Prior art keywords
powder
frit
glaze
carbonate
wollastonite
Prior art date
Application number
CN201510987398.7A
Other languages
Chinese (zh)
Inventor
高世明
Original Assignee
襄阳高铭矿业有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 襄阳高铭矿业有限公司 filed Critical 襄阳高铭矿业有限公司
Priority to CN201510987398.7A priority Critical patent/CN105753326A/en
Publication of CN105753326A publication Critical patent/CN105753326A/en

Links

Classifications

    • CCHEMISTRY; METALLURGY
    • C03GLASS; MINERAL OR SLAG WOOL
    • C03CCHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C8/00Enamels; Glazes; Fusion seal compositions being frit compositions having non-frit additions
    • C03C8/02Frit compositions, i.e. in a powdered or comminuted form
    • C03C8/04Frit compositions, i.e. in a powdered or comminuted form containing zinc
    • CCHEMISTRY; METALLURGY
    • C03GLASS; MINERAL OR SLAG WOOL
    • C03CCHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C8/00Enamels; Glazes; Fusion seal compositions being frit compositions having non-frit additions
    • C03C8/14Glass frit mixtures having non-frit additions, e.g. opacifiers, colorants, mill-additions

Abstract

The invention provides a diamond glaze for ceramic tiles.One), a formula comprises: spodumene powder, frit powder, potassium feldspar powder, calcined talc powder, barium carbonate powder, wollastonite powder, kaolin powder, white alundum powder, and zinc oxide; two), a preparation method comprises the steps: 1, preparing the frit powder, potassium feldspar, wollastonite, raw talc, barium carbonate, calcite, quartz, crude aluminum oxide, 95 zinc oxide, potassium carbonate and strontium carbonate, 1), placing all materials in a melting furnace, and heating to 1500 DEG C to obtain frit; 2), taking out for cooling to normal temperature, crushing, screening with a 100-mesh screen for use, and if disqualification occurs, crushing and screening until qualification; 2, placing all materials of formula one) into a stirrer, and stirring well to obtain the diamond glaze.The method has a simple process, the diamond glaze has high glaze, can prevent cracking, cut facture and the like, has excellent wear resistance and is useful in the production of polished tiles closer to nature and richer in color.

