CN108117637A - 聚芳酯树脂和电子照相感光体 - Google Patents
聚芳酯树脂和电子照相感光体 Download PDFInfo
- Publication number
- CN108117637A CN108117637A CN201711221435.9A CN201711221435A CN108117637A CN 108117637 A CN108117637 A CN 108117637A CN 201711221435 A CN201711221435 A CN 201711221435A CN 108117637 A CN108117637 A CN 108117637A
- Authority
- CN
- China
- Prior art keywords
- resin
- chemical formula
- general formula
- alkyl
- phenyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种聚芳酯树脂和电子照相感光体。聚芳酯树脂由下述通式(1)表示。通式(1)中,R1和R2各自独立,表示氢原子或者甲基。r和s表示0以上49以下的整数。t和u表示1以上50以下的整数。r+s+t+u=100。r+t=s+u。X和Y各自独立,表示化学式(1‑1)、化学式(1‑2)、化学式(1‑3)或者化学式(1‑4)所示的二价基。X和Y彼此不同。【化1】【化2】
Description
技术领域
本发明涉及聚芳酯树脂和电子照相感光体。
背景技术
电子照相感光体作为像承载体用在电子照相方式的图像形成装置(例如,打印机或者多功能一体机)中。电子照相感光体具备感光层。电子照相感光体例如有单层型电子照相感光体和层叠型电子照相感光体。在单层型电子照相感光体中,感光层具有电荷产生功能和电荷传输功能。在层叠型电子照相感光体中,感光层具备电荷产生层和电荷输送层,电荷产生层具有电荷产生功能,电荷输送层具有电荷传输功能。
专利文献1中,记载了一种聚芳酯树脂,其具有化学式(Resin-7)表示的重复单元。还有,记载了含有上述聚芳酯树脂的电子照相感光体。
【化1】
〔专利文献〕
专利文献1:日本特开平08-110646号公报
发明内容
然而,关于专利文献1所述的聚芳酯树脂,聚芳酯树脂中的分子链彼此的缠结低,聚芳酯树脂的敛集性低,不能充分提高耐磨损性。
本发明是鉴于上述课题而作出的,其目的在于提供一种使电子照相感光体表现出优异耐磨损性的聚芳酯树脂。还有,另一目的在于提供一种感光层耐磨损性优异的电子照相感光体。
本发明的聚芳酯树脂由下述通式(1)表示。
【化2】
所述通式(1)中,R1和R2各自独立,表示氢原子或者甲基。r和s表示0以上49以下的整数。t和u表示1以上50以下的整数。r+s+t+u=100。r+t=s+u。X和Y各自独立,表示化学式(1-1)、化学式(1-2)、化学式(1-3)或者化学式(1-4)所示的二价基。X和Y彼此不同。
【化3】
本发明的电子照相感光体具备导电性基体和感光层。所述感光层含有电荷产生剂、空穴输送剂和粘结树脂。所述粘结树脂含有上述的聚芳酯树脂。
〔发明效果〕
本发明的聚芳酯树脂能够使电子照相感光体表现出优异的耐磨损性。还有,本发明的电子照相感光体的耐磨损性优异。
附图说明
图1(a)是表示本发明的第二实施方式所涉及的电子照相感光体的结构的一个例子的示意性剖面图。
图1(b)是表示本发明的第二实施方式所涉及的电子照相感光体的结构的一个例子的示意性剖面图。
图1(c)是表示本发明的第二实施方式所涉及的电子照相感光体的结构的一个例子的示意性剖面图。
图2(a)是表示本发明的第二实施方式所涉及的电子照相感光体的结构的另一个例子的示意性剖面图。
图2(b)是表示本发明的第二实施方式所涉及的电子照相感光体的结构的另一个例子的示意性剖面图。
图2(c)是表示本发明的第二实施方式所涉及的电子照相感光体的结构的另一个例子的示意性剖面图。
图3是化学式(Resin-1)所示的聚芳酯树脂的1H-NMR光谱。
具体实施方式
以下,对本发明的实施方式进行详细说明,但本发明不被以下的实施方式所限定,在本发明的目的范围内可以适当变更后再进行实施。另外,存在适当地省略了重复说明之处的情况,但并不因此限定发明的要旨。另外,本说明书中,有时在化合物名称之后加上“类”来统称该化合物及其衍生物。在化合物名称之后加上“类”来表示聚合物名称的情况下,表示聚合物的重复单元源自该化合物或者其衍生物。
以下,C1-C8烷基、C1-C6烷基、C1-C4烷基、C1-C8烷氧基、C1-C4烷氧基和C5-C7环烷烃的含义分别如下。
C1-C8烷基是直链状或者支链状的,且是无取代的。C1-C8烷基例如有:甲基、乙基、丙基、异丙基、正丁基、仲丁基、叔丁基、戊基、异戊基、新戊基、己基、庚基或者辛基。
C1-C6烷基是直链状或者支链状的,且是无取代的。C1-C6烷基例如有:甲基、乙基、丙基、异丙基、正丁基、仲丁基、叔丁基、戊基、异戊基、新戊基或者己基。
C1-C4烷基是直链状或者支链状的,且是无取代的。C1-C4烷基例如有:甲基、乙基、丙基、异丙基、正丁基、仲丁基或者叔丁基。
C1-C8烷氧基是直链状或者支链状的,且是无取代的。C1-C8烷氧基例如有:甲氧基、乙氧基、正丙氧基、异丙氧基、正丁氧基、仲丁氧基、叔丁氧基、戊氧基、异戊氧基、新戊氧基、己氧基、庚氧基或者辛氧基。
C1-C4烷氧基是直链状或者支链状的,且是无取代的。C1-C4烷氧基例如有:甲氧基、乙氧基、正丙氧基、异丙氧基、正丁氧基、仲丁氧基或者叔丁氧基。
C5-C7环烷烃是无取代的。C5-C7环烷烃例如有:环戊烷、环己烷或者环庚烷。
<第一实施方式:聚芳酯树脂>
聚芳酯树脂由下述通式(1)表示。以下,这样的聚芳酯树脂有时记载为聚芳酯树脂(1)。
【化4】
通式(1)中,R1和R2各自独立,表示氢原子或者甲基。r和s表示0以上49以下的整数。t和u表示1以上50以下的整数。r+s+t+u=100。r+t=s+u。X和Y各自独立,表示化学式(1-1)、化学式(1-2)、化学式(1-3)或者化学式(1-4)所示的二价基。X和Y彼此不同。
【化5】
从进一步提高感光体的耐磨损性的观点来看,聚芳酯树脂(1)优选为具有化学式(1-4)所示的二价基。具体来说,通式(1)中,在s表示0的情况下,优选为Y表示化学式(1-4)所示的二价基。还有,在s表示1以上整数的情况下,优选为X或者Y表示化学式(1-4)所示的二价基。
