CN1092226C - 三元乙丙橡胶防水卷材的制备方法 - Google Patents

三元乙丙橡胶防水卷材的制备方法 Download PDF

Info

Publication number
CN1092226C
CN1092226C CN 99111713 CN99111713A CN1092226C CN 1092226 C CN1092226 C CN 1092226C CN 99111713 CN99111713 CN 99111713 CN 99111713 A CN99111713 A CN 99111713A CN 1092226 C CN1092226 C CN 1092226C
Authority
CN
China
Prior art keywords
rubber
preparation
enter
disulfide
zinc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 99111713
Other languages
English (en)
Other versions
CN1281886A (zh
Inventor
李生田
马惠敏
丁金英
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changchun Institute of Applied Chemistry of CAS
Original Assignee
Changchun Institute of Applied Chemistry of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changchun Institute of Applied Chemistry of CAS filed Critical Changchun Institute of Applied Chemistry of CAS
Priority to CN 99111713 priority Critical patent/CN1092226C/zh
Publication of CN1281886A publication Critical patent/CN1281886A/zh
Application granted granted Critical
Publication of CN1092226C publication Critical patent/CN1092226C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明属于三元乙丙橡胶防水卷材的制备方法。该方法采用以硫磺加低温快速硫化助剂的硫化体系。助剂是：二硫醇基苯并噻唑、二硫化二苯并噻唑、二硫化四甲基秋兰姆、甲基苯基二硫代氨基甲酸锌、乙烯硫脲。本发明除选择混合助剂防喷霜外，还加了防喷剂沥青，提高了防喷的可靠性，以利于粘结。沥青在整个体系中又改善了加工性能，使胶料更易混匀，有利于提高防水卷材的物理性能。

