CN109651910A - A kind of coating - Google Patents
A kind of coating Download PDFInfo
- Publication number
- CN109651910A CN109651910A CN201811598943.3A CN201811598943A CN109651910A CN 109651910 A CN109651910 A CN 109651910A CN 201811598943 A CN201811598943 A CN 201811598943A CN 109651910 A CN109651910 A CN 109651910A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- coating
- mixture
- mixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of coating, the raw material components including following parts by weight: 100-200 parts of lotion, 8-15 parts of ethylene glycol, 6-12 parts of coalescing agent, 3-7 parts of thickener, 250-450 parts of nano composite powder, 50-100 parts of wollastonite in powder, 30-60 parts of titanium dioxide, 2-5 parts of cellulose, 3-5 parts of dispersing agent, 1-3 parts of wetting agent, 1-3 parts of defoaming agent, 1-3 parts of fungicide, 1-3 parts of multifunctional assistant, 250-300 parts of water；The present invention respectively develops the coating for being suitable for painting or coated on inner wall of building and exterior wall, all has high compactness, can effectively prevent coating surface contamination, xanthochromia；Ultraviolet light can be prevented through coating, and can ultra-violet radiation resisting destruction, reduce by ultraviolet radiation destroy and occur contamination, xanthochromia, decomposition and so on rate, coating covering power can be effectively improved；And there is stronger chemical stability, light resistance and weatherability, have the advantages that adhesive force is strong, flintiness is big, be not susceptible to shelling peeling, luster performance does not take off change for a long time, can also prolong the service life.
Description
Technical field
The present invention relates to chemical technology field more particularly to a kind of coating.
Background technique
As a kind of novel environmental-friendly construction material, coating is answered in the decoration and protection of exterior walls of buildings and inner wall surface
Consequence is occupied in, keeps building wall beautiful and clean, while can also play protection building wall, is extended and is used the longevity
The effect of life gradually substitutes the traditional decorations material such as common stone material, and will persistently keep this advantage in following its, has wide
Market prospects.
Currently, existing coating is primarily present following disadvantage: killing bacterium, mould proof, absorption ultraviolet light function first is that not having
Energy；Second is that poor adhesive force, easy to aging dimmed, and it is insufficient with the adhesiveness of the original cement bottom layer of wall, cause delamination to be peeled off；Third is that
Since the interior wall coating of building focuses on decoration and environmental protection, and exterior coating emphasis is protected and durable, lacks while External Wall applies
The development of material and interior wall coating.
Summary of the invention
Present invention solves the technical problem that be to overcome the deficiencies of existing technologies, provide a kind of high compactness, adhesive force it is strong,
Flintiness is big, is not susceptible to shelling peels off, luster performance does not take off the coating of change for a long time.
In order to solve the above-mentioned technical problem, the present invention is addressed by following technical proposals:
A kind of coating, the raw material components including following parts by weight: 50-100 parts of lotion, 5-15 parts of ethylene glycol, film forming help
4-8 parts of agent, 2-4 parts of thickener, 400-600 parts of nano composite powder, 4 parts of cellulose, 5 parts of dispersing agent, 1-2 parts of wetting agent, defoaming
1-2 parts of agent, 1-2 parts of fungicide, 1-3 parts of multifunctional assistant, 300-500 parts of water.Wherein, lotion uses acrylate copolymer,
On the one hand, the water resistance that can effectively improve coating prevents the solia particles such as dust from penetrating into coating with moisture and leading to coating surface
Contamination and xanthochromia；On the other hand, acrylate copolymer is compared to the benzene second being used to as binder that existing coating is often used
For alkene-acrylate copolymer, it is sensitive low that reaction is irradiated to ultraviolet light, it is not easy to decompose jaundice；Cellulose using it is non-from
The water dissolvable cellulose ether of subtype, can be the hydroxyethyl ether cellulose of different molecular weight, be primarily used to increase viscosity,
Improve storage stability and workability；The addition of nano composite powder is so that coating final products have the characteristics that high compactness, together
