CN107954601A - Colorful plus grain reaction glaze and preparation method thereof - Google Patents
Colorful plus grain reaction glaze and preparation method thereof Download PDFInfo
- Publication number
- CN107954601A CN107954601A CN201711263840.7A CN201711263840A CN107954601A CN 107954601 A CN107954601 A CN 107954601A CN 201711263840 A CN201711263840 A CN 201711263840A CN 107954601 A CN107954601 A CN 107954601A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- colorful
- zinc oxide
- red
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of colorful plus grain reaction glaze and preparation method thereof, the component of glaze and each component mass parts are as follows used in colorful plus grain reaction glaze：35 parts~38 parts of potassium feldspar；10 parts~13 parts of bone ash；3 parts~6 parts of talcum；6 parts~8 parts of Jiepai clay；15 parts~18 parts of barium carbonate；4 parts~6 parts of zinc oxide；10 parts~13 parts of zirconium silicate；Red granules：10 parts；Black particle：5 parts；Wherein, red granules：50 parts~60 parts of potassium feldspar；3 parts~6 parts of zinc oxide；3 parts~4 parts of strontium carbonate；Red 30 parts~35 parts of base；Black particle：50 parts~60 parts of potassium feldspar；3 parts~6 parts of zinc oxide；3 parts~4 parts of strontium carbonate；30 parts~35 parts of fast black base.The present invention can make the glaze no longer as monochrome particles glaze is so dull, and be full of art atmosphere.
Description
Technical field
The present invention relates to a kind of colorful plus grain reaction glaze and preparation method thereof.
Background technology
At present, the single colour glaze that in the market occurs adds the glaze of grain very much, and trend is led in field on one point, but mostly
Add the glaze of grain, all succinctly, can not to meet requirement.
The content of the invention
The technical problems to be solved by the invention are the defects of overcoming the prior art, there is provided a kind of colorful plus grain reaction glaze,
It can make the glaze no longer as monochrome particles glaze is so dull, and be full of art atmosphere.
In order to solve the above technical problems, the technical scheme is that：A kind of colorful plus grain reaction glaze, used in it
The component and each component mass parts of glaze are as follows：
35 parts~38 parts of potassium feldspar；10 parts~13 parts of bone ash；3 parts~6 parts of talcum；6 parts~8 parts of Jiepai clay；Barium carbonate 15
Part~18 parts；4 parts~6 parts of zinc oxide；10 parts~13 parts of zirconium silicate；Red granules：10 parts；Black particle：5 parts；Wherein,
Red granules：50 parts~60 parts of potassium feldspar；3 parts~6 parts of zinc oxide；3 parts~4 parts of strontium carbonate；Red 30 parts of base~
35 parts；
Black particle：50 parts~60 parts of potassium feldspar；3 parts~6 parts of zinc oxide；3 parts~4 parts of strontium carbonate；30 parts of fast black base~
35 parts.
Present invention also offers a kind of preparation method of colorful plus grain reaction glaze, the step of method, is as follows：
A) stock up according to each component and each component mass parts；
B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of the Zong Wu Liao ︰ Qiu ︰ water in glaze in addition to red granules and black particle,
When wet ball grinding 12~14 is small, after total material after ball milling crosses 200 mesh sieves, the red granules of corrresponding quality part and black are then added
Coloured particles, are modulated into 53~54 Baume concentration, glaze are made, and take clean base substrate leaching glaze；
C) base substrate for having soaked glaze is put into roller kilns to form to fire in 1200 DEG C of oxidizing atmospheres.
After employing above-mentioned technical proposal, of the invention colorful plus grain reaction glaze, be by red granules, black particle,
Fired in 1200 DEG C of roller kilns, by the strong opaque of base glaze, and weak mobility, it is melt into a main body, make this
Glaze is no longer so dull as monochrome particles glaze, and is full of art atmosphere, is definitely worth product, which can be large quantities of
The production of amount, disclosure satisfy that the demand of domestic and international client, in following one or two years, may proceed to lead trend.
Embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, the present invention is made into
One step is described in detail.
Embodiment one
A kind of colorful plus grain reaction glaze, the component of glaze and each component mass parts are as follows used in it：
35 parts of potassium feldspar；10 parts of bone ash；3 parts of talcum；6 parts of Jiepai clay；15 parts of barium carbonate；4 parts of zinc oxide；Zirconium silicate 10
Part；Red granules：10 parts；Black particle：5 parts；Wherein,
Red granules：50 parts of potassium feldspar；3 parts of zinc oxide；3 parts of strontium carbonate；Red 30 parts of base；
Black particle：50 parts of potassium feldspar；3 parts of zinc oxide；3 parts of strontium carbonate；30 parts of fast black base.
