CN108395783A - A kind of wood inside door anticorrosive paint capable of purifying air and preparation method thereof - Google Patents
A kind of wood inside door anticorrosive paint capable of purifying air and preparation method thereof Download PDFInfo
- Publication number
- CN108395783A CN108395783A CN201810199558.5A CN201810199558A CN108395783A CN 108395783 A CN108395783 A CN 108395783A CN 201810199558 A CN201810199558 A CN 201810199558A CN 108395783 A CN108395783 A CN 108395783A
- Authority
- CN
- China
- Prior art keywords
- parts
- purifying air
- inside door
- anticorrosive paint
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of wooden inside door anticorrosive paints capable of purifying air and preparation method thereof, include the raw material of following parts by weight meter:25 30 parts of polyacrylic resin, 18 23 parts of epoxy resin, 12 18 parts of organosiloxane resins, 8 16 parts of barium sulfate, 5 12 parts of talcum powder, 58 parts of diatomite, 4.5 8.5 parts of bamboo charcoal powder, 2.8 4.5 parts of negative ion powder, 35 parts of Folium Artemisiae Argyi powder, 2.8 4.2 parts of Peppermint essential oil, 47 parts of wood-fibred, 36 parts of nano zine oxide, 36 parts of nano magnesia, 36 parts of nano-titanium dioxide, 2.2 3.6 parts of lithium carbonate, 1.2 1.8 parts of pigment, 2.5 3.6 parts of mould inhibitor, the raw materials such as 2.2 3.5 parts of antioxidant;Coating of the present invention has good Corrosion Protection, and caking property is strong, not easily to fall off, and coating is good, and anti-aging property is excellent, is not easy to chap, capable of purifying air.
Description
Technical field
The present invention relates to anticorrosive paint technology fields, and in particular to it is a kind of wood inside door anticorrosive paint capable of purifying air and its
Preparation method.
Background technology
The wooden inside door is traditional architecture door, is mainly prepared by primary raw material of timber, anti-corrosive properties are poor, by external environment
It influencing seriously, when the sunlight time is long, easily drying cracks, and when external environment is excessively moist, hygroscopic moisture regain is rotted,
In order to extend the usage time of the wooden inside door, the big more options of people spray one layer of anticorrosive paint as protective layer in the wooden interior door skin,
To resist erosion of the external environment to the wooden inside door.
Containing harmful chemicals such as formaldehyde in the coating sprayed in the prior art, it is detrimental to health, and coating
Bad adhesion, it is easy to fall off or crack, influence the overall beautiful and service life time of the wooden inside door.
Invention content
For problems of the prior art, the present invention provides a kind of wooden inside door anticorrosive paint capable of purifying air and
Preparation method, coating of the present invention have good Corrosion Protection, and caking property is strong, not easily to fall off, and coating is good, can purify sky
Gas, anti-aging property is excellent, is not easy to chap, and can extend the service life of the wooden inside door coated on the wooden inside door outer layer.
In order to achieve the above object, the present invention is achieved through the following technical solutions:
A kind of wood inside door anticorrosive paint capable of purifying air, includes the raw material of following parts by weight meter:
25-30 parts of polyacrylic resin, 18-23 parts of epoxy resin, 12-18 parts of organosiloxane resins, barium sulfate 8-16
It is part, 5-12 parts of talcum powder, 5-8 parts of diatomite, 4.5-8.5 parts of bamboo charcoal powder, 2.8-4.5 parts of negative ion powder, 3-5 parts of Folium Artemisiae Argyi powder, thin
2.8-4.2 parts of lotus essential oil, 4-7 parts of wood-fibred, 3-6 parts of nano zine oxide, 3-6 parts of nano magnesia, nano-titanium dioxide 3-6
Part, 2.2-3.6 parts of lithium carbonate, 1.2-1.8 parts of pigment, 2.5-3.6 parts of mould inhibitor, 2.2-3.5 parts of antioxidant, levelling agent 1.3-
20-25 parts of 2.8 parts, 2.1-3.2 parts of adhesion promoter, 1.8-2.5 parts of coalescents and water.