When have the advantages that high temperature resistant, rub resistance, with high hardness；Ethylene glycol main function is as solvent, and ethylene glycol can will be in coating
Film forming matter dissolves or is separated into homogeneous liquid, in order to paint coating or coated on building masonry wall when is constructed into
Film, the volatile characteristic after the completion of construction due to ethylene glycol enable ethylene glycol to volatilize in an atmosphere from coating；Film forming helps
Agent uses alcohol ester 12, plays the Plastic Flow for promoting latex particle and elastic deformation, reduces the minimum film formation temperature of lotion, changes
The effect of kind paint film property；Multifunctional assistant uses AMP-95 multifunctional assistant, and AMP-95 multifunctional assistant is current a small number of tools
There are one of low molecular weight and overbasic industrial amine, has the function of adjusting the pH stable of lotion adhesive, additionally have
The excellent function such as dispersion, thickening, non-discolouring, and it is also equipped with antimicrobial (sterilization) characteristic, while also can be reduced VOC (volatilization
Property organic compound) total amount, facilitate promoted environmental-protecting performance；Wetting agent can be used for improving the surface tension and permeability of coating,
Coating is set preferably to soak ground, so that the adhesive force of coating is improved, especially to raising priming paint to the adhesive force of ground；
Defoaming agent effectively eliminates extra foam, improves the quality of coating final products.
Preferably, being matched by 50-100 parts of lotion, 5-15 parts of ethylene glycol, 4-8 parts of coalescing agent, 2-4 parts of thickener
Than and mix, mixture A is then stirred and is made to the lotion after mixing, ethylene glycol, coalescing agent, thickener, is stirred
It mixes speed and mixing time is respectively 60 revs/min and 20 minutes.
It is stirred and is made mixture B preferably, 400-600 parts of nano composite powder is added in mixture A, is stirred
It mixes speed and mixing time is respectively 600 revs/min and 30 minutes.
Preferably, by 4 parts of cellulose, 5 parts of dispersing agent, 1-2 parts of wetting agent, 1-2 parts of defoaming agent, 1-2 parts of fungicide, more
1-3 parts of function additive, 300-500 parts of water matched and mixed, then to after mixing cellulose, dispersing agent, wetting agent,
Defoaming agent, fungicide, multifunctional assistant, water are stirred and are made mixture C, and mixing speed and mixing time are respectively 60
Rev/min and 5 minutes.
A kind of coating, the raw material components including following parts by weight: 100-200 parts of lotion, 8-15 parts of ethylene glycol, film forming help
6-12 parts of agent, 3-7 parts of thickener, 250-450 parts of nano composite powder, 50-100 parts of wollastonite in powder, 30-60 parts of titanium dioxide, fiber
2-5 parts plain, 3-5 parts of dispersing agent, 1-3 parts of wetting agent, 1-3 parts of defoaming agent, 1-3 parts of fungicide, 1-3 parts of multifunctional assistant, water
250-300 parts；Wherein, lotion uses acrylate copolymer, on the one hand, the paint film that color inhibition coating can be made to be formed causes
It is close, the water resistance of paint film can be effectively improved, prevents the solia particles such as dust from penetrating into paint film with moisture and leading to being stained with for surface of the paint film
Dirty and xanthochromia；On the other hand, acrylate copolymer is compared to the styrene-the third being used to as binder that existing coating is often used
For olefin(e) acid ester copolymer, it is sensitive low that reaction is irradiated to ultraviolet light, it is not easy to decompose jaundice；Ethylene glycol main function is conduct
Solvent, the film forming matter in coating can be dissolved or be separated into homogeneous liquid by ethylene glycol, in order to paint or coat coating
It constructs when on building masonry wall film forming, the volatile characteristic after the completion of construction due to ethylene glycol enables ethylene glycol from coating
Middle volatilization is in an atmosphere；Cellulose uses non-ionic water dissolvable cellulose ether, can be the ethoxy of different molecular weight
Cellulose ether is primarily used to increase viscosity, improves storage stability and workability；The addition of nano composite powder is so that apply
Material final products have the characteristics that high compactness, while having the advantages that high temperature resistant, rub resistance, with high hardness；The effect of titanium dioxide is not
