CN108101368A - Coloured glaze and white reaction grain collocation glaze and preparation method thereof - Google Patents
Coloured glaze and white reaction grain collocation glaze and preparation method thereof Download PDFInfo
- Publication number
- CN108101368A CN108101368A CN201711263802.1A CN201711263802A CN108101368A CN 108101368 A CN108101368 A CN 108101368A CN 201711263802 A CN201711263802 A CN 201711263802A CN 108101368 A CN108101368 A CN 108101368A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- component
- white reaction
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of coloured glaze and white reaction grain collocation glaze and preparation method thereof, coloured glaze is with having color glaze in glaze used in white reaction grain collocation glaze and adding in the white reaction particle in color glaze；The component and each component mass parts of the color glaze are as follows：35 parts~38 parts of potassium feldspar；5 parts~8 parts of bone ash；10 parts~14 parts of calcite；8 parts~10 parts of talcum；12 parts~16 parts of Jiepai clay；5 parts~8 parts of barium carbonate；6 parts~13 parts of color toner；The each component and each component mass parts of white reaction particle are as follows：32 parts~35 parts of potassium feldspar；10 parts~15 parts of albite；10 parts~14 parts of calcite；8 parts~12 parts of zinc oxide；10 parts~12 parts of titanium oxide；4 parts~5 parts of Guizhou clay；8 parts~10 parts of wollastonite.The present invention forms the white particle effect alternate with colored particle after mutually being melted with white reaction particle by coloured glaze, relaxation and happiness can be made one by using.
Description
Technical field
The present invention relates to a kind of coloured glazes and white reaction grain collocation glaze and preparation method thereof.
Background technology
At present, the monochromatic reaction glaze occurred on the market, mostly based on furnace transmutation glaze, however furnace transmutation glaze is to the control on burning till
System requirement is too high, and larger aberration is be easy to cause when firing typical products in mass production.
The content of the invention
The technical problems to be solved by the invention are the defects of overcoming the prior art, provide a kind of coloured glaze and white reaction
Grain collocation glaze, it forms the white particle effect alternate with colored particle after mutually being melted with white reaction particle by coloured glaze
Fruit, relaxation and happiness can be made one by using.
In order to solve the above technical problems, the technical scheme is that：A kind of coloured glaze and white reaction grain collocation glaze,
In glaze used in it there is color glaze and add in the white reaction particle in color glaze；The component of the color glaze
And each component mass parts are as follows：35 parts~38 parts of potassium feldspar；5 parts~8 parts of bone ash；10 parts~14 parts of calcite；Talcum 8 parts~10
Part；12 parts~16 parts of Jiepai clay；5 parts~8 parts of barium carbonate；6 parts~13 parts of color toner；The each component of white reaction particle and each
Constituent mass part is as follows：32 parts~35 parts of potassium feldspar；10 parts~15 parts of albite；10 parts~14 parts of calcite；8 parts of zinc oxide~
12 parts；10 parts~12 parts of titanium oxide；4 parts~5 parts of Guizhou clay；8 parts~10 parts of wollastonite.
The present invention also provides the preparation method of a kind of coloured glaze and white reaction grain collocation glaze, the step of method, is as follows：
A) color glaze is stocked up according to each component and each component quality：
B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of coloured glaze material ︰ ball ︰ water, when wet ball grinding 12~14 is small, the face after ball milling
After colour glaze crosses 200 mesh sieves, it is for use to be modulated into 53~54 Baume concentration；
C) white reaction particle is stocked up according to each component and each component quality：
D) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of white reaction material ︰ ball ︰ water, when wet ball grinding 12~14 is small, after ball milling
After white reaction material crosses 200 mesh sieves, half-dried, 50 mesh sieves excessively are dried to, in 1000 degrees Celsius of firing granulating, crushed 60~80 mesh
Sieve, is added in color glaze in the ratio of 10g/ kilograms of color glaze, is modulated into 51~53 Baume concentration, takes on clean green body
Panchromatic glaze；
E) green body for having soaked glaze is put into roller kilns to be fired in 1200 DEG C of oxidizing atmospheres.
