CN109275785A - A kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method - Google Patents
A kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method Download PDFInfo
- Publication number
- CN109275785A CN109275785A CN201710588884.0A CN201710588884A CN109275785A CN 109275785 A CN109275785 A CN 109275785A CN 201710588884 A CN201710588884 A CN 201710588884A CN 109275785 A CN109275785 A CN 109275785A
- Authority
- CN
- China
- Prior art keywords
- nano montmorillonite
- mycotoxin
- feed addictive
- bacillus subtilis
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antibacterials, absorbing mycotoxin nano montmorillonite feed addictive preparation method, belong to additive for farm animal feed field, product of the present invention is made of following raw material according to weight percent: nano montmorillonite 40-50%, zinc oxide 1-5%, yeast cell wall 4-6%, bacillus subtilis freeze-dried powder 5-8%, vitamin C 4-5%, propionic acid/propionate 10-15%, sodium Diacetate 7-11%.The present invention has stronger ion-exchange capacity and mycotoxin adsorption ability, the loss of nutriment will not be generated simultaneously, simultaneously the present invention can effectively preventing livestock and poultry diarrhea, inhibit mould proliferation, absorption degradation mycotoxin, mitigate mycotoxin growth of animals or poultry is influenced, improves animal and bird intestines colony balance, improve the use of growth of animals or poultry performance, effective reduction antibiotic during livestock and poultry cultivation.
Description
Technical field
The present invention relates to feed additive fields, and in particular to a kind of antibacterial, absorbing mycotoxin nano montmorillonite feed
Addictive preparation method.
Background technique
During growth of animal, it all can pass through metabolic nutrition substance along with various harmful bacterias, some meetings, have
Be then by generate toxin come influence animal body health and normal immunological, to reduce efficiency of feed utilization and growth
Energy.
At present feed addictive in the market, generally use zinc oxide, copper sulphate, Peracetic acid, propionic acid, yeast cells
Wall, probiotics etc. inhibit the proliferation of bacterium, fungi, and by adding copper in feed addictive, zinc has not only played its antibacterial
Effect can also promote growth of animal, add yeast cell wall and probiotics mainly passes through yeast cell wall and probiotics metabolism
Product blocks harmful bacteria in intestinal colonisation, while can also promote the proliferation of intestinal beneficial bacterium, improves intestinal flora balance.
Montmorillonite (montmorillonite) also known as montmorillonite or montmorillonite, are a kind of alumino-silicates, mainly at
It is divided into octahedra hectorite microparticle, layered arrangement sial of the 2:1 being pumped by oxygen-octahedron and alumina octahedral containing the crystallization water
Hydrochlorate mineral have good dispersibility and ion exchangeable, can be with using this feature of montmorillonite heterogeneity distribution of charges
For adsorbing the mycotoxin of mould generation.The montmorillonite product usually to circulate in the market, is mostly to have absorption to aflatoxin
Effect, it is unobvious to other mycotoxin adsorption effects, exist simultaneously the drawbacks such as absorption amino acid, vitamin.
Summary of the invention
The present invention provides a kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method.Main purpose
It is to solve the disadvantage that the prior art currently on the market, existing product is overcome to adsorb single mycotoxin, non-antibacterial, absorption nutrition
The defects of element, can effectively inhibit harmful bacteria growth, absorbing mycotoxin, not adsorb nutrient.
The technical solution adopted by the invention is as follows:
A kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method, it is characterised in that with weight percent
Meter, is made of following components: nano montmorillonite 40-50%, zinc oxide 1-5%, yeast cell wall 4-6%, bacillus subtilis freeze-drying
Powder 5-8%, vitamin C 4-5%, propionic acid/propionate 10-15%, sodium Diacetate 7-11%.
Preferably, a kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method, according to weight
Percentages, including following components: nano montmorillonite 48%, zinc oxide 2.5%, yeast cell wall 5%, bacillus subtilis freeze-drying
Powder 7%, vitamin C 4.5%, propionic acid/propionate 14%, sodium Diacetate 10%.
A kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method are as follows:
Respectively by nano montmorillonite, zinc oxide, yeast cell wall, bacillus subtilis freeze-dried powder, vitamin C, propionic acid/propionic acid
Salt, sodium Diacetate proportionally by feed addictive mixing unit be uniformly mixed to get.
The process of preparing of the bacillus subtilis freeze-dried powder, is realized by following process means:
1) bacillus subtilis is subjected to fermented and cultured, culture medium prescription (%): corn flour 3, soybean cake powder using fermentation medium
2 (hydrolyzate adds 121 DEG C of hydrolysis 30min of 0.5%NaOH, cooling, filtering), peptone 0.2, KH2PO4 0.15,
K2HPO40.15、NaSO4 0.15、CaCl20.03, MnSO4 0.01、MgSO40.06, NaCl 0.2, glucose 0.5 is spat
Temperature -80 0.03, pH8.0,37 DEG C of constant temperature incubation 48h.
2) after fermentation, fermentation liquid sterile working is fitted into centrifuge, under the conditions of 25 DEG C, 10000 rpm/min from
5 min of the heart discards supernatant liquid, and gained centrifugal sediment is bacterium mud, and bacterium mud is suspended again with 1% peptone water solution becomes
Suspension, and bacillus subtilis bacteria concentration is made to be about 109 cfu/mL。
3) it will be atomized in bacillus subtilis bacterium solution prepared by step 2 injection atomizer, air pressure is when atomization
0.72 kgf/cm2, fluid pressure is 0.45 kgf/cm2。
4) liquid droplet after being atomized is used in the collecting tank equipped with appropriate calcium chloride solution (0.55 mol/L), and process is collected
In by magnetic stirring apparatus be gently mixed calcium chloride solution harden 20 min, then use highly dense the screen to filtrate, and with distill washing
It washs twice, is then transferred in packaging material (with chitosan with example) lactic acid solution (chitosan C 1.0%(w/v) and lactic acid 0.5%(v/ again
V)), being gently mixed 10 min is coated with alginate microcapsules surface uniformly.
5) it filters and then the microcapsules for washing the step 4) preparation is done again in -72 DEG C of 6 h of freeze-drying in -75 DEG C
Dry 18 h, pressure is set as 5.28 Pa to get bacillus subtilis freeze-dried powder when dry.
The invention patent enhances the exchanging orientation absorption of its interlayer electronics by being modified to high-purity hydrated alumino-silicate
Ability, can selective absorption feed and the intracorporal mycotoxin of animal, and be fixed and lose pathogenicity, with large intestine
Wriggling excretes, and avoids intestinal mucosa injury.And the nutriments such as vitamin, microelement are not adsorbed.Yeast is thin in invention
Cell wall, bacillus subtilis freeze-drying meal component have mycotoxin, harmful bacteria removal, maintenance intestinal health, raising animal immune
Good effect.Propionic acid/propionate, sodium Diacetate ingredient have obvious action to inhibition fungus growth proliferation in the present invention.
Remarkable result of the invention is, the present invention can effectively preventing livestock and poultry diarrhea, inhibit mould proliferation, absorption degradation
Mycotoxin, mitigation mycotoxin influence growth of animals or poultry, improve animal and bird intestines colony balance, improve growth of animals or poultry performance, have
Use of the reduction antibiotic of effect during livestock and poultry cultivation.
Specific embodiment
In order to which the purpose of the present invention, technical solution and advantage is more clearly understood, with reference to embodiments to this hair
It is bright to be described further:
Embodiment one, a kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method, according to weight percent
Meter, each component: nano montmorillonite 40%, zinc oxide 5%, yeast cell wall 6%, bacillus subtilis freeze-dried powder 7%, vitamin C 5%,
Propionic acid/propionate 15%, sodium Diacetate 11%.
Nano montmorillonite granularity≤the 100nm, can pass fully through 325 meshes, specific surface area >=240m2/g。
The yeast cell wall its mannan content 28%, beta-dextran content 25%, water-soluble protein content >=30%.
