CN109400216A - It paints on a kind of ceramic glaze drawing method and application on mill base and ceramic glaze - Google Patents
It paints on a kind of ceramic glaze drawing method and application on mill base and ceramic glaze Download PDFInfo
- Publication number
- CN109400216A CN109400216A CN201811457363.2A CN201811457363A CN109400216A CN 109400216 A CN109400216 A CN 109400216A CN 201811457363 A CN201811457363 A CN 201811457363A CN 109400216 A CN109400216 A CN 109400216A
- Authority
- CN
- China
- Prior art keywords
- ceramic
- glaze
- mill base
- ceramic glaze
- painting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses drawing method and application on paint on ceramic glaze mill base and ceramic glaze, on ceramic glaze drawing mill base by following mass fraction material composition: 50~80 parts of pigment, 2.5~5.0 parts of peach gum, 40~50 parts of water.Drawing method on ceramic glaze is the following steps are included: select the flawless qualified ceramic whiteware of glaze, mill base is modulated using pigment, peach gum, water, then it is aided with hair dryer on ceramic whiteware glaze with mill base to paint, enter kiln grilling after the porcelain finished is dry to 700~1050 DEG C, 25~50min of heat preservation, well arranged, agile natural Ceramic Painting works can be obtained.Mill base of painting on ceramic glaze of the present invention can be applied on ceramic glaze paint.Mill base viscosity of the present invention is suitble to paint, and adhesive force is strong, the works which obtains, more natural reality.
Description
Technical field
The invention belongs to technical field of ceramic production, and in particular to paint on paint on a kind of ceramic glaze mill base and ceramic glaze
Methods and applications.
Background technique
During ceramic sintering, needs to be decorated in ceramic surface, i.e., draw art pattern on ceramic surface.It is existing
Some ceramic surface drawing methods include painting under glaze and painting on glaze, paint (being usually in-glaze decoration) in glaze, wherein ceramic glaze
Upper drawing sintering procedure are as follows:
1, the flawless qualified ceramic whiteware of glaze is selected, and ceramic whiteware glaze is resistant to 730~850 DEG C of barbecue；
2, on the glaze of ceramic whiteware, pattern is drawn with colorant on ceramic glaze；
4, enter kiln grilling to 730~850 DEG C after the porcelain finished is dry, examining qualified is finished product.
In the above method, since porcelain piece glaze is very smooth, colorant is dipped with writing brush and is painted on it, be difficult to draw dry and wet
Deep or light and textural effect, so that the art for the Chinese ink painting that drawing cannot be formed in such dizzy dye of painting on rice paper on glaze be made to imitate
Fruit watches so that the pattern of ceramic surface is more stiff and reserve value is lower.
Summary of the invention
The technical problem to be solved in the present invention is to provide drawing method on paint on a kind of ceramic glaze mill base and ceramic glaze and
Using.The invention modulates a kind of viscosity and is suitble to paint, and the very strong mill base of adhesive force can be on Ceramic glaze according to creation
Intention draws dense or light thin or thick coat of colo(u)r.
In order to solve the above technical problems, the present invention provides mill base of painting on a kind of ceramic glaze, the mill base is by following quality
The material composition of number: 50~80 parts of pigment, 2.5~5.0 parts of peach gum, 40~50 parts of water.
Pigment of the present invention is ceramic glazing dyestuff.
Peach gum of the present invention is any one or two kinds in peach peach gum and mountain peach glue.To be secreted out of in peach bark
The resin come, using virgin rubber, without processing.
The present invention also provides drawing method on the ceramic glaze for mill base of painting on a kind of above-mentioned ceramic glaze, the drawing methods
The following steps are included:
(1) the flawless qualified ceramic whiteware of glaze is selected, and ceramic whiteware glaze is resistant to 730~850 DEG C of barbecue；
(2) mill base is modulated using pigment, peach gum, water, first pigment is added to the water in proportion when modulating mill base, peach is added after mixing well
Glue mixes, and peach gum is dissolved using preceding with warm water immersion；Then it is aided with hair dryer on ceramic whiteware glaze with mill base to paint；
(3) enter kiln grilling after the porcelain finished is dry to 700~1050 DEG C, 25~50min of heat preservation, can be obtained it is well arranged,
Agile natural Ceramic Painting works.