Preferably, include the raw material of following parts by weight meter:28 parts of polyacrylic resin, 20 parts of epoxy resin, organic silica
15 parts of alkane resin, 12 parts of barium sulfate, 8 parts of talcum powder, 7 parts of diatomite, 6.5 parts of bamboo charcoal powder, 3.6 parts of negative ion powder, Folium Artemisiae Argyi powder 3.8
Part, 3.5 parts of Peppermint essential oil, 5 parts of wood-fibred, 5 parts of nano zine oxide, 5 parts of nano magnesia, 5 parts of nano-titanium dioxide, lithium carbonate
3.2 parts, 1.5 parts of pigment, 3.1 parts of mould inhibitor, 3.2 parts of antioxidant, 2.1 parts of levelling agent, 2.7 parts of adhesion promoter, film forming
22 parts of 2.2 parts of auxiliary agent and water.
Preferably, the pigment is that one or more of titanium white, iron oxide red, cobalt blue, verdigris, silver-colored light combine.
Preferably, the mould inhibitor is 1,2-benzisothiazolin-3-one, 2- (4- thiazolyls) benzimidazole, tetramethyl
One or more of two thio thiurams and 2,4,5,6- daconil Ms combine.
Preferably, the antioxidant is butylated hydroxy anisole, dibutyl hydroxy toluene, propylgallate and Te Ding
One or more of base hydroquinone combines.
Preferably, the levelling agent is one kind or several in acrylic acid-2-ethyl caproite, hydroxypropyl acrylate and dimethylbenzene
Kind combines.
Preferably, the adhesion promoter is γ-mercaptopropyl trimethoxysilane, γ-(methacryloxy) third
One or more of base trimethoxy silane and β-(3,4- epoxyhexyls) ethyl trimethyl silane combine.
Preferably, the coalescents are propylene-glycol ethyl ether, butyl glycol ether, propandiol butyl ether, butyl glycol ether ethyl alcohol
One or more of ester and Lauryl Alcohol ester combine.
A kind of preparation method of above-mentioned wooden inside door anticorrosive paint capable of purifying air is also disclosed in the present invention, specifically,
Include the following steps:
(1) each raw material is weighed according to the raw material weight number of wooden inside door anticorrosive paint capable of purifying air;
(2) by polyacrylic resin, epoxy resin, organosiloxane resins, barium sulfate, talcum powder, diatomite, bamboo charcoal
Powder, negative ion powder, Folium Artemisiae Argyi powder, wood-fibred, nano zine oxide, nano magnesia, nano-titanium dioxide, lithium carbonate, pigment and water
Mixing, is warming up to 80-90 degrees Celsius, with 1500-2000 revs/min, stirs 25-30 minutes, is uniformly mixed;
(3) mixture obtained in step (2) is made every effort to promote with Peppermint essential oil, mould inhibitor, antioxidant, levelling agent, attachment
After being stirred into agent and coalescents, progress dispersion mixing is uniform in merging ultrasonic dispersing machine, and dispersion temperature 55-60 is Celsius
Degree, jitter time 15-20 minutes, to get wooden inside door anticorrosive paint capable of purifying air after being cooled to room temperature.
The present invention has following advantageous effect:
(1) coating of the present invention has good Corrosion Protection, and caking property is strong, not easily to fall off, and coating is good, and appearance is equal
Even, anti-aging property is excellent, is not easy to chap, and can extend the service life of the wooden inside door coated on the wooden inside door outer layer.
(2) wood-fibred is added in raw material of the present invention, the unique irregular sector structure of wood-fibred causes fiber combinations to be arranged
There are a large amount of irregular gaps when row, organic molecule and inorganic molecule can be filled in gap, is that material overall structure is stablized
Densification has very strong toughness and anti-aging property.
(3) negative ion powder is added in raw material of the present invention, negative ion powder is added in coating, can play purification Interior Space
Gas improves indoor air quality, promotes blood circulation of human body to improve the immunity of the human body and boosts metabolism.Alleviate essence to reach
Refreshing fatigue improves the effect of energy, while can adsorb the wooden inside door itself other harmful substances with indoor release.
(4) Folium Artemisiae Argyi powder and Peppermint essential oil are added in raw material of the present invention, Folium Artemisiae Argyi powder and Peppermint essential oil, can as natural materials
To improve the smell of coating, increase the fine smell of coating, while can be with pure and fresh room air, the organic substance released has
Beneficial to health.
Specific implementation mode
The specific implementation mode of the present invention is further described with reference to embodiment, following embodiment is only used for more
Technical scheme of the present invention is clearly demonstrated, and not intended to limit the protection scope of the present invention.