1, a kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method include the next steps:
1) bacillus subtilis is subjected to fermented and cultured, culture medium prescription (%): corn flour 3, soybean cake powder using fermentation medium
2 (hydrolyzate adds 121 DEG C of hydrolysis 30min of 0.5%NaOH, cooling, filtering), peptone 0.2, KH2PO4 0.15,
K2HPO40.15、NaSO4 0.15、CaCl20.03, MnSO4 0.01、MgSO40.06, NaCl 0.2, glucose 0.5 is spat
Temperature -80 0.03, pH8.0,37 DEG C of constant temperature incubation 48h.
2) after fermentation, fermentation liquid sterile working is fitted into centrifuge, under the conditions of 25 DEG C, 10000 rpm/min from
5 min of the heart discards supernatant liquid, and gained centrifugal sediment is bacterium mud, and bacterium mud is suspended again with 1% peptone water solution becomes
Suspension, and bacillus subtilis bacteria concentration is made to be about 109 cfu/mL。
3) it will be atomized in bacillus subtilis bacterium solution prepared by step 2 injection atomizer, air pressure is when atomization
0.72 kgf/cm2, fluid pressure is 0.45 kgf/cm2。
4) liquid droplet after being atomized is used in the collecting tank equipped with appropriate calcium chloride solution (0.55 mol/L), and process is collected
In by magnetic stirring apparatus be gently mixed calcium chloride solution harden 20 min, then use highly dense the screen to filtrate, and with distill washing
It washs twice, is then transferred in packaging material (with chitosan with example) lactic acid solution (chitosan C 1.0%(w/v) and lactic acid 0.5%(v/ again
V)), being gently mixed 10 min is coated with alginate microcapsules surface uniformly.
5) it filters and then the microcapsules for washing the step 4) preparation is done again in -72 DEG C of 6 h of freeze-drying in -75 DEG C
Dry 18 h, pressure is set as 5.28 Pa to get bacillus subtilis freeze-dried powder when dry.
2, by nano montmorillonite, zinc oxide, yeast cell wall, bacillus subtilis freeze-dried powder, vitamin C, propionic acid/propionic acid
Salt, sodium Diacetate are proportionally uniformly mixed by feed addictive mixing unit to get feed addictive of the present invention.
Embodiment two, a kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method, according to weight hundred
Divide than meter, each component: nano montmorillonite 44%, zinc oxide 2.5%, yeast cell wall 5%, bacillus subtilis freeze-dried powder 5%, dimension life
Plain C4.5%, propionic acid/propionate 13%, sodium Diacetate 9%.
Nano montmorillonite granularity≤the 100nm, can pass fully through 325 meshes, specific surface area >=240m2/g。
The yeast cell wall its mannan content 28%, beta-dextran content 25%, water-soluble protein content >=30%.
1, a kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method the following steps are included:
1) bacillus subtilis is subjected to fermented and cultured, culture medium prescription (%): corn flour 3, soybean cake powder using fermentation medium
2 (hydrolyzate adds 121 DEG C of hydrolysis 30min of 0.5%NaOH, cooling, filtering), peptone 0.2, KH2PO4 0.15,
K2HPO40.15、NaSO4 0.15、CaCl20.03, MnSO4 0.01、MgSO40.06, NaCl 0.2, glucose 0.5 is spat
Temperature -80 0.03, pH8.0,37 DEG C of constant temperature incubation 48h.
2) after fermentation, fermentation liquid sterile working is fitted into centrifuge, under the conditions of 25 DEG C, 10000 rpm/min from
5 min of the heart discards supernatant liquid, and gained centrifugal sediment is bacterium mud, and bacterium mud is suspended again with 1% peptone water solution becomes
Suspension, and bacillus subtilis bacteria concentration is made to be about 109 cfu/mL。
3) it will be atomized in bacillus subtilis bacterium solution prepared by step 2 injection atomizer, air pressure is when atomization
0.72 kgf/cm2, fluid pressure is 0.45 kgf/cm2。
4) liquid droplet after being atomized is used in the collecting tank equipped with appropriate calcium chloride solution (0.55 mol/L), and process is collected
In by magnetic stirring apparatus be gently mixed calcium chloride solution harden 20 min, then use highly dense the screen to filtrate, and with distill washing
It washs twice, is then transferred in packaging material (with chitosan with example) lactic acid solution (chitosan C 1.0%(w/v) and lactic acid 0.5%(v/ again
V)), being gently mixed 10 min is coated with alginate microcapsules surface uniformly.
