CN106187323A - A kind of Imitation Rock Porcelain Tiles with three-dimensional decorative effect and production method thereof - Google Patents
A kind of Imitation Rock Porcelain Tiles with three-dimensional decorative effect and production method thereof Download PDFInfo
- Publication number
- CN106187323A CN106187323A CN201510217605.0A CN201510217605A CN106187323A CN 106187323 A CN106187323 A CN 106187323A CN 201510217605 A CN201510217605 A CN 201510217605A CN 106187323 A CN106187323 A CN 106187323A
- Authority
- CN
- China
- Prior art keywords
- porcelain tiles
- imitation rock
- rock porcelain
- fabric
- decorative effect
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of Imitation Rock Porcelain Tiles with three-dimensional decorative effect and production method thereof, comprise the following steps: (1) prepares Imitation Rock Porcelain Tiles base substrate powder according to a conventional method；(2) Imitation Rock Porcelain Tiles fabric is prepared；(3) Imitation Rock Porcelain Tiles body preparation；(4) body drying；(5) starch adhesive A is drenched；(6) printing fabric B；(7) it is dried after executing cloth fabric；(8) spray infiltration ink；(9) burn till；(10) edging.The invention has the beneficial effects as follows and solve the cost increase that in prior art, starch adhesive and assistant toner consumption cause greatly, pattern texture lacks the problem that solid grain is expressed, solve the show-through inaesthetic technical problems of deep processing such as existing ceramic brick with permeated pattern fluting, chamfering, it is provided that the production method of the Imitation Rock Porcelain Tiles that a kind of more environmentally friendly economy, decorative effect are more rich simultaneously.
Description
Technical field
The present invention relates to architectural pottery technical field, more particularly to a kind of Imitation Rock Porcelain Tiles with three-dimensional decorative effect and production method thereof.
Background technology
At present, oozing colored Imitation Rock Porcelain Tiles product is the effect reaching imitation natural stone stricture of vagina or wood grain, commonly used " oozing flower " polishing technology, and experienced by terms of oozing flower process from silk screen printing comprise soluble-salt ooze colored liquid to spray infiltration ink upgrading.Chinese patent CN102795892B describes one and oozes colored Imitation Rock Porcelain Tiles and production method thereof, starch adhesive is thrown by drenching porcelain on green body layer surface, on the one hand the length of penetration oozing colored salt can be down to 0.3 ~ 0.5mm from 2 ~ 3mm of tradition pattern permeating tile, expand the use kind oozing colored salt, enriched pattern；On the other hand reduce the grinding thichness of polishing process, decrease waste material generation amount.Assistant toner coordinates the use of ink-jet infiltration ink to be obviously improved color saturation and the lightness of decorative pattern, and clean mark is fine and smooth.But, single use ink-jet realizes imitation natural stone stricture of vagina or wood grain makes the decoration of ceramic tile be only limited to planar yardstick, the gully of the hole in bag or wood grain and fluctuating is but short of to the expression of stereoscopic level.Additionally, starch adhesive all uses multiple tracks glaze pouring to execute cloth, starch adhesive large usage quantity, and the assistant toner of the corresponding higher cost introduced is the most on the high side, causes production cost higher.
Summary of the invention
Present invention aim to address that starch adhesive and assistant toner consumption in prior art cause greatly relatively costly, pattern texture lacks the problem that solid grain is expressed, it is provided that the production method of the Imitation Rock Porcelain Tiles that a kind of more environmentally friendly economy, decorative effect are more rich.
It is a further object of the present invention to provide the Imitation Rock Porcelain Tiles with three-dimensional decorative effect using the method to produce.