Qualified ceramic whiteware in the step (1) of the present invention is Bone China, magnesia porcelain, general ceramic whiteware, high ceramic whiteware, ultrawhite porcelain, blueness
Any one in porcelain.
The glazed thickness of drawing method coat of colo(u)r is 0.05~0.3mm on ceramic glaze of the present invention.
Hair dryer in step (2) of the present invention uses hot wind.
Hair dryer regulating wind power in step (2) of the present invention, can distinguish cold-hot wind.
The invention also includes on a kind of ceramic glaze paint mill base paint on ceramic glaze in application.
It is suitble to draw the beneficial effects of adopting the technical scheme are that the 1, present invention modulates a kind of viscosity
It draws, the very strong mill base of adhesive force can draw dense or light thin or thick pigment on Ceramic glaze according to creation intention
Layer.2, the wind blows mill base of present invention hair dryer when picture is made a draft is intended to flow substantially to tie out on glaze according to drawing
Structure, this method have atmosphere, natural, agile effect, are sufficiently formed the artistic effect of the Chinese ink painting of dizzy dye.3, this hair
Then the bright hot wind blown out in drawing using hair dryer, the mill base rapid draing that paving can be made to apply polish it again above it
The mill base of his color, can according to picture actual situation, the difference of deep or light, density and far and near transparent effect, can it is one or many into
Row is drawn, is polished, to reach the artistic effect of product ink, plot point, moreover it is possible to be superimposed multiple color, generate the effect of confluent invasion.
4, the present invention forms dense, the dim and realistic picture combined by the control to ceramic pigment shade, and process is careful
Tidy up, adjust after make ceramic art fine work.5, to add peach gum to be modulated into water viscous for colorant on ceramic low-temp glaze of the present invention
The strong mill base of thick adhesive force, the characteristic not absorbed water using ceramics are applied out greatly with sprinkling color, scribbling sketch drawing method on glaze upper berth
Profile is caused, wind-force and temperature blowout natural landscape, shape, texture of hair dryer etc. is recycled, cloud and mist, mountain stone and birds and flowers knot occurs
Structure, then be subject to it is careful delineate, render, colouring, form complete works, more natural reality.6. painting on ceramic glaze of the present invention
Method is suitable for but is not limited to the glazes such as Bone China, magnesia porcelain, general ceramic whiteware, high ceramic whiteware, ultrawhite porcelain, celadon, it is resistant to 730~
The porcelain of 850 DEG C of barbecues can be applicable in.
Specific embodiment
The present invention will be further described in detail below with reference to specific embodiments.
Embodiment 1
The present embodiment porcelain glaze kind is Bone China, drawing method on ceramic glaze the following steps are included:
(1) the flawless qualified Bone China of glaze is selected, and its glaze is resistant to 730~850 DEG C of barbecue；
(2) in parts by mass, mill base is modulated using 50 parts of pigment, 5 parts of peach peach gums, 50 parts of water, is aided with hair dryer heat with mill base
Wind is painted on ceramic whiteware glaze；
(3) enter kiln grilling after the porcelain finished is dry to 780 DEG C, heat preservation 30min, can be obtained it is well arranged, it is agile naturally
Ceramic Painting works.
Ceramic painting works glazed thickness obtained by the present embodiment is 0.2mm, and works are lively, active, and it is deep or light to depict dry and wet
And textural effect, the artistic effect of the Chinese ink painting for dizzy dye of painting on rice paper is embodied, watches and reserve value is higher.
