CN109455945A - 一种反射型防蓝光玻璃及其制备方法 - Google Patents
一种反射型防蓝光玻璃及其制备方法 Download PDFInfo
- Publication number
- CN109455945A CN109455945A CN201811633504.1A CN201811633504A CN109455945A CN 109455945 A CN109455945 A CN 109455945A CN 201811633504 A CN201811633504 A CN 201811633504A CN 109455945 A CN109455945 A CN 109455945A
- Authority
- CN
- China
- Prior art keywords
- blue light
- reflection
- type anti
- preparation
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种反射型防蓝光玻璃及其制备方法，包括：玻璃基材和防蓝光涂层；制备方法为：在玻璃表面涂布一层防蓝光涂层，70～80℃烘干30s至1min，然后进行UV固化，得反射型防蓝光玻璃。本发明反射型防蓝光玻璃，制备工艺简单，只需在基材表面涂布一层防蓝光涂层；本发明反射型防蓝光玻璃透明度高、附着力强、加工性好等性能，有利于实现产业化，同时反射的高能蓝光还可提高色域、增强产品光源的亮度。
Description
技术领域
本发明涉及显示技术领域，尤其涉及一种反射型防蓝光玻璃及其制备方法。
背景技术
随着科技的发展，电子产品在人们的生活中已经得到广泛的应用，但是这些产品在使用时会发出高能蓝光，长期的蓝光照射视网膜会产生自由基,而这些自由基会导致视网膜色素上皮细胞衰亡,从而引起视网膜病变等多种眼科疾病。
目前,相关报道的反射型防蓝光玻璃研究相对较少,主要集中于镀膜工艺。但其缺点也显而易见：工艺复杂，设备投资高，效率低，成本较高。
本发明涉及一种反射型防蓝光玻璃及其制备方法，只需在基材表面涂布一层防蓝光涂层，利用不同聚合单体结构的自组装，形成聚合物的网络，实现高低折射率匹配，达到380-450nm波段的反射，实现防蓝光功能；同时反射的部分近紫外光还可提高色域、增强产品光源的亮度。本发明工艺简单，成本低廉，具有很好的应用前景。
发明内容
本发明的目的之一在于提出一种反射型防蓝光玻璃，该反射型防蓝光玻璃透明度高、附着力强、加工性好，蓝光反射率可达50％，可克服现有技术中的不足。
为实现上述发明目的，本发明采用如下技术方案：
一种反射型防蓝光玻璃，其特征在于，包括玻璃基材和防蓝光涂层，所述的防蓝光涂层是具有反射功能的涂布液。
本发明的另一目的在于提出一种反射型防蓝光玻璃及其制备方法，其工艺简单，易于规模化生产，且原料易得，设备投资少，成本低廉，该方法为：
将防蓝光涂层用OSP10#或RDS4#线棒(润湿间隙10μm)均匀的涂在玻璃基材的表面，然后在70～80℃的真空干燥箱中烘1min，取出经过40mj/cm2-800mj/cm2的UV固化机，得反射型防蓝光玻璃。
如上所述的防蓝光涂层包括：可聚合单体、手性分子、引发剂和溶剂，通过聚合成为交联聚合物网络；可聚合单体的组分的质量百分比在1～50％wt之间；手性分子的质量百分比在1～20％wt之间；引发剂的质量百分比在0～10％wt；溶剂的质量百分比在1～80％wt之间；再加入组分的质量百分比在0.0001～5％wt之间的润湿流平剂，改善防蓝光涂层与玻璃基材的结合能力。
