CN109352882A - 去除高压二极管引脚树脂毛刺工艺 - Google Patents
去除高压二极管引脚树脂毛刺工艺 Download PDFInfo
- Publication number
- CN109352882A CN109352882A CN201811252014.7A CN201811252014A CN109352882A CN 109352882 A CN109352882 A CN 109352882A CN 201811252014 A CN201811252014 A CN 201811252014A CN 109352882 A CN109352882 A CN 109352882A
- Authority
- CN
- China
- Prior art keywords
- basket
- voltage diode
- temperature
- burr
- syd712
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种去除高压二极管引脚树脂毛刺工艺，去除压塑后高压二极管半成品的引脚树脂毛刺，它包括如下步骤;（1）工艺准备；（2）去除树脂毛刺；（3）清洗；（4）烘干。构思巧妙，设计合理，利用SYD712去毛刺液浸泡高压二极管，软化剥离高压二极管引脚的毛刺，去毛刺效果好，工效快，省时省工，每人每班可处理50个生产批。人工刮毛刺每人每班次生产量为1.2批。大大提高了劳动生产率。
Description
技术领域
本发明涉及高压二极管电极引线表面处理技术，具体涉及一种去除高压二极管引脚树脂毛刺工艺。
背景技术
为了保证引线外观和易焊性，高压二极管引线一般采用无氧铜线表面镀银。镀银引线与硅块组装烧结后，经过一系列清洗处理，硅块表面涂胶钝化，然后以环氧树脂进行模压封装。在进行封装过程中，位于塑封模进料口引线会有树脂毛刺残留，这种树脂毛刺会影响产品外观与可焊性，因此高压二极管生产工程设置有去毛刺工序，手工以刮刀刮除引线表面附着毛刺，费时费工，成本高。
发明内容
为解决上述问题，本发明提出一种一种去除高压二极管引脚树脂毛刺工艺，构思巧妙，设计合理，利用SYD712去毛刺液浸泡高压二极管，软化剥离高压二极管引脚的毛刺，去毛刺效果好，工效快，省时省工，每人每班可处理50个生产批。人工刮毛刺每人每班次生产量为1.2批。大大提高了劳动生产率。
本发明的技术方案：
一种去除高压二极管引脚树脂毛刺工艺，去除压塑后高压二极管半成品的引脚树脂毛刺，它包括如下步骤
（1）工艺准备
准备好不锈钢筐篮、不锈钢钩子；将后固化好的高压二极管倒入不锈钢筐篮；检查SYD712去毛刺液槽装置的加热器、冷却水通风橱是否正常SYD712去毛刺液槽装置的加热器温度设定为65℃±3℃，并每天用温度计测量一次液温，应为65℃±3℃,不符应作调节；检查SYD712去毛刺液槽装置内液量是否在液位标记，液位标记为40L±5L，不足时应向槽内加入SYD712去毛刺液至液位标记；确认排水装置及液槽无泄漏；确认压空压力大于5.5Kg/cm2；确认高压水枪压力为5Mpa；确认高温箱的温度设定为130℃±5℃。
（2）去除树脂毛刺
接通电源，开启排风装置，开启温度控制器，进行升温；将每批高压硅堆均分成四筐篮待处理；当温度升至设定温度后，用不锈钢钩子钩住筐篮，放入SYD712去毛刺液槽装置内，每槽允许放入两筐篮高压硅堆；待浸泡75min~80min，用不锈钢钩子将筐篮取出；将筐篮放入水洗槽清洗10min±5min.；开启高压水枪，对筐篮内管子进行喷射，使引线根部毛刺受高温冲击去除干净。
（3）清洗
将筐篮放入纯水槽洗5min~10min，将毛刺冲洗干净；并用空气枪吹净筐篮表面的水珠。
（4）烘干
开启高温箱电源，升温至设定温度，将不锈钢筐篮放到高温箱内部，10 1.5h±0.1h后，将筐篮取出，待冷却后，将待加工品收入保管箱内，完成高压二极管引脚树脂毛刺的去除。
对上述技术方案作进一步的改进和细化，在步骤（1）中所述的SYD712去毛刺液的配方为：异丙醇与二甲基甲酰胺按照重量比15：85混合配置而成。
对上述技术方案作进一步的改进和细化，在步骤（1）（2）中所述的SYD712去毛刺液槽装置的型号为ZH-127；在步骤（1）（4）中所述的高温箱的型号为L30-4A 0℃~300℃。
本发明优点是，构思巧妙，设计合理，利用SYD712去毛刺液浸泡高压二极管，软化剥离高压二极管引脚的毛刺，去毛刺效果好，工效快，省时省工，每人每班可处理50个生产批。人工刮毛刺每人每班次生产量为1.2批。大大提高了劳动生产率。