通式(1)中,在r表示1以上整数的情况下,也可以是R1和R2中的一个表示氢原子,R1和R2中另一个表示甲基。
聚芳酯树脂(1)具有:摩尔分数r/(r+t)的化学式(1-5)所示重复单元、摩尔分数s/(s+u)的化学式(1-6)所示重复单元、摩尔分数t/(r+t)的通式(1-7)所示重复单元和摩尔分数u/(s+u)的通式(1-8)所示重复单元。以下,这些重复单元有时分别记载为重复单元(1-5)、(1-6)、(1-7)和(1-8)。
【化6】
通式(1-5)、通式(1-6)、通式(1-7)和通式(1-8)中,R1和R2各自独立,表示氢原子或者甲基。X和Y各自独立,表示化学式(1-1)、化学式(1-2)、化学式(1-3)或者化学式(1-4)所示的二价基。X和Y彼此不同。
在r和s表示1以上整数的情况下,聚芳酯树脂(1)在上述4个重复单元以外,可以不含其它重复单元。还有,聚芳酯树脂(1)也可以含有重复单元(1-5)~(1-8)以外的重复单元。聚芳酯树脂(1)中,相对于重复单元的物质的量的总计,重复单元(1-5)~(1-8)的物质的量的合计的比率(摩尔分数)优选为0.80以上,更优选为0.90以上,进一步优选为1.00。
聚芳酯树脂(1)中的重复单元(1-5)~(1-8)的排列只要是来自芳香族二醇的重复单元与来自芳香族二羧酸的重复单元彼此相邻即可,不做特别的限定。例如,重复单元(1-5)与重复单元(1-6)或者重复单元(1-8)相邻而相互键合。同样地,重复单元(1-7)与重复单元(1-6)或者重复单元(1-8)相邻而相互键合。聚芳酯树脂(1)也可以含有重复单元(1-5)~(1-8)以外的重复单元。
通式(1)中的r和t表示0以上49以下的整数。s和u表示1以上50以下的整数。r+s+t+u=100。r+t=s+u。s/(s+u)优选为0.30以上0.70以下。s/(s+u)表示:聚芳酯树脂(1)中,重复单元(1-6)的物质的量相对于重复单元(1-6)的物质的量和重复单元(1-8)的物质的量的合计的比率(摩尔分数)。
聚芳酯树脂(1)例如有:化学式(Resin-1)~(Resin-10)所示的聚芳酯树脂(以下,有时分别记载为聚芳酯树脂(Resin-1)~(Resin-10))。
【化7】
【化8】
从耐磨损性的观点来看,聚芳酯树脂(1)的粘均分子量优选为10,000以上,更优选为大于20,000,进一步优选为大于30,000,特别优选为大于45,000。在聚芳酯树脂(1)的粘均分子量是10,000以上的情况下,粘结树脂的耐磨损性高,电荷输送层不易磨损。另一方面,聚芳酯树脂(1)的粘均分子量优选为80,000以下,更优选为54,000以下。在聚芳酯树脂(1)的粘均分子量是80,000以下的情况下,在形成电荷输送层时,往往聚芳酯树脂(1)容易溶解到溶剂中,从而容易形成电荷输送层。
(聚芳酯树脂(1)的制造方法)
聚芳酯树脂(1)的制造方法只要能够制造聚芳酯树脂(1)即可,不做特别的限定。这样的制造方法例如有:用于构成聚芳酯树脂(1)的重复单元的芳香族二醇和芳香族二羧酸进行缩聚的方法。聚芳酯树脂(1)的合成方法没有特别限定,能够采用众所周知的合成方法(更具体地来说,溶液聚合、熔融聚合或者界面聚合等)。以下,对聚芳酯树脂(1)的制造方法的一个例子进行说明。
例如,按照反应方程式(R-1)所示的反应(以下,有时记载为反应(R-1))或者类似方法,制造聚芳酯树脂(1)。聚芳酯树脂的制造方法例如含有反应(R-1)。
【化9】
反应(R-1)中,通式(1-11)中的R1、通式(1-12)中的R2、通式(1-9)中的X和通式(1-10)中的Y分别与通式(1)中的R1、R2、X和Y含义相同。
反应(R-1)中,通式(1-9)所示的芳香族二羧酸和通式(1-10)所示的芳香族二羧酸(以下,有时分别记载为芳香族二羧酸(1-9)和(1-10))与通式(1-11)所示的芳香族二醇和通式(1-12)所示的芳香族二醇(以下,有时分别记载为芳香族二醇(1-11)和(1-12))进行反应,得到聚芳酯树脂(1)。
芳香族二羧酸(1-9)和(1-10)例如有:4,4′-二苯醚二甲酸、4,4′-联苯二甲酸或者2,6-萘二羧酸。反应(R-1)中,在芳香族二羧酸(1-9)和(1-10)的基础上,还可以使用其它芳香族二羧酸。另外,反应(R-1)中,可以使用芳香族二羧酸衍生物来代替芳香族二羧酸。芳香族二羧酸衍生物例如有:芳香族二羧酸(1-9)和(1-10)的卤代烷酰或者酸酐。
芳香族二醇(1-11)和(1-12)例如有:1,1-双(4-羟基苯基)-3,3-二甲基-5-甲基环己烷或者1,1-双(4-羟基-3-甲基苯基)-3,3-二甲基-5-甲基环己烷。反应(R-1)中,在芳香族二醇(1-11)和(1-12)的基础上,还可以使用其它芳香族二醇。其它芳香族二醇例如有:双酚A、双酚S、双酚E或者双酚F。另外,反应(R-1)中,可以使用芳香族二醇衍生物来代替芳香族二醇。芳香族二醇衍生物例如有:二乙酸盐。
相对于芳香族二羧酸(1-9)和(1-10)的合计物质的量1摩尔,芳香族二醇(1-11)和(1-12)的合计物质的量优选为0.9摩尔以上1.1摩尔以下。理由是:当在上述范围内时,容易提纯聚芳酯树脂(1),聚芳酯树脂(1)的收率得到提高。
反应(R-1)也可以在碱和催化剂的存在下进行。催化剂例如有:叔铵(更具体地来说,三烷基胺等)或者季铵盐(更具体地来说,苄基三甲基氯化铵等)。碱例如有:碱金属的氢氧化物(更具体地来说,氢氧化钠或者氢氧化钾等)、碱土金属的氢氧化物(更具体地来说,氢氧化钙等)。反应(R-1)也可以在溶剂中和惰性气体气氛下进行。溶剂例如有:水或者三氯甲烷。惰性气体例如有:氩气。反应(R-1)的反应时间优选为2小时以上5小时以下。反应温度优选为5℃以上25℃以下。
聚芳酯树脂(1)的制造中,根据需要也可以包含其它工序。其它工序例如有提纯工序。提纯方法例如有众所周知的方法(更具体地来说,过滤、层析或者析晶等)。
<第二实施方式:电子照相感光体>
本发明的电子照相感光体(以下,有时记载为感光体)具备导电性基体和感光层。感光体例如有:层叠型电子照相感光体(以下,有时记载为层叠型感光体)或者单层型电子照相感光体(以下,有时记载为单层型感光体)。
