CN103030430A - Method for preparing gorgeous space-time glaze - Google Patents

Method for preparing gorgeous space-time glaze Download PDF

Info

Publication number
CN103030430A
CN103030430A CN2012105350750A CN201210535075A CN103030430A CN 103030430 A CN103030430 A CN 103030430A CN 2012105350750 A CN2012105350750 A CN 2012105350750A CN 201210535075 A CN201210535075 A CN 201210535075A CN 103030430 A CN103030430 A CN 103030430A
Authority
CN
China
Prior art keywords
glaze
percent
particulate
calcite
frit
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012105350750A
Other languages
Chinese (zh)
Other versions
CN103030430B (en
Inventor
文智勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TOP COLLECTION CO Ltd
Original Assignee
TOP COLLECTION CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TOP COLLECTION CO Ltd filed Critical TOP COLLECTION CO Ltd
Priority to CN201210535075.0A priority Critical patent/CN103030430B/en
Publication of CN103030430A publication Critical patent/CN103030430A/en
Application granted granted Critical
Publication of CN103030430B publication Critical patent/CN103030430B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a method for preparing a gorgeous space-time glaze. The method comprises the following steps of: preparing materials containing the following components in percentage by weight: 38 to 42 percent of potassium feldspar, 10 to 13 percent of calcite, 2 to 3 percent of dolomite, 3 to 4 percent of talc, 2 to 3 percent of zinc oxide, 4 to 6 percent of kaolin, 20 to 24 percent of frits, 2 to 5 percent of granules, and 8 to 10 percent of an inclusion red pigment; performing wet ball milling for 20 to 24 hours in a ratio of the materials to balls to water of 1:1.5:1.2; sieving the ball-milled glaze through a sieve of 100 to 140 meshes, additionally adding 5 to 8 percent of the granules into the completely sieved glaze, and blending the mixture into glaze slip of 50-60 Baume degrees; and soaking a blank with a bright and clean appearance into the glaze slip, and firing in an oxidizing atmosphere at 1,200 to 1,230 DEG C, thereby obtaining a finished product. By adopting the method, the surface of porcelain seems to be in the shape of dandelions which are instantly scattered and seems to be in the shape of a starry sky, and the porcelain is close to the nature and has strong infectivity.

