradient effect, similar to natural stone texture;And coating is prepared with the aqueous materials of environmental protection, and to various substrates, adhesive force is good, has excellent color developing, hardness is high, and beautiful, wear-resisting, waterproof, anti-corrosion can customize according to demand.And the coating construction is simple is convenient, and speed of application is fast.
Description
Technical field
The invention belongs to artistic floors technical fields, and in particular to a kind of environment-friendly imitation stone texture artistic floors coating and
Preparation method.
Background technique
For a long time, stone floor is changeable with its texture, and gracefulness is noble and firmly gets people and likes.But stone material adds in exploitation
Serious welding during work, price are again prohibitively expensive.Therefore, people always search for the substitute of stone material.In recent years, ground
Level ground paint gradually replaces stone material, is widely used in market, supermarket and office space ground.Floor paint has beautiful, wear-resisting, resistance to
Water, solvent resistant, easy construction, it is cheap the advantages that.Under the effort of research staff, traditional monochromatic terrace gradually declines, more
Color terrace flourishes.Colorful terrace uses water-soluble colorful coating, and after construction, terrace is rich in color, and magnificent mansion gives
The enjoyment of beauty.But colorful terrace can not still simulate the grain effect of lithotome, not be able to satisfy some consumers to high life
The pursuit of quality living.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of environment-friendly imitation stone texture artistic floors coating and its preparation
Method.Environment-friendly imitation stone texture artistic floors coating of the invention is prepared with the aqueous materials of environmental protection, is adhered to various substrates
Power is good, has excellent color developing, and hardness is high, and beautiful, wear-resisting, waterproof, anti-corrosion can customize according to demand, analog stone material
Distortion melting in process of crustal movement such as is interpenetrated at the variations of generations, and texture exquisiteness is changeable, there is color gradient effect, with
Natural stone texture is similar.
To achieve the above object, the present invention adopts the following technical scheme:
A kind of environment-friendly imitation stone texture artistic floors coating: it is mixed by colored base-material and curing agent 5-20:1 in mass ratio
After uniformly, sprayed with special process;The colored base-material is made of base paint and mill base, and base paint includes following weight
The raw material of part: 200-400 parts of deionized water, 500-800 parts of water-base resin, 10-30 parts of coalescing agent, 1-5 parts of bleeding agent, defoaming
1-5 parts of agent, 5-20 parts of thickener, 1-5 parts of preservative;The mass ratio of base paint and mill base is 1000:1-5.
The curing agent is Aquolin® 268, Aquolin® 270 and Aquolin® One or more of 278
Composition.
The water-base resin is Wantipro0676, the composition of one or both of Wantipro0639.
The coalescing agent is one of Eastman Texanol, Dowanol DPnB and Dowanol PPh or several
The composition of kind;The bleeding agent is SN-WET 996, the composition of one or both of BASF CF-11;The defoaming agent
For BYK-024, Coadd®The composition of one or more of DF-425, Rhodoline DF6008;The thixotropic agent is
Cabopol® ETD 2020 NF, Cabopol® The composition of one or more of 941 NF or Laponite S482;It is described
Thickener is Vesmody®U300, Vesmody®U902, Coadd®A018, Coadd®The group of one or more of U501
Close object;The preservative is CMIT/MIT, BIT and KATHON®The composition of one or both of LXE;The mill base is
Clear aqueous mill base.
The preparation step of the base paint is as follows:
1) deionized water of formula ratio is added in reaction kettle, controls 300-400 revs/min of revolving speed, is slowly added to thixotroping
Agent;
2) bleeding agent, defoaming agent, coalescing agent and water-base resin are sequentially added, is stirred 10-15 minutes;
3) it is slowly added to thickener and preservative, is stirred 30-40 minutes.
The preparation method of environment-friendly imitation stone texture artistic floors coating, steps are as follows:
1) mill base is added in base paint, colored base-material is made respectively, colored base-material and curing agent as primitive color are pressed
Formula rate is added in coating storage tank, after mixing evenly, is sprayed using the spray gun that bore is 2.0 and completely uses putty and transparent priming in advance
Processed substrate;
2) according to design requirement, the curing agent of other colored base-materials and formula ratio, stirring are separately added into coating storage tank
After uniformly, decorative spraying is carried out;
3) go out different decorative patterns using spray gun air-blowing;
4) to coating dry solidification to get stone texture-like artistic floors coating.