After employing above-mentioned technical proposal, coloured glaze of the invention and white reaction grain collocation glaze, which is to pass through face
The white particle that color glaze mutually melts generation with white reaction particle is alternate with colored particle, the reaction based on coloured glaze
Glaze, it is simple for process, stabilization is burnt till, can be produced in enormous quantities, for the glaze based on light color system, using can make one easily pleased
Soon, at home and abroad the one seat for reacting glaze product can be occupied in market.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, the present invention is made into
One step is described in detail.
Embodiment one
A kind of coloured glaze has color glaze in glaze used in it and adds in coloured glaze with white reaction grain collocation glaze
White reaction particle in material；The component and each component mass parts of the color glaze are as follows：35 parts of potassium feldspar；5 parts of bone ash；Side
Solve 10 parts of stone；8 parts of talcum；12 parts of Jiepai clay；5 parts of barium carbonate；6 parts of color toner；The each component and each group of white reaction particle
Divide mass parts as follows：32 parts of potassium feldspar；10 parts of albite；10 parts of calcite；8 parts of zinc oxide；10 parts of titanium oxide；4 parts of Guizhou clay；
8 parts of wollastonite.
A kind of the step of preparation method of coloured glaze and white reaction grain collocation glaze, method, is as follows：
A) color glaze is stocked up according to each component and each component quality：
B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of coloured glaze material ︰ ball ︰ water, when wet ball grinding 12 is small, the coloured glaze after ball milling
After expecting 200 mesh sieves, it is for use to be modulated into 53~54 Baume concentration；
C) white reaction particle is stocked up according to each component and each component quality：
D) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of white reaction material ︰ ball ︰ water, when wet ball grinding 14 is small, the white after ball milling
After reaction material crosses 200 mesh sieves, half-dried, 50 mesh sieves excessively are dried to, in 1000 degrees Celsius of firing granulating, 60~80 mesh sieves is crushed, presses
The ratio of 10g/ kilograms of color glaze is added in color glaze, is modulated into 51~53 Baume concentration, is taken panchromatic on clean green body
Glaze；
E) green body for having soaked glaze is put into roller kilns to be fired in 1200 DEG C of oxidizing atmospheres.
Embodiment two
A kind of coloured glaze has color glaze in glaze used in it and adds in coloured glaze with white reaction grain collocation glaze
White reaction particle in material；The component and each component mass parts of the color glaze are as follows：38 parts of potassium feldspar；8 parts of bone；Fang Xie
14 parts of stone；10 parts of talcum；16 parts of Jiepai clay；8 parts of barium carbonate；13 parts of color toner；The each component and each group of white reaction particle
Divide mass parts as follows：35 parts of potassium feldspar；15 parts of albite；14 parts of calcite；12 parts of zinc oxide；12 parts of titanium oxide；Guizhou clay 5
Part；10 parts of wollastonite.
A kind of the step of preparation method of coloured glaze and white reaction grain collocation glaze, method, is as follows：
A) color glaze is stocked up according to each component and each component quality：
B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of coloured glaze material ︰ ball ︰ water, when wet ball grinding 14 is small, the coloured glaze after ball milling
After expecting 200 mesh sieves, it is for use to be modulated into 53~54 Baume concentration；
C) white reaction particle is stocked up according to each component and each component quality：
D) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of white reaction material ︰ ball ︰ water, when wet ball grinding 14 is small, the white after ball milling
After reaction material crosses 200 mesh sieves, half-dried, 50 mesh sieves excessively are dried to, in 1000 degrees Celsius of firing granulating, 60~80 mesh sieves is crushed, presses
The ratio of 10g/ kilograms of color glaze is added in color glaze, is modulated into 51~53 Baume concentration, is taken panchromatic on clean green body
Glaze；
E) green body for having soaked glaze is put into roller kilns to be fired in 1200 DEG C of oxidizing atmospheres.