Description

The making method of gorgeous space-time glaze
Technical field
The present invention relates to a kind of making method of gorgeous space-time glaze.
Background technology
At present, in the porcelain industry, the moulding of porcelain base is the basis of quality products, the allotment of glaze makes porcelain more bright and colourful, the porcelain base of same moulding, often because of the difference of glaze, and human consumer's vision is produced different impacts, the sort of grain that adds is in glaze, reaction is at glaze, make the people feel the unusual of it, this also becomes the another kind of fashion of current porcelain industry, night, the at night some point star of black is interspersed, bright and colourful, its picture is mapped on the porcelain, can reach the effect of making us equally pleasing.
Summary of the invention
Technical problem to be solved by this invention is to overcome the deficiencies in the prior art, provides a kind of porcelain surface that can make to exactly like taraxacum unrestrained moment, like starry sky, porcelain is got close to nature, and have the making method of the gorgeous space-time glaze of stronger infectivity.
The present invention solves the problems of the technologies described above the technical scheme of taking: a kind of making method of gorgeous space-time glaze, and the step of the method is as follows:
(1) gets the raw materials ready according to following component and weight percent
Potassium felspar sand 38% ~ 42% calcite 10% ~ 13%
Rhombspar 2% ~ 3% talcum 3% ~ 4%
Zinc oxide 2% ~ 3% kaolin 4% ~ 6%
Frit 20% ~ 24% particulate material 2% ~ 5%
Wrap up red 8% ~ 10%;
Wherein, particulate material is got the raw materials ready by following component and weight percent: potassium felspar sand 15% ~ 20%, frit 40% ~ 45%, calcite 8%, quartz 12% ~ 18%, Guizhou clay 2%, zinc oxide 5% ~ 10% titanium oxide 10% ~ 15%, particle is got the raw materials ready through granulation, excessively obtains particulate material behind 20 ~ 80 mesh sieves;
Constitutive material component and the weight percent of frit are: borax 40% ~ 45%, quartz 25% ~ 32%, potassium felspar sand 15% ~ 20%, yellow soda ash 5% ~ 8%, calcite 5% ~ 7%;
(2) by material: ball: water=1:1.5:1.2, wet ball grinding 20 ~ 24 hours;
(3) glaze behind the ball milling is crossed 100 ~ 140 mesh sieves, adds in addition 5% ~ 8% particulate material in the glaze after 100% sieve, again the glaze slip of furnishing 50 ~ 60 degree Beaume;
(4) get the bright and clean base substrate of appearance and immerse this glaze slip after, under 1200 ℃ ~ 1230 ℃ oxidizing atmosphere, fire finished product.
After having adopted technique scheme, the gorgeous space-time glaze of making by present method, the glaze layer thickness is suitably 0.2 ~ 0.45mm, glaze of the present invention is to exactly like taraxacum with its glazing effect to be scattered moment and to gain the name, adopting parcel red is tinting material, the finished product glaze of making exactly likes taraxacum unrestrained moment, allows the people experience the be scattered aestheticism picture of moment of taraxacum, and is bright and colourful.
Embodiment
Content of the present invention is easier to be expressly understood that the below is according to specific embodiment in order to make, and the present invention is further detailed explanation,
Embodiment one
A kind of making method of gorgeous space-time glaze, the step of the method is as follows:
(1) gets the raw materials ready according to following component and weight percent
Potassium felspar sand 42% calcite 11%
Rhombspar 2% talcum 4%
Zinc oxide 2% kaolin 5%
Frit 21% particulate material 3%
Wrap up red 10%;
Wherein, particulate material is got the raw materials ready by following component and weight percent: potassium felspar sand 16%, and frit 41%, calcite 8%, quartz 13%, Guizhou clay 2%, zinc oxide 6%, titanium oxide 14%, particle are got the raw materials ready through granulation, excessively obtain particulate material behind 30 mesh sieves;
Constitutive material component and the weight percent of frit are: borax 41%, quartz 32%, potassium felspar sand 15%, yellow soda ash 5%, calcite 7%;
(2) by material: ball: water=1:1.5:1.2, wet ball grinding 21 hours;
(3) glaze behind the ball milling is crossed 110 mesh sieves, adds in addition 6% particulate material in the glaze after 100% sieve, again the glaze slip of furnishing 50 ~ 60 degree Beaume;
(4) get the bright and clean base substrate of appearance and immerse this glaze slip after, under 1200 ℃ ~ 1230 ℃ oxidizing atmosphere, fire finished product.
The gorgeous space-time glaze glaze that present method makes exactly likes taraxacum and trickles down moment, like starry sky, porcelain is got close to nature, and have stronger infectivity, and is bright and colourful.
Embodiment two
A kind of making method of gorgeous space-time glaze, the step of the method is as follows:
(1) gets the raw materials ready according to following component and weight percent
Potassium felspar sand 38% calcite 12%
Rhombspar 3% talcum 4%
Zinc oxide 3% kaolin 5%
Frit 22% particulate material 5%
Wrap up red 8%;
Wherein, particulate material is got the raw materials ready by following component and weight percent: potassium felspar sand 19%, and frit 40%, calcite 8%, quartz 12%, Guizhou clay 2%, zinc oxide 9% titanium oxide 10%, particle is got the raw materials ready through granulation, excessively obtains particulate material behind 70 mesh sieves;
Constitutive material component and the weight percent of frit are: borax 40%, quartz 25%, potassium felspar sand 20%, yellow soda ash 8%, calcite 7%;
(2) by material: ball: water=1:1.5:1.2, wet ball grinding 24 hours;
(3) glaze behind the ball milling is crossed 140 mesh sieves, adds in addition 7% particulate material in the glaze after 100% sieve, again the glaze slip of furnishing 50 ~ 60 degree Beaume;
(4) get the bright and clean base substrate of appearance and immerse this glaze slip after, under 1200 ℃ ~ 1230 ℃ oxidizing atmosphere, fire finished product.
The gorgeous space-time glaze glaze that present method makes exactly likes taraxacum and trickles down moment, like starry sky, porcelain is got close to nature, and have stronger infectivity, and is bright and colourful.
Embodiment three
A kind of making method of gorgeous space-time glaze, the step of the method is as follows:
(1) gets the raw materials ready according to following component and weight percent
Potassium felspar sand 40% calcite 12%
Rhombspar 2% talcum 4%
Zinc oxide 3% kaolin 5%
Frit 22% particulate material 3%
Wrap up red 9%;
Wherein, particulate material is got the raw materials ready by following component and weight percent: potassium felspar sand 17%, and frit 43%, calcite 8%, quartz 12%, Guizhou clay 2%, zinc oxide 8% titanium oxide 10%, particle is got the raw materials ready through granulation, excessively obtains particulate material behind 50 mesh sieves;
Constitutive material component and the weight percent of frit are: borax 43%, quartz 29%, potassium felspar sand 17%, yellow soda ash 6%, calcite 5%;
(2) by material: ball: water=1:1.5:1.2, wet ball grinding 22 hours;
(3) glaze behind the ball milling is crossed 120 mesh sieves, adds in addition 6% particulate material in the glaze after 100% sieve, again the glaze slip of furnishing 50 ~ 60 degree Beaume;
(4) get the bright and clean base substrate of appearance and immerse this glaze slip after, under 1200 ℃ ~ 1230 ℃ oxidizing atmosphere, fire finished product.
The gorgeous space-time glaze glaze that present method makes exactly likes taraxacum and trickles down moment, like starry sky, porcelain is got close to nature, and have stronger infectivity, and is bright and colourful.
Above-described specific embodiment; purpose of the present invention, technical scheme and beneficial effect are further described; institute is understood that; the above only is specific embodiments of the invention; be not limited to the present invention; within the spirit and principles in the present invention all, any modification of making, be equal to replacement, improvement etc., all should be included within protection scope of the present invention.

