CN107841064A - 一种pvc台布塑料及其制备方法 - Google Patents

一种pvc台布塑料及其制备方法 Download PDF

Info

Publication number
CN107841064A
CN107841064A CN201711128722.5A CN201711128722A CN107841064A CN 107841064 A CN107841064 A CN 107841064A CN 201711128722 A CN201711128722 A CN 201711128722A CN 107841064 A CN107841064 A CN 107841064A
Authority
CN
China
Prior art keywords
parts
pvc
tablecloths
counterdie
stabilizer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711128722.5A
Other languages
English (en)
Inventor
贺海兰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Foshan Gaoming District Productivity Promotion Center
Original Assignee
Foshan Gaoming District Productivity Promotion Center
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Foshan Gaoming District Productivity Promotion Center filed Critical Foshan Gaoming District Productivity Promotion Center
Priority to CN201711128722.5A priority Critical patent/CN107841064A/zh
Publication of CN107841064A publication Critical patent/CN107841064A/zh
Pending legal-status Critical Current

Abstract

本发明所述一种PVC台布塑料及其制作方法，底膜包括：PVC粉77‑82份，DOP 20‑30份，碳酸钙8‑18份，稳定剂2‑3份，发泡剂1‑2份，大豆油3‑6份，二氧化钛0.5‑2份，功能助剂0.3‑0.6份，颜料0.1‑0.2份；面膜包括：PVC粉70‑80份，DOP 25‑30份，碳酸钙10‑20份，稳定剂2‑3份，大豆油5‑12份，二氧化钛0.5‑2份，功能助剂0.6‑0.8份，颜料0.1‑0.2份，通过该成分配比，使台布塑料安全环保，对环境污染小，使用寿命长，耐磨和抗菌性好。

Description

一种PVC台布塑料及其制备方法
技术领域
本发明属于塑料台布技术领域，具体地说，涉及一种PVC台布塑料及其制作方法。
背景技术
台布，是一类覆盖于台、桌面上用以防污或增加美观的纺织品。
塑料台布多以PVC材质的为主，PVC台布具有颜色和花型多样，易搭配多种装修风格，是软装潢不错的选择。这款桌布耐脏，易清洗，易携带。使用寿命长，不易褪色、掉色。PVC台布早在欧美国家非常流行，近年来日本及东南亚国家由于天气较热，PVC台布在这些国家也开始流行，在我国因其价廉物美的特性也受到众多家庭的欢迎。
但是，老化现象是PVC台布的一大缺陷，因此提高PVC台布的抗老化性能成为研究和开发PVC台布产品的一个重要方向，而且现有的PVC台布只具有截留细菌的功能而没有抑菌或杀菌性能，在长时间运行的情况下容易受生物污染，从而降低了PVC台布的使用寿命。
同时，PVC台布给人民生活带来方便，给人类也带来了较大的环保隐患，随着人民生活水平、环保意识的不断提高，人民对PVC台布的环保要求也越来越高。
发明内容
本发明克服了现有技术中的缺点，提供了一种PVC台布塑料及其制作方法，其安全环保，成本低且耐用可靠。
为了解决上述技术问题，本发明是通过以下技术方案实现的：
一种PVC台布塑料，包括有底膜和面膜，
底膜包括：PVC粉77-82份，DOP 20-30份，碳酸钙8-18份，稳定剂2-3份，发泡剂1-2份，大豆油3-6份，二氧化钛0.5-2份，功能助剂0.3-0.6份，颜料0.1-0.2份；
面膜包括：PVC粉70-80份，DOP 25-30份，碳酸钙10-20份，稳定剂2-3份，大豆油5-12份，二氧化钛0.5-2份，功能助剂0.6-0.8份，颜料0.1-0.2份。
进一步，还添加所述PVC粉质量分数0.05～0.1％的土茯苓粉。
进一步，还添加所述PVC粉质量分数0.03～0.05％的天麻粉。
进一步，还添加所述PVC粉质量分数0.02～0.04％的硼砂。
进一步，所述稳定剂为钙锌类稳定剂。
进一步，所述功能助剂为苯甲基硅油。
一种PVC台布的制备方法，包括以下步骤：
1)将底膜的PVC粉过筛后按比例加入其余各种组分，高速搅拌，之后经密炼机塑化；
2)再经二次开炼机塑化，接着经挤出机输送至胶布机进行压延形成底膜，同理制得面膜；
3)将步骤中的底膜和面膜高温贴合；
4)将步骤2)中的透明膜经印花机后形成透明印花膜，再将透明印花膜覆盖于步骤中的面膜上方，且高温贴合，最后再经压纹、冷却、收卷。
与现有技术相比，本发明的有益效果是：
本发明所述一种PVC台布塑料及其制作方法，底膜包括：PVC粉77-82份，DOP 20-30份，碳酸钙8-18份，稳定剂2-3份，发泡剂1-2份，大豆油3-6份，二氧化钛0.5-2份，功能助剂0.3-0.6份，颜料0.1-0.2份；面膜包括：PVC粉70-80份，DOP 25-30份，碳酸钙10-20份，稳定剂2-3份，大豆油5-12份，二氧化钛0.5-2份，功能助剂0.6-0.8份，颜料0.1-0.2份，通过该成分配比，使台布塑料安全环保，对环境污染小，使用寿命长，耐磨和抗菌性好。
具体实施方式
以下对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
一种PVC台布塑料，包括有底膜和面膜，
底膜包括：PVC粉80份，DOP 22份，碳酸钙12份，稳定剂2.4份，发泡剂1.3份，大豆油5份，二氧化钛1份，功能助剂0.52份，颜料0.15份；
面膜包括：PVC粉74份，DOP 28份，碳酸钙17份，稳定剂2.6份，大豆油8份，二氧化钛1.3份，功能助剂0.7份，颜料0.16份，稳定剂为钙锌类稳定剂，功能助剂为苯甲基硅油
还添加PVC粉质量分数0.07％的土茯苓粉，0.04％的天麻粉，0.03％的硼砂。
一种PVC台布的制备方法，包括以下步骤：
1)将底膜的PVC粉过筛后按比例加入其余各种组分，高速搅拌，之后经密炼机塑化；
2)再经二次开炼机塑化，接着经挤出机输送至胶布机进行压延形成底膜，同理制得面膜；
3)将步骤中的底膜和面膜高温贴合；
4)将步骤2)中的透明膜经印花机后形成透明印花膜，再将透明印花膜覆盖于步骤中的面膜上方，且高温贴合，最后再经压纹、冷却、收卷。
5)对得到的PVC台布塑料进行性能测试，其结果如下：
最后应说明的是：以上仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换，但是凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (7)