层叠型感光体具备电荷产生层和电荷输送层,电荷产生层和电荷输送层作为感光层。以下,参照图1(a)~图1(c),对第二实施方式所涉及的层叠型感光体1的结构进行说明。图1(a)~图1(c)是表示层叠型感光体1的结构的示意性剖面图。如图1(a)所示,层叠型感光体1具备导电性基体2和感光层3。感光层3具备电荷产生层3a和电荷输送层3b。如图1(a)所示,层叠型感光体1中,可以在导电性基体2上具备电荷产生层3a,并在电荷产生层3a之上再具备电荷输送层3b。还有,如图1(b)所示,层叠型感光体1中,也可以在导电性基体2上具备电荷输送层3b,并在电荷输送层3b之上再具备电荷产生层3a。如图1(a)所示,电荷输送层3b可以配置为层叠型感光体1的最外表面层。电荷输送层3b可以是一层(单层)的。
如图1(a)所示,感光层3可以直接配置在导电性基体2上。还有,如图1(c)所示,层叠型感光体1例如具备:导电性基体2、中间层4(底涂层)和感光层3。如图1(c)所示,感光层3也可以间接配置在导电性基体2上。如图1(c)所示,中间层4可以设置在导电性基体2与电荷产生层3a之间。中间层4例如也可以设置在电荷产生层3a与电荷输送层3b之间。电荷产生层3a可以是单层的,也可以是若干层的。
参照图2(a)~图2(c),对第二实施方式所涉及的单层型感光体1的结构进行说明。图2(a)~图2(c)是表示单层型感光体1的结构的示意性剖面图。如图2(a)所示,单层型感光体1具备导电性基体2和感光层3。感光层3是单层的感光层(单层型感光层)。如图2(a)所示,感光层3可以直接配置在导电性基体2上。还有,如图2(b)所示,单层型感光体1例如具备:导电性基体2、中间层4(底涂层)和感光层3。如图2(b)所示,感光层3也可以间接配置在导电性基体2上。如图2(b)所示,中间层4可以设置在导电性基体2与单层型感光层之间。图2(c)如所示,单层型感光体1也可以具备作为最外表面层的保护层5。
第二实施方式所涉及的感光体1的耐磨损性优异。其理由推测如下。第二实施方式所涉及的感光体1含有作为粘结树脂的聚芳酯树脂(1)。聚芳酯树脂(1)中,具有来自芳香族二醇的重复单元和来自芳香族二羧酸的重复单元,该芳香族二醇具有3,3-二甲基-5-甲基亚环己基,该芳香族二羧酸具有通式(1-1)~(1-4)所示的二价基。具有这种结构的聚芳酯树脂(1)中,分子链彼此的缠结不易降低,分子的敛集性不易降低。还有,具有这种结构的聚芳酯树脂(1)相对于溶剂的溶解性高,因此容易制备出用于形成感光层3的涂布液。其结果,容易得到层密度高的感光层3。因此,第二实施方式所涉及的感光体1的耐磨损性优异。
以下,对第二实施方式所涉及的感光体1的要素(导电性基体2、感光层3和中间层4)进行说明。另外,也对感光体1的制造方法进行说明。
[1.导电性基体]
导电性基体2只要是能够用作感光体1的导电性基体即可,不做特别的限定。导电性基体2中,至少表面部由导电性材料构成就可以。导电性基体的例子有:由导电性材料构成的导电性基体。导电性基体的例子还有:由导电性材料包覆的导电性基体。导电性材料例如有:铝、铁、铜、锡、铂、银、钒、钼、铬、镉、钛、镍、钯或者铟。这些导电性材料中,可以单独使用一种,也可以组合两种以上来使用。两种以上的组合例如有合金(更具体地来说,铝合金、不锈钢或者黄铜)。这些导电性材料中,由电荷从感光层3到导电性基体2的移动良好的方面来看,优选为铝或者铝合金。
导电性基体2的形状可以按照所使用的图像形成装置的结构适当选择。导电性基体2的形状例如有:片状或者鼓状。还有,导电性基体2的厚度可以根据导电性基体2的形状适当选择。
[2.感光层]
感光层3含有电荷产生剂、空穴输送剂和粘结树脂。粘结树脂含有聚芳酯树脂(1)。感光层3也可以含有添加剂。层叠型感光体1的感光层3具备电荷产生层3a和电荷输送层3b。电荷产生层3a含有电荷产生剂。电荷输送层3b含有空穴输送剂和粘结树脂。电荷产生层3a的厚度只要能够使电荷产生层3a充分发挥作用即可,不做特别的限定。具体来说,电荷产生层3a的厚度优选为0.01μm以上5μm以下,更优选为0.1μm以上3μm以下。电荷输送层3b的厚度只要能够使电荷输送层3b充分发挥作用即可,不做特别的限定。具体来说,电荷输送层3b的厚度优选为2μm以上100μm以下,更优选为5μm以上50μm以下。
单层型感光体1的感光层3含有电荷产生剂、空穴输送剂和粘结树脂。单层型感光层的厚度只要能够使单层型感光层充分发挥作用即可,不做特别的限定。具体来说,单层型感光层的厚度可以是5μm以上100μm以下,优选为10μm以上50μm以下。
[2-1.共通的结构要素]
以下,对电荷产生剂、空穴输送剂、粘结树脂和添加剂进行说明。再对感光体1的制造方法进行说明。
[2-1-1.电荷产生剂]
电荷产生剂只要是感光体1用的电荷产生剂即可,不做特别的限定。电荷产生剂例如有:酞菁类颜料、苝颜料、双偶氮颜料、二硫酮吡咯并吡咯(dithioketo-pyrrolopyrrole)颜料、无金属萘酞菁颜料、金属萘酞菁颜料、方酸颜料、三偶氮颜料、靛蓝颜料、甘菊蓝颜料、菁颜料;硒、硒-碲、硒-砷、硫化镉、非晶硅之类的无机光导材料的粉末;吡喃盐、蒽嵌蒽醌颜料、三苯甲烷颜料、士林颜料、甲苯胺颜料、吡唑啉颜料或者喹吖啶酮颜料。酞菁颜料例如有:酞菁颜料或者酞菁衍生物的颜料。酞菁颜料例如有:无金属酞菁颜料(更具体地来说,X型无金属酞菁颜料(x-H2Pc)等)。酞菁衍生物的颜料例如有:金属酞菁颜料(更具体地来说,氧钛酞菁颜料或者V型羟基镓酞菁颜料等)。对酞菁类颜料的晶体形状不作特别限定,可以使用各种晶体形状的酞菁类颜料。酞菁类颜料的晶体形状例如有:α型、β型或者Y型。电荷产生剂可以单独使用一种,也可以组合两种以上来使用。这些电荷产生剂中,优选为Y型氧钛酞菁颜料。
Y型氧钛酞菁颜料在Cu-Kα特征X射线衍射光谱中,在布拉格角2θ±0.2°=27.2°具有主峰。CuKα特征X射线衍射光谱中的主峰是指在布拉格角(2θ±0.2°)为3°以上40°以下的范围中具有第一大或者第二大强度的峰。
(CuKα特征X射线衍射光谱的测量方法)
对CuKα特征X射线衍射光谱的测量方法进行说明。将样品(氧钛酞菁颜料)填充到X射线衍射装置(Rigaku Corporation制造“RINT(日本注册商标)1100”)的样品支架中,在X射线管Cu、管电压40kV、管电流30mA及CuKα特征X射线波长的条件下,对X射线衍射光谱进行测量。测量范围(2θ)是3°以上40°以下(起始角3°、停止角40°),扫描速度例如是10°/分。从所得X射线衍射光谱中确定主峰,读取主峰的布拉格角。
