CN101255009A - 一种无铅无镉玻璃色釉及其制备方法 - Google Patents

一种无铅无镉玻璃色釉及其制备方法 Download PDF

Info

Publication number
CN101255009A
CN101255009A CNA200810035794XA CN200810035794A CN101255009A CN 101255009 A CN101255009 A CN 101255009A CN A200810035794X A CNA200810035794X A CN A200810035794XA CN 200810035794 A CN200810035794 A CN 200810035794A CN 101255009 A CN101255009 A CN 101255009A
Authority
CN
China
Prior art keywords
oxide
powder
glass
poured
cadmium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA200810035794XA
Other languages
English (en)
Inventor
谭中全
司彦荣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Wengao Glass & Enamel Application Color Glaze Co Ltd
Original Assignee
Shanghai Wengao Glass & Enamel Application Color Glaze Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Wengao Glass & Enamel Application Color Glaze Co Ltd filed Critical Shanghai Wengao Glass & Enamel Application Color Glaze Co Ltd
Priority to CNA200810035794XA priority Critical patent/CN101255009A/zh
Publication of CN101255009A publication Critical patent/CN101255009A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种无铅无镉玻璃色釉，其特征在于，由以下原料组成：氧化锌、氧化钡、二氧化硅、二氧化钛、硝酸钾、碳酸锂、氧化锡、硼酸、氧化铝、二氧化锆，制备方法为：将称取的所有原料放入搅拌机中搅拌，将搅拌均匀的粉料加入转炉加温进行熔制，使粉料完全熔化；将烧熔的熔液倒入常温的水池中冷却，凝结成半熟玻璃结晶；然后放入球磨机球磨；将球磨过的半熟玻璃粉末倒入烘干机中烘干后经打碎筛粉即为玻璃色釉。本发明的优点是不含有铅、镉，有利于环保。

