CN109133641A - 高遮盖力黑色环保钢化玻璃油墨及其制备方法 - Google Patents
高遮盖力黑色环保钢化玻璃油墨及其制备方法 Download PDFInfo
- Publication number
- CN109133641A CN109133641A CN201811290757.3A CN201811290757A CN109133641A CN 109133641 A CN109133641 A CN 109133641A CN 201811290757 A CN201811290757 A CN 201811290757A CN 109133641 A CN109133641 A CN 109133641A
- Authority
- CN
- China
- Prior art keywords
- flux
- tempered glass
- covering power
- environmental protection
- black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于油墨技术领域,具体涉及高遮盖力黑色环保钢化玻璃油墨及其制备方法。包含的各组分的重量百分比如下:黑色剂:30%~38%;熔剂:40%~50%;调墨油:18%~25%;总计100%。本发明提供的高遮盖力黑色环保钢化玻璃油墨及其制备方法,与现有技术相比,本发明的有益效果是:环保,适用范围宽而且遮盖力高等优良特性。
Description
技术领域
本发明属于油墨技术领域,具体涉及高遮盖力黑色环保钢化玻璃油墨及其制备方法。
背景技术
钢化玻璃油墨是一种通过丝网印刷于玻璃表面的玻璃釉料,主要由熔剂、色剂、调墨油和助剂研磨均匀而成,并经过高温烧烤后,在玻璃表面形成一层与玻璃紧密结合的“薄膜”,能够起到保护、装饰玻璃和遮挡光线等作用。
随着家电、建筑、汽车和光伏等行业的发展,人们对玻璃外观的要求越来越高。普通的油墨印刷在玻璃上经过钢化烧烤后,其墨层存在透光率大,遮盖力不够,沙眼较多等缺陷。影响这一缺陷的因素较多,包括熔剂的配方组成、烧制工艺、球磨细度以及与色剂和调墨油混合的工艺等,都需要综合考虑。目前,国内外的高档的钢化玻璃油墨主要是美国福禄和荷兰庄信万丰等公司的产品。因此研发出低成本无铅环保,并具有高遮盖率的钢化玻璃油墨具有重要的意义。
发明内容
本发明克服了现有环保黑色钢化玻璃油墨的技术缺点,提供了一种高遮盖力黑色环保钢化玻璃油墨及其制备方法。
为了实现上述目的,本发明通过以下技术方案实现:
具体技术方案为:
高遮盖力黑色环保钢化玻璃油墨,包含的各组分的重量百分比如下:
黑色剂:30%~38%;
熔剂:40%~50%;
调墨油:18%~25%;
总计100%。
所述的黑色剂为铜铬黑色剂。
所述的熔剂,基料的各组分质量百分比:氧化锂1~4%、氧化钠0~3.5%、氧化钾0~2%、氧化硼2~6%、氧化锌1~5%,氧化硅20~40%、氧化钛1~5%、氧化锆1~5%和氧化铋40~65%,总计100%。
所述的熔剂的软化温度在420~570℃,热膨胀系数在63~90×10-7/K。
高遮盖力黑色环保钢化玻璃油墨的制备方法,包括以下步骤:
熔剂制备,按配方比例准确称量熔剂基料的原料,将其一起混合放入高温坩埚炉在1250℃熔制40min,然后使其熔融液体流入水中淬冷,再用球磨机湿法磨,先粗磨至D90:15um,然后使用3mm球子磨细至D50:2~2.5um;D90:4~5um,包装待用;
将熔剂和黑色剂使用球子直径为8mm球磨湿混4h,然后烘干、打分和气流粉碎,包装待用;
最后,将混合的粉料和调墨油高速分散、轧墨3~4遍。
由于影响黑色钢化玻璃油墨遮盖力不高的因素较多,其中有两个主要因素:1、黑色剂加入量不够多;2、熔剂的颗粒细度不够集中。
油墨中黑色剂含量越多,其遮盖力越高,普通油墨黑色剂含量占粉料总量在25%~37%左右。如果想要继续增加黑色剂的含量,熔剂的熔融温度需要降低。本专利通过调节熔剂组成配方降低其熔融温度,从而使得黑色剂含量达到40~47%。
油墨中熔剂的颗粒细度越集中,其粉料与调墨油混合越均匀,分散越好,油墨烧烤在玻璃上后缺陷越少,遮盖理越强。普通油墨球磨熔剂一次性将熔剂从块状球磨至超细粉,本专利通过分级球磨熔剂,从而达到颗粒集中。
本发明提供的高遮盖力黑色环保钢化玻璃油墨及其制备方法,与现有技术相比,本发明的有益效果是:环保,适用范围宽而且遮盖力高等优良特性。