Embodiment 2
The present embodiment porcelain glaze kind is Bone China, drawing method on ceramic glaze the following steps are included:
(1) the flawless qualified Bone China of glaze is selected, and its glaze is resistant to 730~850 DEG C of barbecue；
(2) in parts by mass, mill base is modulated using 55 parts of pigment, 3 parts of mountain peach glue, 45 parts of water, is aided with hair dryer hot wind with mill base
It paints on ceramic whiteware glaze；
(3) enter kiln grilling after the porcelain finished is dry to 760 DEG C, heat preservation 30min, can be obtained it is well arranged, it is agile naturally
Ceramic Painting works.
Ceramic painting works glazed thickness obtained by the present embodiment is 0.1mm, and works are lively, active, and it is deep or light to depict dry and wet
And textural effect, the artistic effect of the Chinese ink painting for dizzy dye of painting on rice paper is embodied, watches and reserve value is higher.
Embodiment 3
The present embodiment porcelain glaze kind is the high ceramic whiteware in Jing Dezhen, drawing method on ceramic glaze the following steps are included:
(1) the high ceramic whiteware in the flawless qualified Jing Dezhen of glaze is selected, and its glaze is resistant to 730~850 DEG C of barbecue；
(2) in parts by mass, mill base is modulated using 50 parts of pigment, 3 parts of peach peach gums and 2 parts of mountain peach glue, 50 parts of water, it is auxiliary with mill base
It is painted on ceramic whiteware glaze with hair dryer hot wind；
(3) enter 800 DEG C of kiln grilling, heat preservation 30min after the porcelain finished is dry, well arranged, agile natural pottery can be obtained
Porcelain paint.
Ceramic painting works glazed thickness obtained by the present embodiment is 0.3mm, and works are lively, active, and it is deep or light to depict dry and wet
And textural effect, the artistic effect of the Chinese ink painting for dizzy dye of painting on rice paper is embodied, watches and reserve value is higher.
Embodiment 4
The present embodiment porcelain glaze kind is the general ceramic whiteware in Jing Dezhen, drawing method on ceramic glaze the following steps are included:
(1) the general ceramic whiteware in the flawless qualified Jing Dezhen of glaze is selected, and its glaze is resistant to 730~850 DEG C of barbecue；
(2) in parts by mass, mill base is modulated using 50 parts of pigment, 3 parts of peach peach gums and 2 parts of mountain peach glue, 50 parts of water, it is auxiliary with mill base
It is painted on ceramic whiteware glaze with hair dryer hot wind；
(3) enter kiln grilling after the porcelain finished is dry to 820 DEG C, heat preservation 30min, can be obtained it is well arranged, it is agile naturally
Ceramic Painting works.
Ceramic painting works glazed thickness obtained by the present embodiment is 0.3mm, and works are lively, active, and it is deep or light to depict dry and wet
And textural effect, the artistic effect of the Chinese ink painting for dizzy dye of painting on rice paper is embodied, watches and reserve value is higher.
Embodiment 5
The present embodiment porcelain glaze kind is Jing Dezhen ultrawhite porcelain, drawing method on ceramic glaze the following steps are included:
(1) the flawless qualified Jing Dezhen ultrawhite porcelain of glaze is selected, and its glaze is resistant to 730~850 DEG C of barbecue；
(2) in parts by mass, mill base is modulated using 60 parts of pigment, 5 parts of mountain peach glue, 40 parts of water, is aided with hair dryer hot wind with mill base
It paints on ceramic whiteware glaze；
(3) enter kiln grilling after the porcelain finished is dry to 790 DEG C, heat preservation 30min, can be obtained it is well arranged, it is agile naturally
Ceramic Painting works.
Ceramic painting works glazed thickness obtained by the present embodiment is 0.2mm, and works are lively, active, and it is deep or light to depict dry and wet
And textural effect, the artistic effect of the Chinese ink painting for dizzy dye of painting on rice paper is embodied, watches and reserve value is higher.