The beneficial effects of the present invention are:
1) it is that viscosity reduces rapidly when by high shear forces the characteristics of thixotropic agent, stops then restoring high viscous when shearing
Degree.Coating is in spraying process, the coating having been coated with is in high shear and low sheraing coexists state.Coating passes through spray gun high speed
It spraying, injects the coating sprayed, be high shear forces, viscosity of the coating drastically reduces, and the coating for applying interlayer is interpenetrated,
Mill base therein is able to be mixed into of the same colour;Since coating has certain viscosity, the range of high shear forces is restricted, from injection
Point is remoter, and the shear action being subject to is weaker, and the infiltration immixture between coating is weaker, makees at this point, thixotropic agent primarily serves isolation
With not being mixed substantially between each coating.The present invention utilizes this feature, adjusts concentration of the thixotropic agent in system, cooperation
The viscosity of thickener regulation system controls the coverage of shearing force in spraying process, bears the coating of different location different
Shear action, and obtain the coating of color gradient effect accordingly;
2) torsion of environment-friendly imitation stone texture artistic floors coating analog stone material of the invention in process of crustal movement
Song melting such as is interpenetrated at the variations of generations, and texture exquisiteness is changeable, there is color gradient effect, similar to natural stone texture;
3) environment-friendly imitation stone texture artistic floors coating of the invention is prepared with the aqueous materials of environmental protection, to various substrates
Adhesive force is good, has excellent color developing, hardness is high, and beautiful, wear-resisting, waterproof, anti-corrosion can customize according to demand;
4) environment-friendly imitation stone texture artistic floors coating construction is simple of the invention is convenient, and speed of application is fast.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described.
Obviously, described embodiment is only a part of the invention, and based on the embodiments of the present invention, those skilled in the art exist
Every other embodiment obtained under the premise of creative work is not made, shall fall within the protection scope of the present invention.
Embodiment 1
A kind of environment-friendly imitation marble grain artistic floors coating, by weight by three kinds of colored base-material summations and curing agent
After 9:1 is mixed respectively, sprayed with special process.
The curing agent is Aquolin® 278。
Described three kinds colored base-materials prepare weight and mill base proportion is as follows: 1000 parts of base paints add 5 parts of yellow transparent colors
Slurry, 100 parts of base paints add 0.4 part of red, transparent mill base and 400 parts of base paints add 1.8 parts of transparent mill bases of grey.
The base paint includes following raw material and its parts by weight: 200 parts of deionized water, Wantipro® 0639 700
Part, 20 parts of Texanol, 996 5 parts of SN-WET, 1 part of BYK-024, Cabopol® 2 parts of 2020 NF of ETD, Vesmody®
10 parts of U300, KATHON®1 part of LXE.
The preparation step of base paint is as follows:
1) deionized water of formula ratio is added in reaction kettle, controls 350 revs/min of revolving speed, is slowly added to Cabopol®
ETD 2020 NF;
2) SN-WET 996, BYK-024, Texanol, Wantipro are sequentially added® 0639, it stirs 15 minutes;
3) it is slowly added to Vesmody®U300 and KATHON®LXE is stirred 40 minutes;
A kind of preparation method of environment-friendly imitation stone texture artistic floors coating:
It 1) will be as the 1000 of primitive color parts of yellow base-materials and 111 parts of Aquolin® 278 are added coating storage by formula rate
In tank, after mixing evenly, sprayed using the spray gun that bore is 2.0 full in advance with putty and the processed substrate of transparent priming;
2) according to design requirement, 400 parts of grey base-materials and 44 parts of Aquolin are added in coating storage tank® 278, stirring is equal
After even, decorative spraying is carried out, pays attention to controlling pressure, mixes spray-coating surface not exclusively with lower layer tinter;
3) go out different decorative patterns using spray gun air-blowing;
4) 100 parts of red base-materials and 11 parts of Aquolin are added in coating storage tank® 278, after mixing evenly, interspersed
Property spraying, pays attention to control pressure, make spray-coating surface not exclusively with lower layer paint mix;
5) go out different decorative patterns using spray gun air-blowing.Pay attention to controlling pressure, several colored paints is avoided to be thoroughly mixed;
6) to coating dry solidification to get parian texture artistic floors coating.