Embodiment 1
A kind of wood inside door anticorrosive paint capable of purifying air, includes the raw material of following parts by weight meter:
25 parts of polyacrylic resin, 18 parts of epoxy resin, 12 parts of organosiloxane resins, 8 parts of barium sulfate, 5 parts of talcum powder,
5 parts of diatomite, 4.5 parts of bamboo charcoal powder, 2.8 parts of negative ion powder, 3 parts of Folium Artemisiae Argyi powder, 2.8 parts of Peppermint essential oil, 4 parts of wood-fibred, nano oxygen
Change 3 parts of zinc, 3 parts of nano magnesia, 3 parts of nano-titanium dioxide, 2.2 parts of lithium carbonate, 1.2 parts of pigment, 2.5 parts of mould inhibitor, antioxygen
20 parts of 2.2 parts of agent, 1.3 parts of levelling agent, 2.1 parts of adhesion promoter, 1.8 parts of coalescents and water.
Pigment is titanium white.
Mould inhibitor is 1,2- benzisothiazole-3-ketones and 2- (4- thiazolyls) benzimidazole according to mass ratio 1:1 mixing
Composition.
Antioxidant is butylated hydroxy anisole and dibutyl hydroxy toluene according to mass ratio 2:1 mixing composition.
Levelling agent is acrylic acid-2-ethyl caproite.
Adhesion promoter is γ-mercaptopropyl trimethoxysilane.
Coalescents are propylene-glycol ethyl ether, butyl glycol ether and propandiol butyl ether according to mass ratio 1:1:1 mixing composition.
A kind of preparation method of above-mentioned wooden inside door anticorrosive paint capable of purifying air is also disclosed in the present embodiment, specifically
Ground includes the following steps:
(1) each raw material is weighed according to the raw material weight number of wooden inside door anticorrosive paint capable of purifying air;
(2) by polyacrylic resin, epoxy resin, organosiloxane resins, barium sulfate, talcum powder, diatomite, bamboo charcoal
Powder, negative ion powder, Folium Artemisiae Argyi powder, wood-fibred, nano zine oxide, nano magnesia, nano-titanium dioxide, lithium carbonate, pigment and water
Mixing, is warming up to 80 degrees Celsius, with 1500 revs/min, stirs 25 minutes, is uniformly mixed;
(3) mixture obtained in step (2) is made every effort to promote with Peppermint essential oil, mould inhibitor, antioxidant, levelling agent, attachment
After being stirred into agent and coalescents, progress dispersion mixing is uniform in merging ultrasonic dispersing machine, 55 degrees Celsius of dispersion temperature,
Jitter time 15 minutes, to get wooden inside door anticorrosive paint capable of purifying air after being cooled to room temperature.
Embodiment 2
A kind of wood inside door anticorrosive paint capable of purifying air, includes the raw material of following parts by weight meter:
30 parts of polyacrylic resin, 23 parts of epoxy resin, 18 parts of organosiloxane resins, 16 parts of barium sulfate, talcum powder 12
Part, 8 parts of diatomite, 8.5 parts of bamboo charcoal powder, 4.5 parts of negative ion powder, 5 parts of Folium Artemisiae Argyi powder, 4.2 parts of Peppermint essential oil, wood-fibred 7 part, nanometer
6 parts of zinc oxide, 6 parts of nano-titanium dioxide, 3.6 parts of lithium carbonate, 1.8 parts of pigment, 3.6 parts of mould inhibitor, resists 6 parts of nano magnesia
25 parts of 3.5 parts of oxidant, 2.8 parts of levelling agent, 3.2 parts of adhesion promoter, 2.5 parts of coalescents and water.
Pigment is iron oxide red and silver-colored light according to mass ratio 1:1 mixing composition.
Mould inhibitor is two thio thiuram of tetramethyl and 2,4,5,6- daconil Ms according to mass ratio 2:3 mixing groups
At.
Antioxidant is propylgallate and tert-butylhydroquinone according to mass ratio 2:1 mixing composition.
Levelling agent is hydroxypropyl acrylate.
Adhesion promoter is γ-(methacryloxy) propyl trimethoxy silicane.
Coalescents are Lauryl Alcohol ester.