Embodiment 6
The present embodiment porcelain glaze kind is the magnesia porcelain in Shandong, drawing method on ceramic glaze the following steps are included:
(1) the magnesia porcelain in the flawless qualified Shandong of glaze is selected, and its glaze is resistant to 730~850 DEG C of barbecue；
(2) in parts by mass, mill base is modulated using 50 parts of pigment, 3 parts of peach peach gums, 50 parts of water, is aided with hair dryer heat with mill base
Wind is painted on ceramic whiteware glaze；
(3) enter kiln grilling after the porcelain finished is dry to 820 DEG C, heat preservation 30min, can be obtained it is well arranged, it is agile naturally
Ceramic Painting works.
Ceramic painting works glazed thickness obtained by the present embodiment is 0.2mm, and works are lively, active, and it is deep or light to depict dry and wet
And textural effect, the artistic effect of the Chinese ink painting for dizzy dye of painting on rice paper is embodied, watches and reserve value is higher.
Embodiment 7
The present embodiment porcelain glaze kind is Jing Dezhen porcelain plate, drawing method on ceramic glaze the following steps are included:
(1) the flawless qualified Jing Dezhen porcelain plate of glaze is selected, and its glaze is resistant to 730~850 DEG C of barbecue；
(2) in parts by mass, mill base is modulated using 55 parts of pigment, 4 parts of mountain peach glue, 45 parts of water, is aided with hair dryer hot wind with mill base
It paints on ceramic whiteware glaze；
(3) enter kiln grilling after the porcelain finished is dry to 780 DEG C, heat preservation 30min, can be obtained it is well arranged, it is agile naturally
Ceramic Painting works.
Ceramic painting works glazed thickness obtained by the present embodiment is 0.15mm, and works are lively, active, and it is deep or light to depict dry and wet
And textural effect, the artistic effect of the Chinese ink painting for dizzy dye of painting on rice paper is embodied, watches and reserve value is higher.
Embodiment 8
The present embodiment porcelain glaze kind is sclerotin encaustic disk, drawing method on ceramic glaze the following steps are included:
(1) the flawless qualified sclerotin encaustic disk of glaze is selected, and its glaze is resistant to 730~850 DEG C of barbecue；
(2) in parts by mass, mill base is modulated using 50 parts of pigment, 1 part of peach peach gum and 3 parts of mountain peach glue, 50 parts of water, it is auxiliary with mill base
It is painted on ceramic whiteware glaze with hair dryer hot wind；
(3) enter kiln grilling after the porcelain finished is dry to 760 DEG C, heat preservation 30min, can be obtained it is well arranged, it is agile naturally
Ceramic Painting works.
Ceramic painting works glazed thickness obtained by the present embodiment is 0.3mm, and works are lively, active, and it is deep or light to depict dry and wet
And textural effect, the artistic effect of the Chinese ink painting for dizzy dye of painting on rice paper is embodied, watches and reserve value is higher.
Embodiment 9
The present embodiment porcelain glaze kind is Bone China, drawing method on ceramic glaze the following steps are included:
(1) the flawless qualified Bone China of glaze is selected, and its glaze is resistant to 730~850 DEG C of barbecue；
(2) in parts by mass, mill base is modulated using 80 parts of pigment, 2.5 parts of mountain peach glue, 47 parts of water, is aided with hair dryer heat with mill base
Wind is painted on ceramic whiteware glaze；
(3) enter kiln grilling after the porcelain finished is dry to 700 DEG C, heat preservation 50min, can be obtained it is well arranged, it is agile naturally
Ceramic Painting works.
Ceramic painting works glazed thickness obtained by the present embodiment is 0.05mm, and works are lively, active, and it is deep or light to depict dry and wet
And textural effect, the artistic effect of the Chinese ink painting for dizzy dye of painting on rice paper is embodied, watches and reserve value is higher.