Description

一种无铅无镉玻璃色釉及其制备方法
技术领域
本发明涉及一种无铅无镉玻璃色釉及其制备方法，用于玻璃表面颜色喷色、印刷、涂层，属于色釉技术领域。
背景技术
我国拥有自己的玻璃色釉是在1965年，至今仍然维持这种配方，而原配方其主要成份：二氧化硅30％-40％、氧化锌2％-6％、二氧化钛3％-10％、氧化铅30％-45％、硼酸10％-20％、硝酸钾3％-8％、碳酸镉4％-8％。
按该配方制备的玻璃色釉含铅量相当高，且稳定性差，特别是白色釉料很容易反铅即硫化铅，而且对环境有着很大的危害。
发明内容
本发明的目的是提供一种无铅无镉玻璃色釉及其制备方法。
为实现以上目的，本发明的技术方案是提供一种无铅玻璃色釉，其特征在于，由以下重量百分比原料组成：氧化锌10％-20％、氧化钡5％-10％、二氧化硅10％-30％、二氧化钛3％-10％、硝酸钾5％-10％、碳酸锂5％-10％、氧化锡0％-5％、硼酸10％-25％、氧化铝3％-6％、二氧化锆0％-6％。
一种无铅无镉玻璃色釉的制备方法，其特征在于，该方法为：
第一步.按重量百分比称取原料：氧化锌10％-20％、氧化钡5％-10％、二氧化硅10％-30％、二氧化钛3％-10％、硝酸钾5％-10％、碳酸锂5％-10％、氧化锡0％-5％、硼酸10％-25％、氧化铝3％-6％、二氧化锆0％-6％；
第二步.将称取的所有原料放入搅拌机中搅拌20分钟-40分钟，其转速为20转-40转/分钟；
第三步.将搅拌均匀的粉料加入转炉加温进行熔制，温度为1150℃-1500℃，使粉料完全熔化；
第四步.将烧熔的熔液倒入常温的水池中冷却，凝结成半熟玻璃结晶；
第五步.将第四步得到的半熟玻璃结晶放入球磨机，加入5％-50％的泽色剂球磨5-10天；
第六步.将球磨过的半熟玻璃粉末倒入烘干机中烘干，烘至含水量低于0.36％以下后经打碎筛粉即为玻璃色釉。
本发明在原有玻璃色釉配方的基础上删除了氧化铅和氧化镉，增加了氧化锂、氧化锡、氧化钡、氧化铝、氧化锆，其主要的目的增加乳着力、遮盖力、有弹性，起到化学稳定性，具有耐酸碱之功效，并达到无铅的目的。
本发明的优点是不含有铅，有利于环保。
具体实施方式
以下结合实施例对本发明作进一步说明。
一种无铅无镉玻璃色釉的制备方法为：
第一步.按重量百分比称取各原料：
  品名   实施例1配方   实施例2配方   实施例3配方
  二氧化硅   20   23   25
  氧化钡   10   9   8
  二氧化钛   10   9   8
  硝酸钾   10   8   7
  氧化锌   10   15   20
  碳酸锂   10   8   6
  氧化锡   5   4   3
  硼酸   17   16   15
  氧化铝   5   4   3
  二氧化锆   3   4   5
第二步.将称取的所有原料放入搅拌机中搅拌30分钟，其转速为20转/分钟；
第三步.将搅拌均匀的粉料加入转炉加温进行熔制，温度为1150-1500℃，使粉料完全熔化；
第四步.将烧熔的熔液倒入常温的水池中冷却，凝结成半熟玻璃结晶；
第五步.将第四步得到的半熟玻璃结晶放入球磨机，加入5-50％的泽色剂球磨5-10天，其中加镉红的泽色剂为红色，加钴兰的泽色剂为蓝色，加镉黄的泽色剂为黄色，加绿色素的泽色剂为绿色，加黑色素的泽色剂为黑色等；
第六步.将球磨过的半熟玻璃粉末倒入烘干机中烘干，烘至含水量低于0.36％后经打碎筛粉即为玻璃色釉。
使用时，将玻璃色釉与松油混合研磨后即可直接使用，印刷或喷色于玻璃表面，经580℃-850℃退火炉烧制即成为各种形状花形的玻璃工艺制品。
本发明与原玻璃色釉的性能对比表：
  性能   实施例1   实施例2   实施例3   原玻璃色釉
  稳定性   一般   稳定性较好   稳定性较强   稳定性差
  含铅量   无   无   无   有
  遮盖力   强   强   一般   一般
  光泽度   光泽度较差   一般   光泽度好   一般
  熔点   低   一般   熔点偏高   一般

Claims (2)

1.一种无铅无镉玻璃色釉，其特征在于，有以下重量百分比原料组成：氧化锌10％-20％、氧化钡5％-10％、二氧化硅10％-30％、二氧化钛3％-10％、硝酸钾5％-10％、碳酸锂5％-10％、氧化锡0％-5％、硼酸10％-25％、氧化铝3％-6％、二氧化锆0％-6％。
2.一种无铅无镉玻璃色釉的制备方法，其特征在于，该方法为：
第一步.按重量百分比称取原料：氧化锌10％-20％、氧化钡5％-10％、二氧化硅10％-30％、二氧化钛3％-10％、硝酸钾5％-10％、碳酸锂5％-10％、氧化锡0％-5％、硼酸10％-25％、氧化铝3％-6％、二氧化锆0％-6％；
第二步.将称取的所有原料放入搅拌机中搅拌20分钟-40分钟，其转速为20转-40转/分钟；
第三步.将搅拌均匀的粉料加入转炉加温进行熔制，温度为1150℃-1500℃，使粉料完全熔化；
第四步.将烧熔的熔液倒入常温的水池中冷却，凝结成半熟玻璃结晶；
第五步.将第四步得到的半熟玻璃结晶放入球磨机，加入5％-50％的泽色剂球磨5-10天；
第六步.将球磨过的半熟玻璃粉末倒入烘干机中烘干，烘至含水量低于0.36％以下后经打碎筛粉即为玻璃色釉。
CNA200810035794XA 2008-04-09 2008-04-09 一种无铅无镉玻璃色釉及其制备方法 Pending CN101255009A (zh)