CN108441080A - 一种水性无机复古地坪涂料 - Google Patents
一种水性无机复古地坪涂料 Download PDFInfo
- Publication number
- CN108441080A CN108441080A CN201810381199.5A CN201810381199A CN108441080A CN 108441080 A CN108441080 A CN 108441080A CN 201810381199 A CN201810381199 A CN 201810381199A CN 108441080 A CN108441080 A CN 108441080A
- Authority
- CN
- China
- Prior art keywords
- coating
- agent
- inorganic
- terrace
- antibacterial agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种水性无机复古地坪涂料；包括如下组分：水性环氧树脂、固化剂、水、酸性硅溶胶、润滑剂、硫酸钡、硅酸铝、硅酸钾、无机分散剂、二丙二醇丁醚、2‑甲基丙烯酸甲酯、有机胍类抗菌剂、石英粉、硅丙乳液、地坪灰、脱气剂、钛白粉、遮味剂。本发明还涉及上述涂料的制备方法，本发明涂料中添加有机胍类抗菌剂组分，其组分与其它组份相互融合有协同作用，可以消除因地坪膜因漆膜受灰尘、水泥灰、沥青、焦油、煤烟、酸性物质、树脂、昆虫、鸟类、化学品等物质的侵入、附着和沾污产生的斑点；本发明使用的助剂都是常规产品，大大降低的生产成本，有较好的经济效益。
Description
技术领域
本发明涉及水性无机涂料，具体地，涉及一种水性无机复古地坪涂料。
背景技术
涂料是一种具有保护功能又有美化物体的产品，人们在生活中处处可见，它泛应用在建筑、钢铁制品、木器等各个领域，已成为当今社会不可缺少的装饰材料。
在大量使用的涂料和油漆中，由于产品的各组分不同直接影响到了产品的质量与性价比，同时也可以把产品的问题赤裸的暴漏了出来，比如，很多产品在使用一段时间就会出现粉化、脱落、褪色现象，使其没有充分发挥自己的作用，导致了环保功能大大降低，丧失了对物体及物品的装饰目的。造成上述现象的原因：内因和外因；内因主要是产品配方或工艺的问题；尤其，在地坪膜上有与漆膜颜色不同的斑点的现象，漆膜受灰尘、水泥灰、沥青、焦油、煤烟、酸性物质、树脂、昆虫、鸟类、化学品等物质的侵入、附着和沾污引起；所用颜料不耐酸碱，或生长霉菌所致。
外因就是产品处于环境的影响。克服内因的方法可以调整产品的组分或者改进工艺；克服外因的方法可以针对产品处于的环境进行考察，比如主要是紫外线影响导致，那么可以在涂料中添加抗紫外线的组分，进而使得产品得以改进。
目前的地坪涂料是采用聚氨酯树脂、醇脂等原料为主剂，添加颜料，溶剂，助剂、固化剂经过调配制备而成的地面装饰材料。常见的比如环氧树脂地坪漆等，地坪涂料对于美化、保护地面，起到防尘，耐磨，易清洁，防潮湿，不易开裂等优点，所以在很多场合得到应用，如：工厂的生产车间地面、商业场地面、车库地面等。但现有技术中的地坪涂料气味重、防火能力差、附着力差、易老化开裂、起层，特别是遇高温以后回释放一种毒性非常大的化学物质，人体吸入以后对身体健康造成了危害；因为现有的涂料施工时回与固化剂或者稀释剂混合使用，人工操作困难，固化时间也比较长，并且需要的工艺步骤比较复杂，成活周期也比较场，从而大大降低了工作效率。因此，需要一种新型的地坪涂料。