Embodiment 10
The present embodiment porcelain glaze kind is Bone China, drawing method on ceramic glaze the following steps are included:
(1) the flawless qualified Bone China of glaze is selected, and its glaze is resistant to 730~850 DEG C of barbecue；
(2) in parts by mass, mill base is modulated using 70 parts of pigment, 4 parts of peach peach gums, 43 parts of water, is aided with hair dryer heat with mill base
Wind is painted on ceramic whiteware glaze；
(3) enter kiln grilling after the porcelain finished is dry to 1050 DEG C, heat preservation 25min, can be obtained it is well arranged, it is agile naturally
Ceramic Painting works.
Ceramic painting works glazed thickness obtained by the present embodiment is 0.25mm, and works are lively, active, and it is deep or light to depict dry and wet
And textural effect, the artistic effect of the Chinese ink painting for dizzy dye of painting on rice paper is embodied, watches and reserve value is higher.
As can be seen from the above embodiments, drawing method is applicable to draw on the glaze of different porcelain glaze kinds on ceramic glaze of the present invention
Burning process is drawn, mill base is modulated using pigment, peach gum, water, is aided with hair dryer hot wind, improves pigment in the adhesive force of glaze, solution
Determined over-glaze decoration cannot multi-level color addition the problem of, picture is drawn using hair dryer blowing force, to obtain lively, living
It sprinkles, ceramic painting works on the glaze with halation effect, embodies the art effect of the Chinese ink painting for dizzy dye of painting on rice paper
Fruit, watches and reserve value is higher.
The above embodiments are only used to illustrate and not limit the technical solutions of the present invention, although referring to above-described embodiment to this hair
It is bright to be described in detail, those skilled in the art should understand that: still the present invention can be modified or be waited
With replacement, without departing from the spirit or scope of the invention, or any substitutions, should all cover in power of the invention
In sharp claimed range.
Claims (9)
1. mill base of painting on a kind of ceramic glaze, which is characterized in that the mill base by following mass fraction material composition: pigment 50
~80 parts, 2.5~5.0 parts of peach gum, 40~50 parts of water.
2. mill base of painting on a kind of ceramic glaze according to claim 1, which is characterized in that the pigment is face on ceramic glaze
Material.
3. mill base of painting on a kind of ceramic glaze according to claim 1, which is characterized in that the peach gum be peach peach gum and
Any one in mountain peach glue or two kinds.
4. drawing method on the ceramic glaze based on mill base of painting on a kind of ceramic glaze described in claim 1-3 any one,
Be characterized in that, the drawing method the following steps are included:
(1) the flawless qualified ceramic whiteware of glaze is selected, and ceramic whiteware glaze is resistant to 730~850 DEG C of barbecue；
(2) mill base is modulated using pigment, peach gum, water, first pigment is added to the water in proportion when modulating mill base, peach is added after mixing well
Glue mixes, and peach gum is dissolved using preceding with warm water immersion；Then it is aided with hair dryer on ceramic whiteware glaze with mill base to paint；
(3) enter kiln grilling after the porcelain finished is dry to 700~1050 DEG C, 25~50min of heat preservation, can be obtained it is well arranged,
Agile natural Ceramic Painting works.
5. drawing method on a kind of ceramic glaze according to claim 4, which is characterized in that the qualification in the step (1)
Ceramic whiteware is Bone China, magnesia porcelain, general ceramic whiteware, high ceramic whiteware, ultrawhite porcelain, any one in celadon.
6. drawing method on a kind of ceramic glaze according to claim 4, which is characterized in that drawing method on the ceramic glaze
The glazed thickness of coat of colo(u)r is 0.05~0.3mm.
7. drawing method on a kind of ceramic glaze according to claim 4-6 any one, which is characterized in that the step
(2) hair dryer in uses hot wind.
8. drawing method on a kind of ceramic glaze according to claim 4-6 any one, which is characterized in that the step
(2) the hair dryer regulating wind power in, can distinguish cold-hot wind.
9. on a kind of ceramic glaze described in claim 1-3 drawing mill base paint on ceramic glaze in application.