The technical scheme is that the production method of a kind of Imitation Rock Porcelain Tiles with three-dimensional decorative effect, comprise the following steps:
(1) Imitation Rock Porcelain Tiles base substrate powder is prepared according to a conventional method, standby；
(2) preparing Imitation Rock Porcelain Tiles fabric, the siccative chemical composition that the Imitation Rock Porcelain Tiles fabric of employing is divided into starch adhesive A and fabric B two kinds, starch adhesive A and fabric B is consistent, similar to base substrate powder in step (1), but wherein K2O+Na2O:6 ~ 8%, impurity≤4%(is all weight percentage)；The siccative of starch adhesive A uses feldspar poor material and kaolin families plastic raw material to carry out dispensing, but the siccative of fabric B all uses aluminium oxide, quartz, feldspar non-plastic raw material to carry out dispensing；The slurry of two kinds of fabrics all control fineness be 325 mesh sieve margins within 0.5%, proportion is 1.60 ~ 1.90g/cm3Wherein the siccative of starch adhesive A becomes to meet pouring with auxiliary additive wet ball grinding and executes the slurry of performance requirement, the siccative of fabric B and auxiliary additive wet ball grinding meet size performance and require post-drying, make dry powder, and the printing fabric meeting printing performance it is mixed with stamp-pad ink, auxiliary additive, standby；
(3) Imitation Rock Porcelain Tiles body preparation: by Imitation Rock Porcelain Tiles base substrate powder prepared in step (1) according to the pattern texture designed, carry out multitube cloth, then paving cloth is in brick machine die cavity, under the pressure of 20 ~ 50MPa, Imitation Rock Porcelain Tiles base substrate powder pressing is become Imitation Rock Porcelain Tiles green compact；
(4) body drying: Imitation Rock Porcelain Tiles green compact step (3) prepared are dried in dry kiln at 150 ~ 300 DEG C；
(5) starch adhesive A is drenched: Imitation Rock Porcelain Tiles starch adhesive A glaze pouring step (2) prepared executes cloth Imitation Rock Porcelain Tiles green surface after the drying, and the weight of the executed starch adhesive of unit are is 400 ~ 800g/m2；
(6) printing fabric B: Imitation Rock Porcelain Tiles fabric B typography step (2) prepared executes cloth in the billet surface drenching starch adhesive A；
(7) it is dried after executing cloth fabric: the Imitation Rock Porcelain Tiles green compact executing fabric are dried in dry kiln at 150 ~ 300 DEG C again；
(8) spray infiltration ink: use Digital ink-jet printer to be sprayed on Imitation Rock Porcelain Tiles base substrate by the pattern designed, coordinate blank pattern texture so that brick body surface and base substrate have close texture and quality；
(9) burn till: the Imitation Rock Porcelain Tiles green compact that step (8) is jetted through permeating ink are placed in roller kilns the conventional Imitation Rock Porcelain Tiles firing temperature system of use, pressure regime and atmosphere system, once-firing, firing temperature is 1150 ~ 1250 DEG C, and firing period is 40 ~ 90min, prepares Imitation Rock Porcelain Tiles semi-finished product；
(10) edging: utilizing conventional edging process equipment, double finished bricks carries out edging process, prepares the Imitation Rock Porcelain Tiles finished product with three-dimensional decorative effect.
In above step, all that do not add special instruction, all use conventional control means of the prior art.
For completing second goal of the invention, use the Imitation Rock Porcelain Tiles with three-dimensional decorative effect produced by above-mentioned steps.
Containing kaolin families plastic raw material in the formula of prior art, directly it is prepared as printing fabric, easily affecting printing performance because of plastic raw material sticky net, in step of the present invention (2), fabric B all uses aluminium oxide, quartz, feldspar non-plastic raw material to carry out dispensing, preferably solves problems.
Step (2) comprises auxiliary colorant ZnO, TiO in the auxiliary additive of fabric B2In one or more, the auxiliary additive of starch adhesive A does not comprise ZnO, TiO2Etc. auxiliary colorant.
As further technical scheme, in step (2), the auxiliary additive addition of fabric B is calculated as ZnO for 0.2 ~ 1% with fabric siccative, TiO2It is 0.2 ~ 5%.
