CN104325823A - Glazed porcelain polished tile and production method thereof - Google Patents

Glazed porcelain polished tile and production method thereof Download PDF

Info

Publication number
CN104325823A
CN104325823A CN201410528602.4A CN201410528602A CN104325823A CN 104325823 A CN104325823 A CN 104325823A CN 201410528602 A CN201410528602 A CN 201410528602A CN 104325823 A CN104325823 A CN 104325823A
Authority
CN
China
Prior art keywords
production
glazing
pattern
porcelain
polished brick
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410528602.4A
Other languages
Chinese (zh)
Inventor
李华云
樊叶利
夏昌奎
钟金明
彭西洋
王广山
郑为兵
许家祥
邓国庆
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
DEQING NABEL CERAMIC Co Ltd
Original Assignee
DEQING NABEL CERAMIC Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DEQING NABEL CERAMIC Co Ltd filed Critical DEQING NABEL CERAMIC Co Ltd
Priority to CN201410528602.4A priority Critical patent/CN104325823A/en
Publication of CN104325823A publication Critical patent/CN104325823A/en
Pending legal-status Critical Current

Abstract

The invention relates to a glazed porcelain polished tile and a production method thereof. The method comprises: a) preparation of ordinary porcelain tile formula powder; b) transparent glaze application to a thickness of 0.5-1.0mm; c) firing at a temperature of 1100-1200DEG C; and d) edging polishing. The method is characterized in that: it also includes a pattern forming step between the step a) and step b). And the pattern forming step is realized through coordination of cloth molding and pattern printing. Due to combination of distribution, ink jetting, rubber rolls, silk-screen printing and other decoration means, the surface pattern of the glazed porcelain polished tile prepared by the method provided by the invention has more exquisite and vivid effects and richer layering than single mechanical mixing and distribution ways, thus realizing technical innovation of traditional porcelain polished tiles.