Embodiment three
A kind of coloured glaze has color glaze in glaze used in it and adds in coloured glaze with white reaction grain collocation glaze
White reaction particle in material；The component and each component mass parts of the color glaze are as follows：36 parts of potassium feldspar；7 parts of bone ash；Side
Solve 12 parts of stone；9 parts of talcum；14 parts of Jiepai clay；7 parts of barium carbonate；10 parts of color toner；The each component and each group of white reaction particle
Divide mass parts as follows：33 parts of potassium feldspar；12 parts of albite；12 parts of calcite；10 parts of zinc oxide；10 parts of titanium oxide；Guizhou clay 4
Part；9 parts of wollastonite.
A kind of the step of preparation method of coloured glaze and white reaction grain collocation glaze, method, is as follows：
A) color glaze is stocked up according to each component and each component quality：
B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of coloured glaze material ︰ ball ︰ water, when wet ball grinding 13 is small, the coloured glaze after ball milling
After expecting 200 mesh sieves, it is for use to be modulated into 53~54 Baume concentration；
C) white reaction particle is stocked up according to each component and each component quality：
D) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of white reaction material ︰ ball ︰ water, when wet ball grinding 13 is small, the white after ball milling
After reaction material crosses 200 mesh sieves, half-dried, 50 mesh sieves excessively are dried to, in 1000 degrees Celsius of firing granulating, 60~80 mesh sieves is crushed, presses
The ratio of 10g/ kilograms of color glaze is added in color glaze, is modulated into 51~53 Baume concentration, is taken panchromatic on clean green body
Glaze；
E) green body for having soaked glaze is put into roller kilns to be fired in 1200 DEG C of oxidizing atmospheres.
The coloured glaze that three above embodiment is prepared passes through with white reaction grain collocation glaze it has been observed that it can
The white particle effect alternate with colored particle is presented, relaxation and happiness can be made one by using.
Particular embodiments described above has carried out the purpose of the present invention, technical solution and advantageous effect further in detail
It describes in detail bright, it should be understood that the above is only a specific embodiment of the present invention, is not intended to limit the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution, improvement and etc. done should be included in the guarantor of the present invention
Within the scope of shield.
Claims (2)
- The glaze 1. a kind of coloured glaze and white reaction grain are arranged in pairs or groups, which is characterized in that have in glaze used in it color glaze and Add in the white reaction particle in color glaze；The component and each component mass parts of the color glaze are as follows：35 parts of potassium feldspar ~38 parts；5 parts~8 parts of bone ash；10 parts~14 parts of calcite；8 parts~10 parts of talcum；12 parts~16 parts of Jiepai clay；5 parts of barium carbonate ~8 parts；6 parts~13 parts of color toner；The each component and each component mass parts of white reaction particle are as follows：Potassium feldspar 32 parts~35 Part；10 parts~15 parts of albite；10 parts~14 parts of calcite；8 parts~12 parts of zinc oxide；10 parts~12 parts of titanium oxide；Guizhou clay 4 Part~5 parts；8 parts~10 parts of wollastonite.
- A kind of 2. preparation method of coloured glaze as described in claim 1 and white reaction grain collocation glaze, it is characterised in that method The step of it is as follows：A) color glaze is stocked up according to each component and each component quality：B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of coloured glaze material ︰ ball ︰ water, when wet ball grinding 12~14 is small, the coloured glaze after ball milling After expecting 200 mesh sieves, it is for use to be modulated into 53~54 Baume concentration；C) white reaction particle is stocked up according to each component and each component quality：D) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of white reaction material ︰ ball ︰ water, when wet ball grinding 12~14 is small, the white after ball milling After reaction material crosses 200 mesh sieves, half-dried, 50 mesh sieves excessively are dried to, in 1000 degrees Celsius of firing granulating, 60~80 mesh sieves is crushed, presses The ratio of 10g/ kilograms of color glaze is added in color glaze, is modulated into 51~53 Baume concentration, is taken panchromatic on clean green body Glaze；E) green body for having soaked glaze is put into roller kilns to be fired in 1200 DEG C of oxidizing atmospheres.