As further technical scheme, the printing surface sizing process in step (6) can use silk screen printing or glue roller printing.
As further technical scheme, in step (8), ink ejection face layer thickness is 0.3 ~ 1.0mm.
As further technical scheme, after step (10) edging processes, polishing or soft throwing PROCESS FOR TREATMENT can be used.If the Imitation Rock Porcelain Tiles surface prepared by the present invention is processed by shot blasting, a kind of polished brick in porcelain character with three-dimensional decorative effect can be obtained.Process according to soft throwing, i.e. obtain a kind of porcelain Asia light brick with three-dimensional decorative effect.
Compared with the prior art that patent documentation CN102795892B etc. reports, the present invention has following several respects advantage:
1, material is saved
Prior art is for reaching suitable surface thickness, and in practical operation, the techniques of the identical starch adhesive of twice are drenched in many employings, and all introduce a certain proportion of auxiliary colorant in starch adhesive, to coordinate follow-up ink-jetting pattern, strengthen the hair color effect of ink.Different, the present invention executes in the first starch adhesive A of cloth without ZnO, TiO2Etc. auxiliary colorant, compared with prior art, decrease the consumption of auxiliary colorant, reduce production cost.The present invention executes the second fabric of cloth and does not the most use pouring starch adhesive technique, but the siccative of fabric B and auxiliary additive wet ball grinding are met size performance and require post-drying, make dry powder, and the printing fabric meeting printing performance it is mixed with stamp-pad ink, auxiliary additive, fabric B is printed onto the billet surface drenching starch adhesive A by the mode using printing, pouring starch adhesive compared to existing technology, fabric B uses typography that precoat thickness can be greatly reduced, saves the consumption of starch adhesive.
2, loss is reduced
The pouring starch adhesive operation of prior art, starch adhesive Chang Yin is trapped in recovering tray or sticks to cause waste and loss on belt conveyor, its waste is about about the 20% of starch adhesive total amount, and the present invention uses typography when executing cloth second fabric, then can be substantially reduced the waste of fabric, its fabric utilization rate is up to more than 95%.
3, texture-rich
Existing ink-jet is oozed colored Imitation Rock Porcelain Tiles and is typically used pure color base substrate, texture is only limitted to the ink-jetting pattern of billet surface, decorative effect is dull, and the present invention forms certain decorative pattern by base substrate powder is carried out multitube cloth by the pattern texture designed, and combine digital ink-jet infiltration technology, incrustation is organically combined with base substrate texture, has greatly enriched conventional ink-jet and oozed the decorative effect of colored Imitation Rock Porcelain Tiles.
Existing ink-jet is oozed colored Imitation Rock Porcelain Tiles and is used pouring twice starch adhesive technique, and billet surface is all covered by starch adhesive, can only be merely as the supporting body of subsequent i alphakjet pattern, and starch adhesive layer is confined to two-dimension plane structure, it is difficult to realize the decorative effect of stereo concave-convex.And the present invention uses printing web process can realize different lines textures as required, really realize point-line-face multiple texture even combination of Z-Correct bump mapping Z-correct.
Additionally, the present invention prints web process can use the uneven printing in local.Owing to common printed glaze fire degree is relatively low, the lines of printing easily melt, having Self-leveling effect, hachure texture is easily filled and led up because glaze is melted so that printing lines are confined to thick lines texture, and decoration texture is the finest and the smoothest.Compared with common printed glaze, the fiery degree of fabric of the present invention is high, glass is few mutually, not there is the temperature flowing of common glaze, thus stria can be printed, stria caves in owing to fire degree height will not soften in burning till, and after remaining to burn till process, therefore decoration texture is finer and smoother, gully and the hole of a small amount of uneven distribution of stereoscopic three-dimensional level be can form after burning till process, thus the crackle of lithotome and pore or the sagging lines of wood grain and hole etc. reproduced the most realistically.