Description

A kind of glazing polished brick in porcelain character and production method thereof
Technical field
The present invention relates to architectural pottery technical field, be specifically related to a kind of glazing polished brick in porcelain character and production method thereof.
Background technology
Along with the change of growth in the living standard and life style, the esthetic requirement of consumer to building and ornament materials is more and more higher, and this demand effectively facilitates the development of building and ornament materials industry.
Wall or floor tile is one of main material of building and ornament materials, is mainly divided into two large classes: polished bricks and glazed tile.Existing polished brick in porcelain character picture on surface mainly overall batch mixing, multitube cloth, the modes such as flower, micro mist cloth of oozing is formed, and prepares from pure color to particle, oozes flower, micro mist and the ceramic polished brick product of lines micro mist.Be limited to equipment and technology, polished brick in porcelain character distributing mode means are few, and mechanical material distributing surface detail decoration is dull, decorative effect is abundant not.Chinese patent CN200410050914.5A discloses the technique that a kind of overall mixing method produces polished brick in porcelain character, suppress by add the mixing of a certain proportion of monocrystalline silicon inside base substrate powder after, product surface forms flash metal luster spot effect, owing to being mechanical batch mixing, can not control the flash of light spot distribution of finished surface, gained flash effect aesthetic feeling is not strong; Chinese patent CN201110277391.8A discloses a kind of method that polished tile simulating texture of natural stone prepared by multitube cloth, the simulation to natural stone texture is realized by multiple distribution device, this simulation also has its limitation, be limited to the color that the quantity of distribution device and often kind of distribution device hold, it cannot realize the production that color-grading effect and Color Range such as to enrich at the product.
With polished brick in porcelain character unlike, glazed tile does not present pattern by base substrate itself, but on base substrate, drench cosmetic soil, execute cover-coat enamel after again by the decorative means such as rubber roll, silk screen printed patterns.Prevailing along with ink-jet technology, the variation of printed patterns mode, glazed tile decorated style takes on an entirely new look, and market sale is dominate gradually.
Although traditional polished brick in porcelain character is more and more subject to the impact of glazed tile, but the serviceability that traditional polished brick in porcelain character has is good, and soil resistance, wearability are good etc., and advantage still cannot be replaced by glazed tile, and these advantages make it still have application space.In order to improve the decorative effect of existing polished brick in porcelain character and reduce production cost, insider's exploratory development always expects can there be further lifting to polished brick in porcelain character incrustation pattern process.
Summary of the invention
The problem that traditional polished brick in porcelain character surface detail decoration technique is dull in order to break through, decorative effect enriches not, the invention provides a kind of production method of glazing polished brick in porcelain character, can obtain the decorative effect that matches in excellence or beauty with glazed tile and reduce production cost.
Technical scheme of the present invention is as follows:
A production method for glazing polished brick in porcelain character, comprising:
A) preparation of common Imitation Rock Porcelain Tiles formula powder;
B) clear frit is executed: glazing thickness 0.5 ~ 1.0mm;
C) burn till: firing temperature 1100 ~ 1200 DEG C;
D) edging polishing;
It is characterized in that: step a) and b) between also comprise pattern forming step, described pattern forming step is shaping by cloth and pattern printing coordinates and realizes.
Described cloth is shaping is the pattern forming certain decorative effect with apparatus for distributing on surface, preferred mode is that multitube cloth conventional during polished brick in porcelain character is produced is shaping or micro mist cloth is shaping, forms the grain surfaces such as pimple, bulky grain and/or micro mist lines.
It is the pattern formed on surface by the method for machinery because described cloth is shaping, be limited by equipment and technology, decorative effect has its limitation, bright spot of the present invention is on the basis of shaping the formed pattern of cloth, introduce pattern printing means, the two cooperatively interacts, and forms complementary decorative effect.Pattern cooperation is herein equivalent on the basis of traditional polished bricks distributing technique, and the veinpatterns design formed with base substrate cloth for background, then with the pattern that the printing of pattern typography coordinates with base substrate skin texture, makes printed patterns and base substrate skin texture combine together.Although both distributing technique and pattern typography separately application belong to prior art, but the two is combined application, natural texture train of thought can be built at ceramic tile surface, printed patterns is highlighted again by base substrate skin texture, it is overall that the two can form the fusion with special-effect, makes product surface aesthetic feeling have great lifting.
Pattern printing of the present invention is ink jet printing, glue roller printing and/or serigraphy.Described pattern printing mainly plays two aspects: one is the color after supplementary billet surface is burnt, and makes billet surface color abundanter; Two is supplementing billet surface texture, such that superficial makings is more naturally true to nature, the abundanter exquisiteness of level.
In order to make decorative effect abundanter, described cloth is shaping, also comprise the soft throwing of green compact between pattern printing, and make green surface have a kind of crude concavo-convex texture, pattern printing means shaping with cloth is combined, and forms a kind of third dimension picture of vision drop.In order to make, concavo-convex texture, cloth are shaping, pattern printing three decorative effect realizes best fit, and the thickness that the soft throwing of described green compact is skimmed is not more than 0.5mm.
Clear frit that step b) of the present invention is executed is polishing glaze, mainly plays two aspects: one is protection product with pattern on surface, makes the pattern of billet surface printing and/or the soft throwing of green compact be able to intact reservation; Two is the antifouling properties improving goods.
The glazing polished brick in porcelain character surface detail that production method of the present invention is produced, owing to combining the printing technology such as cloth and ink-jet, decorative means variation, texture is finer and smoother more true to nature by mechanical material distributing mode than simple, color is abundanter, level is more various, achieves the technological innovation of traditional polished brick in porcelain character.
Compared to traditional polished brick in porcelain character, adopt the Imitation Rock Porcelain Tiles produced of the present invention except above-mentioned decorative pattern is finer and smoother, true to nature, abundant except, also there are other advantages.Semi-finished product after tradition polished brick in porcelain character burns till need the top layer that polishing jettisoning 0.5 ~ 1.0mm is thick, and the semifinished product thickness adopting method of the present invention to produce is at 0.2 ~ 0.5mm, significantly reduce polishing slag generation, both reduce fixed-end forces cost, additionally reduce the impact on environment.In addition, for traditional polished brick in porcelain character, in order to cost-saving, often take secondary material distributing technology, bottom uses inferior raw material, often makes bottom inferior reveal when aft-loaded airfoil such as fluting, chamferings, the aesthetic feeling of impact decoration.Adopt the glazing polished brick in porcelain character that the method for the invention is produced, due to the minimizing of polishing thickness and the existence of clear frit layer, make can not reveal when aft-loaded airfoil such as fluting, chamferings with the bottom inferior of secondary material distributing product, thus the decorative effect of goods can not be affected, achieve the variation of product following process mode.
Compared to glazed tile, the glazing polished brick in porcelain character that the present invention produces have employed the blank forming technique being different from glazed tile, base substrate is made to become a part for whole decorative pattern by cloth, the every sheet of base substrate formed by distributing mode all presents different patterns, for variable effects is introduced in brick surface, incrustation is full of variety, no longer stereotyped.In addition, the method for the invention is save pouring cosmetic soil than glazed tile production technology, is executed cover-coat enamel step, the technological process of production is shortened, reduces production cost.
It should be noted that, will through the step of super-dry after powder pressing is shaping, the continuity of the present invention in order to describe, does not mention the drying steps that those skilled in the art are readily appreciated that in the particular content of invention, but this not illustrates that drying is unwanted.
Detailed description of the invention
The production method of [embodiment 1] glazing polished brick in porcelain character of the present invention, comprises the following steps:
1) preparation of common Imitation Rock Porcelain Tiles formula powder;
2) pattern is formed
1. adopt polished brick in porcelain character bulky grain cloth shaping;
2. the ceramic digital ink-jet machine inkjet print image 1. coordinated with step;
3) clear frit is executed: glazing thickness 0.5mm;
4) burn till: firing temperature is 1150 DEG C, firing period 60min;
5) edging polishing.
The production method of [embodiment 2] glazing polished brick in porcelain character of the present invention, comprises the following steps:
1) preparation of common Imitation Rock Porcelain Tiles formula powder;
2) pattern is formed
1. adopt ceramic polished tile micro mist cloth shaping;
2. the glue roller printing pattern 1. coordinated with step;
3) clear frit is executed: glazing thickness 0.7mm;
4) burn till: firing temperature is 1180 DEG C, firing period 55min;
5) edging polishing.
The production method of [embodiment 3] glazing polished brick in porcelain character of the present invention, comprises the following steps:
1) preparation of common Imitation Rock Porcelain Tiles formula powder;
2) pattern is formed
1. adopt polished brick in porcelain character multitube cloth shaping;
2. the screen printed pattern 1. coordinated with step;
3) clear frit is executed: glazing thickness 1.0mm;
4) burn till: firing temperature is 1200 DEG C, firing period 45min;
5) edging polishing.