A kind of preparation method of above-mentioned wooden inside door anticorrosive paint capable of purifying air is also disclosed in the present embodiment, specifically
Ground includes the following steps:
(1) each raw material is weighed according to the raw material weight number of wooden inside door anticorrosive paint capable of purifying air;
(2) by polyacrylic resin, epoxy resin, organosiloxane resins, barium sulfate, talcum powder, diatomite, bamboo charcoal
Powder, negative ion powder, Folium Artemisiae Argyi powder, wood-fibred, nano zine oxide, nano magnesia, nano-titanium dioxide, lithium carbonate, pigment and water
Mixing, is warming up to 90 degrees Celsius, with 2000 revs/min, stirs 30 minutes, is uniformly mixed;
(3) mixture obtained in step (2) is made every effort to promote with Peppermint essential oil, mould inhibitor, antioxidant, levelling agent, attachment
After being stirred into agent and coalescents, progress dispersion mixing is uniform in merging ultrasonic dispersing machine, 60 degrees Celsius of dispersion temperature,
Jitter time 20 minutes, to get wooden inside door anticorrosive paint capable of purifying air after being cooled to room temperature.
Embodiment 3
A kind of wood inside door anticorrosive paint capable of purifying air, includes the raw material of following parts by weight meter:
28 parts of polyacrylic resin, 20 parts of epoxy resin, 15 parts of organosiloxane resins, 12 parts of barium sulfate, talcum powder 8
Part, 5 parts of wood-fibred, is received 7 parts of diatomite, 6.5 parts of bamboo charcoal powder, 3.6 parts of negative ion powder, 3.8 parts of Folium Artemisiae Argyi powder, 3.5 parts of Peppermint essential oil
Rice 5 parts of zinc oxide, 5 parts of nano magnesia, 5 parts of nano-titanium dioxide, 3.2 parts of lithium carbonate, 1.5 parts of pigment, 3.1 parts of mould inhibitor,
22 parts of 3.2 parts of antioxidant, 2.1 parts of levelling agent, 2.7 parts of adhesion promoter, 2.2 parts of coalescents and water.
Pigment is cobalt blue, verdigris and silver-colored light according to mass ratio 1:1:1 mixing composition.
Mould inhibitor is 1,2- benzisothiazole-3-ketones and two thio thiuram of tetramethyl according to mass ratio 1:1 mixing group
At.
Antioxidant is butylated hydroxy anisole and propylgallate according to mass ratio 1:1 mixing composition.
Levelling agent is acrylic acid-2-ethyl caproite and dimethylbenzene according to mass ratio 3:1 mixing composition.
Adhesion promoter is that γ-mercaptopropyl trimethoxysilane and β-(3,4- epoxyhexyls) ethyl trimethyl silane are pressed
According to mass ratio 2:1 mixing composition.
Coalescents are propandiol butyl ether and butyl glycol ether ethyl alcohol ester according to mass ratio 1:1 mixing composition.
A kind of preparation method of above-mentioned wooden inside door anticorrosive paint capable of purifying air is also disclosed in the present embodiment, specifically
Ground includes the following steps:
(1) each raw material is weighed according to the raw material weight number of wooden inside door anticorrosive paint capable of purifying air;
(2) by polyacrylic resin, epoxy resin, organosiloxane resins, barium sulfate, talcum powder, diatomite, bamboo charcoal
Powder, negative ion powder, Folium Artemisiae Argyi powder, wood-fibred, nano zine oxide, nano magnesia, nano-titanium dioxide, lithium carbonate, pigment and water
Mixing, is warming up to 86 degrees Celsius, with 1800 revs/min, stirs 26 minutes, is uniformly mixed;
(3) mixture obtained in step (2) is made every effort to promote with Peppermint essential oil, mould inhibitor, antioxidant, levelling agent, attachment
After being stirred into agent and coalescents, progress dispersion mixing is uniform in merging ultrasonic dispersing machine, 58 degrees Celsius of dispersion temperature,
Jitter time 17 minutes, to get wooden inside door anticorrosive paint capable of purifying air after being cooled to room temperature.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, although with reference to aforementioned reality
Applying example, invention is explained in detail, for those skilled in the art, still can be to aforementioned each implementation
Technical solution recorded in example is modified or equivalent replacement of some of the technical features.All essences in the present invention
With within principle, any modification, equivalent replacement, improvement and so on should all be included in the protection scope of the present invention god.