Description

三元乙丙橡胶防水卷材的制备方法
本发明属于三元乙丙橡胶防水卷材的制备方法。
三元乙丙橡胶防水卷材是一种高性能弹性体建筑防水卷材，由于其耐水性、弹性、耐老化性、耐日光性、耐臭氧性、耐化学腐蚀性等一系列宝贵特性，因此广泛应用于屋面、卫生间、地下室、净水池、水库、隧道、机场、高速公路等建筑工程的防水。
中国保定橡胶一厂生产三元乙丙橡胶防水卷材为丁基橡胶和三元乙丙橡胶并用构成二元组份体系，日本东洋橡胶公司，美国Garisle Ine生产单组份三元乙丙橡胶型防水卷材，由于这两类体系中无极性官能团，故其粘结性较差，造成三元乙丙橡胶防水层搭接处易开裂，使整体防水性能下降，产生渗漏，因助剂应用不妥，开炼时胶料温度达100℃左右时，易产生焦烧，损耗上升，不利于降低成本。
本发明的目的是提供一种三元乙丙橡胶防水卷材的制备方法，该方法引进第三组份氯丁橡胶经调节助剂制得性能优良的三元乙丙橡胶防水卷材。
本发明第三组份一氯丁橡胶的引进，增加了本体系的极性，提高了粘结性能，防止三元乙丙橡胶防水卷材搭接处开裂，增强防水的可靠性，为了确保正常硫化，采用以硫磺加低温快速硫化助剂的硫化体系。助剂是：2-硫醇基苯并噻唑、二硫化二苯并噻唑、二硫化四甲基秋兰姆、甲基苯基二硫代氨基甲酸锌、乙烯硫脲。本发明除选择混合助剂防喷霜外，还加了防喷剂沥青，提高了防喷的可靠性，以利于粘结。沥青在整个体系中又改善了加工性能，使胶料更易混匀，有利于提高防水卷材的物理性能。
本发明三元乙丙橡胶防水卷材选用原料配比以重量比计，三元乙丙橡胶60-70、丁基橡胶10-26、氯丁橡胶4-25，这三种胶一起先塑炼、然后进入密炼机再加入炭黑50-70、轻质碳酸钙50-70、固体苯并呋喃茚树脂2-7、沥青2-10、环烷油10-20、氧化锌5-10、四[3-(3.5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯0.5-1、硬脂酸0.7-1.2、2-硫醇基苯并噻唑0.5-1.5、二硫化二苯并噻唑0.5-1.5，二硫化四甲基秋兰姆0.5-1.5、甲基苯基二硫代氨基甲酸锌0.1-0.7、乙烯硫脲0.1-1、硫磺0.5-1.5混炼，卸料后再进入开炼机热炼、卸料进入成型机成型，机头温度70～80℃，最后进入硫化装置硫化，硫化温度145～160℃，正硫化时间10-110分钟内均能达到理想的硫化效果。这一较宽的正硫化温度和时间，在非连续硫化实践中显得尤为重要，最终制备强度8.1Mpa、断裂伸长率520％、脆性温度-43℃、热老化保持率(强度86.8％)、直角撕裂强度260N/cm、臭氧老化(500ppm、168h×40℃伸长率40％)静态无裂纹、卷材粘合剥离强度15N/10mm。
本发明提供的实施例如下：
实施例1：三元乙丙橡胶60，氯丁橡胶25，丁基橡胶15，炭黑50，轻质碳酸钙60，环烷油15，氧化锌10，四[3-(3.5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯1.0，沥青2，固体苯并呋喃茚树脂7，硬脂酸0.7，2-硫醇基苯并噻唑0.4，二硫化二苯并噻唑0.8，二硫化四甲基秋兰姆1.5，甲基基苯基二硫代氨基甲酸锌0.1，乙烯硫脲1.0，硫磺0.5，硫化条件145℃×10min。
实施例2：三元乙丙橡胶70，氯丁橡胶4，丁基橡胶26，炭黑50，轻质碳酸钙60，环烷油10，氧化锌5，四[3-(3.5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯0.5，沥青10，固体苯并呋喃茚树脂2，硬脂酸0.9，2-硫醇基苯并噻唑0.4，二硫化二苯并噻唑0.5，二硫化四甲基秋兰姆1.5，甲基基苯基二硫代氨基甲酸锌0.1，乙烯硫脲0.1，硫磺1.5，硫化条件150℃×10min。
实施例3：三元乙丙橡胶70，氯丁橡胶20，丁基橡胶10，炭黑50，轻质碳酸钙50，环烷油15，氧化锌5，四[3-(3.5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯1.0，沥青2，固体苯并呋喃茚树脂2，硬脂酸0.8，2-硫基苯并噻唑1.5，二硫化二苯并噻唑0.5，二硫化四甲基秋兰姆0.8，甲基苯基二硫代氨基甲酸锌0.4，乙烯硫脲0.7，硫磺0.7，硫化条件150℃×10min。
实施例4：三元乙丙橡胶70，氯丁橡胶10，丁基橡胶20，炭黑50，轻质碳酸钙50，环烷油15，氧化锌5，四[3-(3.5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯0.5，沥青4，固体苯并呋喃茚树脂3，硬脂酸1，2-硫醇基苯并噻唑1，二硫化二苯并噻唑0.5，二硫化四甲基秋兰姆0.5，甲基苯基二硫代氨基甲酸锌0.7，乙烯硫脲0.5，硫磺1.2，硫化条件155℃×10min。
实施例5：三元乙丙橡胶70，氯丁橡胶10，丁基橡胶20，炭黑70，轻质碳酸钙50，环烷油20，氧化锌5，四[3-(3.5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯0.5，沥青4，固体苯并呋喃茚树脂5，硬脂酸1.2，2-硫醇基苯并噻唑0.5，二硫化二苯并噻唑1.5，二硫化四甲基秋兰姆1.5，甲基苯基二硫代氨基甲酸锌0.1，乙烯硫脲0.2，硫磺0.6，硫化条件160℃×10min。
实施例6：三元乙丙橡胶70，氯丁橡胶10，丁基橡胶20，炭黑50，轻质碳酸钙70，环烷油15，氧化锌8，四[3-(3.5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯0.5，沥青7，固体苯并呋喃茚树脂2，硬脂酸1，2-硫醇基苯并噻唑1，二硫化二苯并噻唑0.8，二硫化四甲基秋兰姆0.8，甲基苯基二硫代氨基甲酸锌0.1，乙烯硫脲0.2，硫磺0.8，硫化条件150℃×10min。

Claims (1)

1、一种三元乙丙橡胶防水卷材的制备方法，其特征在于选用原料配比以重量比计，三元乙丙橡胶60-70、丁基橡胶10-26、氯丁橡胶4-25；这三种胶一起先塑炼，然后进入密炼机再加入炭黑50-70、轻轻质碳酸钙50-70、固体苯并呋喃茚树脂2-7、沥青2-10、环烷油10-20、氧化锌5-10、四[3-(3.5-二叔丁基-4-羟基苯基)丙酸]季戊四醇酯0.5-1、硬脂酸0.7-1.2、  2-硫醇基苯并噻唑0.2-1.5、二硫化二苯并噻唑0.5-1.5、二硫化四甲基秋兰姆0.5-1.5、甲基苯基二硫代氨基甲酸锌0.1-0.7、乙烯硫脲0.1-1、硫磺0.5-1.5混炼，卸料后再进入开炼机热炼、卸料进入成型机成型，机头温度70～80℃，最后进入硫化装置硫化，硫化温度145～160℃，正硫化时间10-110分钟。
CN 99111713 1999-07-26 1999-07-26 三元乙丙橡胶防水卷材的制备方法 Expired - Fee Related CN1092226C (zh)