Description

A kind of ceramic tile diamond glaze
Technical field
The present invention relates to a kind of ceramic tile and produce the glaze used, specifically a kind of ceramic tile diamond glaze.
Background technology
Ceramic tile uses extremely wide at building field, widely used while, various technological improvements promote products perfection to be also continuous appearance, but existing ceramic tile is ubiquitous light anti-" water ripples ", wear no resistance, third dimension of patterns is weak, polish aborning and easily wear the defects such as glaze and be difficult to solve, existing enterprise is in order to solve this defect, emphasis concentrates the research and development super flat glaze of Buddha's warrior attendant glaze, re-polishing after namely glaze paint being thickeied, thus solve the defect existed, but this settling mode goes out to reveal the problem wasting raw material and increasing production cost, the defect making existence cannot be solved technically at all.
Summary of the invention
The present invention provides a kind of ceramic tile diamond glaze, adopts scientific formula and simple process, and the firm glaze intensity of institute's pan is high, wearability is good.
The present invention includes sieving with 100 mesh filter screens after broken for frit pulverizer, and the technical scheme adopted is in that:
One) percentage by weight formula:
Spodumene powder 15~40%, frit powder 10~15%, feldspar in powder 10~15%, burning Pulvis Talci 5~15%, brium carbonate powder 8~15%, wollastonite in powder 10~15%, kaolin powder 5~8%, white alundum powder 1~5%, zinc oxide 5~7%,
Two) preparation method:
Step 1, first preparing frit powder, its frit powder percentage by weight formula is as follows: potash feldspar 20~30%, wollastonite 4~6%, raw Talcum 5~8%, brium carbonate 5~8%, calcite 16~20%, quartz 20~22%, thick aluminium oxide 10~14%, 95 zinc oxide 2~4%, potassium carbonate 1~3%, strontium carbonate 1~2%,
The preparation of frit powder:
1) calciner is put in the mixing of whole dispensings, heat to 1500 DEG C, namely obtain frit;
2) crush with pulverizer after frit takes out and is cooled to room temperature, then sieve with 100 eye mesh screens and continue to employ, defective again crush be screened to qualified;
Step 2, by one) percentage by weight formulation material all puts into blender and is uniformly mixed and namely becomes diamond glaze.
The present invention has following advantageous effect: pass through technique scheme, owing to composition of raw materials is scientific and reasonable, various formulation materials are preferred each through what become more meticulous, in addition process is extremely simple, the frit in formula is machined especially with scientific formula and processes, the every physical index of Buddha's warrior attendant glaze thus constituted is optimized comprehensively, its hardness ratio conventional products hardness significantly improves, the tile product water ripple phenomenon produced gets a new look, wearability and thermal shock resistance improve comprehensively, eliminate delayed crazing that glaze paint is likely to occur and phenomenon is split in cutting, ceramic tile glaze paint can be allowed to prepare texture more natural, color is abundanter, thus solve many problems affecting quality that existing ceramic tile glaze exists, scientific formulation, preparation technology is simple, the mirror effect equal with throwing face brick can be obtained after using.
Detailed description of the invention
Embodiment 1:
One) percentage by weight formula:
Spodumene powder 40%, frit powder 10%, feldspar in powder 10%, burning Pulvis Talci 5%, brium carbonate powder 8%, wollastonite in powder 10%, kaolin powder 5%, white alundum powder 1%, zinc oxide 5%,
Two) preparation method:
Step 1, first preparing frit powder, its frit powder percentage by weight formula is as follows: potash feldspar 30%, wollastonite 4%, raw Talcum 5%, brium carbonate 5%, calcite 16%, quartz 20%, thick aluminium oxide 10%, 95 zinc oxide 2%, potassium carbonate 1%, strontium carbonate 1%,
The preparation of frit powder:
1) calciner is put in the mixing of whole dispensings, heat to 1500 DEG C, namely obtain frit;
2) crush with pulverizer after frit takes out and is cooled to room temperature, then sieve with 100 eye mesh screens and continue to employ, defective again crush be screened to qualified;
Step 2, by one) percentage by weight formulation material all puts into blender and is uniformly mixed and namely becomes diamond glaze.
Embodiment 2
One) percentage by weight formula:
Spodumene powder 27%, frit powder 13%, feldspar in powder 13%, burning Pulvis Talci 10%, brium carbonate powder 12%, wollastonite in powder 13%, kaolin powder 7%, white alundum powder 3%, zinc oxide 6%,
Two) preparation method:
Step 1, first preparing frit powder, its frit powder percentage by weight formula is as follows: potash feldspar 25%, wollastonite 5%, raw Talcum 6%, brium carbonate 7%, calcite 18%, quartz 21%, thick aluminium oxide 12%, 95 zinc oxide 3%, potassium carbonate 2%, strontium carbonate 1.5%,
The preparation of frit powder:
1) calciner is put in the mixing of whole dispensings, heat to 1500 DEG C, namely obtain frit;
2) crush with pulverizer after frit takes out and is cooled to room temperature, then sieve with 100 eye mesh screens and continue to employ, defective again crush be screened to qualified;
Step 2, by one) percentage by weight formulation material all puts into blender and is uniformly mixed and namely becomes diamond glaze.
Embodiment 3
One) percentage by weight formula:
Spodumene powder 15%, frit powder 15%, feldspar in powder 15%, burning Pulvis Talci 15%, brium carbonate powder 15%, wollastonite in powder 15%, kaolin powder 8%, white alundum powder 5%, zinc oxide 7%,
Two) preparation method:
Step 1, first preparing frit powder, its frit powder percentage by weight formula is as follows: potash feldspar 20%, wollastonite 6%, raw Talcum 8%, brium carbonate 8%, calcite 20%, quartz 22%, thick aluminium oxide 14%, 95 zinc oxide 4%, potassium carbonate 3%, strontium carbonate 2%,
The preparation of frit powder:
1) calciner is put in the mixing of whole dispensings, heat to 1500 DEG C, namely obtain frit;
2) crush with pulverizer after frit takes out and is cooled to room temperature, then sieve with 100 eye mesh screens and continue to employ, defective again crush be screened to qualified;
Step 2, by one) percentage by weight formulation material all puts into blender and is uniformly mixed and namely becomes diamond glaze.

