CN108017135A - 一种翠熔体活化水球的制作方法及使用方法 - Google Patents
一种翠熔体活化水球的制作方法及使用方法 Download PDFInfo
- Publication number
- CN108017135A CN108017135A CN201711246488.6A CN201711246488A CN108017135A CN 108017135 A CN108017135 A CN 108017135A CN 201711246488 A CN201711246488 A CN 201711246488A CN 108017135 A CN108017135 A CN 108017135A
- Authority
- CN
- China
- Prior art keywords
- crushed
- mesh
- emerald green
- melt
- water polo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种翠熔体活化水球的制作方法及使用方法。它包括以下步骤：a、将翠熔体晶体粉碎至700‑1100目；b、将陶土粉碎至700‑1100目，活性炭粉碎至700‑1100目；c、将陶土按65‑69%，翠熔体晶体按25‑30%，活性炭1‑10%混合配比；d、将上述三种材料按比例放进气流粉碎机，粉碎至850目形成功能粉末，制成所需形状后在800‑1000℃下烧结成型得到翠熔体活化水球。其优点在于：将其投放在水中，增强了人体的血液循环，加快新陈代谢，增强了人体免疫力，提高了负离子浓度，结合人体细胞，排出人体内的毒素，增强了人体的抗菌能力和免疫能力，该材料无放射性物质，无重金属，不但有效改善了水质，而且还具有抗菌、去污和除异味的作用，具备了有效预防各种疾病的功能。
Description
技术领域
本发明涉及一种活化水质处理物质的制作方法，具体地说是一种翠熔体活化水球的制作方法及使用方法。
背景技术
饮用水对人体的健康至关重要，目前市场上已有各种矿泉水、纯净水、离子水、营养水等产品，当然还具有用来改善水质的功能装置（如：通过电子激化改变水分子的装置），但是现有的这些饮用水处理方式大多数存在着功能单一或者成本高等缺陷。
翠熔体是由多种矿石纯晶体（已去除杂质），经1200℃以上的高温溶质成墨绿色的新型晶体，通过特殊物理加工，利用超气流粉碎机提纯精良而成的粉末状材料，它具有消除异味和达到抑菌的效果，还具有能降低三高、减肥、有预防脂肪肝、中风和癌症的功效，但是尚无将其用于水质处理材料的记载。
发明内容
本发明要解决的技术问题是提供一种能够将翠熔体材料制成活化水球，从而有效改善水质并起到有效预防各种疾病功能的翠熔体活化水球的制作方法及使用方法。
为了解决上述技术问题，本发明的翠熔体的活化水球的制作方法，包括以下步骤：
a、将翠熔体晶体粉碎至700-1100目；
b、将陶土粉碎至700-1100目，活性炭粉碎至700-1100目；
c、将陶土按65-69%，翠熔体晶体按25-30%，活性炭1-10%混合配比；
d、将上述三种材料按比例放进气流粉碎机，粉碎至850目形成功能粉末，制成所需形状后在800-1000℃下烧结成型得到翠熔体活化水球。
所述翠熔体是由多种已去除杂质的矿石纯晶体，经过1200-1350℃的高温溶质成墨绿色的晶体。
一种如上述活化水球的使用方法，将制成的翠熔体活化水球加入酒类材料中使用。
本发明的优点在于：
通过采用上述方法将翠熔体材料制成的活化水球，将其投放在水中，增强了人体的血液循环，加快新陈代谢，增强了人体免疫力，提高了负离子浓度，结合人体细胞，排出人体内的毒素，增强了人体的抗菌能力和免疫能力，另外，该材料无放射性物质，无重金属，不但有效改善了水质，而且还具有抗菌、去污和除异味的作用，具备了有效预防各种疾病的功能。