5) it filters and then the microcapsules for washing the step 4) preparation is done again in -72 DEG C of 6 h of freeze-drying in -75 DEG C
Dry 18 h, pressure is set as 5.28 Pa to get bacillus subtilis freeze-dried powder when dry.
2, by nano montmorillonite, zinc oxide, yeast cell wall, bacillus subtilis freeze-dried powder, vitamin C, propionic acid/propionic acid
Salt, sodium Diacetate are proportionally uniformly mixed by feed addictive mixing unit to get feed addictive of the present invention.
Embodiment three, a kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method, according to weight hundred
Divide than meter, each component: nano montmorillonite 48%, zinc oxide 2.5%, yeast cell wall 5%, bacillus subtilis freeze-dried powder 7%, dimension life
Plain C4.5%, propionic acid/propionate 14%, sodium Diacetate 10%.
Nano montmorillonite granularity≤the 100nm, can pass fully through 325 meshes, specific surface area >=240m2/g。
The yeast cell wall its mannan content 28%, beta-dextran content 25%, water-soluble protein content >=30%.
1, a kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method the following steps are included:
1) bacillus subtilis is subjected to fermented and cultured, culture medium prescription (%): corn flour 3, soybean cake powder using fermentation medium
2 (hydrolyzate adds 121 DEG C of hydrolysis 30min of 0.5%NaOH, cooling, filtering), peptone 0.2, KH2PO4 0.15,
K2HPO40.15、NaSO4 0.15、CaCl20.03, MnSO4 0.01、MgSO40.06, NaCl 0.2, glucose 0.5 is spat
Temperature -80 0.03, pH8.0,37 DEG C of constant temperature incubation 48h.
2) after fermentation, fermentation liquid sterile working is fitted into centrifuge, under the conditions of 25 DEG C, 10000 rpm/min from
5 min of the heart discards supernatant liquid, and gained centrifugal sediment is bacterium mud, and bacterium mud is suspended again with 1% peptone water solution becomes
Suspension, and bacillus subtilis bacteria concentration is made to be about 109 cfu/mL。
3) it will be atomized in bacillus subtilis bacterium solution prepared by step 2 injection atomizer, air pressure is when atomization
0.72 kgf/cm2, fluid pressure is 0.45 kgf/cm2。
4) liquid droplet after being atomized is used in the collecting tank equipped with appropriate calcium chloride solution (0.55 mol/L), and process is collected
In by magnetic stirring apparatus be gently mixed calcium chloride solution harden 20 min, then use highly dense the screen to filtrate, and with distill washing
It washs twice, is then transferred in packaging material (with chitosan with example) lactic acid solution (chitosan C 1.0%(w/v) and lactic acid 0.5%(v/ again
V)), being gently mixed 10 min is coated with alginate microcapsules surface uniformly.
5) it filters and then the microcapsules for washing the step 4) preparation is done again in -72 DEG C of 6 h of freeze-drying in -75 DEG C
Dry 18 h, pressure is set as 5.28 Pa to get bacillus subtilis freeze-dried powder when dry.
2, by nano montmorillonite, zinc oxide, yeast cell wall, bacillus subtilis freeze-dried powder, vitamin C, propionic acid/propionic acid
Salt, sodium Diacetate are proportionally uniformly mixed by feed addictive mixing unit to get feed addictive of the present invention.
Example IV, a kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method, according to weight hundred
Divide than meter, each component: nano montmorillonite 50%, zinc oxide 1%, yeast cell wall 4%, bacillus subtilis freeze-dried powder 8%, vitamin
C4%, propionic acid/propionate 10%, sodium Diacetate 7%.
