CN107829569A - 砌筑墙体裂缝的处理方法 - Google Patents
砌筑墙体裂缝的处理方法 Download PDFInfo
- Publication number
- CN107829569A CN107829569A CN201711054257.5A CN201711054257A CN107829569A CN 107829569 A CN107829569 A CN 107829569A CN 201711054257 A CN201711054257 A CN 201711054257A CN 107829569 A CN107829569 A CN 107829569A
- Authority
- CN
- China
- Prior art keywords
- crack
- masonry panel
- shaped groove
- shaped
- unit method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种砌筑墙体裂缝的处理方法,包括以下步骤:沿砌筑墙体裂缝将其两侧的抹灰层铲除直至露出砌筑墙体;沿砌筑墙体裂缝切割多个V形槽,V形槽与裂缝垂直,V形槽的两端钻定位孔以插入U形拉结筋;在V形槽的两端定位孔中注入水泥浆,将U形拉结筋两侧弯起部分插入裂缝两侧的定位孔内,使U形拉结筋插入孔内部分与水泥浆形成锚固,U形拉结筋主体埋入V形槽内,采用砂浆嵌补裂缝并覆盖V形槽,并初步抹平;沿裂缝范围铺贴钢丝网以覆盖整个砌筑墙体裂缝,通过水泥砂浆找平后,采用乳胶腻子将修补部位抹平至与原有墙面一样平。本发明提出的砌筑墙体裂缝的处理方法,实现了修补裂缝并对裂缝的发展起一定的抑制作用。
Description
技术领域
本发明涉及建筑施工技术领域,尤其涉及一种砌筑墙体裂缝的处理方法。
背景技术
裂缝主要有混凝土墙面裂缝和砌体墙面裂缝。砌体墙面裂缝主要是由于不均匀地基沉降,温度变化等原因引起,还有部分是由于外力引起,如大锤狠砸墙面等。这种开裂不仅仅是抹面层开裂,往往内部砌筑墙体的砌体也一起开裂。
现有施工过程中处理此类裂缝一般采用先铲除裂缝周边抹面层,砂浆填缝,然后贴布,面层抹浆修补的方式。此种方式对于较小较浅墙面裂缝有效,但对于较深较长的墙面裂缝,采用此方法后仅短期内有效,之后仍会在原裂缝位置及裂缝延展方向产生新的裂缝。由于不均匀地基沉降,温度变化影响是一个长期的过程。但这个过程前期变化会比较大,之后会逐步趋于平缓,趋于平缓后裂缝修补效果会比较好。但我们无法判断前期变化何时趋于平缓,由于施工的需要,往往发现裂缝后,需要短期内进行裂缝处理。
采用本发明的裂缝处理方法,通过对裂缝两侧墙体采取一定的约束,能有效控制原有裂缝位置新的裂缝的产生,对裂缝的发展有一定的抑制作用,增强墙体的强度,同时无需对建筑沉降是否稳定进行预判,减小外力及内力对裂缝的影响,适用于仍处于裂缝扩大趋势期的砌筑墙体裂缝。
发明内容
本发明的主要目的在于提供一种砌筑墙体裂缝的处理方法,旨在修补裂缝并对裂缝的发展起一定的抑制作用。
为实现上述目的,本发明提供一种砌筑墙体裂缝的处理方法,包括以下步骤:
沿砌筑墙体裂缝将其两侧的抹灰层铲除直至露出砌筑墙体;
沿砌筑墙体裂缝切割多个V形槽,多个槽在砌筑墙体裂缝长度方向均匀分布,V形槽与裂缝垂直,V形槽的两端钻定位孔以插入U形拉结筋;