Claims (1)

1. a ceramic tile diamond glaze, sieves with 100 mesh filter screens including after broken for frit pulverizer, it is characterised in that:
One) percentage by weight formula:
Spodumene powder 15~40%, frit powder 10~15%, feldspar in powder 10~15%, burning Pulvis Talci 5~15%, brium carbonate powder 8~15%, wollastonite in powder 10~15%, kaolin powder 5~8%, white alundum powder 1~5%, zinc oxide 5~7%,
Two) preparation method:
Step 1, first preparing frit powder, its frit powder percentage by weight formula is as follows: potash feldspar 20~30%, wollastonite 4~6%, raw Talcum 5~8%, brium carbonate 5~8%, calcite 16~20%, quartz 20~22%, thick aluminium oxide 10~14%, 95 zinc oxide 2~4%, potassium carbonate 1~3%, strontium carbonate 1~2%,
The preparation of frit powder:
1) calciner is put in the mixing of whole dispensings, heat to 1500 DEG C, namely obtain frit;
2) crush with pulverizer after frit takes out and is cooled to room temperature, then sieve with 100 eye mesh screens and continue to employ, defective again crush be screened to qualified;
Step 2, by one) percentage by weight formulation material all puts into blender and is uniformly mixed and namely becomes diamond glaze.
CN201510987398.7A 2015-12-27 2015-12-27 Diamond glaze for ceramic tiles CN105753326A (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
CN201510987398.7A CN105753326A (en) 2015-12-27 2015-12-27 Diamond glaze for ceramic tiles

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
CN201510987398.7A CN105753326A (en) 2015-12-27 2015-12-27 Diamond glaze for ceramic tiles

Publications (1)

Publication Number Publication Date
CN105753326A true CN105753326A (en) 2016-07-13

Family

ID=56342177

Family Applications (1)

Application Number Title Priority Date Filing Date
CN201510987398.7A CN105753326A (en) 2015-12-27 2015-12-27 Diamond glaze for ceramic tiles

Country Status (1)

Country Link
CN (1) CN105753326A (en)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105948820A (en) * 2016-04-29 2016-09-21 佛山市东鹏陶瓷有限公司 Wear-resistant glaze and method for preparing glazed tile by utilizing the same
CN105967523A (en) * 2016-04-29 2016-09-28 佛山市东鹏陶瓷有限公司 Frit used for glaze, and making method thereof
CN106219978A (en) * 2016-07-18 2016-12-14 北京杭瑞商贸有限公司 Margarita glaze, pearl glaze and preparation method thereof and pearl glaze ceramic
CN107226619A (en) * 2017-06-02 2017-10-03 佛山石湾华鹏陶瓷有限公司 A kind of acidproof Buddha's warrior attendant glaze and preparation method, acidproof Buddha's warrior attendant glaze Ceramic Tiles preparation method
CN108101368A (en) * 2017-12-05 2018-06-01 湖南陶润会文化传播有限公司 Coloured glaze and white reaction grain collocation glaze and preparation method thereof
CN108821588A (en) * 2018-06-25 2018-11-16 广东家美陶瓷有限公司 High alumina titanate ceramics glaze, ink-jet Ceramic Tiles of the glaze of titanate ceramics containing high alumina and preparation method thereof
CN109250900A (en) * 2018-12-07 2019-01-22 佛山市东鹏陶瓷有限公司 A kind of negative ion powder, glaze and preparation method thereof

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101555129A (en) * 2009-05-12 2009-10-14 潮州市联源陶瓷制作有限公司 Household strengthen porcelain containing bone substances and production technology thereof
CN102515703A (en) * 2011-12-20 2012-06-27 四川新中源陶瓷有限公司 Production technology of super-flat high-crystal stone tile
CN103214270A (en) * 2013-04-19 2013-07-24 深圳市永丰源瓷业有限公司 Formula material of preventing high-temperature pigment from glaze-crawling for bone china and preparation process thereof
CN104003762A (en) * 2014-06-13 2014-08-27 广东松发陶瓷股份有限公司 Bone matte glaze and method for manufacturing bone china product by using same

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101555129A (en) * 2009-05-12 2009-10-14 潮州市联源陶瓷制作有限公司 Household strengthen porcelain containing bone substances and production technology thereof
CN102515703A (en) * 2011-12-20 2012-06-27 四川新中源陶瓷有限公司 Production technology of super-flat high-crystal stone tile
CN103214270A (en) * 2013-04-19 2013-07-24 深圳市永丰源瓷业有限公司 Formula material of preventing high-temperature pigment from glaze-crawling for bone china and preparation process thereof
CN104003762A (en) * 2014-06-13 2014-08-27 广东松发陶瓷股份有限公司 Bone matte glaze and method for manufacturing bone china product by using same