发明内容
针对现有技术中的缺陷，本发明的目的是提供一种水性无机复古地坪涂料。
第一个方面，本发明提供一种水性无机复古地坪涂料，包括如下重量份数的各组分：
其中，
所述酸性硅溶胶为泰州协盛精铸科技有限公司生产的，其产品特性为：SiO2含量30-31％，Na20含量<0.006％，PH值2-4；
所述无机分散剂为千佑化工生产的型号为AKN-298；
所述遮味剂包括香精，化工原料不可能100％消除味道，在本发明组分中加入遮味剂，不但覆盖了某种化工原料散发的味道，而且还可以散发出让人舒适的味道；尤其是地下车库，经常有汽车尾气的味道，该涂料可以消除因汽车尾气散发的异味，让人有舒适感。
所述有机胍类抗菌剂为上海鹏图化工科技有限公司生产的型号为LXE-1杀菌剂，所述胍类抗菌剂是呈阳离子性的一种抗菌剂，在溶液中能与阴离子的表面活性剂相互作用，使得胍类抗菌剂分子上的阳离子氨基明显减少，使得抗菌效果明显降低，所以本发明组分中采用的非阴离子的表面活性剂，其使得本发明各组分之间相互融合，相互作用，不减少其原有的功能，所以本发明的各组分的配比不是简单的组合，而是通过大量的实验得出的。
第二方面，本发明还涉及前述的水性无机复古地坪涂料的制备方法，所述方法包括如下步骤：
步骤1，按涂料的各组及组份，依次向搅拌机中加入水性环氧树脂、水、酸性硅溶胶、润滑剂、硫酸钡、硅酸铝、硅酸钾、无机分散剂、二丙二醇丁醚、2-甲基丙烯酸甲酯、有机胍类抗菌剂，高速搅拌，时间为10分钟，
步骤2，再加入石英粉、硅丙乳液、地坪灰、脱气剂、钛白粉，固化剂，高速搅拌，时间为10分钟，搅拌均匀，即可。
与现有技术相比，本发明具有如下的有益效果：
(1)本发明在涂料中添加有机胍类抗菌剂组分，其组分与其它组份可以相互融合有协同作用，同时起到了消除因地坪膜因漆膜受灰尘、水泥灰、沥青、焦油、煤烟、酸性物质、树脂、昆虫、鸟类、化学品等物质的侵入、附着和沾污引起，产生的斑点作用；
(2)本发明采用硅酸盐乳液，因其具有与建筑材料的相容性，渗透能力强，使涂膜具有较好的附着力，从而使得涂料不起皮、开裂等现象；
(3)本发明采用的组分都是常规原料，成本低，有较好的经济前景。
(4)本发明涂料具有无味、环保的特点。
(5)本发明涂料中的各组组分之间具有协同作用，其相互制约，使得本发明具有耐磨、不开裂、防火、抗菌等优点。
(6)本发明涂料所采用的有机胍类抗菌剂为上海鹏图化工科技有限公司生产的型号为LXE-1杀菌剂，所述胍类抗菌剂是呈阳离子性的一种抗菌剂，在溶液中能与阴离子的表面活性剂相互作用，使得胍类抗菌剂分子上的阳离子氨基明显减少，使得抗菌效果明显降低，所以本发明组分中采用的非阴离子的表面活性剂，其使得本发明各组分之间相互融合，相互作用，不减少其原有的功能，所以本发明的各组分的配比不是简单的组合，而是通过大量的实验得出的。
(7)本发明组分中加入遮味剂，不但覆盖了某种化工原料散发的味道，而且还可以散发出让人感觉舒适气息；尤其是地下车库，经常有汽车尾气的味道，该涂料可以消除因汽车尾气散发的异味，让人有舒适感。
具体实施方式
下面结合具体实施例对本发明进行详细说明。以下实施例将有助于本领域的技术人员进一步理解本发明，但不以任何形式限制本发明。应当指出的是，对本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进。这些都属于本发明的保护范围。
实施例
本实施例提供一种水性无机复古地坪涂料，包括如下重量份数的各组分：
其中，