Compared with prior art, the present invention is obtained provides the benefit that solve that starch adhesive and assistant toner consumption in prior art cause greatly relatively costly, pattern texture lacks the problem that solid grain is expressed, and solves the show-through inaesthetic technical problems of deep processing such as existing ceramic brick with permeated pattern fluting, chamfering simultaneously.Printing fabric mode not only provide significant conservation the consume of fabric consumption, reduce production cost, fabric height fire degree character remains to keep original lines texture after making to burn simultaneously, realize the decorative effect of 3 D stereo level, match with base substrate entire body cloth texture, it is achieved that bag or the reproduction true to nature of wood texture.
Detailed description of the invention
Embodiment 1
(1) prepare Imitation Rock Porcelain Tiles base substrate powder according to a conventional method, allocate 3 kinds of color powders standby；
(2) Imitation Rock Porcelain Tiles fabric is prepared, fabric A uses feldspar poor material and kaolin families plastic raw material to carry out dispensing, the siccative of fabric B all uses aluminium oxide, quartz, feldspar non-plastic raw material to carry out dispensing, wet ball grinding, the slurry of two kinds of fabrics all control fineness be 325 mesh sieve margins within 0.5%, proportion is 1.78g/cm3Wherein the siccative of starch adhesive A becomes to meet pouring with auxiliary additive wet ball grinding and executes the slurry of performance requirement, the siccative of fabric B and auxiliary additive wet ball grinding meet size performance and require post-drying, make dry powder, and the printing fabric meeting printing performance it is mixed with stamp-pad ink, auxiliary additive, standby.The chemical composition range of two kinds of fabrics is (weight portion): SiO2: 66%, Al2O3: 17%, MgO+CaO:2.0%, K2O+Na2O:5%, surplus is impurity, also needs additional ZnO 0.2%, TiO in fabric B2 1%。
(3) Imitation Rock Porcelain Tiles body preparation: by Imitation Rock Porcelain Tiles base substrate powder prepared in step (1) according to the pattern texture designed, carries out multitube cloth, and then paving cloth is in brick machine die cavity, under the pressure of 30MPa, Imitation Rock Porcelain Tiles base substrate powder pressing is become Imitation Rock Porcelain Tiles green compact；
(4) Imitation Rock Porcelain Tiles green compact step (3) prepared are dried in dry kiln at 150 DEG C；
(5) starch adhesive A is drenched: Imitation Rock Porcelain Tiles starch adhesive A glaze pouring step (2) prepared executes cloth Imitation Rock Porcelain Tiles green surface after the drying, and the weight of the executed starch adhesive of unit are is 800g/m2；
(6) printing fabric B: Imitation Rock Porcelain Tiles fabric B silk-screen printing technique step (2) prepared executes cloth in the billet surface drenching starch adhesive A；
(7) it is dried after executing cloth fabric: the Imitation Rock Porcelain Tiles green compact executing fabric are dried in dry kiln at 200 DEG C again；
(8) spray infiltration ink: use Digital ink-jet printer to be sprayed on Imitation Rock Porcelain Tiles base substrate by the pattern designed, coordinate blank pattern texture so that brick body surface and base substrate have close texture and quality, and ink jet layer thickness is 0.3mm；
(9) burn till: the Imitation Rock Porcelain Tiles green compact that step (8) is jetted through permeating ink are placed in roller kilns the conventional Imitation Rock Porcelain Tiles firing temperature system of use, pressure regime and atmosphere system, once-firing, firing temperature is 1160 DEG C, and firing period is 85min, prepares Imitation Rock Porcelain Tiles semi-finished product；
(10) edging: utilizing conventional edging process equipment, double finished bricks carries out edging process, i.e. obtains the Imitation Rock Porcelain Tiles finished product of a kind of natural surface with three-dimensional decorative effect.