可以单独使用在所需区域具有吸收波长的电荷产生剂,也可以组合两种以上的电荷产生剂来使用。还有,例如,在数字光学式图像形成装置中,优选为使用在700nm以上波长区域具有感光度的感光体。另外,数字光学式图像形成装置例如有:使用半导体激光器之类光源的激光打印机或者传真机。因此,例如优选为酞菁类颜料,更优选为Y型氧钛酞菁颜料(Y-TiOPc)。
使用短波长激光源的图像形成装置中所使用的感光体中,优选使用蒽嵌蒽醌类颜料或者苝类颜料来作为电荷产生剂。另外,短波长激光光源例如具有350nm以上550nm以下范围的波长。
电荷产生剂例如是化学式(CGM-1)~(CGM-4)表示的酞菁颜料(以下,有时记载为电荷产生剂(CGM-1)~(CGM-4))。
【化10】
【化11】
【化12】
【化13】
相对于电荷产生层用粘结树脂(以下,有时记载为基体树脂)100质量份,电荷产生剂的含量优选为5质量份以上1000质量份以下,更优选为30质量份以上500质量份以下。
[2-1-2.空穴输送剂]
空穴输送剂例如有:三苯胺衍生物、二胺衍生物(更具体地来说,N,N,N′,N′-四苯基苯二胺衍生物、N,N,N′,N′-四苯基萘二胺衍生物或者N,N,N′,N′-四苯基亚菲基二胺(N,N,N′,N′-tetraphenyl phenanthrylene diamine)衍生物等);恶二唑类化合物(更具体地来说,2,5-二(4-甲基氨基苯基)-1,3,4-恶二唑等);苯乙烯类化合物(更具体地来说,9-(4-二乙氨基苯乙烯基)蒽等);咔唑类化合物(更具体地来说,聚乙烯基咔唑等);有机聚硅烷化合物;吡唑啉类化合物(更具体地来说,1-苯基-3-(对二甲基氨基苯基)吡唑啉等);腙类化合物;吲哚类化合物;恶唑类化合物;异恶唑类化合物;噻唑类化合物;噻二唑类化合物;咪唑类化合物;吡唑类化合物;三唑类化合物。
从提高感光体1的耐磨损性的观点来看,这些空穴输送剂中,优选为通式(2)、通式(3)或者通式(4)所示的化合物(以下,有时分别记载为空穴输送剂(2)、(3)和(4))。为了在提高感光体1的耐磨损性之外还提高感光体1的感光度特性,空穴输送剂更优选为含有通式(2)或者通式(3)表示的化合物。空穴输送剂进一步优选为含有通式(3)所示的化合物。
【化14】
通式(2)中,Q1表示氢原子、C1-C8烷基、C1-C8烷氧基或者苯基。苯基中,也可以由C1一C8烷基取代基进行了取代。Q2各自独立,表示C1-C8烷基、C1-C8烷氧基或者苯基。Q3、Q4、Q5、Q6和Q7各自独立,表示氢原子、C1-C8烷基、C1-C8烷氧基或者苯基。Q3、Q4、Q5、Q6和Q7中相邻的两个可以相互键合形成环。a表示0以上5以下的整数。在a表示2以上5以下整数的情况下,结合在同一个苯基上的若干个Q2彼此可以相同或不同。
【化15】
通式(3)中,Q8、Q10、Q11、Q12、Q13和Q14各自独立,表示氢原子、C1-C8烷基、C1-C8烷氧基或者苯基。Q9和Q15各自独立,表示C1-C8烷基、C1-C8烷氧基或者苯基。b表示0以上5以下的整数。在b表示2以上5以下整数的情况下,结合在同一个苯基上的若干个Q9彼此可以相同或不同。c表示0以上4以下的整数。在c表示2以上4以下整数的情况下,结合在同一个亚苯基上的若干个Q15彼此可以相同或不同。k表示0或者1。
【化16】
通式(4)中,Ra、Rb和Rc各自独立,表示C1-C8烷基、苯基或者C1-C8烷氧基。q表示0以上4以下的整数。在q表示2以上4以下整数的情况下,结合在同一个亚苯基上的若干个Rc彼此可以相同或不同。m和n各自独立,表示0以上5以下的整数。在m表示2以上5以下整数的情况下,结合在同一个苯基上的若干个Rb彼此可以相同或不同。在n表示2以上5以下整数的情况下,结合在同一个苯基上的若干个Ra彼此可以相同或不同。
通式(2)中,Q1表示的苯基优选为由C1-C8烷基取代基进行取代了的苯基,更优选为由甲基取代基进行取代了的苯基,进一步优选为对甲基苯基。
通式(2)中,Q2表示的C1-C8烷基优选为C1-C6烷基,更优选为C1-C4烷基,进一步优选为甲基。a优选为表示0或者1。
通式(2)中,Q3~Q7表示的C1-C8烷基优选为C1-C4烷基,更优选为正丁基。通式(2)中,Q3~Q7表示的C1-C8烷氧基优选为C1-C4烷氧基,更优选为甲氧基或者乙氧基。通式(2)中,Q3~Q7各自独立,优选为表示氢原子、C1-C8烷基或者C1-C8烷氧基,更优选为表示氢原子、C1-C4烷基或者C1-C4烷氧基。
通式(2)中,也可以是Q3~Q7中相邻的两个相互键合形成环(更具体地来说,苯环或者C5-C7环烷烃)。例如,也可以是Q3~Q7中相邻的Q6和Q7相互键合形成苯环或者C5-C7环烷烃。在Q3~Q7中相邻的两个相互键合形成苯环的情况下,该苯环与Q3~Q7所结合的苯基进行缩合而形成双环稠环基(萘基)。在Q3~Q7中相邻的两个相互键合形成C5-C7环烷烃的情况下,该C5-C7环烷烃与Q3~Q7所结合的苯基进行缩合而形成双环稠环基。这样的情况下,C5-C7环烷烃与苯基的缩合部位可以含有双键。优选为Q3~Q7中相邻的两个相互键合形成C5-C7环烷烃,更优选为形成环己烷。
通式(2)中,优选为:Q1表示氢原子或者由C1-C8烷基取代基进行了取代的苯基,Q2表示C1-C8烷基,Q3~Q7各自独立地表示氢原子、C1-C8烷基或者C1-C8烷氧基,a表示0或者1。优选为Q3~Q7中相邻的两个相互键合形成环。
通式(3)中,Q8和Q10~Q14表示的C1-C8烷基优选为C1-C4烷基,更优选为甲基或者乙基。通式(3)中,优选为:Q8和Q10~Q14各自独立地表示氢原子、C1-C4烷基或者苯基,b和c表示0。
通式(4)中,优选为Ra和Rb所表示的C1-C8烷基表示甲基、乙基或者正辛基。通式(4)中,优选为:Ra和Rb表示C1-C8烷基,m和n各自独立地表示0或者1,q表示0。
空穴输送剂(2)例如有:化学式(HTM-1)~(HTM-4)所示的空穴输送剂(以下,有时分别记载为空穴输送剂(HTM-1)~(HTM-4))。空穴输送剂(3)例如有:化学式(HTM-5)~(HTM-7)所示的空穴输送剂(以下,有时分别记载为空穴输送剂(HTM-5)~(HTM-7))。空穴输送剂(4)例如有:化学式(HTM-8)~(HTM-10)所示的空穴输送剂(以下,有时分别记载为空穴输送剂(HTM-8)~(HTM-10))。
【化17】
【化18】
【化19】
层叠型感光体中,相对于粘结树脂100质量份,空穴输送剂的含量优选为10质量份以上200质量份以下,更优选为20质量份以上100质量份以下。