Embodiment 2
A kind of environment-friendly imitation marble grain artistic floors coating, by weight by three kinds of colored base-material summations and curing agent
After 5:1 is mixed respectively, sprayed with special process.
The curing agent is Aquolin® 270。
Described three kinds colored base-materials prepare weight and mill base proportion is as follows: 1000 parts of base paints add 2 parts of purple Transparent color
Slurry, 100 parts of base paints add 0.5 part of red, transparent mill base and 600 parts of base paints add 1.8 parts of transparent mill bases of grey.
The base paint includes following raw material and its parts by weight: 400 parts of deionized water, Wantipro® 0639 500
Part, 10 parts of Texanol, 996 3 parts of SN-WET, 3 parts of BYK-024, Cabopol® 941 2 parts of NF, Vesmody® U300
20 parts, KATHON®1 part of LXE;
The preparation step of base paint is as follows:
1) deionized water of formula ratio is added in reaction kettle, controls 350 revs/min of revolving speed, is slowly added to Cabopol®
941 NF;
2) SN-WET 996, BYK-024, Texanol, Wantipro are sequentially added® 0639, it stirs 15 minutes;
3) it is slowly added to Vesmody®U300 and KATHON®LXE is stirred 40 minutes.
A kind of preparation method of environment-friendly imitation stone texture artistic floors coating:
It 1) will be as the 1000 of primitive color parts of purple base-materials and 200 parts of Aquolin® 270 are added coating storage by formula rate
In tank, after mixing evenly, sprayed using the spray gun that bore is 2.0 full in advance with putty and the processed substrate of transparent priming;
2) according to design requirement, 600 parts of grey base-materials and 120 parts of Aquolin are added in coating storage tank® 270, stirring
After uniformly, decorative spraying is carried out, pays attention to control pressure, mixes spray-coating surface not exclusively with lower layer tinter;
3) go out different decorative patterns using spray gun air-blowing;
4) 100 parts of red base-materials and 20 parts of Aquolin are added in coating storage tank® 270, after mixing evenly, interspersed
Property spraying, pays attention to control pressure, make spray-coating surface not exclusively with lower layer paint mix;
5) go out different decorative patterns using spray gun air-blowing.Pay attention to controlling pressure, several colored paints is avoided to be thoroughly mixed;
6) to coating dry solidification to get parian texture artistic floors coating.
Embodiment 3
A kind of environment-friendly imitation marble grain artistic floors coating, by weight by three kinds of colored base-material summations and curing agent
After 20:1 is mixed respectively, sprayed with special process.
The curing agent is Aquolin® 268。
Described three kinds colored base-materials prepare weight and mill base proportion is as follows: 1000 parts of base paints are as base-material, 100 parts of bases
0.4 part of blue-tinted transparent mill base of Qi Tianjia and 300 parts of base paints add 1.2 parts of yellow transparent mill bases.
The base paint includes following raw material and its parts by weight: 400 parts of deionized water, Wantipro® 0639 500
Part, 10 parts of Texanol, 996 3 parts of SN-WET, 3 parts of BYK-024,3 parts of Laponite S482, Vesmody® U300 20
Part, KATHON®1 part of LXE.
The preparation step of base paint is as follows:
1) deionized water of formula ratio is added in reaction kettle, controls 350 revs/min of revolving speed, is slowly added to Laponite
S482;
2) SN-WET 996, BYK-024, Texanol, Wantipro are sequentially added® 0639, it stirs 15 minutes;
3) it is slowly added to Vesmody®U300 and KATHON®LXE is stirred 40 minutes.