Embodiment 2
(1) prepare Imitation Rock Porcelain Tiles base substrate powder according to a conventional method, allocate 5 kinds of color powders standby；
(2) Imitation Rock Porcelain Tiles fabric is prepared, fabric A uses feldspar poor material and kaolin families plastic raw material to carry out dispensing, the siccative of fabric B all uses aluminium oxide, quartz, feldspar non-plastic raw material to carry out dispensing, wet ball grinding, the slurry of two kinds of fabrics all control fineness be 325 mesh sieve margins within 0.5%, proportion is 1.80g/cm3Wherein the siccative of starch adhesive A becomes to meet pouring with auxiliary additive wet ball grinding and executes the slurry of performance requirement, the siccative of fabric B and auxiliary additive wet ball grinding meet size performance and require post-drying, make dry powder, and the printing fabric meeting printing performance it is mixed with stamp-pad ink, auxiliary additive, standby.The chemical composition range of two kinds of fabrics is (weight portion): SiO2: 62%, Al2O3: 19%, MgO+CaO:2.0%, K2O+Na2O:7%, surplus is impurity, also needs additional ZnO 0.5%, TiO in fabric B2 4%。
(3) Imitation Rock Porcelain Tiles body preparation: by Imitation Rock Porcelain Tiles base substrate powder prepared in step (1) according to the pattern texture designed, carries out multitube cloth, and then paving cloth is in brick machine die cavity, under the pressure of 40MPa, Imitation Rock Porcelain Tiles base substrate powder pressing is become Imitation Rock Porcelain Tiles green compact；
(4) Imitation Rock Porcelain Tiles green compact step (3) prepared are dried in dry kiln at 200 DEG C；
(5) starch adhesive A is drenched: Imitation Rock Porcelain Tiles starch adhesive A glaze pouring step (2) prepared executes cloth Imitation Rock Porcelain Tiles green surface after the drying, and the weight of the executed starch adhesive of unit are is 600g/m2；
(6) printing fabric B: Imitation Rock Porcelain Tiles fabric B silk-screen printing technique step (2) prepared executes cloth in the billet surface drenching starch adhesive A；
(7) it is dried after executing cloth fabric: the Imitation Rock Porcelain Tiles green compact executing fabric are dried in dry kiln at 180 DEG C again；
(8) spray infiltration ink: use Digital ink-jet printer to be sprayed on Imitation Rock Porcelain Tiles base substrate by the pattern designed, coordinate blank pattern texture so that brick body surface and base substrate have close texture and quality, and ink jet layer thickness is 0.8mm；
(9) burn till: the Imitation Rock Porcelain Tiles green compact that step (8) is jetted through permeating ink are placed in roller kilns the conventional Imitation Rock Porcelain Tiles firing temperature system of use, pressure regime and atmosphere system, once-firing, firing temperature is 1200 DEG C, and firing period is 60min, prepares Imitation Rock Porcelain Tiles semi-finished product；
(10) edging and polishing: utilizing conventional edging process equipment, double finished bricks carries out edging process, then be processed by shot blasting Imitation Rock Porcelain Tiles surface, i.e. obtains a kind of polished brick in porcelain character finished product with three-dimensional decorative effect.
