CN108624111A - 一种外墙抗裂腻子 - Google Patents

一种外墙抗裂腻子 Download PDF

Info

Publication number
CN108624111A
CN108624111A CN201810860466.7A CN201810860466A CN108624111A CN 108624111 A CN108624111 A CN 108624111A CN 201810860466 A CN201810860466 A CN 201810860466A CN 108624111 A CN108624111 A CN 108624111A
Authority
CN
China
Prior art keywords
parts
wall crack
resisting
resisting putty
glass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810860466.7A
Other languages
English (en)
Inventor
刘德远
程秋苹
张静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huaibei Qingfeng Coating Co Ltd
Original Assignee
Huaibei Qingfeng Coating Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huaibei Qingfeng Coating Co Ltd filed Critical Huaibei Qingfeng Coating Co Ltd
Priority to CN201810860466.7A priority Critical patent/CN108624111A/zh
Publication of CN108624111A publication Critical patent/CN108624111A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种外墙抗裂腻子，外墙抗裂腻子包括以下按重量份计的原料：白水泥350‑450份，双飞粉550‑640份，纤维素3‑7份，聚乙烯醇4‑8份，可再分散胶粉8‑13份，木质纤维素1‑3份，玻璃纤维1‑3份。本发明配方合理，改变了腻子的柔韧性，保水性，提高砂浆的粘度，增加工作效能及质量，防止抹灰层开裂，脱落，增加附着强度，同时可增加防水性，粘接强度好，增加砂浆的弹性，并有较长开放时间，赋予砂浆优良的耐碱性，改善砂浆的粘附性、粘合性、抗折强度、可塑造性、耐磨性和施工性。

Description

一种外墙抗裂腻子
技术领域
本发明涉及外墙装饰涂料技术领域，具体涉及一种外墙抗裂腻子。
背景技术
腻子是平整墙体表面的一种装饰凝材料，是一种厚浆状涂料，是涂料粉刷前必不可少的一种产品。涂施于底漆上或直接涂施于物体上，用以清除被涂物表面上高低不平的缺陷。采用少量漆基、大量填料及适量的着色颜料配制而成，所用颜料主要是铁红、炭黑、铬黄等，填料主要是重碳酸钙、滑石粉等。腻子可填补局部有凹陷的工作表面，也可在全部表面刮除，通常是在底漆干透后，施涂于底漆表面，要求附着性好、烘烤过程中不产生裂纹。目前，建筑墙体的装饰普遍使用传统的腻子粉，该腻子粉用白乳胶、107胶、钛白粉等制成，这种材料存在粘结力差、接缝处易出现开裂等缺点，并且墙体表面易卷皮、掉渣、龟裂、脱粉等，性能达不到应用要求。
发明内容
本发明所要解决的技术问题在于传统腻子粉的粘结力差，涂刷后易出现开裂的问题。
本发明通过以下技术方案来解决上述技术问题：
一种外墙抗裂腻子，包括以下按重量份计的原料：
白水泥350-450份，双飞粉550-640份，纤维素3-7份，聚乙烯醇4-8份，可再分散胶粉8-13份，木质纤维素1-3份，玻璃纤维1-3份。
进一步地，所述外墙抗裂腻子包括以下按重量份计的原料：
白水泥400份，双飞粉600份，纤维素5份，聚乙烯醇5份，可再分散胶粉10份，木质纤维素2份，玻璃纤维2份。
进一步地，所述聚乙烯醇为1788聚乙烯醇。
进一步地，所述外墙抗裂腻子的原料中还包括抗裂助剂2-6份。
进一步地，所述抗裂助剂包括以下按重量份计的原料：
水30-50份，粗石英砂20-40份，细石英砂10-30份，重钙粉10-30份，纯丙烯酸弹性乳液20-50份，消泡剂0.1-0.2份，甲基纤维素0.2-0.6份，玻璃微珠5-10份，玻璃胶20-30份。
进一步地，所述抗裂助剂包括以下按重量份计的原料：
水45份，粗石英砂30份，细石英砂20份，重钙粉21份，纯丙烯酸弹性乳液40份，消泡剂0.15份，甲基纤维素0.4份，玻璃微珠8份，玻璃胶26份。
进一步地，所述粗石英砂的细度为100-150目。
进一步地，所述细石英砂的细度为150-250目。
进一步地，所述抗裂助剂的制备方法为：(1)将粗石英砂、细石英砂、重钙粉、甲基纤维素、玻璃微珠混合并充分搅拌均匀，得到混合物料；(2)依次将纯丙烯酸弹性乳液和玻璃胶加入水中充分搅拌均匀后，边搅拌边加入混合物料，混合均匀后加入消泡剂，继续搅拌均匀，烘烤得到所述抗裂助剂。
本发明与现有技术相比，具有如下的有益效果：
本发明配方合理，改变了腻子的柔韧性，保水性，提高砂浆的粘度，增加工作效能及质量，防止抹灰层开裂，脱落，增加附着强度，同时可增加防水性，粘接强度好，增加砂浆的弹性，并有较长开放时间，赋予砂浆优良的耐碱性，改善砂浆的粘附性、粘合性、抗折强度、可塑造性、耐磨性和施工性。
具体实施方式
下面结合实施例对本发明作进一步说明。
实施例1
一种外墙抗裂腻子，包括以下按重量份计的原料：
白水泥350份，双飞粉550份，纤维素3份，聚乙烯醇4份，可再分散胶粉8份，木质纤维素1份，玻璃纤维1份，抗裂助剂2份。
所述聚乙烯醇为1788聚乙烯醇。
所述抗裂助剂包括以下按重量份计的原料：
水30份，粗石英砂20份，细石英砂10份，重钙粉10份，纯丙烯酸弹性乳液20份，消泡剂0.1份，甲基纤维素0.2份，玻璃微珠5份，玻璃胶20份。
其中，所述粗石英砂的细度为100目，所述细石英砂的细度为150目。
所述抗裂助剂的制备方法为：(1)将粗石英砂、细石英砂、重钙粉、甲基纤维素、玻璃微珠混合并充分搅拌均匀，得到混合物料；(2)依次将纯丙烯酸弹性乳液和玻璃胶加入水中充分搅拌均匀后，边搅拌边加入混合物料，混合均匀后加入消泡剂，继续搅拌均匀，烘烤得到所述抗裂助剂。
实施例2
一种外墙抗裂腻子，包括以下按重量份计的原料：
白水泥400份，双飞粉600份，纤维素5份，聚乙烯醇5份，可再分散胶粉10份，木质纤维素2份，玻璃纤维2份，抗裂助剂4份。
所述聚乙烯醇为1788聚乙烯醇。
所述抗裂助剂包括以下按重量份计的原料：
水45份，粗石英砂30份，细石英砂20份，重钙粉21份，纯丙烯酸弹性乳液40份，消泡剂0.15份，甲基纤维素0.4份，玻璃微珠8份，玻璃胶26份。
其中，所述粗石英砂的细度为130目，所述细石英砂的细度为200目。
所述抗裂助剂的制备方法为：(1)将粗石英砂、细石英砂、重钙粉、甲基纤维素、玻璃微珠混合并充分搅拌均匀，得到混合物料；(2)依次将纯丙烯酸弹性乳液和玻璃胶加入水中充分搅拌均匀后，边搅拌边加入混合物料，混合均匀后加入消泡剂，继续搅拌均匀，烘烤得到所述抗裂助剂。
实施例3
一种外墙抗裂腻子，包括以下按重量份计的原料：
白水泥450份，双飞粉640份，纤维素7份，聚乙烯醇8份，可再分散胶粉13份，木质纤维素3份，玻璃纤维3份，抗裂助剂6份。
所述聚乙烯醇为1788聚乙烯醇。
所述抗裂助剂包括以下按重量份计的原料：
水50份，粗石英砂40份，细石英砂30份，重钙粉30份，纯丙烯酸弹性乳液50份，消泡剂0.2份，甲基纤维素0.6份，玻璃微珠10份，玻璃胶30份。
其中，所述粗石英砂的细度为150目，所述细石英砂的细度为250目。
所述抗裂助剂的制备方法为：(1)将粗石英砂、细石英砂、重钙粉、甲基纤维素、玻璃微珠混合并充分搅拌均匀，得到混合物料；(2)依次将纯丙烯酸弹性乳液和玻璃胶加入水中充分搅拌均匀后，边搅拌边加入混合物料，混合均匀后加入消泡剂，继续搅拌均匀，烘烤得到所述抗裂助剂。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (9)