[2-1-3.粘结树脂]
粘结树脂用在层叠型感光体的电荷输送层中或者单层型感光体的感光层中。粘结树脂含有聚芳酯树脂(1)。
关于粘结树脂,可以单独使用聚芳酯树脂(1),也可以在无损本发明效果的范围内包含聚芳酯树脂(1)以外的其它树脂。其它树脂例如有:热塑性树脂、热固性树脂或者光固化树脂。热塑性树脂例如有:聚芳酯树脂(1)以外的聚芳酯树脂、聚碳酸酯树脂、苯乙烯类树脂、苯乙烯-丁二烯共聚物、苯乙烯-丙烯腈共聚物、苯乙烯-顺丁烯二酸共聚物、苯乙烯-丙烯酸共聚物、丙烯酸共聚物、聚乙烯树脂、乙烯-醋酸乙烯酯共聚物、氯化聚乙烯树脂、聚氯乙烯树脂、聚丙烯树脂、离聚物、氯乙烯-醋酸乙烯酯共聚物、聚酯树脂、醇酸树脂、聚酰胺树脂、聚氨酯树脂、聚砜树脂、邻苯二甲酸二烯丙酯树脂、酮树脂、聚乙烯醇缩丁醛树脂、聚醚树脂或者聚酯树脂。热固性树脂例如有:硅酮树脂、环氧树脂、酚醛树脂、脲醛树脂、三聚氰胺树脂或者其它交联性热固性树脂。光固化树脂例如有:环氧-丙烯酸类树脂或者聚氨酯-丙烯酸类共聚物。这些树脂中,可以单独使用,也可以并用两种以上。相对于粘结树脂100质量份,聚芳酯树脂(1)的含量优选为80质量份以上,更优选为90质量份以上,进一步优选为100质量份。
第二实施方式中,相对于电荷输送层所含的全部结构要素(例如,空穴输送剂或者粘结树脂)的总质量,粘结树脂的含量比率优选为40质量%以上,更优选为80质量%以上。
[2-1-4.添加剂]
在不对电子照相特性带来不良影响的范围内,电荷产生层3a、电荷输送层3b、单层型感光层和中间层4中的至少一个也可以含有各种添加剂。添加剂例如有:劣化抑制剂(更具体地来说,抗氧化剂、自由基捕获剂、猝灭剂或者紫外线吸收剂等)、软化剂、表面改性剂、增量剂、增稠剂、分散稳定剂、蜡、电子受体化合物、供体、表面活性剂或者流平剂。
抗氧化剂例如有:受阻酚化合物、受阻胺化合物、硫醚化合物或者亚磷酸酯化合物。这些抗氧化剂中,优选为受阻酚化合物和受阻胺化合物。
相对于粘结树脂100质量份,电荷输送层3b中的抗氧化剂添加量优选为0.1质量份以上10质量份以下。抗氧化剂添加量在这样的范围内时,容易抑制感光体被氧化而造成的电气特性下降。
电子受体化合物例如有联苯醌衍生物,优选为3,3′,5,5′-四叔丁基-4,4′-联苯醌。
[2-2.非共通结构要素]
层叠型感光体1中,电荷产生层3a可以含有电荷产生层用粘结树脂(以下,有时记载为基体树脂)。基体树脂只要能够用在感光体1中即可,没有特别的限定。基体树脂例如有:热塑性树脂、热固性树脂或者光固化树脂。热塑性树脂例如有:苯乙烯类树脂、苯乙烯-丁二烯共聚物、苯乙烯-丙烯腈共聚物、苯乙烯-顺丁烯二酸共聚物、苯乙烯-丙烯酸类共聚物、丙烯酸共聚物、聚乙烯树脂、乙烯-醋酸乙烯酯共聚物、氯化聚乙烯树脂、聚氯乙烯树脂、聚丙烯树脂、离聚物、氯乙烯-醋酸乙烯酯共聚物、醇酸树脂、聚酰胺树脂、聚氨基甲酸酯树脂、聚碳酸酯树脂、聚芳酯树脂、聚砜树脂、邻苯二甲酸二烯丙酯树脂、酮树脂、聚乙烯醇缩丁醛树脂、聚醚树脂或者聚酯树脂。热固性树脂例如有:硅酮树脂、环氧树脂、酚醛树脂、脲醛树脂、三聚氰胺树脂或者其它交联性热固性树脂。光固化树脂例如有:环氧丙烯酸类树脂或者聚氨酯-丙烯酸类树脂。这些树脂中,可以单独使用一种,也可以组合两种以上来使用。
对于基体树脂,虽然也例示了与上述粘结树脂相同的树脂,不过,在同一个层叠型感光体1中一般选择与粘结树脂不同的树脂。理由如下。在制造层叠型感光体1时,通常按顺序形成电荷产生层3a、电荷输送层3b,因此在电荷产生层3a上涂布电荷输送层用涂布液。在形成电荷输送层3b时,要求电荷产生层3a不溶解于电荷输送层用涂布液的溶剂中。于是,在同一个层叠型感光体1中,基体树脂通常选择与粘结树脂不同的树脂。
[3.中间层]
第二实施方式所涉及的感光体1也可以具有中间层4(例如,底涂层)。中间层4例如含有无机颗粒和树脂(中间层用树脂)。中间层4存在时,能够维持可抑制漏电发生这种程度的绝缘状态,同时使曝光感光体1时产生的电流流动顺利,能够抑制电阻的增加。
无机颗粒例如有:金属(更具体地来说,铝、铁或者铜等)的颗粒、金属氧化物(更具体地来说,二氧化钛、氧化铝、氧化锆、氧化锡或者氧化锌等)的颗粒或者非金属氧化物(更具体地来说,二氧化硅等)的颗粒。这些无机颗粒中,可以单独使用一种,也可以两种以上并用。还有,也可以对无机颗粒进行表面处理。
中间层用树脂只要能够用作形成中间层4的树脂即可,没有特别的限定。
[4.感光体1的制造方法]
对感光体1的制造方法进行说明。感光体1的制造方法例如具有感光层形成工序。
[4-1.层叠型感光体的制造方法]
层叠型感光体1的制造方法中,感光层形成工序具有电荷产生层形成工序和电荷输送层形成工序。电荷产生层形成工序中,首先制备用于形成电荷产生层3a的涂布液(以下,有时记载为电荷产生层用涂布液)。将电荷产生层用涂布液涂布在导电性基体2上,形成涂布膜。然后,通过适当的方法使涂布膜干燥,去除涂布膜所含的溶剂的至少一部分,从而形成电荷产生层3a。电荷产生层用涂布液例如含有电荷产生剂、基体树脂和溶剂。通过使电荷产生剂和基体树脂溶解或者分散在溶剂中,来制备这样的电荷产生层用涂布液。电荷产生层用涂布液中,也可以根据需要加入添加剂。
电荷输送层形成工序中,首先制备用于形成电荷输送层3b的涂布液(以下,有时记载为电荷输送层用涂布液)。将电荷输送层用涂布液涂布在电荷产生层3a上,形成涂布膜。然后,通过用适当的方法使涂布膜干燥,去除涂布膜所含的溶剂的至少一部分,从而形成电荷输送层3b。电荷输送层用涂布液含有空穴输送剂、作为粘结树脂的聚芳酯树脂(1)以及溶剂。可以通过使空穴输送剂和聚芳酯树脂(1)溶解或者分散在溶剂中,来制备电荷输送层用涂布液。电荷输送层用涂布液中,根据需要也可以加入添加剂。
[4-2.单层型感光体的制造方法]
关于单层型感光体1的制造方法,在感光层形成工序中,制备用于形成感光层3的涂布液(以下,有时记载为感光层用涂布液)。将感光层用涂布液涂布在导电性基体2上,形成涂布膜。然后,通过用适当的方法使涂布膜干燥,去除涂布膜所含的溶剂的至少一部分,从而形成感光层3。感光层用涂布液例如含有电荷产生剂、空穴输送剂、作为粘结树脂的聚芳酯树脂(1)以及溶剂。通过使电荷产生剂、空穴输送剂和聚芳酯树脂(1)溶解或者分散在溶剂中,来制备这样的感光层用涂布液。感光层用涂布液中,根据需要也可以加入添加剂。