It only covers and decorates, prior effect is the physical and chemical performance for improving coating, enhances chemical stability, is covered so that improving
Power, reducing power, anticorrosive property, fast light, weatherability, and enhance the mechanical strength and adhesive force of paint film, crackle is prevented, is prevented ultraviolet
The transmission of line and moisture extends the paint film service life to postpone aging, and titanium dioxide has excellent pigment performance, and nontoxic, and
People more favor in the coating of the white and light color that are generated by titanium dioxide；The effect of wollastonite in powder is: it is good reinforcing, both
The toughness and durability of coating can be improved, but coating surface can be kept smooth with and good glossiness, and improve
It is anti-to scrub with resistance to weathering energy, it can also reduce the oil absorption of coating and ink and keep alkalinity, there is resistance to corrosion, and can be with
The bright coating of high quality is obtained, and there is good equalization and anti-aging property, keeps coating available preferably
Mechanical strength increases durability, increases adherence and corrosion resistance, it may have good coverage rate, adhesive force；Coalescing agent
Using alcohol ester 12, the Plastic Flow for promoting latex particle and elastic deformation are played, the minimum film formation temperature of lotion is reduced, improves
The effect of paint film property；Multifunctional assistant uses AMP-95 multifunctional assistant, and AMP-95 multifunctional assistant is that current minority has
One of low molecular weight and overbasic industrial amine, have the function of adjusting the pH stable of lotion adhesive, additionally have and divide
The excellent function such as scattered, thickening, non-discolouring, and it is also equipped with antimicrobial (sterilization) characteristic, while also can be reduced VOC (volatility
Organic compound) total amount, help to promote environmental-protecting performance；Wetting agent can be used for improving the surface tension and permeability of coating, make
Coating can preferably soak ground, so that the adhesive force of coating is improved, especially to raising priming paint to the adhesive force of ground；Disappear
Infusion effectively eliminates extra foam, improves the quality of coating final products.
Preferably, by lotion 100-200 parts, 8-15 parts of ethylene glycol, 6-12 parts of coalescing agent, 3-7 parts of thickener progress
It matches and mixes, mixture D is then stirred and be made to the lotion after mixing, ethylene glycol, coalescing agent, thickener,
Mixing speed and mixing time are respectively 60 revs/min and 20 minutes.
Preferably, being matched by 250-450 parts of nano composite powder, 50-100 parts of wollastonite in powder, 30-60 parts of titanium dioxide
Than then mixture E being stirred and being made to nano composite powder, wollastonite in powder, the titanium dioxide after mixing, by mixture E
It is added in mixture D and is stirred and is made mixture F, mixing speed and mixing time are respectively 600 revs/min and 30 points
Clock.
Preferably, pressing cellulose 2-5 parts, 3-5 parts of dispersing agent, 1-3 parts of wetting agent, 1-3 parts of defoaming agent, fungicide 1-3
Part, 1-3 parts of multifunctional assistant, 250-300 parts of water matched and mixed, then to the cellulose after mixing, dispersing agent, profit
Humectant, defoaming agent, fungicide, multifunctional assistant, water are stirred and are made mixture G, mixing speed and mixing time difference
For 60 revs/min and 5 minutes.
It is stirred and is made mixture H preferably, mixture F is added in mixture G, when mixing speed is with stirring
Between be respectively 60 revs/min and 5 minutes.
The present invention is due to using above technical scheme, and have significant technical effect: the present invention is respectively to suitable for powder
Brush or the coating coated on inner wall of building and exterior wall are developed, and are all had high compactness, be can effectively prevent coating surface
It stains, xanthochromia；Ultraviolet light can be prevented to penetrate coating, and the destruction of energy ultra-violet radiation resisting, reduce and destroyed by ultraviolet radiation
And occur contamination, xanthochromia, decomposition and so on rate, coating covering power can be effectively improved；And there is stronger chemistry
Stability, light resistance and weatherability, have that adhesive force is strong, flintiness is big, is not susceptible to that shelling is peeled off, luster performance does not take off for a long time
The advantages of change, can also prolong the service life.