Nano montmorillonite granularity≤the 100nm, can pass fully through 325 meshes, specific surface area >=240m2/g。
The yeast cell wall its mannan content 28%, beta-dextran content 25%, water-soluble protein content >=30%.
1, a kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method include the next steps:
1) bacillus subtilis is subjected to fermented and cultured, culture medium prescription (%): corn flour 3, soybean cake powder using fermentation medium
2 (hydrolyzate adds 121 DEG C of hydrolysis 30min of 0.5%NaOH, cooling, filtering), peptone 0.2, KH2PO4 0.15,
K2HPO40.15、NaSO4 0.15、CaCl20.03, MnSO4 0.01、MgSO40.06, NaCl 0.2, glucose 0.5 is spat
Temperature -80 0.03, pH8.0,37 DEG C of constant temperature incubation 48h.
2) after fermentation, fermentation liquid sterile working is fitted into centrifuge, under the conditions of 25 DEG C, 10000 rpm/min from
5 min of the heart discards supernatant liquid, and gained centrifugal sediment is bacterium mud, and bacterium mud is suspended again with 1% peptone water solution becomes
Suspension, and bacillus subtilis bacteria concentration is made to be about 109 cfu/mL。
3) it will be atomized in bacillus subtilis bacterium solution prepared by step 2 injection atomizer, air pressure is when atomization
0.72 kgf/cm2, fluid pressure is 0.45 kgf/cm2。
4) liquid droplet after being atomized is used in the collecting tank equipped with appropriate calcium chloride solution (0.55 mol/L), and process is collected
In by magnetic stirring apparatus be gently mixed calcium chloride solution harden 20 min, then use highly dense the screen to filtrate, and with distill washing
It washs twice, is then transferred in packaging material (with chitosan with example) lactic acid solution (chitosan C 1.0%(w/v) and lactic acid 0.5%(v/ again
V)), being gently mixed 10 min is coated with alginate microcapsules surface uniformly.
5) it filters and then the microcapsules for washing the step 4) preparation is done again in -72 DEG C of 6 h of freeze-drying in -75 DEG C
Dry 18 h, pressure is set as 5.28 Pa to get bacillus subtilis freeze-dried powder when dry.
2, by nano montmorillonite, zinc oxide, yeast cell wall, bacillus subtilis freeze-dried powder, vitamin C, propionic acid/propionic acid
Salt, sodium Diacetate are proportionally uniformly mixed by feed addictive mixing unit to get feed addictive of the present invention.
Specific experiment verifying is as follows:
Experimental example 1, nutrition adsorption experiment
It takes 3 formulation product of the embodiment of the present invention to be tested, takes 10 100mL triangular flasks, number 1-10 accurately weighs experiment sample
Each 1g of product, is added in the triangular flask of number, is dissolved respectively with 10mL Wahaha Pure Water, respectively into the triangular flask of number 1-5
0.01g VB1, VB2, VB6, VB12, methionine is added, is respectively added in 6-10 control group triangular flask general with equivalent of the present invention
Logical montmorillonite sample, 10mL Wahaha Pure Water dissolution, sequentially adds 0.01g VB1, VB2, VB6, VB12, methionine, constant temperature
25 DEG C, 100r/min processing 3h, measure VB1, VB2, VB6, VB12, methionine content variation respectively, and test result is shown in Table 1.
1 present invention of table adsorbs situation to each vitamin and methionine
Nutrition type | Product of the present invention (g) | Common montmorillonite (g) |
VB1 | 0.0098 | 0.0045 |
VB2 | 0.0099 | 0.0058 |
VB6 | 0.0095 | 0.0061 |
VB12 | 0.0097 | 0.0032 |
Methionine | 0.009 | 0.0024 |
The present invention is seldom to vitamin, amino acid adsorbed it can be seen from 1 result of table, does not adsorb substantially, produces using the present invention
Product, which will not be led to the problem of, adsorbs nutrient.