Embodiment 3
(1) prepare Imitation Rock Porcelain Tiles base substrate powder according to a conventional method, allocate 4 kinds of color powders standby；
(2) Imitation Rock Porcelain Tiles fabric is prepared, fabric A uses feldspar poor material and kaolin families plastic raw material to carry out dispensing, the siccative of fabric B all uses aluminium oxide, quartz, feldspar non-plastic raw material to carry out dispensing, wet ball grinding, the slurry of two kinds of fabrics all control fineness be 325 mesh sieve margins within 0.5%, proportion is 1.86g/cm3Wherein the siccative of starch adhesive A becomes to meet pouring with auxiliary additive wet ball grinding and executes the slurry of performance requirement, the siccative of fabric B and auxiliary additive wet ball grinding meet size performance and require post-drying, make dry powder, and the printing fabric meeting printing performance it is mixed with stamp-pad ink, auxiliary additive, standby.The chemical composition range of two kinds of fabrics is (weight portion): SiO2: 65%, Al2O3: 17%, MgO+CaO:2.0%, K2O+Na2O:8%, surplus is impurity, also needs additional ZnO 0.8%, TiO in fabric B2 3%。
(3) Imitation Rock Porcelain Tiles body preparation: by Imitation Rock Porcelain Tiles base substrate powder prepared in step (1) according to the pattern texture designed, carries out multitube cloth, and then paving cloth is in brick machine die cavity, under the pressure of 50MPa, Imitation Rock Porcelain Tiles base substrate powder pressing is become Imitation Rock Porcelain Tiles green compact；
(4) Imitation Rock Porcelain Tiles green compact step (3) prepared are dried in dry kiln at 270 DEG C；
(5) starch adhesive A is drenched: Imitation Rock Porcelain Tiles starch adhesive A glaze pouring step (2) prepared executes cloth Imitation Rock Porcelain Tiles green surface after the drying, and the weight of the executed starch adhesive of unit are is 400g/m2；
(6) printing fabric B: Imitation Rock Porcelain Tiles fabric B roller typography step (2) prepared executes cloth in the billet surface drenching starch adhesive A；
(7) it is dried after executing cloth fabric: the Imitation Rock Porcelain Tiles green compact executing fabric are dried in dry kiln at 250 DEG C again；
(8) spray infiltration ink: use Digital ink-jet printer to be sprayed on Imitation Rock Porcelain Tiles base substrate by the pattern designed, coordinate blank pattern texture so that brick body surface and base substrate have close texture and quality, and ink ejection face layer thickness is 0.5mm；
(9) burn till: the Imitation Rock Porcelain Tiles green compact that step (8) is jetted through permeating ink are placed in roller kilns the conventional Imitation Rock Porcelain Tiles firing temperature system of use, pressure regime and atmosphere system, once-firing, firing temperature is 1230 DEG C, and firing period is 50min, prepares Imitation Rock Porcelain Tiles semi-finished product；
(10) edging and soft throwing: utilizing conventional edging process equipment, double finished bricks carries out edging process, then Imitation Rock Porcelain Tiles surface carries out soft throwing process, i.e. obtains a kind of porcelain Asia light brick finished product with three-dimensional decorative effect.
Above example is only in order to illustrate that technical scheme is not intended to limit, although being described in detail the present invention with reference to preferred embodiment, those of ordinary skill in the field are to be understood that.Still can modify the detailed description of the invention of invention or portion of techniques feature is carried out equivalent, without deviating from the spirit of technical solution of the present invention, it all should be contained in the middle of the technical scheme scope that the present invention is claimed.