Specific embodiment
Below with reference to embodiment, present invention is further described in detail.
A kind of coating is mainly used for painting or be coated on inner wall of building, the raw material components including following parts by weight:
50-100 parts of lotion, 5-15 parts of ethylene glycol, 4-8 parts of coalescing agent, 2-4 parts of thickener, 400-600 parts of nano composite powder, fiber
Plain 4 parts, 5 parts of dispersing agent, 1-2 parts of wetting agent, 1-2 parts of defoaming agent, 1-2 parts of fungicide, 1-3 parts of multifunctional assistant, water 300-500
Part.Wherein, lotion uses acrylate copolymer, on the one hand, the compact in paint film that color inhibition coating can be made to be formed, it can be effective
The water resistance for improving paint film prevents the solia particles such as dust from leading to contamination and the xanthochromia of surface of the paint film with moisture infiltration paint film；
On the other hand, acrylate copolymer is used to be total to as the cinnamic acrylic ester of binder compared to what existing coating was often used
For polymers, it is sensitive low that reaction is irradiated to ultraviolet light, it is not easy to decompose jaundice；Cellulose uses non-ionic water dissolvable
Cellulose ether can be the hydroxyethyl ether cellulose of different molecular weight, is primarily used to increase viscosity, improves storage stability
And workability；The addition of nano composite powder has high temperature resistant, resistance to so that coating final products have the characteristics that high compactness
Friction, advantage with high hardness；Coalescing agent uses alcohol ester 12, plays the Plastic Flow for promoting latex particle and elastic deformation,
It reduces the minimum film formation temperature of lotion, improve the effect of paint film property；Multifunctional assistant uses AMP-95 multifunctional assistant, AMP-
95 multifunctional assistants are that current minority has one of low molecular weight and overbasic industrial amine, have the pH for adjusting lotion adhesive
It is worth stable function, additionally there is the excellent function such as dispersion, thickening, non-discolouring, and be also equipped with antimicrobial (sterilization) spy
Property, while also can be reduced VOC (volatile organic compounds) total amount, help to promote environmental-protecting performance；Wetting agent can be used for improving
The surface tension and permeability of coating, enable coating preferably to soak ground, to improve the adhesive force of coating, especially pair
Priming paint is improved to the adhesive force of ground；Defoaming agent effectively eliminates extra foam, improves the quality of coating final products.
In the present embodiment, by 50-100 parts of lotion, 5-15 parts of ethylene glycol, 4-8 parts of coalescing agent, 2-4 parts of thickener progress
It matches and mixes, mixture A is then stirred and be made to the lotion after mixing, ethylene glycol, coalescing agent, thickener,
Mixing speed and mixing time are respectively 60 revs/min and 20 minutes.
In the present embodiment, 400-600 parts of nano composite powder is added in mixture A and is stirred and is made mixture B,
Mixing speed and mixing time are respectively 600 revs/min and 30 minutes.
In the present embodiment, by 4 parts of cellulose, 5 parts of dispersing agent, 1-2 parts of wetting agent, 1-2 parts of defoaming agent, 1-2 parts of fungicide,
1-3 parts of multifunctional assistant, 300-500 parts of water matched and mixed, then to the cellulose after mixing, dispersing agent, wetting
Agent, defoaming agent, fungicide, multifunctional assistant, water are stirred and are made mixture C, and mixing speed and mixing time are respectively
60 revs/min and 5 minutes.