以下,对感光层形成工序进行详细的说明。关于电荷产生层用涂布液、电荷输送层用涂布液和感光层用涂布液(以下,有时将这3种涂布液都记载为涂布液)中所含有的溶剂,只要能够使涂布液所含的各成分溶解或者分散、并且通过之后的干燥处理容易除去涂布膜中的溶剂即可,不做特别的限定。溶剂例如有:醇(更具体地来说,甲醇、乙醇、异丙醇或者丁醇等)、脂肪烃(更具体地来说,正己烷、辛烷或者环己烷等)、芳香族烃(更具体地来说,苯、甲苯或者二甲苯等)、卤化烃(更具体地来说,二氯甲烷、二氯乙烷、四氯化碳或者氯苯等)、醚(更具体地来说,二甲醚、二乙醚、四氢呋喃、乙二醇二甲醚或者二甘醇二甲醚等)、酮(更具体地来说,丙酮、甲基乙基酮或者环己酮等)、酯(更具体地来说,乙酸乙酯或者乙酸甲酯等)、二甲基甲醛、二甲基甲酰胺或者二甲基亚砜。这些溶剂可以单独使用,也可以组合两种以上来使用。这些溶剂中,优选为使用非卤代溶剂。2种以上的组合例如有:混合溶剂(更具体地来说,甲醇、丁醇和甲苯的混合溶剂;丙二醇单甲醚和四氢呋喃的混合溶剂;或者四氢呋喃和甲苯的混合溶剂等)。
而且,电荷输送层用涂布液中含有的溶剂优选为不同于电荷产生层用涂布液中含有的溶剂。其理由是:在制造层叠型感光体1时,通常按顺序形成电荷产生层3a、电荷输送层3b,因此在电荷产生层3a上涂布电荷输送层用涂布液,于是,在形成电荷输送层时,要求电荷产生层3a不溶解于电荷输送层用涂布液的溶剂中。
通过将各成分进行混合并分散到溶剂中,来制备涂布液。对于混合或者分散的操作,例如可以使用:珠磨机、辊磨机、球磨机、磨碎机、油漆振荡器或者超声波分散器。
为了提高各成分的分散性或者所形成的各层的表面平整度,例如,涂布液中也可以含有表面活性剂或者流平剂。
使用涂布液进行涂布的方法只要是能够均匀涂布上涂布液的方法即可,不做特别的限定。涂布方法例如有:浸涂法、喷涂法、旋涂法或者棒涂法。
去除涂布液所含的至少一部分溶剂的方法只要是能够使涂布液中的溶剂蒸发的方法即可,不做特别的限定。去除方法例如有:加热、减压或者加热与减压的并用。更具体地来说,可以举出使用高温干燥机或者减压干燥机进行热处理(热风干燥)的方法。热处理条件例如是40℃以上150℃以下的温度以及3分钟以上120分钟以下的时间。
另外,感光体1的制造方法中,根据需要也可以进一步具有形成中间层4的工序。形成中间层4的工序中,可以适当地选择众所周知的方法。
【实施例】
以下,使用实施例对本发明进行更具体的说明。另外,本发明不以任何方式限定于实施例的范围。
<聚芳酯树脂的制造>
[聚芳酯树脂(Resin-1)的制造]
使用三口烧瓶作为反应容器。该反应容器是具备温度计、三通阀和200mL滴液漏斗的容量1L的三口烧瓶。在反应容器中,放入1,1-双(4-羟基苯基)-3,3,5-三甲基环己烷25.63g(82.86毫摩尔)、叔丁基苯酚0.124g(0.826毫摩尔)、氢氧化钠7.84g(196毫摩尔)以及苄基三丁基氯化铵0.240g(0.768毫摩尔)。然后,对反应容器内进行氩气置换。然后,再将水600mL放入反应容器中。使反应容器的内部温度保持在20℃,对反应容器内的内含物进行1小时的搅拌。然后,将反应容器的内部温度冷却到10℃。其结果,得到碱性水溶液。
另一方面,使2,6-萘二甲酰氯(2,6-Naphthalene dicarboxylic aciddichloride)9.84g(38.9毫摩尔)、4,4′-氧二苯甲酰氯(4,4′-oxybisbenzoic aciddichloride)11.47g(38.9毫摩尔)溶解到三氯甲烷300g中。其结果,得到三氯甲烷溶液。
然后,使上述碱性溶液的温度达到10℃。用时110分钟,通过滴液漏斗将上述三氯甲烷溶液缓慢滴加到碱性水溶液中,开始聚合反应。将反应容器内的内部温度调节到13±3℃,对反应容器的内含物进行3小时的搅拌,进行聚合反应。
然后,使用倾析器去除反应容器的内含物中的上层(水层),得到有机层。然后,在容量2L的三口烧瓶中放入离子交换水500mL之后,放入所得有机层。再放入三氯甲烷300g和乙酸6mL。将三口烧瓶的内含物在室温(25℃)下搅拌30分。然后,使用倾析器去除三口烧瓶的内含物中的上层(水层),得到有机层。使用水500mL,用分液漏斗对所得有机层进行8次清洗。其结果,得到水洗后的有机层。
接下来,对水洗后的有机层进行过滤,得到滤液。在容量3L的三角烧瓶中,放入甲醇1.5L。将所得滤液缓慢滴加到三角烧瓶中,得到沉淀物。通过过滤来滤出沉淀物。将所得沉淀物在温度70℃下真空干燥12小时。其结果,得到聚芳酯树脂(Resin-1)。聚芳酯树脂(Resin-1)的产量是35.3g,收率是88.7mol%。
[聚芳酯树脂(Resin-2)~(Resin-10)的制造]
将1,1-双(4-羟基苯基)-3,3′-二甲基-5-甲基环己烷变更为聚芳酯树脂((Resin-2)~(Resin-6))的起始材料,即芳香族二醇,将2,6-萘二甲酰氯(2,6-Naphthalenedicarboxylic acid dichloride)和4,4′-氧二苯甲酰氯(4,4′-oxybisbenzoic aciddichloride)变更为聚芳酯树脂((Resin-2)~(Resin-6))的起始材料,即卤代烷酰,在使用2种不同的芳香族二醇作为起始材料的情况下,将2种芳香族二醇的含量比变更为与摩尔分数相当的含量比,除了上述这些以外,与聚芳酯树脂(Resin-1)一样地分别制造聚芳酯树脂(Resin-2)~(Resin-6)。还有,除了将2种不同的芳香族二羧酸的卤代烷酰的含量比变更为与摩尔分数相当的含量比以外,与聚芳酯树脂(Resin-5)一样地分别制造聚芳酯树脂(Resin-7)~(Resin-10)。
接下来,使用质子核磁共振光谱仪(日本分光株式会社制造、300MHz),测量所制造的聚芳酯树脂(Resin-1)~(Resin-10)的1H-NMR光谱。使用CDCl3作为溶剂。使用四甲基硅烷(TMS)作为内标物。其中,以聚芳酯树脂(Resin-1)为代表例。
图3表示聚芳酯树脂(Resin-1)的1H-NMR光谱。图3中,横轴表示化学位移(单位:ppm),纵轴表示信号强度(单位:任意单位)。还有,聚芳酯树脂(Resin-1)的化学位移值如下。聚芳酯树脂(Resin-1):8.81(d,2H),8.17-8.26(m,6H),8.09(d,2H),7.02-7.48(m,20H),2.74(brs,2H),2.50(brs,2H),2.02(brm,4H),1.41(brs,2H),1.23(brs,2H),0.99(d,12H),0.42(d,6H).