所述酸性硅溶胶为泰州协盛精铸科技有限公司生产的，其产品特性为：SiO2含量30-31％，Na20含量<0.006％，PH值2-4；
所述无机分散剂为千佑化工生产的型号为AKN-298；
所述有机胍类抗菌剂为上海鹏图化工科技有限公司生产的型号为LXE-1杀菌剂。
上述水性无机复古地坪涂料的制备方法，所述方法包括如下步骤：
步骤1，按涂料的各组及组份，依次向搅拌机中加入水性环氧树脂、水、酸性硅溶胶、润滑剂、硫酸钡、硅酸铝、硅酸钾、无机分散剂、二丙二醇丁醚、2-甲基丙烯酸甲酯、有机胍类抗菌剂，高速搅拌，时间为10分钟，
步骤2，再加入石英粉、硅丙乳液、地坪灰、脱气剂、钛白粉，固化剂，高速搅拌，时间为10分钟，搅拌均匀，即可，
其各组分按以下配比使用：
本发明采用上述各组分制备涂料，其各组分及份数为最佳实施例配比，各组分之间不但能充分溶合，而且能充分发挥其作用，得到的最终产品，不会出现分层、结块等不良现象，其使用效果显著，解决了现有地坪涂料因灰尘、水泥灰、沥青、焦油、煤烟、酸性物质、树脂、昆虫、鸟类、化学品等物质的侵入、附着和沾污引起的斑点的问题；大大延长了产品的使用寿命。所述遮味剂包括香精，化工原料不可能100％消除味道，本发明组分中加入遮味剂，不但覆盖了某种化工原料散发的味道，而且还可以散发出让人感觉舒适气息；尤其是地下车库，经常有汽车尾气的味道，该涂料可以消除因汽车尾气散发的异味，让人有舒适感。
综上所述：本发明在涂料中添加有机胍类抗菌剂组分，其组分与其它组份可以相互融合有协同作用，可以消除因地坪膜因漆膜受灰尘、水泥灰、沥青、焦油、煤烟、酸性物质、树脂、昆虫、鸟类、化学品等物质的侵入、附着和沾污产生的斑点；本发明采用硅酸盐乳液，因其具有与建筑材料的相容性，渗透能力强，使涂膜具有较好的附着力，从而使得涂料不起皮、开裂等现象；本发明采用的组分都是常规原料，成本低，有较好的经济前景。本发明涂料具有无味、环保的特点。本发明涂料中的各组组分之间具有协同作用，其相互制约，使得本发明具有耐磨、不开裂、防火、抗菌等优点。本发明涂料所采用的有机胍类抗菌剂为上海鹏图化工科技有限公司生产的型号为LXE-1杀菌剂，所述胍类抗菌剂是呈阳离子性的一种抗菌剂，在溶液中能与阴离子的表面活性剂相互作用，使得胍类抗菌剂分子上的阳离子氨基明显减少，使得抗菌效果明显降低，所以本发明组分中采用的非阴离子的表面活性剂，其使得本发明各组分之间相互融合，相互作用，不减少其原有的功能，所以本发明的各组分的配比不是简单的组合，而是通过大量的实验得出的。
以上对本发明的具体实施例进行了描述。需要理解的是，本发明并不局限于上述特定实施方式，本领域技术人员可以在权利要求的范围内做出各种变形或修改，这并不影响本发明的实质内容。
Claims (2)
1.一种水性无机复古地坪涂料，其特征在于，包括如下重量份数的各组分：
其中，
所述酸性硅溶胶为泰州协盛精铸科技有限公司生产的，其产品特性为：SiO2含量30-31％，Na20含量<0.006％，PH值2-4；
所述无机分散剂为千佑化工生产的型号为AKN-298；
所述有机胍类抗菌剂为上海鹏图化工科技有限公司生产的型号为LXE-1杀菌剂。
2.一种如权利要求1所述水性无机复古地坪涂料的制备方法，其特征在于，所述方法包括如下步骤：
步骤1，按涂料的各组及组份，依次向搅拌机中加入水性环氧树脂、水、酸性硅溶胶、润滑剂、硫酸钡、硅酸铝、硅酸钾、无机分散剂、二丙二醇丁醚、2-甲基丙烯酸甲酯、有机胍类抗菌剂，高速搅拌，时间为10分钟，
步骤2，再加入石英粉、硅丙乳液、地坪灰、脱气剂、钛白粉，固化剂，遮味剂，高速搅拌，时间为10分钟，搅拌均匀，即可。