CN108611863A - 一种无磷无氮型精练剂及其制备和使用方法 - Google Patents
一种无磷无氮型精练剂及其制备和使用方法 Download PDFInfo
- Publication number
- CN108611863A CN108611863A CN201810474722.9A CN201810474722A CN108611863A CN 108611863 A CN108611863 A CN 108611863A CN 201810474722 A CN201810474722 A CN 201810474722A CN 108611863 A CN108611863 A CN 108611863A
- Authority
- CN
- China
- Prior art keywords
- free type
- scouring agent
- phosphorus nitrogen
- type scouring
- fatty alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种无磷无氮型精练剂及其制备和使用方法。其中所述无磷无氮型精练剂，其制备组分包括异构脂肪醇聚氧乙烯醚、脂肪醇聚氧乙烯聚氧丙烯醚、松香聚氧乙烯醚羧酸盐、仲烷基磺酸钠和水。本发明提供了一种无磷无氮型精练剂，其不含磷、氮、APEO并可生物降解，是一种环保型精练剂；而且，其在使用时精练毛效高、白度好。
Description
技术领域
本发明涉及一种纺织染整行业使用的精练剂及其制造和使用方法，尤其是，一种用在纤维素纤维梭织布处理中使用的精练剂及其制备和使用方法。
背景技术
已知，印染行业是纺织工业的重要组成本分，又是能耗较高、污水排放量较大的行业。而随着社会的不断向前发展，环境问题越来越受到社会的重视，相应的对于环境保护的呼声也是越来越高，因此，官方对于企业节能环保减排的要求也是越来越高。
对于印染行业来讲，开展节能减排工作，除了研发高效、节水、节能设备，开发并推广应用节能、节水的实用新技术外；采用高效、环保、节水、节能的染化料是现阶段最行之有效的办法，且投入少，见效快。
以其中的精练剂为例而言。目前，业界使用的大部分精练剂，都是由直链脂肪醇聚氧乙烯醚、异构脂肪醇聚氧乙烯醚、十二烷基苯磺酸盐、烷基磷酸酯盐、脂肪醇聚氧乙烯醚磷酸盐等复配而来。对于这些业界常用的精练剂，其均是在高温下使用的，例如，100℃；并且在使用后，很多都存在着生物降解缓慢的情况，很明显会对环保产生很大不利影响。
这是因为这些精练剂中含有的磷酸酯 ( 盐 ) 类表面活性剂，会大幅提高污水的化学耗氧量(COD)。进一步的，由于这些未经处理的含有大量的氮、磷营养物质的污水大部分是直接排放到江河湖泊中，其营养物质超过了这些承载水体的自净能力，因而会直接导致这些水体的富营养化污染，从而使得由氮、磷元素造成的水体污染日趋严重。这种对水体环境的危害，可参看关于“太湖蓝藻爆发”的相关新闻报道，同时这也导致了官方对于印染厂污水排放的 COD 值进行了更为严格的控制。
另外，在业界使用的这些精练剂中，有些精练剂竟然还在使用对环境具有潜在危害的烷基酚聚氧乙烯醚（APEO）这类非环保原料，明显是不符合现在社会对于环境保护的要求。
因此，确有必要开发一种新型的环保型的精练剂，来克服现有技术中的缺陷。
发明内容
本发明的目的在于提供一种无磷无氮型精练剂，其不含磷、氮、APEO并可生物降解，是一种环保型精练剂；而且，其在使用时精练毛效高、白度好。
为了实现上述目的，本发明采用的技术方案如下：
一种无磷无氮型精练剂，其制备组分包括异构脂肪醇聚氧乙烯醚、脂肪醇聚氧乙烯聚氧丙烯醚、松香聚氧乙烯醚羧酸盐、仲烷基磺酸钠和水，其中各组分的重量百分比为 ：
异构脂肪醇聚氧乙烯醚 5％~10％；
脂肪醇聚氧乙烯聚氧丙烯醚 10％~20％；
松香聚氧乙烯醚羧酸盐 18％~30％；
仲烷基磺酸钠 15％~25％；
水 25％~50％。
进一步的，在不同实施方式中，其中所述异构脂肪醇聚氧乙烯醚的重量百分比为5％~8％。
进一步的，在不同实施方式中，其中所述脂肪醇聚氧乙烯聚氧丙烯醚的重量百分比为12％~16％。
进一步的，在不同实施方式中，其中所述松香聚氧乙烯醚羧酸盐的重量百分比为20％~25％。
进一步的，在不同实施方式中，其中所述仲烷基磺酸钠的重量百分比为16％~20％。
进一步的，在不同实施方式中，其中所述水的重量百分比为31％~47％。
本发明的又一个实施方式提供了一种制备本发明涉及的所述无磷无氮型精练剂的制备方法，其包括以下步骤：
向反应釜中按重量百分比依次加入所述已经熔化了的异构脂肪醇聚氧乙烯醚、脂肪醇聚氧乙烯聚氧丙烯醚，开起搅拌器，充分搅拌30~50分钟；
按重量百分比依次加入所述松香聚氧乙烯醚羧酸盐和仲烷基磺酸钠，边搅拌边升温至50~60℃；
加入计量好的纯水，继续在50~60℃下保温搅拌1~2小时；
充分搅拌均匀后，降温至30~40℃过滤出料，即得所述无磷无氮型精练剂。