具体实施方式
下面结合具体实施方式，对本发明的翠熔体活化水球的制作方法作进一步详细说明。
实施例一：
本实施例的翠熔体的活化水球的制作方法，包括以下步骤：
a、翠熔体是由多种已去除杂质的矿石纯晶体，经过1200℃以上的高温溶质成墨绿色的晶体。
b、将翠熔体晶体粉碎至700目；
c、将陶土粉碎至700目，活性炭粉碎至700目；
d、将陶土按65%，翠熔体晶体按25%，活性炭10%混合配比；
e、将上述三种材料按比例放进气流粉碎机，粉碎至800目形成功能粉末，制成所需形状后在800℃下烧结成型得到翠熔体活化水球。
实施例二：
本实施例的翠熔体活化水球的制作方法，包括以下步骤：
a、将翠熔体晶体粉碎至800目；
b、将陶土粉碎至800目，活性炭粉碎至800目；
c、将陶土按67%，翠熔体晶体按30%，活性炭3%混合配比；
d、将上述三种材料按比例放进气流粉碎机，粉碎至850目形成功能粉末，制成所需形状后在850℃下烧结成型得到翠熔体活化水球。
另外，需要重点说明的是上述的翠熔体是采用如背景技术中所描述的由多种矿石纯晶体（已去除杂质），经1300℃的高温溶质成墨绿色的新型晶体并经过物理加工后利用超气流粉碎机提纯精良而成的粉末状材料。
经过实践证明，采用本实施例所获得的活化水球放置在水中，随着温度的高低改变水分子的活性功能能够使水制结构得到改变，水分子解力高达38赫兹，（检测JY/T007-196），从而使水分子团得到改善（大分子团改为小分子团），其作用可增强人体的血液循环，加快新陈代谢，增强人体免疫力，并可提高负离子浓度，结合人体细胞，排出人体内的毒素，增强人体的抗菌能力和免疫能力，另外，获得的活性水球具有抗菌、去污和除异味的作用，对白色念珠球菌、黄金色葡萄球菌、大肠杆菌、肺炎克雷白氏菌的抑菌能力可达到99%，并且去除甲醛、氨气、硫化氢气体的能力达到90%。
实施例三：
本实施例的翠熔体的活化水球的制作方法，包括以下步骤：
a、翠熔体是由多种已去除杂质的矿石纯晶体，经过1350℃的高温溶质成墨绿色的晶体；
b、将翠熔体晶体粉碎至1100目；
c、将陶土粉碎至1100目，活性炭粉碎至1100目；
d、将陶土按69%，翠熔体晶体按30%，活性炭1%混合配比；
e、将上述三种材料按比例放进气流粉碎机，粉碎至1200目形成功能粉末，制成所需形状后在1000℃下烧结成型得到翠熔体活化水球。
经过本实施例获得的活性水球具有抗菌、去污和除异味的作用，对白色念珠球菌、黄金色葡萄球菌、大肠杆菌、肺炎克雷白氏菌的抑菌能力可达到99%，并且去除甲醛、氨气、硫化氢气体的能力达到85%。
实施例四：
经过申请人的研究发现，将制成的翠熔体活化水球加入酒类材料中使用具有意外的效果，经过实践证明，通过将翠熔体活化水球加入酒类材料中后，一方面，能够迅速中和酒的PH值，PH值为7-7.5，另外一方面，使酒的纯度提高，再一方面，使酒的分子状态变小，还使酒更加浓香，增进了口感。
Claims (3)
1.一种翠熔体的活化水球的制作方法，其特征在于，包括以下步骤：
a、将翠熔体晶体粉碎至700-1100目；
b、将陶土粉碎至700-1100目，活性炭粉碎至700-1100目；
c、将陶土按65-69%，翠熔体晶体按25-30%，活性炭1-10%混合配比；
d、将上述三种材料按比例放进气流粉碎机，粉碎至800-1200目形成功能粉末，制成所需形状后在800-1000℃下烧结成型得到翠熔体活化水球。
2.按照权利要求1所述的翠熔体的活化水球的制作方法，其特征在于：所述翠熔体是由多种已去除杂质的矿石纯晶体，经过1200-1350℃的高温溶质成墨绿色的晶体。
3.一种如权利要求1或2所述活化水球的使用方法，其特征在于：将制成的翠熔体活化水球加入酒类材料中使用。