通过1H-NMR光谱和化学位移值,确认得到了聚芳酯树脂(Resin-1)。对于聚芳酯树脂(Resin-2)~(Resin-10)也是同样的,通过1H-NMR光谱和化学位移值,分别确认得到了聚芳酯树脂(Resin-2)~(Resin-10)。
<感光体的材料>
(粘结树脂)
如上述那样制造了聚芳酯树脂(Resin-1)~(Resin-10)来作为粘结树脂。还有,准备聚芳酯树脂(Resin-11)。聚芳酯树脂(Resin-11)是由化学式(Resin-11)表示的。
【化20】
(电荷产生剂)
准备第二实施方式中说明了的电荷产生剂(CGM-2)。电荷产生剂(CGM-2)是化学式(CGM-2)所示的Y型氧钛酞菁颜料(Y型氧钛酞菁结晶)。结晶结构是Y型。
Y型氧钛酞菁结晶在CuKα特征X射线衍射光谱图中,在布拉格角2θ±0.2°=9.2°、14.5°、18.1°、24.1°、27.2°具有峰值,主峰是27.2°。另外,CuKα特征X射线衍射光谱是按照第二实施方式中说明了的测量装置和测量条件进行测量的。
(空穴输送剂)
准备第二实施方式中说明了的空穴输送剂(HTM-1)~(HTM-10)。
<感光体的制造>
[感光体(A-1)的制造]
以下,对实施例1所涉及的感光体(A-1)的制造进行说明。
(中间层的形成)
首先,准备经过了表面处理的二氧化钛(Tayca株式会社制造“试生产样品SMT-A”、平均一次粒径10nm)。具体来说,使用氧化铝和二氧化硅对二氧化钛进行表面处理后,再在将表面处理过的二氧化钛进行湿式分散的同时,使用聚甲基氢硅氧烷进行表面处理,这样得到的二氧化钛就是所准备的二氧化钛。然后,将经过了表面处理的二氧化钛(2质量份)、聚酰胺树脂AMILAN(日本注册商标)(东丽株式会社制造“CM8000”)(聚酰胺6、聚酰胺12、聚酰胺66和聚酰胺610的四元共聚聚酰胺树脂)(1质量份)添加到混合溶剂中。混合溶剂含有甲醇(10质量份)、丁醇(1质量份)和甲苯(1质量份)。使用珠磨机,将这些材料(经过了表面处理的二氧化钛和聚酰胺树脂)和混合溶剂混合5小时,使材料分散到混合溶剂中。由此,制备出中间层用涂布液。
使用孔径5μm的过滤器,对所得中间层用涂布液进行过滤。然后,使用浸涂法,在作为导电性基体的铝制鼓状支撑体(直径30mm、全长246mm)的表面上,涂布中间层用涂布液,形成涂布膜。接下来,使涂布膜在130℃干燥30分钟,在导电性基体(鼓状支撑体)上形成中间层(膜厚1.5μm)。
(电荷产生层的形成)
将Y型氧钛酞菁颜料(1.5质量份)和作为基体树脂的聚乙烯醇缩醛树脂(积水化学工业株式会社制造“S-LEC BX-5”)(1质量份)添加到混合溶剂中。混合溶剂含有丙二醇单甲醚(40质量份)和四氢呋喃(40质量份)。使用珠磨机,将这些材料(Y型氧钛酞菁颜料和聚乙烯醇缩醛树脂)和混合溶剂混合12小时,使材料分散到混合溶剂中,制造出电荷产生层用涂布液。使用孔径3μm的过滤器,对所得电荷产生层用涂布液进行过滤。然后,使用浸涂法,将所得过滤液涂布在上述那样形成的中间层上,形成涂布膜。将涂布膜在50℃干燥5分钟。由此,在中间层上形成电荷产生层(膜厚0.3μm)。
(电荷输送层的形成)
将作为空穴输送剂的空穴输送剂(HTM-1)50质量份、作为添加剂的受阻酚抗氧化剂(BASF株式会社制造“IRGANOX(日本注册商标)1010”)2质量份、作为电子受体化合物的3,3′,5,5′-四叔丁基-4,4′-联苯醌2质量份、作为粘结树脂的聚芳酯树脂(Resin-1)(粘均分子量49,200)100质量份添加到混合溶剂中。混合溶剂含有四氢呋喃550质量份和甲苯150质量份。将这些材料(空穴输送剂(HTM-1)、受阻酚抗氧化剂、3,3′,5,5′-四叔丁基-4,4′-联苯醌和聚芳酯树脂(Resin-1))和混合溶剂进行12小时的混合,使材料分散到混合溶剂中。从而制备出电荷输送层用涂布液。
使用孔径3μm的过滤器,对所得电荷输送层用涂布液进行过滤。然后,使用浸涂法,将所得过滤液涂布在上述那样形成的电荷产生层上,并使其在120℃下干燥40分钟。由此,在电荷产生层上形成电荷输送层(膜厚20μm)。如此,得到感光体(A-1)。感光体(A-1)是在导电性基体上依次层叠有中间层、电荷产生层和电荷输送层的结构。
[感光体(A-2)~(A-19)和(B-1)]
除了下述事项的变更以外,通过与感光体(A-1)一样的方法,制造出感光体(A-2)~(A-19)和(B-1)。将空穴输送剂(HTM-1)变更为表1所述的空穴输送剂。将聚芳酯树脂(Resin-1)变更为表1所述的粘结树脂。
<感光体的性能评价>
(带电电位V0的测量)
对于感光体(A-1)~(A-19)和感光体(B-1)的每一个,使用鼓感光度试验机(GENTEC株式会社制造),转速设为31rpm,测量鼓流入电流是-10μmA时的表面电位。将测量的表面电位作为带电电位(V0)。测量环境是温度23℃与湿度50%RH。
(曝光后电位VL的测量)
对于感光体(A-1)~(A-19)和感光体(B-1)的每一个,使用鼓感光度试验机(GENTEC株式会社制造),转速设为31rpm,使感光体带电到-600V。然后,使用带通滤波器从卤素灯的光中取出单色光(波长:780nm;曝光量:0.8μJ/cm2),照射到感光体的表面上。在单色光的照射结束后,再经过80毫秒之后,测量表面电位。将测量的表面电位作为曝光后电位(VL)。测量环境是温度23℃与湿度50%RH。
(感光体的耐磨损性评价)
对于感光体(A-1)~(A-19)和感光体(B-1)的每一个,将制造中所制备的电荷输送层用涂布液涂布在缠绕于铝管(直径:78mm)的聚丙烯片材(厚度0.3mm)上。将其在120℃干燥40分钟,制作出形成了膜厚30μm的电荷输送层的磨损评价测试用片材。
将电荷输送层从该聚丙烯片材上剥离,粘贴在贴纸S-36(TABER公司制造)上,制作出样品。将制作的样品设置到旋转式磨损试验机(株式会社东洋精机制作所制造)中,使用砂轮CS-10(TABER公司制造),在负荷500gf且转速60rpm的条件下旋转1,000转,进行磨损评价测试。测量磨损量(mg/1000转),即磨损评价测试前后的样品质量变化。基于所得磨损量,评价感光体的耐磨损性。
表1表示感光体(A-1)~(A-19)和感光体(B-1)的结构和性能评价结果。表1中,“空穴输送剂”栏的HTM-1~HTM-10分别表示空穴输送剂(HTM-1)~(HTM-10)。“粘结树脂”栏的分子量是粘均分子量。“粘结树脂”栏的种类Resin-1~Resin-11分别表示聚芳酯树脂(Resin-1)~(Resin-11)。
【表1】
如表1所示,感光体(A-1)~(A-19)中,感光层含有电荷产生剂、空穴输送剂和粘结树脂。粘结树脂含有聚芳酯树脂(Resin-1)~(Resin-10)中的一个。聚芳酯树脂(Resin-1)~(Resin-10)是通式(1)所示聚芳酯树脂中的聚芳酯树脂。如表1所示,感光体(A-1)~(A-19)的磨损量是3.5mg以上5.5mg以下。