A kind of coating is mainly used for painting or be coated on exterior walls of buildings, the raw material components including following parts by weight:
100-200 parts of lotion, 8-15 parts of ethylene glycol, 6-12 parts of coalescing agent, 3-7 parts of thickener, 250-450 parts of nano composite powder, silicon
50-100 parts of limestone flour, 30-60 parts of titanium dioxide, 2-5 parts of cellulose, 3-5 parts of dispersing agent, 1-3 parts of wetting agent, 1-3 parts of defoaming agent,
1-3 parts of fungicide, 1-3 parts of multifunctional assistant, 250-300 parts of water.Wherein, lotion uses acrylate copolymer, on the one hand, can
So that the compact in paint film that color inhibition coating is formed, can effectively improve the water resistance of paint film, prevent the solia particles such as dust with water
Divide contamination and the xanthochromia for penetrating into paint film and leading to surface of the paint film；On the other hand, acrylate copolymer often makes compared to existing coating
For being used to as the copolymer in cinnamic acrylic ester of binder, it is sensitive low that reaction is irradiated to ultraviolet light, it is not easy to
Decompose jaundice；Cellulose uses non-ionic water dissolvable cellulose ether, can be the hydroxyethyl cellulose of different molecular weight
Ether is primarily used to increase viscosity, improves storage stability and workability；The addition of nano composite powder is so that coating is final
Product has the characteristics that high compactness, while having the advantages that high temperature resistant, rub resistance, with high hardness；The effect of titanium dioxide is not only
It covers and decoration, prior effect is the physical and chemical performance for improving coating, enhance chemical stability, so that improve covering power, disappear
Color power, anticorrosive property, fast light, weatherability, and enhance the mechanical strength and adhesive force of paint film, prevent crackle, prevent ultraviolet light and
The transmission of moisture extends the paint film service life to postpone aging, and titanium dioxide has excellent pigment performance, and nontoxic, and people
More favor in the coating of the white and light color that are generated by titanium dioxide；The effect of wollastonite in powder is: it is good reinforcing, it both can be with
Improve the toughness and durability of coating, but coating surface can be kept smooth with and good glossiness, and improve anti-wash
Brush and resistance to weathering energy can also reduce the oil absorption of coating and ink and keep alkalinity, have resistance to corrosion, and available
The bright coating of high quality, and there is good equalization and anti-aging property, make the available better machinery of coating
Intensity increases durability, increases adherence and corrosion resistance, it may have good coverage rate, adhesive force；Coalescing agent uses
Alcohol ester 12 plays the Plastic Flow for promoting latex particle and elastic deformation, reduces the minimum film formation temperature of lotion, improves paint film
The effect of performance；Multifunctional assistant uses AMP-95 multifunctional assistant, and AMP-95 multifunctional assistant is current a small number of with low point
One of son amount and overbasic industrial amine, have the function of adjusting the pH stable of lotion adhesive, additionally have dispersion, increase
The excellent function such as thick, non-discolouring, and it is also equipped with antimicrobial (sterilization) characteristic, while also can be reduced VOC (volatile organic
Close object) total amount, help to promote environmental-protecting performance；Wetting agent can be used for improving the surface tension and permeability of coating, enable coating
It is enough preferably to soak ground, so that the adhesive force of coating is improved, especially to raising priming paint to the adhesive force of ground；Defoaming agent has
Extra foam is eliminated to effect, improves the quality of coating final products.
In the present embodiment, by 100-200 parts of lotion, 8-15 parts of ethylene glycol, 6-12 parts of coalescing agent, 3-7 parts of thickener into
Row matches and mixes, be then stirred to the lotion after mixing, ethylene glycol, coalescing agent, thickener and mixture is made
D, mixing speed and mixing time are respectively 60 revs/min and 20 minutes.
In the present embodiment, matched by 250-450 parts of nano composite powder, 50-100 parts of wollastonite in powder, 30-60 parts of titanium dioxide
Than then mixture E being stirred and being made to nano composite powder, wollastonite in powder, the titanium dioxide after mixing, by mixture E
It is added in mixture D and is stirred and is made mixture F, mixing speed and mixing time are respectively 600 revs/min and 30 points
Clock.
In the present embodiment, by 2-5 parts of cellulose, 3-5 parts of dispersing agent, 1-3 parts of wetting agent, 1-3 parts of defoaming agent, fungicide 1-
3 parts, 1-3 parts of multifunctional assistant, 250-300 parts of water matched and mixed, then to after mixing cellulose, dispersing agent,
Wetting agent, defoaming agent, fungicide, multifunctional assistant, water are stirred and are made mixture G, mixing speed and mixing time point
It Wei not be 60 revs/min and 5 minutes.
In the present embodiment, mixture F is added in mixture G and is stirred and mixture H, mixing speed and stirring is made
Time is respectively 60 revs/min and 5 minutes.