Claims (9)
1. a kind of wood inside door anticorrosive paint capable of purifying air, which is characterized in that including following raw material by weight:Poly- third
25-30 parts of olefin(e) acid resin, 18-23 parts of epoxy resin, 12-18 parts of organosiloxane resins, 8-16 parts of barium sulfate, talcum powder 5-12
Part, 5-8 parts of diatomite, 4.5-8.5 parts of bamboo charcoal powder, 2.8-4.5 parts of negative ion powder, 3-5 parts of Folium Artemisiae Argyi powder, Peppermint essential oil 2.8-4.2
Part, 4-7 parts of wood-fibred, 3-6 parts of nano zine oxide, 3-6 parts of nano magnesia, 3-6 parts of nano-titanium dioxide, lithium carbonate 2.2-
3.6 parts, 1.2-1.8 parts of pigment, 2.5-3.6 parts of mould inhibitor, 2.2-3.5 parts of antioxidant, 1.3-2.8 parts of levelling agent, adhesive force
20-25 parts of 2.1-3.2 parts of accelerating agent, 1.8-2.5 parts of coalescents and water.
2. wood inside door according to claim 1 anticorrosive paint capable of purifying air, which is characterized in that including following parts by weight
The raw material of meter:28 parts of polyacrylic resin, 20 parts of epoxy resin, 15 parts of organosiloxane resins, 12 parts of barium sulfate, talcum powder 8
Part, 5 parts of wood-fibred, is received 7 parts of diatomite, 6.5 parts of bamboo charcoal powder, 3.6 parts of negative ion powder, 3.8 parts of Folium Artemisiae Argyi powder, 3.5 parts of Peppermint essential oil
Rice 5 parts of zinc oxide, 5 parts of nano magnesia, 5 parts of nano-titanium dioxide, 3.2 parts of lithium carbonate, 1.5 parts of pigment, 3.1 parts of mould inhibitor,
22 parts of 3.2 parts of antioxidant, 2.1 parts of levelling agent, 2.7 parts of adhesion promoter, 2.2 parts of coalescents and water.
3. wood inside door according to claim 1 anticorrosive paint capable of purifying air, which is characterized in that the pigment is titanium
In vain, one or more of iron oxide red, cobalt blue, verdigris, silver-colored light combine.
4. wood inside door according to claim 1 anticorrosive paint capable of purifying air, which is characterized in that the mould inhibitor is 1,
2- benzisothiazole-3-ketones, 2- (4- thiazolyls) benzimidazole, two thio thiuram of tetramethyl and 2,4,5,6- tetrachloro isophthalic
One or more of dintrile combines.
5. wood inside door anticorrosive paint capable of purifying air according to claim 1, which is characterized in that the antioxidant is
One or more of butylated hydroxy anisole, dibutyl hydroxy toluene, propylgallate and tert-butylhydroquinone combine.
6. wood inside door according to claim 1 anticorrosive paint capable of purifying air, which is characterized in that the levelling agent is third
One or more of olefin(e) acid -2- ethylhexyls, hydroxypropyl acrylate and dimethylbenzene combine.
7. wood inside door according to claim 1 anticorrosive paint capable of purifying air, which is characterized in that the adhesive force promotes
Agent be γ-mercaptopropyl trimethoxysilane, γ-(methacryloxy) propyl trimethoxy silicanes and β-(3,4- epoxies oneself
Base) one or more of ethyl trimethyl silane combines.
8. wood inside door anticorrosive paint capable of purifying air according to claim 1, which is characterized in that the coalescents are
One or more of propylene-glycol ethyl ether, butyl glycol ether, propandiol butyl ether, butyl glycol ether ethyl alcohol ester and Lauryl Alcohol ester are tied
It closes.
9. a kind of preparation method of such as claim 1-8 any one of them wood inside doors anticorrosive paint capable of purifying air, special
Sign is, includes the following steps:
(1) each raw material is weighed according to the raw material weight number of wooden inside door anticorrosive paint capable of purifying air;
(2) by polyacrylic resin, epoxy resin, organosiloxane resins, barium sulfate, talcum powder, diatomite, bamboo charcoal powder, negative
Ion powder, Folium Artemisiae Argyi powder, wood-fibred, nano zine oxide, nano magnesia, nano-titanium dioxide, lithium carbonate, pigment and water mixing,
It is warming up to 80-90 degrees Celsius, with 1500-2000 revs/min, stirs 25-30 minutes, is uniformly mixed;
(3) by mixture obtained in step (2) and Peppermint essential oil, mould inhibitor, antioxidant, levelling agent, adhesion promoter
After being stirred with coalescents, progress dispersion mixing is uniform in merging ultrasonic dispersing machine, 55-60 degrees Celsius of dispersion temperature,
Jitter time 15-20 minutes, to get wooden inside door anticorrosive paint capable of purifying air after being cooled to room temperature.