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
李天伶: "锂质低热膨胀釉", 《中国陶瓷》 *

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105948820A (en) * 2016-04-29 2016-09-21 佛山市东鹏陶瓷有限公司 Wear-resistant glaze and method for preparing glazed tile by utilizing the same
CN105967523A (en) * 2016-04-29 2016-09-28 佛山市东鹏陶瓷有限公司 Frit used for glaze, and making method thereof
CN105967523B (en) * 2016-04-29 2019-01-04 佛山市东鹏陶瓷有限公司 A kind of glaze and its manufacturing method
CN105948820B (en) * 2016-04-29 2019-01-22 佛山市东鹏陶瓷有限公司 A kind of Wear-resistant glaze material and the method using its preparation glazed tile
CN106219978A (en) * 2016-07-18 2016-12-14 北京杭瑞商贸有限公司 Margarita glaze, pearl glaze and preparation method thereof and pearl glaze ceramic
CN107226619A (en) * 2017-06-02 2017-10-03 佛山石湾华鹏陶瓷有限公司 A kind of acidproof Buddha's warrior attendant glaze and preparation method, acidproof Buddha's warrior attendant glaze Ceramic Tiles preparation method
CN108101368A (en) * 2017-12-05 2018-06-01 湖南陶润会文化传播有限公司 Coloured glaze and white reaction grain collocation glaze and preparation method thereof
CN108821588A (en) * 2018-06-25 2018-11-16 广东家美陶瓷有限公司 High alumina titanate ceramics glaze, ink-jet Ceramic Tiles of the glaze of titanate ceramics containing high alumina and preparation method thereof
CN109250900A (en) * 2018-12-07 2019-01-22 佛山市东鹏陶瓷有限公司 A kind of negative ion powder, glaze and preparation method thereof

Similar Documents

Publication Publication Date Title
CN102584351B (en) Method for preparing jadeite microcrystal glass ceramic composite board
CN104119063B (en) A kind of with burner hearth slag be major ingredient natural romantic charm ceramic tile modelled after an antique and manufacture method thereof
CN101538164B (en) Process for preparing super-low expansion ceramic material
CN103102178B (en) Purple matt glaze and preparation method thereof
CN103626523A (en) Ceramic tile with dry particle glaze-decorated surface and manufacturing method thereof
CN105712701B (en) A kind of single layer glaze transmutation brick and preparation method thereof
CN104016719B (en) Reactive crystallization glaze with sagging effect and preparation method thereof
CN106966598B (en) A kind of low temperature high-hardness, wearable throws glaze and preparation method thereof entirely
CN101255067B (en) Preparation method of metal-imitation glaze
CN102390933B (en) Dry grain for crystal throwing brick and method for preparing crystal throwing brick
CN101918338A (en) A kind of polycrystal alumina transparent ceramic and preparation method thereof with preferred orientation
CN1931779A (en) Color light wall tile and its making process
CN105753322B (en) A kind of medium temperature plum green glaze and medium temperature plum green Longquan celadon
EP0688740B1 (en) Method for the production of sheets for building and decoration which resemble natural stone
CN101314549B (en) Metallic glaze composition
CN101348330B (en) Preparation of low temperature metal-lustrous glaze for ceramic
CN1693247A (en) Chemically and thermally pre-stressable lithium aluminosilicate float glass of high temperature resistance
CN105948820A (en) Wear-resistant glaze and method for preparing glazed tile by utilizing the same
CN103102078A (en) Preparation method of microcrystal dry grains, microlite ceramic tile and production method of microlite ceramic tile
CN106336116A (en) Ceramic glaze, preparation method and method for making ceramic by utilization of ceramic glaze
CN105565666B (en) The three-dimensional red chestnut frosted artistic glaze preparation method of ceramic vessel
CN104478483B (en) A kind of double-deck furnace transmutation glaze and preparation method thereof
CN105948503A (en) Wear-resistant transparent glaze and method for preparing glazed tile by utilizing same
CN107417115B (en) Method for manufacturing high-hardness high-wear-resistance glaze
CN105669037B (en) It is layered the processing method of crystallite stone ceramic tile

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
RJ01 Rejection of invention patent application after publication
RJ01 Rejection of invention patent application after publication

Application publication date: 20160713