In short, the foregoing is merely presently preferred embodiments of the present invention, it is all according to equalization made by scope of the present invention patent
Variation and modification, shall all be covered by the patent of the invention.
Claims (9)
1. a kind of coating, it is characterised in that: the raw material components including following parts by weight: 50-100 parts of lotion, ethylene glycol 5-15
Part, 4-8 parts of coalescing agent, 2-4 parts of thickener, 400-600 parts of nano composite powder, 4 parts of cellulose, 5 parts of dispersing agent, wetting agent 1-
2 parts, 1-2 parts of defoaming agent, 1-2 parts of fungicide, 1-3 parts of multifunctional assistant, 300-500 parts of water.
2. a kind of coating according to claim 1, it is characterised in that: by lotion 50-100 parts, 5-15 parts of ethylene glycol, film forming
4-8 parts of auxiliary agent, 2-4 parts of thickener matched and mixed, then to the lotion after mixing, ethylene glycol, coalescing agent, thickening
Agent is stirred and is made mixture A, and mixing speed and mixing time are respectively 60 revs/min and 20 minutes.
3. a kind of coating according to claim 2, it is characterised in that: mixing is added in 400-600 parts of nano composite powder
Mixture B is stirred and is made in object A, and mixing speed and mixing time are respectively 600 revs/min and 30 minutes.
4. a kind of coating according to claim 3, it is characterised in that: press 4 parts of cellulose, 5 parts of dispersing agent, wetting agent 1-2
Part, 1-2 parts of defoaming agent, 1-2 parts of fungicide, 1-3 parts of multifunctional assistant, 300-500 parts of water matched and mixed, then to mixed
Cellulose, dispersing agent, wetting agent, defoaming agent, fungicide, multifunctional assistant, water after conjunction are stirred and mixture are made
C, mixing speed and mixing time are respectively 60 revs/min and 5 minutes.
5. a kind of coating, it is characterised in that: the raw material components including following parts by weight: 100-200 parts of lotion, ethylene glycol 8-15
Part, 6-12 parts of coalescing agent, 3-7 parts of thickener, 250-450 parts of nano composite powder, 50-100 parts of wollastonite in powder, titanium dioxide 30-
60 parts, 2-5 parts of cellulose, 3-5 parts of dispersing agent, 1-3 parts of wetting agent, 1-3 parts of defoaming agent, 1-3 parts of fungicide, multifunctional assistant 1-
3 parts, 250-300 parts of water.
6. a kind of coating according to claim 5, it is characterised in that: by lotion 100-200 parts, 8-15 parts of ethylene glycol, at
6-12 parts of film auxiliary agent, 3-7 parts of thickener matched and mixed, then to after mixing lotion, ethylene glycol, coalescing agent,
Thickener is stirred and is made mixture D, and mixing speed and mixing time are respectively 60 revs/min and 20 minutes.
7. a kind of coating according to claim 6, it is characterised in that: press nano composite powder 250-450 parts, wollastonite in powder
50-100 parts, 30-60 parts of titanium dioxide are matched, and are then carried out to nano composite powder, wollastonite in powder, the titanium dioxide after mixing
Mixture E is stirred and be made, mixture E is added in mixture D and is stirred and mixture F, mixing speed and stirring is made
Time is respectively 600 revs/min and 30 minutes.
8. a kind of coating according to claim 7, it is characterised in that: press cellulose 2-5 parts, 3-5 parts of dispersing agent, wetting agent
1-3 parts, 1-3 parts of defoaming agent, 1-3 parts of fungicide, 1-3 parts of multifunctional assistant, 250-300 parts of water matched and mixed, then
Cellulose, dispersing agent, wetting agent, defoaming agent, fungicide, multifunctional assistant, water after mixing is stirred and is made mixed
Object G is closed, mixing speed and mixing time are respectively 60 revs/min and 5 minutes.
9. a kind of coating according to claim 8, it is characterised in that: mixture F is added in mixture G and is stirred simultaneously
Mixture H is made, mixing speed and mixing time are respectively 60 revs/min and 5 minutes.