1.一种PVC台布塑料，其特征在于，包括有底膜和面膜，
所述底膜包括：PVC粉77-82份，DOP 20-30份，碳酸钙8-18份，稳定剂2-3份，发泡剂1-2份，大豆油3-6份，二氧化钛0.5-2份，功能助剂0.3-0.6份，颜料0.1-0.2份；
所述面膜包括：PVC粉70-80份，DOP 25-30份，碳酸钙10-20份，稳定剂2-3份，大豆油5-12份，二氧化钛0.5-2份，功能助剂0.6-0.8份，颜料0.1-0.2份。
2.根据权利要求1所述一种PVC台布塑料，其特征在于，还添加所述PVC粉质量分数0.05～0.1％的土茯苓粉。
3.根据权利要求1所述一种PVC台布，其特征在于，还添加所述PVC粉质量分数0.03～0.05％的天麻粉。
4.根据权利要求1所述一种PVC台布，其特征在于，还添加所述PVC粉质量分数0.02～0.04％的硼砂。
5.根据权利要求1所述一种PVC台布，其特征在于，所述稳定剂为钙锌类稳定剂。
6.根据权利要求1所述一种PVC台布，其特征在于，所述功能助剂为苯甲基硅油。
7.根据权利要求1所述一种PVC台布的制备方法，其特征在于，包括以下步骤：
1)将底膜的PVC粉过筛后按比例加入其余各种组分，高速搅拌，之后经密炼机塑化；
2)再经二次开炼机塑化，接着经挤出机输送至胶布机进行压延形成底膜，同理制得面膜；
3)将步骤中的底膜和面膜高温贴合；
4)将步骤2)中的透明膜经印花机后形成透明印花膜，再将透明印花膜覆盖于2)步骤中的面膜上方，且高温贴合，最后再经压纹、冷却、收卷。
CN201711128722.5A 2017-11-15 2017-11-15 一种pvc台布塑料及其制备方法 Pending CN107841064A (zh)