如表1所示,感光体(B-1)中,粘结树脂含有聚芳酯树脂(Resin-11)。聚芳酯树脂(Resin-11)不是通式(1)所示聚芳酯树脂中的聚芳酯树脂。如表1所示,感光体(B-1)的磨损量是8.2mg。
从表1中还可以清楚看出,第二实施方式所涉及的感光体(感光体(A-1)~(A-19))与感光体(B-1)相比,在耐磨损试验中的磨损量少。因此很显然,本发明所涉及的聚芳酯树脂提高感光体的耐磨损性,本发明所涉及的感光体的耐磨损性优异。
如表1所示,感光体(A-1)、(A-10)和(A-13)中,感光层含有作为粘结树脂的聚芳酯树脂(Resin-1)、(Resin-2)和(Resin-5)中的一个。这些聚芳酯树脂是通式(1)中的X或者Y表示通式(1-4)所示二价基的聚芳酯树脂。感光体(A-1)、(A-10)和(A-13)的磨损量都是3.5mg。
如表1所示,感光体(A-11)、(A-12)和(A-14)中,感光层含有作为粘结树脂的聚芳酯树脂(Resin-3)、(Resin-4)和(Resin-6)中的一个。这些聚芳酯树脂不是通式(1)中的X或者Y表示通式(1-4)所示二价基的聚芳酯树脂。感光体(A-11)、(A-12)和(A-14)的磨损量是3.6mg以上5.0mg以下。
从表1中可以清楚看出,感光体(A-1)、(A-10)和(A-13)与感光体(A-11)、(A-12)和(A-14)相比,磨损量少。显然,在感光层含有通式(1)所示聚芳酯树脂的情况下,当聚芳酯树脂是通式(1)中的X或者Y表示通式(1-4)所示二价基的聚芳酯树脂时,这样的感光体与感光层含有其它聚芳酯树脂的感光体相比,其耐磨损性优异。
Claims (10)
1.一种聚芳酯树脂,由下述通式(1)表示,
【化1】
所述通式(1)中,
R1和R2各自独立,表示氢原子或者甲基,
r和s表示0以上49以下的整数,
t和u表示1以上50以下的整数,
r+s+t+u=100,
r+t=s+u,
X和Y各自独立,表示化学式(1-1)、化学式(1-2)、化学式(1-3)或者化学式(1-4)所示的二价基,
X和Y彼此不同,
【化2】
2.根据权利要求1所述的聚芳酯树脂,其特征在于,
所述通式(1)中,
s/(s+u)是0.30以上0.70以下。
3.根据权利要求1所述的聚芳酯树脂,其特征在于,
所述通式(1)中,
在s表示0的情况下,Y表示所述化学式(1-4)所示的所述二价基,
在s表示1以上整数的情况下,X或者Y表示所述化学式(1-4)所示的所述二价基。
4.根据权利要求1所述的聚芳酯树脂,其特征在于,
所述通式(1)中,
r表示1以上的整数,
R1和R2中的一个表示氢原子,
R1和R2中的另一个表示甲基。
5.根据权利要求1或者2所述的聚芳酯树脂,其特征在于,
r和s表示1以上的整数,
不含4个重复单元以外的其它重复单元,
所述4个重复单元由通式(1-5)、通式(1-6)、通式(1-7)和通式(1-8)表示,
【化3】
所述通式(1-5)、所述通式(1-6)、所述通式(1-7)和所述通式(1-8)中,
R1和R2各自独立,表示所述氢原子或者所述甲基,
X和Y各自独立,表示所述化学式(1-1)、所述化学式(1-2)、所述化学式(1-3)或者所述化学式(1-4)所示的所述二价基,
X和Y彼此不同。
6.根据权利要求1所述的聚芳酯树脂,其特征在于,
由化学式(Resin-1)、化学式(Resin-2)、化学式(Resin-3)、化学式(Resin-4)、化学式(Resin-5)、化学式(Resin-6)、化学式(Resin-7)、化学式(Resin-8)、化学式(Resin-9)或者化学式(Resin-10)表示,
【化4】
【化5】
7.一种电子照相感光体,具备导电性基体和感光层,
所述感光层含有电荷产生剂、空穴输送剂和粘结树脂,
所述粘结树脂含有权利要求1或者2所述的聚芳酯树脂。
8.根据权利要求7所述的电子照相感光体,其特征在于,
所述空穴输送剂含有通式(2)、通式(3)或者通式(4)所示的化合物,
【化6】
所述通式(2)中,
Q1表示氢原子、C1-C8烷基、C1-C8烷氧基或者苯基,所述苯基中,也可以由C1-C8烷基取代基进行了取代,
Q2表示C1-C8烷基、C1-C8烷氧基或者苯基,
Q3、Q4、Q5、Q6和Q7各自独立,表示氢原子、C1-C8烷基、C1-C8烷氧基或者苯基,Q3、Q4、Q5、Q6和Q7中相邻的两个可以相互键合形成环,
a表示0以上5以下的整数,在a表示2以上5以下整数的情况下,结合在同一个苯基上的若干个Q2彼此可以相同或不同,
【化7】
所述通式(3)中,
Q8、Q10、Q11、Q12、Q13和Q14各自独立,表示氢原子、C1-C8烷基、C1-C8烷氧基或者苯基,
Q9和Q15各自独立,表示C1-C8烷基、C1-C8烷氧基或者苯基,
b表示0以上5以下的整数,在b表示2以上5以下整数的情况下,结合在同一个苯基上的若干个Q9彼此可以相同或不同,
c表示0以上4以下的整数,在c表示2以上4以下整数的情况下,结合在同一个亚苯基上的若干个Q15彼此可以相同或不同,
k表示0或者1,
【化8】
所述通式(4)中,
Ra、Rb和Rc各自独立,表示C1-C8烷基、苯基或者C1-C8烷氧基,
q表示0以上4以下的整数,在q表示2以上4以下整数的情况下,结合在同一个亚苯基上的若干个Rc彼此可以相同或不同,
m和n各自独立地表示0以上5以下的整数,在m表示2以上5以下整数的情况下,结合在同一个苯基上的若干个Rb彼此可以相同或不同,
在n表示2以上5以下整数的情况下,结合在同一个苯基上的若干个Ra彼此可以相同或不同。
9.根据权利要求8所述的电子照相感光体,其特征在于,
所述通式(2)中,
Q1表示氢原子或者由C1-C8烷基取代基进行了取代的苯基,
Q2表示C1-C8烷基,
Q3、Q4、Q5、Q6和Q7各自独立地表示氢原子、C1-C8烷基或者C1-C8烷氧基,Q3、Q4、Q5、Q6和Q7中相邻的两个可以相互键合形成环,
a表示0或者1,
所述通式(3)中,
Q8、Q10、Q11、Q12、Q13和Q14各自独立地表示氢原子、C1-C4烷基或者苯基,
b和c表示0,
所述通式(4)中,
Ra和Rb各自独立地表示C1-C8烷基,
m和n各自独立地表示0或者1,
q表示0。
10.根据权利要求8或者9所述的电子照相感光体,其特征在于,
所述空穴输送剂由化学式(HTM-1)、化学式(HTM-2)、化学式(HTM-3)、化学式(HTM-4)、化学式(HTM-5)、化学式(HTM-6)、化学式(HTM-7)、化学式(HTM-8)、化学式(HTM-9)或者化学式(HTM-10)表示,
【化9】
【化10】
【化11】