如上所述的可聚合单体具有一个或多个可聚合基团，可聚合基团为：丙烯酰基、甲基丙烯酰基、氟丙烯基、氯丙烯基、三氟甲基丙烯基、氧杂环丁烷基、乙烯醚基、乙烯基甲酮基、马来酰亚胺基、苯基马来酰亚胺基、乙烯基、苯乙烯基、二乙酰基和环氧基中的一种或多种。
如上所述的手性分子为：4-(4-己氧基苯甲酰氧基)苯甲酸-S-(+)-2-辛酯、(13BR)-5,6-二氢-5-(反式-4-丙基环己基)-4H-二萘并[2,1-F:1',2'-H][1,5]二氧杂环壬四烯、双4-(4'-戊基环己基苯甲酸)-(1S)-1-苯基-1,2-乙二醇酯或异戊基联苯腈。
如上所述的引发剂为：2,4,6-三甲基苯甲酰基-二苯基氧化磷、1-羟基-环已基-苯基甲酮、过氧化二苯甲酰、过氧化二异丙苯中的一种或多种。
如上所述的溶剂为四氢呋喃、乙腈、苯、甲苯、二甲苯、丙酮、环丙酮、环己酮、甲苯环己酮、二氧六环、乙二醇、丙三醇、苯乙烯、乙酸乙酯、乙二醇单甲醚中的一种或几种。优选对可聚合单体有良好的溶解性能沸点在60℃-200℃之间、无毒或低毒、无腐蚀性、可回收的溶剂。
如上所述的防蓝光涂层还包括阻聚剂、消泡剂、稀释剂、紫外线吸收剂、取向剂、表面活性剂、紫外固化胶和热固化胶中的一种或多种。
与现有技术相比，本发明的有益之处在于：
①本发明的制作工艺简单，只需在玻璃基材表面涂布一层防蓝光涂布液，制备所得反射型防蓝光玻璃，透光率高，无毒无害，适用范围广，与镀膜工艺相比，大大降低了成本；
②防蓝光涂层，利用不同可聚合单体结构的自组装，形成聚合物的网络，实现高低折射率匹配，达到380-450nm波段的反射，实现防蓝光功能；同时反射的部分近紫外光还可提高色域、增强产品光源的亮度。
附图说明
为了进一步说明产品的性能特给出如下附图。
图1为本发明一个实施例子中防蓝光涂液中的可聚合单体结构式。
图2反射型防蓝光膜的光谱图：图2表明，在400-450nm处的蓝光透截止率50％，反射率为50％，可见光的透过率大于90％。
具体实施方式
以下结合具体实施方式对本发明的技术方案做进一步说明。
实施例1首先将锡纸过平整的铁板放到烘箱中，烘烤至70-90℃(实际正常为75-80℃)；取15份可聚合单体(a)，5份可聚合单体(b)，5份手性分子S811，引发剂0.5份过氧化二异丙苯和0.5份过氧化二苯甲酰、0.1份流平剂聚二甲基硅氧烷、环己酮20份、甲苯20份，将上述物料搅拌混合均匀，制得防蓝光涂布液；用RDS4#线棒(润湿间隙10μm)，均匀涂布在0.1mm的玻璃基材上；涂布完成后，将其放到烘箱锡纸或铁板上，烘烤1min，除去溶剂。最后取出经过40mj/cm2-800mj/cm2的UV固化机，得到反射型防蓝光玻璃。
实施例2首先将锡纸过平整的铁板放到烘箱中，烘烤至70-90℃(实际正常为75-80℃)；10份取可聚合单体(a)，10份可聚合单体(c)，5份手性分子S1011，份引发剂0.4份2,4,6-三甲基苯甲酰基-二苯基氧化磷和0.6份过氧化二苯甲酰、0.1份流平剂Solvesso150、环戊酮25份、二氧六环25份，将上述物料搅拌混合均匀，制得防蓝光涂布液；用RDS4#线棒(润湿间隙10μm)，均匀涂布在0.1mm的玻璃基材上；涂布完成后，将其放到烘箱锡纸或铁板上，烘烤45s，除去溶剂。最后取出经过40mj/cm2-800mj/cm2的UV固化机，得到反射型防蓝光玻璃。
实施例3首先将锡纸过平整的铁板放到烘箱中，烘烤至70-90℃(实际正常为75-80℃)；取10份可聚合单体(b)，10份可聚合单体(c)，3份手性分子S1011，0.6份引发剂1-羟基-环已基-苯基甲酮和0.4份过氧化二苯甲酰、0.1份流平剂二丙酮醇、乙酸乙酯20份、二氧六环25份，将上述物料搅拌混合均匀，制得防蓝光涂布液，用OSP10#线棒(润湿间隙10μm)，均匀涂布在0.1mm的玻璃基材上；涂布完成后，将其放到烘箱锡纸或铁板上，烘烤40s，除去溶剂。最后取出经过40mj/cm2-800mj/cm2的UV固化机，得到反射型防蓝光玻璃。