具体实施方式
一种去除高压二极管引脚树脂毛刺工艺，去除压塑后高压二极管半成品的引脚树脂毛刺，它包括如下步骤：
（1）工艺准备
准备好不锈钢筐篮、不锈钢钩子；将后固化好的高压二极管倒入不锈钢筐篮；检查型号为去毛刺液槽装置的加热器、冷却水通风橱是否正常；型号为ZH-127的SYD712去毛刺液槽装置的加热器温度设定为65℃±3℃，并每天用温度计测量一次液温，应为65℃±3℃,不符应作调节；检查SYD712去毛刺液槽装置内液量是否在液位标记，液位标记为40L±5L，不足时应向槽内加入SYD712去毛刺液至液位标记；确认排水装置及液槽无泄漏；确认压空压力大于5.5Kg/cm2；确认高压水枪压力为5Mpa；确认高温箱的温度设定为130℃±5℃；所述的SYD712去毛刺液的配方为：异丙醇与二甲基甲酰胺按照重量比15：85混合配置而成。
（2）去除树脂毛刺
接通电源，开启排风装置，开启温度控制器，进行升温；将每批高压硅堆均分成四筐篮待处理；当温度升至设定温度后，用不锈钢钩子钩住筐篮，放入SYD712去毛刺液槽装置内，每槽允许放入两筐篮高压硅堆；待浸泡75min~80min，用不锈钢钩子将筐篮取出；将筐篮放入水洗槽清洗10min±5min.；开启高压水枪，对筐篮内管子进行喷射，使引线根部毛刺受高温冲击去除干净。
（3）清洗
将筐篮放入纯水槽洗5min~10min，将毛刺冲洗干净；并用空气枪吹净筐篮表面的水珠。
（4）烘干
开启高温箱电源，升温至设定温度，将不锈钢筐篮放到高温箱内部，10 1.5h±0.1h后，将筐篮取出，待冷却后，将待加工品收入保管箱内，完成高压二极管引脚树脂毛刺的去除。
仪器仪表清单：
| 序 号 | 名 称 | 型 号(编号、规格) |
| 3．1．1 | SYD712液槽装置 | ZH-127 |
| 3．1．2 | 高压水装置 | |
| 3．1．3 | 高温箱 | L30-4A 0℃~300℃ |
装夹工具清单：
| 序 号 | 名 称 | 规 格（编号） |
| 3．2．1 | 不锈钢筐篮 | |
| 3．2．2 | 不锈钢钩子 |
由于文字表达的有限性，而客观上存在无限的具体结构，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进、润饰或变化，也可以将上述技术特征以适当的方式进行组合；这些改进润饰、变化或组合，或未经改进将发明的构思和技术方案直接应用于其它场合的，均应视为本发明的保护范围。
Claims (3)
1.一种去除高压二极管引脚树脂毛刺工艺，去除压塑后高压二极管半成品的引脚树脂毛刺，其特征在于，它包括如下步骤
（1）工艺准备
准备好不锈钢筐篮、不锈钢钩子；将后固化好的高压二极管倒入不锈钢筐篮；检查SYD712去毛刺液槽装置的加热器、冷却水通风橱是否正常SYD712去毛刺液槽装置的加热器温度设定为65℃±3℃，并每天用温度计测量一次液温，应为65℃±3℃,不符应作调节；检查SYD712去毛刺液槽装置内液量是否在液位标记，液位标记为40L±5L，不足时应向槽内加入SYD712去毛刺液至液位标记；确认排水装置及液槽无泄漏；确认压空压力大于5.5Kg/cm2；确认高压水枪压力为5Mpa；确认高温箱的温度设定为130℃±5℃；
（2）去除树脂毛刺
接通电源，开启排风装置，开启温度控制器，进行升温；将每批高压硅堆均分成四筐篮待处理；当温度升至设定温度后，用不锈钢钩子钩住筐篮，放入SYD712去毛刺液槽装置内，每槽允许放入两筐篮高压硅堆；待浸泡75min~80min，用不锈钢钩子将筐篮取出；将筐篮放入水洗槽清洗10min±5min.；开启高压水枪，对筐篮内管子进行喷射，使引线根部毛刺受高温冲击去除干净；
（3）清洗
将筐篮放入纯水槽洗5min~10min，将毛刺冲洗干净；并用空气枪吹净筐篮表面的水珠；
（4）烘干
开启高温箱电源，升温至设定温度，将不锈钢筐篮放到高温箱内部，10 1.5h±0.1h后，将筐篮取出，待冷却后，将待加工品收入保管箱内，完成高压二极管引脚树脂毛刺的去除。
2.根据权利要求1所述的一种去除高压二极管引脚树脂毛刺工艺，其特征在于，在步骤（1）中所述的SYD712去毛刺液的配方为：异丙醇与二甲基甲酰胺按照重量比15：85混合配置而成。
3.根据权利要求1所述的一种去除高压二极管引脚树脂毛刺工艺，其特征在于，在步骤（1）（2）中所述的SYD712去毛刺液槽装置的型号为ZH-127；在步骤（1）（4）中所述的高温箱的型号为L30-4A 0℃~300℃。