A kind of preparation method of environment-friendly imitation stone texture artistic floors coating:
It 1) will be as the 1000 of primitive color parts of colourless base-materials and 50 parts of Aquolin® 268 are added coating storage by formula rate
In tank, after mixing evenly, sprayed using the spray gun that bore is 2.0 full in advance with putty and the processed substrate of transparent priming;
2) according to design requirement, 300 parts of yellow base-materials and 15 parts of Aquolin are added in coating storage tank® 268, stirring is equal
After even, decorative spraying is carried out, pays attention to controlling pressure, mixes spray-coating surface not exclusively with lower layer tinter;
3) go out different decorative patterns using spray gun air-blowing;
4) 100 parts of blue base-materials and 5 parts of Aquolin are added in coating storage tank® 268, after mixing evenly, interspersed
Property spraying, pays attention to control pressure, make spray-coating surface not exclusively with lower layer paint mix;
5) go out different decorative patterns using spray gun air-blowing.Pay attention to controlling pressure, several colored paints is avoided to be thoroughly mixed;
6) to coating dry solidification to get parian texture artistic floors coating.
The foregoing is merely presently preferred embodiments of the present invention, all equivalent changes done according to scope of the present invention patent with
Modification, is all covered by the present invention.
Claims (6)
1. a kind of preparation method of environment-friendly imitation stone texture artistic floors coating, it is characterised in that: the coating is by colored base
Material and curing agent 5-20:1 in mass ratio after mixing, are sprayed with special process;The colored base-material is by base paint
It is formed with mill base, base paint includes the raw material of following parts by weight: 200-400 parts of deionized water, 500-800 parts of water-base resin, at
10-30 parts of film auxiliary agent, 1-5 parts of bleeding agent, 1-5 parts of defoaming agent, 1-10 parts of thixotropic agent, 5-20 parts of thickener, 1-5 parts of preservative;
The mass ratio of base paint and mill base is 1000:1-5;
Specific preparation process is as follows for the environment-friendly imitation stone texture artistic floors coating:
1) mill base is added in base paint, colored base-material is made respectively, by colored base-material and curing agent as primitive color by formula
Ratio is added in coating storage tank, after mixing evenly, is sprayed using the spray gun that bore is 2.0 and is completely handled in advance with putty and transparent priming
The substrate crossed;
2) according to design requirement, it is separately added into the curing agent of other colored base-materials and formula ratio in coating storage tank, stirs evenly
Afterwards, decorative spraying is carried out;
3) go out different decorative patterns using spray gun air-blowing;
4) to coating dry solidification to get stone texture-like artistic floors coating.
2. the preparation method of environment-friendly imitation stone texture artistic floors coating according to claim 1, it is characterised in that: institute
The curing agent stated is Aquolin® 268, Aquolin® 270 and Aquolin® One or more of 278 composition.
3. the preparation method of environment-friendly imitation stone texture artistic floors coating according to claim 1, it is characterised in that: institute
The water-base resin stated is Wantipro0676, the composition of one or both of Wantipro0639.
4. the preparation method of environment-friendly imitation stone texture interior wall coating according to claim 1, it is characterised in that: the touching
Change agent is Cabopol® ETD 2020 NF, Cabopol® The combination of one or more of 941 NF or Laponite S482
Object;The thickener is Vesmody®U300, Vesmody®U902, Coadd®A018 and Coadd®One of U501 or
Several compositions.
5. the preparation method of environment-friendly imitation stone texture artistic floors coating according to claim 1, it is characterised in that: institute
The coalescing agent stated is the combination of one or more of Eastman Texanol, Dowanol DPnB and Dowanol PPh
Object;The bleeding agent is SN-WET 996, the composition of one or both of BASF CF-11;The defoaming agent is BYK-
024, Coadd®The composition of one or more of DF-425, Rhodoline DF6008;The preservative is CMIT/
MIT, BIT and KATHON®The composition of one or both of LXE;The mill base is clear aqueous mill base.
6. the preparation method of environment-friendly imitation stone texture artistic floors coating according to claim 1, it is characterised in that: institute
The preparation step for stating base paint is as follows:
1) deionized water of formula ratio is added in reaction kettle, controls 300-400 revs/min of revolving speed, is slowly added to thixotropic agent;
Bleeding agent, defoaming agent, coalescing agent and water-base resin are sequentially added, is stirred 10-15 minutes;
2) it is slowly added to thickener, is stirred 30-40 minutes;
3) preservative is added, stirs 10-15 minutes, base paint is made.