1.一种外墙抗裂腻子，其特征在于，包括以下按重量份计的原料：
白水泥350-450份，双飞粉550-640份，纤维素3-7份，聚乙烯醇4-8份，可再分散胶粉8-13份，木质纤维素1-3份，玻璃纤维1-3份。
2.根据权利要求1所述的一种外墙抗裂腻子，其特征在于，包括以下按重量份计的原料：
白水泥400份，双飞粉600份，纤维素5份，聚乙烯醇5份，可再分散胶粉10份，木质纤维素2份，玻璃纤维2份。
3.根据权利要求1所述的一种外墙抗裂腻子，其特征在于，所述聚乙烯醇为1788聚乙烯醇。
4.根据权利要求1所述的一种外墙抗裂腻子，其特征在于，所述外墙抗裂腻子的原料中还包括抗裂助剂2-6份。
5.根据权利要求4所述的一种外墙抗裂腻子，其特征在于，所述抗裂助剂包括以下按重量份计的原料：
水30-50份，粗石英砂20-40份，细石英砂10-30份，重钙粉10-30份，纯丙烯酸弹性乳液20-50份，消泡剂0.1-0.2份，甲基纤维素0.2-0.6份，玻璃微珠5-10份，玻璃胶20-30份。
6.根据权利要求5所述的一种外墙抗裂腻子，其特征在于，所述抗裂助剂包括以下按重量份计的原料：
水45份，粗石英砂30份，细石英砂20份，重钙粉21份，纯丙烯酸弹性乳液40份，消泡剂0.15份，甲基纤维素0.4份，玻璃微珠8份，玻璃胶26份。
7.根据权利要求5所述的一种外墙抗裂腻子，其特征在于，所述粗石英砂的细度为100-150目。
8.根据权利要求5所述的一种外墙抗裂腻子，其特征在于，所述细石英砂的细度为150-250目。
9.根据权利要求5所述的一种外墙抗裂腻子，其特征在于，所述抗裂助剂的制备方法为：(1)将粗石英砂、细石英砂、重钙粉、甲基纤维素、玻璃微珠混合并充分搅拌均匀，得到混合物料；(2)依次将纯丙烯酸弹性乳液和玻璃胶加入水中充分搅拌均匀后，边搅拌边加入混合物料，混合均匀后加入消泡剂，继续搅拌均匀，烘烤得到所述抗裂助剂。
CN201810860466.7A 2018-08-01 2018-08-01 一种外墙抗裂腻子 Pending CN108624111A (zh)