具体实施方式
结合实施例说明本发明的具体技术方案。
下面结合实施例对本发明的具体实施方式进行描述,以便本领域技术人员的更好的理解。
实施例1
一种高遮盖力黑色环保钢化玻璃油墨,包含的各组分的重量百分比如下:
黑色剂:32%;熔剂:48%;调墨油:20%;
所述的黑色剂主要为铜铬黑色剂,调墨油外购。
一种高遮盖力黑色环保钢化玻璃油墨用熔剂基料的各组分质量百分比:氧化锂1%、氧化钠1%、氧化钾0.5%、氧化硼3%、氧化锌3%,氧化硅35%、氧化钛2%、氧化锆2%和氧化铋52.5%。。
一种高遮盖力黑色环保钢化玻璃油墨用熔剂的制备方法,
熔剂制备:按配方比例准确称量熔剂基料的原料,将其一起混合放入高温坩埚炉在1250℃熔制40min,然后使其熔融液体流入水中淬冷,再用球磨机湿法磨,先粗磨至D90:15um左右,然后使用3mm球子磨细至D50:2~2.5um;D90:4~5um,包装待用。
将熔剂和黑色剂使用球子直径为8mm球磨湿混4h,然后烘干、打分和气流粉碎,包装待用。
最后,将混合的粉料和调墨油高速分散、轧墨3~4遍,包装待用。
实施例2
一种高遮盖力黑色环保钢化玻璃油墨,包含的各组分的重量百分比如下:
黑色剂:34%;熔剂:46%;调墨油:20%;
所述的黑色剂主要为铜铬黑色剂,调墨油外购。
一种高遮盖力黑色环保钢化玻璃油墨用熔剂基料的各组分质量百分比:氧化锂3%、氧化钠3%、氧化钾1%、氧化硼4%、氧化锌4%,氧化硅30%、氧化钛3%、氧化锆2%和氧化铋50%。
一种高遮盖力黑色环保钢化玻璃油墨用熔剂的制备方法,
熔剂制备:按配方比例准确称量熔剂基料的原料,将其一起混合放入高温坩埚炉在1250℃熔制40min,然后使其熔融液体流入水中淬冷,再用球磨机湿法磨,先粗磨至D90:15um左右,然后使用3mm球子磨细至D50:2~2.5um;D90:4~5um,包装待用。
将熔剂和黑色剂使用球子直径为8mm球磨湿混4h,然后烘干、打分和气流粉碎,包装待用。
最后,将混合的粉料和调墨油高速分散、轧墨3~4遍,包装待用。
实施例3
一种高遮盖力黑色环保钢化玻璃油墨,包含的各组分的重量百分比如下:
黑色剂:36%;熔剂:44%;调墨油:20%;
所述的黑色剂主要为铜铬黑色剂,调墨油外购。
一种高遮盖力黑色环保钢化玻璃油墨用熔剂基料的各组分质量百分比:氧化锂3%、氧化钠3%、氧化钾2%、氧化硼5%、氧化锌4%,氧化硅31%、氧化钛1%、氧化锆1%和氧化铋50%。
一种高遮盖力黑色环保钢化玻璃油墨用熔剂的制备方法,
熔剂制备:按配方比例准确称量熔剂基料的原料,将其一起混合放入高温坩埚炉在1250℃熔制40min,然后使其熔融液体流入水中淬冷,再用球磨机湿法磨,先粗磨至D90:15um左右,然后使用3mm球子磨细至D50:2~2.5um;D90:4~5um,包装待用。
将熔剂和黑色剂使用球子直径为8mm球磨湿混4h,然后烘干、打分和气流粉碎,包装待用。
最后,将混合的粉料和调墨油高速分散、轧墨3~4遍,包装待用。
Claims (5)
1.高遮盖力黑色环保钢化玻璃油墨,其特征在于:包含的各组分的重量百分比如下:
黑色剂:30%~38%;熔剂:40%~50%;调墨油:18%~25%;总计100%。
2.根据权利要求1所述的高遮盖力黑色环保钢化玻璃油墨,其特征在于,所述的黑色剂为铜铬黑色剂。
3.据权利要求1所述的高遮盖力黑色环保钢化玻璃油墨,其特征在于,所述的熔剂,基料的各组分质量百分比:氧化锂1~4%、氧化钠0~3.5%、氧化钾0~2%、氧化硼2~6%、氧化锌1~5%,氧化硅20~40%、氧化钛1~5%、氧化锆1~5%和氧化铋40~65%,总计100%。
4.根据权利要求3所述的高遮盖力黑色环保钢化玻璃油墨,其特征在于,所述的熔剂的软化温度在420~570℃,热膨胀系数在63~90×10-7/K。
5.根据权利要求1所述的高遮盖力黑色环保钢化玻璃油墨的制备方法,其特征在于,包括以下步骤:
熔剂制备,按配方比例准确称量熔剂基料的原料,将其一起混合放入高温坩埚炉在1250℃熔制40min,然后使其熔融液体流入水中淬冷,再用球磨机湿法磨,先粗磨至D90:15um,然后使用3mm球子磨细至D50:2~2.5um;D90:4~5um,包装待用;
将熔剂和黑色剂使用球子直径为8mm球磨湿混4h,然后烘干、打分和气流粉碎,包装待用;
最后,将混合的粉料和调墨油高速分散、轧墨3~4遍。