Claims (1)

1. the making method of a gorgeous space-time glaze is characterized in that the step of the method is as follows:
(1) gets the raw materials ready according to following component and weight percent
Potassium felspar sand 38% ~ 42% calcite 10% ~ 13%
Rhombspar 2% ~ 3% talcum 3% ~ 4%
Zinc oxide 2% ~ 3% kaolin 4% ~ 6%
Frit 20% ~ 24% particulate material 2% ~ 5%
Wrap up red 8% ~ 10%;
Wherein, particulate material is got the raw materials ready by following component and weight percent: potassium felspar sand 15% ~ 20%, frit 40% ~ 45%, calcite 8%, quartz 12% ~ 18%, Guizhou clay 2%, zinc oxide 5% ~ 10% titanium oxide 10% ~ 15%, particle is got the raw materials ready through granulation, excessively obtains particulate material behind 20 ~ 80 mesh sieves;
Constitutive material component and the weight percent of frit are: borax 40% ~ 45%, quartz 25% ~ 32%, potassium felspar sand 15% ~ 20%, yellow soda ash 5% ~ 8%, calcite 5% ~ 7%;
(2) by material: ball: water=1:1.5:1.2, wet ball grinding 20 ~ 24 hours;
(3) glaze behind the ball milling is crossed 100 ~ 140 mesh sieves, adds in addition 5% ~ 8% particulate material in the glaze after 100% sieve, again the glaze slip of furnishing 50 ~ 60 degree Beaume;
(4) get the bright and clean base substrate of appearance and immerse this glaze slip after, under 1200 ℃ ~ 1230 ℃ oxidizing atmosphere, fire finished product.
CN201210535075.0A 2012-12-12 2012-12-12 Method for preparing gorgeous space-time glaze Active CN103030430B (en)