CN108579802A - 一种脱硫催化剂 - Google Patents

一种脱硫催化剂 Download PDF

Info

Publication number
CN108579802A
CN108579802A CN201711489020.XA CN201711489020A CN108579802A CN 108579802 A CN108579802 A CN 108579802A CN 201711489020 A CN201711489020 A CN 201711489020A CN 108579802 A CN108579802 A CN 108579802A
Authority
CN
China
Prior art keywords
parts
oxide
rare earth
desulphurization catalyst
active metal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711489020.XA
Other languages
English (en)
Inventor
田晓亮
田永军
�田�浩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN HAOCHUANG ENERGY SAVING ENVIRONMENTAL PROTECTION EQUIPMENT Co Ltd
Original Assignee
TIANJIN HAOCHUANG ENERGY SAVING ENVIRONMENTAL PROTECTION EQUIPMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN HAOCHUANG ENERGY SAVING ENVIRONMENTAL PROTECTION EQUIPMENT Co Ltd filed Critical TIANJIN HAOCHUANG ENERGY SAVING ENVIRONMENTAL PROTECTION EQUIPMENT Co Ltd
Priority to CN201711489020.XA priority Critical patent/CN108579802A/zh
Publication of CN108579802A publication Critical patent/CN108579802A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种脱硫催化剂，按重量由以下组分组成：三氧化二铝12‑18份；氧化锌5‑10份；氧化镍4‑8份；二氧化钛3‑6份；氧化镁10‑20份；氧化锆1‑10份；MCM‑22分子筛0.1‑10份；氧化稀土1‑15份；活性金属5‑30份；粘结剂8‑12份；助剂24‑28份。本发明中添加的三氧化二铝、氧化锌、氧化镍、二氧化钛、氧化镁、氧化稀土和活性金属能提高产品的活性，催化效果较好，催化效率较高；而且添加的粘结剂可将产品制备成颗粒状、柱状、蜂窝状、拉西环状等各种形状，可供流化床、固定床反应器选用，应用范围广，适合工业推广。

Description

一种脱硫催化剂
技术领域
本发明涉及脱硫技术领域，尤其涉及一种脱硫催化剂。
背景技术
随着世界各国工业化进程的不断加深，SO2污染已超过烟尘污染成为大气环境的第一大污染物。烟气脱硫(FGD)有别于其他脱硫方式是世界上唯一大规模商业化应用的脱硫方法，是控制酸雨和SO2污染的最为有效的技术手段。
目前，市场上的脱硫催化剂种类繁多，但是普遍存在脱硫效果不好的缺陷，研究出一款脱硫效果好的脱硫催化剂已成为当前重要的课题之一。
发明内容
本发明正是针对以上技术问题，提供一种脱硫催化剂。
本发明为实现上述目的，采用以下技术方案：一种脱硫催化剂，其特征在于，按重量由以下组分组成：
所述氧化稀土中的稀土元素选自La、Ce、Pr、Nd、Pm、Sm、Eu、Gd、Tb、Dy、Ho、Er、Tm、Yb、Lu中的至少一种。
所述活性金属为钴、铁、锰中的至少一种。
所述助剂为质量分数为25％的氢氧化钠溶液。
本发明的有益效果是：本发明中添加的三氧化二铝、氧化锌、氧化镍、二氧化钛、氧化镁、氧化稀土和活性金属能提高产品的活性，催化效果较好，催化效率较高；而且添加的粘结剂可将产品制备成颗粒状、柱状、蜂窝状、拉西环状等各种形状，可供流化床、固定床反应器选用，应用范围广，适合工业推广。
具体实施方式
下面结合实施例对本发明作进一步说明：
一种脱硫催化剂，按重量由以下组分组成：
所述氧化稀土中的稀土元素选自La、Ce、Pr、Nd、Pm、Sm、Eu、Gd、Tb、Dy、Ho、Er、Tm、Yb、Lu中的至少一种。
所述活性金属为钴、铁、锰中的至少一种。
所述助剂为质量分数为25％的氢氧化钠溶液。
实施例1一种脱硫催化剂，按重量由以下组分组成：
所述氧化稀土中的稀土元素选自La、Ce、Pr、Nd、Pm、Sm、Eu、Gd、Tb、Dy、Ho、Er、Tm、Yb、Lu中的至少一种。
所述活性金属为钴、铁、锰中的至少一种。
所述助剂为质量分数为25％的氢氧化钠溶液。
实施例2一种脱硫催化剂，按重量由以下组分组成：
所述氧化稀土中的稀土元素选自La、Ce、Pr、Nd、Pm、Sm、Eu、Gd、Tb、Dy、Ho、Er、Tm、Yb、Lu中的至少一种。
所述活性金属为钴、铁、锰中的至少一种。
所述助剂为质量分数为25％的氢氧化钠溶液。
上面对本发明进行了示例性描述，显然本发明具体实现并不受上述方式的限制，只要采用了本发明的方法构思和技术方案进行的各种改进，或未经改进直接应用于其它场合的，均在本发明的保护范围之内。

Claims (4)

1.一种脱硫催化剂，其特征在于，按重量由以下组分组成：
2.根据权利要求1所述的一种脱硫催化剂，其特征在于，所述氧化稀土中的稀土元素选自La、Ce、Pr、Nd、Pm、Sm、Eu、Gd、Tb、Dy、Ho、Er、Tm、Yb、Lu中的至少一种。
3.根据权利要求1所述的一种脱硫催化剂，其特征在于，所述活性金属为钴、铁、锰中的至少一种。
4.根据权利要求1所述的一种脱硫催化剂，其特征在于，所述助剂为质量分数为25％的氢氧化钠溶液。
CN201711489020.XA 2017-12-30 2017-12-30 一种脱硫催化剂 Pending CN108579802A (zh)