Claims (8)
1. the production method of an Imitation Rock Porcelain Tiles with three-dimensional decorative effect, it is characterised in that it comprises the following steps:
(1) Imitation Rock Porcelain Tiles base substrate powder is prepared according to a conventional method, standby；
(2) preparing Imitation Rock Porcelain Tiles fabric, the siccative chemical composition that the Imitation Rock Porcelain Tiles fabric of employing is divided into starch adhesive A and fabric B two kinds, starch adhesive A and fabric B is consistent, similar to base substrate powder in step (1), but wherein K2O+Na2O:6 ~ 8%, impurity≤4%(is all weight percentage)；The siccative of starch adhesive A uses feldspar poor material and kaolin families plastic raw material to carry out dispensing, but the siccative of fabric B all uses aluminium oxide, quartz, feldspar non-plastic raw material to carry out dispensing；The slurry of two kinds of fabrics all control fineness be 325 mesh sieve margins within 0.5%, proportion is 1.60 ~ 1.90g/cm3Wherein the siccative of starch adhesive A becomes to meet pouring with auxiliary additive wet ball grinding and executes the slurry of performance requirement, the siccative of fabric B and auxiliary additive wet ball grinding meet size performance and require post-drying, make dry powder, and the printing fabric meeting printing performance it is mixed with stamp-pad ink, auxiliary additive, standby；
(3) Imitation Rock Porcelain Tiles body preparation: by Imitation Rock Porcelain Tiles base substrate powder prepared in step (1) according to the pattern texture designed, carry out multitube cloth, then paving cloth is in brick machine die cavity, under the pressure of 20 ~ 50MPa, Imitation Rock Porcelain Tiles base substrate powder pressing is become Imitation Rock Porcelain Tiles green compact；
(4) body drying: Imitation Rock Porcelain Tiles green compact step (3) prepared are dried in dry kiln at 150 ~ 300 DEG C；
(5) starch adhesive A is drenched: Imitation Rock Porcelain Tiles starch adhesive A glaze pouring step (2) prepared executes cloth Imitation Rock Porcelain Tiles green surface after the drying, and the weight of the executed starch adhesive of unit are is 400 ~ 800g/m2；
(6) printing fabric B: Imitation Rock Porcelain Tiles fabric B typography step (2) prepared executes cloth in the billet surface drenching starch adhesive A；
(7) it is dried after executing cloth fabric: the Imitation Rock Porcelain Tiles green compact executing fabric are dried in dry kiln at 150 ~ 300 DEG C again；
(8) spray infiltration ink: use Digital ink-jet printer to be sprayed on Imitation Rock Porcelain Tiles base substrate by the pattern designed, coordinate blank pattern texture so that brick body surface and base substrate have close texture and quality；
(9) burn till: the Imitation Rock Porcelain Tiles green compact that step (8) is jetted through permeating ink are placed in roller kilns the conventional Imitation Rock Porcelain Tiles firing temperature system of use, pressure regime and atmosphere system, once-firing, firing temperature is 1150 ~ 1250 DEG C, and firing period is 40 ~ 90min, prepares Imitation Rock Porcelain Tiles semi-finished product；
(10) edging: utilizing conventional edging process equipment, double finished bricks carries out edging process, prepares the Imitation Rock Porcelain Tiles finished product with three-dimensional decorative effect.
There is the production method of the Imitation Rock Porcelain Tiles of three-dimensional decorative effect the most as claimed in claim 1, it is characterised in that: step (2) comprises auxiliary colorant ZnO, TiO in the auxiliary additive of fabric B2In one or more, fabric A does not comprise auxiliary colorant ZnO, TiO2。
3. the auxiliary additive of fabric B as claimed in claim 2, it is characterised in that: described additive addition is calculated as ZnO for 0.2 ~ 1% with fabric siccative, TiO2It is 0.2 ~ 5%.
There is the production method of the Imitation Rock Porcelain Tiles of three-dimensional decorative effect the most as claimed in claim 1, it is characterised in that: the printing web process in step (6) can use silk screen printing or glue roller printing.
There is the production method of the Imitation Rock Porcelain Tiles of three-dimensional decorative effect the most as claimed in claim 1, it is characterised in that: step (6) can use the uneven printing in local so that stereo decoration texture is more life-like.
There is the production method of the Imitation Rock Porcelain Tiles of three-dimensional decorative effect the most as claimed in claim 1, it is characterised in that: step (8) ink ejection face layer thickness is 0.3 ~ 1.0mm.
There is the production method of the Imitation Rock Porcelain Tiles of three-dimensional decorative effect the most as claimed in claim 1, it is characterised in that: after step (10) edging processes, polishing or soft throwing PROCESS FOR TREATMENT can be used.
8. the Imitation Rock Porcelain Tiles with three-dimensional decorative effect prepared by the production method of any one Imitation Rock Porcelain Tiles with three-dimensional decorative effect such as claim 1 ~ 7.