Claims (6)

1. a production method for glazing polished brick in porcelain character, comprising: a) preparation of common Imitation Rock Porcelain Tiles formula powder; B) clear frit is executed: glazing thickness 0.5 ~ 1.0mm; C) burn till: firing temperature 1100 ~ 1200 DEG C; D) edging polishing; It is characterized in that: step a) and b) between also comprise pattern forming step, described pattern forming step is shaping by cloth and pattern printing coordinates and realizes.
2. the production method of glazing polished brick in porcelain character according to claim 1, is characterized in that: described cloth be shaped to the shaping or micro mist cloth of multitube cloth shaping in one.
3. the production method of glazing polished brick in porcelain character according to claim 1, is characterized in that: described pattern printing is ink jet printing, glue roller printing and/or serigraphy.
4. according to the production method of the arbitrary described glazing polished brick in porcelain character of claim 1 ~ 3, it is characterized in that: described cloth is shaping, also comprise the soft throwing of green compact between pattern printing.
5. the production method of glazing polished brick in porcelain character according to claim 4, the thickness that the soft throwing of described green compact is skimmed is not more than 0.5mm.
6. the glazing polished brick in porcelain character of the production method production of the glazing polished brick in porcelain character according to the arbitrary claim of claim 1 ~ 5.
CN201410528602.4A 2014-10-10 2014-10-10 Glazed porcelain polished tile and production method thereof Pending CN104325823A (en)