进一步的，在不同实施方式中，其中加入纯水的步骤是在30~60分钟内加完。
本发明的又一个实施方式提供了一种本发明涉及的所述无磷无氮型精练剂的使用方法，其在冷堆工艺下使用，其中使用的用料包括：烧碱45~55g/L、所述无磷无氮型精练剂12~18g/L、双氧水（100%）25~35g/L以及氧漂稳定剂12~18g/L。
进一步的，在不同实施方式中，其中所述冷堆工艺下是室温二浸二轧，其轧余率为100%。
相对于现有技术，本发明的有益效果是：本发明涉及的一种无磷无氮型精练剂及其制备和使用方法，其中的所述无磷无氮型精练剂采用不含氮、磷元素以及APEO的环保配方，并且在使用中精练毛效高、白度好，使得其是一种处理效率较高的环保型精练剂，具有良好的市场使用推广前景。
具体实施方式
以下将结合实施例，对本发明涉及的一种无磷无氮型精练剂及其制备和使用方法的技术方案作进一步的详细描述。
其中在本发明中，其使用的所有原材料均是常规使用的，可以从市场购得。在本发明中，如非特指，所有的量、百分比、份均为重量单位。
本发明的一个实施方式提供了一种无磷无氮型精练剂，按重量百分比，其组成如下：
异构脂肪醇聚氧乙烯醚 8.2％；
脂肪醇聚氧乙烯聚氧丙烯醚 14.8％；
松香聚氧乙烯醚羧酸盐 26.6％；
仲烷基磺酸钠 15.4％；
水 35.0％。
进一步的，其中所述无磷无氮型精练剂的制备方法，包括以下步骤：
在反应釜里按重量百分比依次加入所述已经熔化了的异构脂肪醇聚氧乙烯醚、脂肪醇聚氧乙烯聚氧丙烯醚，开起搅拌器，充分搅拌30-50分钟；
再依次加入所述松香聚氧乙烯醚羧酸盐和仲烷基磺酸钠，边搅拌边升温至50—60℃；
慢慢加入计量好的纯水（约在30-60分钟内加完），继续在50—60℃下保温搅拌1-2小时；
待充分搅拌均匀后，降温至30—40℃过滤出料，即得所述无磷无氮型精练剂。
在一个所述无磷无氮型精练剂的使用实施方式中，其中涉及的面料为纯棉纱卡20X16面料，工艺为冷堆工艺，涉及的用料包括：
烧碱50g/L；
所述无磷无氮型精练剂15g/L；
双氧水（100%）30g/L；
氧漂稳定剂15g/L；
其中室温二浸二轧，轧余率100%。
进一步的，随后还包括以下的步骤：
室温堆置16~24小时-----热水（95℃）洗3道------冷水洗2道----烘干回潮。
测试毛效和白度：毛效（cm/30min）：14.8；白度：80.5%。
本发明涉及的一种无磷无氮型精练剂及其制备和使用方法，其中的所述无磷无氮型精练剂采用不含氮、磷元素以及APEO的环保配方，并且在使用时精练毛效高、白度好，使得其是一种处理效率较高的环保型精练剂，具有良好的市场使用推广前景。
本发明的技术范围不仅仅局限于上述说明中的内容，本领域技术人员可以在不脱离本发明技术思想的前提下，对上述实施例进行多种变形和修改，而这些变形和修改均应当属于本发明的范围内。
Claims (10)
1.一种无磷无氮型精练剂；其特征在于，其制备组分包括异构脂肪醇聚氧乙烯醚、脂肪醇聚氧乙烯聚氧丙烯醚、松香聚氧乙烯醚羧酸盐、仲烷基磺酸钠和水，其中各组分的重量百分比为 ：
异构脂肪醇聚氧乙烯醚 5％~10％；
脂肪醇聚氧乙烯聚氧丙烯醚 10％~20％；
松香聚氧乙烯醚羧酸盐 18％~30％；
仲烷基磺酸钠 15％~25％；以及
水 25％~50％。
2.根据权利要求1所述的一种无磷无氮型精练剂，其特征在于，其中所述异构脂肪醇聚氧乙烯醚的重量百分比为5％~8％。
3.根据权利要求1所述的一种无磷无氮型精练剂，其特征在于，其中所述脂肪醇聚氧乙烯聚氧丙烯醚的重量百分比为12％~16％。
4.根据权利要求1所述的一种无磷无氮型精练剂，其特征在于，其中所述松香聚氧乙烯醚羧酸盐的重量百分比为20％~25％。
5.根据权利要求1所述的一种无磷无氮型精练剂，其特征在于，其中所述仲烷基磺酸钠的重量百分比为16％~20％。
6.根据权利要求1所述的一种无磷无氮型精练剂，其特征在于，其中所述水的重量百分比为31％~47％。
7.一种制备权利要求1所述的无磷无氮型精练剂的制备方法，其特征在于，其包括以下步骤：
向反应釜中按重量百分比依次加入所述已经熔化了的异构脂肪醇聚氧乙烯醚、脂肪醇聚氧乙烯聚氧丙烯醚，开起搅拌器，充分搅拌30~50分钟；
按重量百分比依次加入所述松香聚氧乙烯醚羧酸盐和仲烷基磺酸钠，边搅拌边升温至50~60℃；
加入计量好的纯水，继续在50~60℃下保温搅拌1~2小时；以及
充分搅拌均匀后，降温至30~40℃过滤出料，即得所述无磷无氮型精练剂。
8.根据权利要求7所述的制备方法，其特征在于，其中加入纯水的步骤是在30~60分钟内加完。
9.一种权利要求1所述的无磷无氮型精练剂的使用方法，其特征在于，其在冷堆工艺下使用，其中的用料包括：烧碱45~55g/L、所述无磷无氮型精练剂12~18g/L、双氧水（100%）25~35g/L以及氧漂稳定剂12~18g/L。
10.根据权利要求9所述的使用方法，其特征在于，其中所述冷堆工艺下是室温二浸二轧，其轧余率为100%。