It is experimental example 2, mould proof and take off mould effect experiment
3 formulation product of the embodiment of the present invention is taken to be tested, mould proof experiment product of the present invention is public according to 500g/T additive amount and 50
Jin feedstuff mixes, and control group does not add this project product then, keeps 25 DEG C of MW temperature, humidity 60% to store 1 month, inspection
Each experimental products peculiar smell, temperature, microorganism situation are surveyed, test result is shown in Table 2.
2 product of the present invention of table tests feedstuff anti-mold effect
Detection | Experimental group | Control group |
Peculiar smell | Nothing | There is musty |
Temperature | 25℃-30℃ | 30℃-45℃ |
Aspergillus flavus | It is not detected | 0.5×104cfu/g |
Sickle-like bacteria | It is not detected | 1×106cfu/g |
Escherichia coli | 1×103cfu/g | 2.01×106cfu/g |
Clostridium botulinum | It is not detected | 1×104cfu/g |
Product of the present invention can effectively prevent feedstuff and go mouldy it can be seen from 2 test result of table, to aspergillus flavus,
Sickle-like bacteria, clostridium botulinum, Escherichia coli proliferation have apparent inhibitory effect, it is seen that the present invention it is mould proof to feedstuff have very
Good function and effect.
It takes 3 formulation product of the embodiment of the present invention to be tested, is added and contains aflatoxin 100ppb, corn equipped with 100g
Zeranol 500ppb, vomitoxin 1000ppb feed in, after mixing be packed into 250mL triangular flask, be added 150mL sterile water
Dissolution, 25 DEG C of constant temperature, 100r/min handle 2.5h, measure aflatoxin, zearalenone, vomitoxin content respectively,
Test result is shown in Table 3:
3 product of the present invention of table tests feed primary toxins removal effect
Detection | Before experiment | After test | Mycotoxin removal rate |
Aflatoxin | 100ppb | 1ppb | 99% |
Zearalenone | 500ppb | 101.96ppb | 79.6% |
Vomitoxin | 1000ppb | 245.69ppb | 75.43% |
Product of the present invention has aflatoxin, zearalenone, vomitoxin de- it can be seen from 3 test result of table
Toxic effect fruit is aflatoxin 99%, zearalenone 79.6%, vomitoxin 75.43% to the removal rate of mycotoxin,
It can be seen that product of the present invention has good function and effect to mycotoxin removal.
The specific embodiment of the invention is described in detail in the above experiment, but the invention is not limited to embodiment, therefore all
Technological development personnel are modified and are belonged to the technical solution, the technical matters that obtain in present inventive concept technical foundation in technical field
This technology invention protection scope.
Claims (4)
1. a kind of antibacterial, absorbing mycotoxin nano montmorillonite feed addictive preparation method, which is characterized in that with weight percent
Than meter, be made of following components: nano montmorillonite 40-50%, zinc oxide 1-5%, yeast cell wall 4-6%, bacillus subtilis are frozen
Dry powder 5-8%, vitamin C 4-5%, propionic acid/propionate 10-15%, sodium Diacetate 7-11%.
2. a kind of antibacterial according to claim 1, absorbing mycotoxin nano montmorillonite feed addictive preparation method,
Be characterized in that, in percentage by weight, including following components: nano montmorillonite 48%, zinc oxide 2.5%, yeast cell wall 5%,
Bacillus subtilis freeze-dried powder 7%, vitamin C 4.5%, propionic acid/propionate 14%, sodium Diacetate 10%.
3. a kind of antibacterial according to claim 1 to 2, absorbing mycotoxin nano montmorillonite feed addictive preparation method,
It is characterized in that, the nano montmorillonite granularity≤100nm, passes fully through 325 meshes, specific surface area >=240m2/g。
4. a kind of antibacterial according to claim 1 to 2, absorbing mycotoxin nano montmorillonite feed addictive preparation method,
It is characterized in that, the yeast cell wall its mannan content 28%, beta-dextran content 25%, water-soluble protein content >=30%.