The step of preparation method of a kind of colorful plus grain reaction glaze, method, is as follows：
A) stock up according to each component and each component mass parts；
B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of the Zong Wu Liao ︰ Qiu ︰ water in glaze in addition to red granules and black particle,
When wet ball grinding 12 is small, after total material after ball milling crosses 200 mesh sieves, the red granules and black of corrresponding quality part are then added
Grain, is modulated into 53~54 Baume concentration, glaze is made, and takes clean base substrate leaching glaze；
C) base substrate for having soaked glaze is put into roller kilns to form to fire in 1200 DEG C of oxidizing atmospheres.
Embodiment two
A kind of colorful plus grain reaction glaze, the component of glaze and each component mass parts are as follows used in it：
38 parts of potassium feldspar；13 parts of bone ash；6 parts of talcum；8 parts of Jiepai clay；18 parts of barium carbonate；6 parts of zinc oxide；Zirconium silicate 13
Part；Red granules：10 parts；Black particle：5 parts；Wherein,
Red granules：60 parts of potassium feldspar；6 parts of zinc oxide；4 parts of strontium carbonate；Red 35 parts of base；
Black particle：60 parts of potassium feldspar；6 parts of zinc oxide；4 parts of strontium carbonate；35 parts of fast black base.
The step of preparation method of a kind of colorful plus grain reaction glaze, method, is as follows：
A) stock up according to each component and each component mass parts；
B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of the Zong Wu Liao ︰ Qiu ︰ water in glaze in addition to red granules and black particle,
When wet ball grinding 14 is small, after total material after ball milling crosses 200 mesh sieves, the red granules and black of corrresponding quality part are then added
Grain, is modulated into 53~54 Baume concentration, glaze is made, and takes clean base substrate leaching glaze；
C) base substrate for having soaked glaze is put into roller kilns to form to fire in 1200 DEG C of oxidizing atmospheres.
Embodiment three
A kind of colorful plus grain reaction glaze, the component of glaze and each component mass parts are as follows used in it：
36 parts of potassium feldspar；12 parts of bone ash；4 parts of talcum；7 parts of Jiepai clay；16 parts of barium carbonate；5 parts of zinc oxide；Zirconium silicate 11
Part；Red granules：10 parts；Black particle：5 parts；Wherein,
Red granules：55 parts of potassium feldspar；4.5 parts of zinc oxide；3.5 parts of strontium carbonate；Red 32 parts of base；
Black particle：55 parts of potassium feldspar；4.5 parts of zinc oxide；3.5 parts of strontium carbonate；32 parts of fast black base.
The step of preparation method of a kind of colorful plus grain reaction glaze, method, is as follows：
A) stock up according to each component and each component mass parts；
B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of the Zong Wu Liao ︰ Qiu ︰ water in glaze in addition to red granules and black particle,
When wet ball grinding 13 is small, after total material after ball milling crosses 200 mesh sieves, the red granules and black of corrresponding quality part are then added
Grain, is modulated into 53~54 Baume concentration, glaze is made, and takes clean base substrate leaching glaze；
C) base substrate for having soaked glaze is put into roller kilns to form to fire in 1200 DEG C of oxidizing atmospheres.
Colorful plus grain reaction glaze prepared by three above embodiment passes through it has been observed that mobility is appropriate, and opaque is good, color
It is color various, meet the requirements.
Particular embodiments described above, has carried out the purpose of the present invention, technical solution and beneficial effect further in detail
Describe in detail it is bright, it should be understood that the foregoing is merely the present invention specific embodiment, be not intended to limit the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution, improvement and etc. done, should be included in the guarantor of the present invention
Within the scope of shield.
Claims (2)
1. a kind of colorful plus grain reaction glaze, it is characterised in that the component of glaze and each component mass parts are as follows used in it：
35 parts~38 parts of potassium feldspar；10 parts~13 parts of bone ash；3 parts~6 parts of talcum；6 parts~8 parts of Jiepai clay；15 parts of barium carbonate~
18 parts；4 parts~6 parts of zinc oxide；10 parts~13 parts of zirconium silicate；Red granules：10 parts；Black particle：5 parts；Wherein,
Red granules：50 parts~60 parts of potassium feldspar；3 parts~6 parts of zinc oxide；3 parts~4 parts of strontium carbonate；Red 30 parts~35 parts of base；
Black particle：50 parts~60 parts of potassium feldspar；3 parts~6 parts of zinc oxide；3 parts~4 parts of strontium carbonate；30 parts~35 parts of fast black base.
2. a kind of preparation method of as claimed in claim 1 colorful plus grain reaction glaze, it is characterised in that the step of method is as follows：
A) stock up according to each component and each component mass parts；
B) according to 1.6 ︰ 0.6 of mass ratio=1 ︰ of the Zong Wu Liao ︰ Qiu ︰ water in glaze in addition to red granules and black particle, wet method
When ball milling 12~14 is small, after total material after ball milling crosses 200 mesh sieves, the red granules and black of corrresponding quality part are then added
Grain, is modulated into 53~54 Baume concentration, glaze is made, and takes clean base substrate leaching glaze；
C) base substrate for having soaked glaze is put into roller kilns to form to fire in 1200 DEG C of oxidizing atmospheres.