实施例4首先将锡纸过平整的铁板放到烘箱中，烘烤至70-90℃(实际正常为75-80℃)；10份取可聚合单体(a)，10份可聚合单体(b)，3份手性分子S811，1份引发剂1-羟基-环已基-苯基甲酮、0.1份流平剂BYKK-346、四氢呋喃20份、乙腈20份，将上述物料搅拌混合均匀，制得防蓝光涂布液；用OSP10#线棒(润湿间隙10μm)，均匀涂布在0.1mm的玻璃基材上；涂布完成后，将其放到烘箱锡纸或铁板上，烘烤30s，除去溶剂。最后取出经过40mj/cm2-800mj/cm2的UV固化机，得到反射型防蓝光玻璃。
最后需要注意的是，公布实施方式的目的在于帮助进一步理解本发明，但是本领域的技术人员可以理解：在不脱离本发明及所附的权利要求的精神和范围内，各种替换和修改都是可能的。因此，本发明不应局限于实施例所公开的内容，本发明要求保护的范围以权利要求书界定的范围为准。
Claims (8)
1.一种反射型防蓝光玻璃，其特征在于，包括玻璃基材和防蓝光涂层，所述的防蓝光涂层是具有反射功能的涂布液。
2.根据权利要求1所述的一种反射型防蓝光玻璃的制备方法，其特征在于，该方法为：将防蓝光涂层用OSP10#或RDS4#线棒(润湿间隙10μm)均匀的涂在玻璃基材的表面，然后在70～80℃的真空干燥箱中烘30s至1min，取出经过40mj/cm2-800mj/cm2的UV固化机，得反射型防蓝光玻璃。
3.根据权利要求2所述的一种反射型防蓝光玻璃的制备方法，其特征在于，所述的防蓝光涂层包括：可聚合单体、手性分子、引发剂和溶剂，通过聚合成为交联聚合物网络；可聚合单体的组分的质量百分比在1～50％wt之间；手性分子的质量百分比在1～20％wt之间；引发剂的质量百分比在0～10％wt；溶剂的质量百分比在1～80％wt之间；再加入组分的质量百分比在0.0001～5％wt之间的润湿流平剂，改善防蓝光涂层与玻璃基材的结合能力。
4.根据权利要求3所述的一种反射型防蓝光玻璃的制备方法，其特征在于，所述的可聚合单体具有一个或多个可聚合基团，可聚合基团为：丙烯酰基、甲基丙烯酰基、氟丙烯基、氯丙烯基、三氟甲基丙烯基、氧杂环丁烷基、乙烯醚基、乙烯基甲酮基、马来酰亚胺基、苯基马来酰亚胺基、乙烯基、苯乙烯基、二乙酰基和环氧基中的一种或多种。
5.根据权利要求3所述的一种反射型防蓝光玻璃的制备方法，其特征在于，所述的手性分子为：4-(4-己氧基苯甲酰氧基)苯甲酸-S-(+)-2-辛酯、(13BR)-5,6-二氢-5-(反式-4-丙基环己基)-4H-二萘并[2,1-F:1',2'-H][1,5]二氧杂环壬四烯、双4-(4'-戊基环己基苯甲酸)-(1S)-1-苯基-1,2-乙二醇酯或异戊基联苯腈。
6.根据权利要求3所述的一种反射型防蓝光玻璃的制备方法，其特征在于，所述的引发剂为：2,4,6-三甲基苯甲酰基-二苯基氧化磷、1-羟基-环已基-苯基甲酮、过氧化二苯甲酰、过氧化二异丙苯中的一种或多种。
7.根据权利要求3所述的一种反射型防蓝光玻璃的制备方法，其特征在于，所述的溶剂为四氢呋喃、乙腈、苯、甲苯、二甲苯、丙酮、环丙酮、环己酮、甲苯环己酮、二氧六环、乙二醇、丙三醇、苯乙烯、乙酸乙酯、乙二醇单甲醚中的一种或几种。优选对可聚合单体有良好的溶解性能沸点在60℃-200℃之间、无毒或低毒、无腐蚀性、可回收的溶剂。
8.根据权利要求3所述一种反射型防蓝光玻璃的制备方法，其特征在于，所述的防蓝光涂层还包括阻聚剂、消泡剂、稀释剂、紫外线吸收剂、取向剂、表面活性剂、紫外固化胶和热固化胶中的一种或多种。