在V形槽的两端定位孔中注入水泥浆,将U形拉结筋两侧弯起部分插入裂缝两侧的定位孔内,使U形拉结筋插入孔内部分与水泥浆形成锚固,U形拉结筋主体埋入V形槽内,采用砂浆嵌补裂缝并覆盖V形槽,并初步抹平;
沿裂缝范围铺贴钢丝网以覆盖整个砌筑墙体裂缝,通过水泥砂浆找平后,采用乳胶腻子将修补部位抹平至与原有墙面一样平。
优选地,沿砌筑墙体裂缝将其两侧的抹灰层铲除时,铲除宽度为墙体裂缝两侧180mm-220mm范围,铲除表面抹灰层直至露出砌筑墙体后,对铲除抹灰层后的外露部分砌体进行充分浇水湿润。
优选地,在砌筑墙体裂缝长度方向每间隔300~400mm切280-320mm长的V型槽,槽深不小于10mm,定位孔直径为8-12mm,孔深为70-90mm。
优选地,V形槽两侧的定位孔以裂缝为中心,两定位孔间距离与U形拉结筋长度相等以便于其插入。
优选地,采用比原砌筑砂浆高一等级的砂浆嵌补裂缝并覆盖V形槽。
优选地,U形拉结筋的钢筋主体埋入V形槽内时,不高于V形槽高度。
优选地,钢丝网的铺贴宽度不小于200mm。
优选地,钢丝网网格面积为15mm×15mm。
优选地,沿裂缝范围铺贴钢丝网以覆盖整个砌筑墙体裂缝,通过水泥砂浆找平后,满贴尼龙网格布,再用乳胶腻子将修补部位抹平。
本发明提出的砌筑墙体裂缝的处理方法,其有益效果如下。
1.采用U形拉结筋拉结对裂缝墙体加固,类似于在墙面上钉订书钉的方式加固墙体,使墙体裂缝部位强度增大,恢复裂缝墙体整体性。此加固形式在墙体裂缝较大,裂缝发展趋势不明的情况下使裂缝墙体重新恢复整体性,对裂缝的发展趋势有抑制作用。
2.采用U形拉结筋对裂缝墙体进行对拉加固,采用钢丝网沿裂缝范围铺贴,满贴高强尼龙网格布这三种裂缝加强措施,能有效地防止裂缝的再产生。
3.采用垂直于裂缝用便携式切割机切V型槽,在V型槽两端等同于拉结筋长度位置钻孔,在孔内注入水泥浆,将U形拉结筋插入孔内,形成锚固拉结。此方法处理复杂裂缝操作性强,无需拆除裂缝墙体即能达到处理效果,能有效避免重复施工,其施工成本低。
附图说明
图1为本发明砌筑墙体裂缝的处理方法的流程示意图;
图2为本发明砌筑墙体裂缝的处理方法在未处理前裂缝的结构示意图;
图3为本发明砌筑墙体裂缝的处理方法在铲除抹灰层后的结构示意图;
图4为本发明砌筑墙体裂缝的处理方法在切割V形槽后的结构示意图;
图5为本发明砌筑墙体裂缝的处理方法在步骤S30完成后的结构示意图;
图6为本发明砌筑墙体裂缝的处理方法在注浆后的结构示意图;
图7为本发明砌筑墙体裂缝的处理方法在铺贴钢丝网后的结构示意图;
图8为本发明砌筑墙体裂缝的处理方法在铺贴钢丝网并找平后的结构示意图;
图9为本发明砌筑墙体裂缝的处理方法在满贴尼龙网格布后的结构示意图;
图10为本发明砌筑墙体裂缝的处理方法在采用乳胶腻子抹平后的结构示意图;
图11为本发明砌筑墙体裂缝的处理方法中U形拉结筋的结构示意图;
图中,1-V形槽,2-U形拉结筋,3-钢丝网,4-尼龙网格布。
本发明目的的实现、功能特点及优点将结合实施例,参照附图做进一步说明。
具体实施方式
应当理解,此处所描述的具体实施例仅仅用以解释本发明,并不用于限定本发明。
需要说明的是,在本发明的描述中,术语“横向”、“纵向”、“上”、“下”、“前”、“后”、“左”、“右”、“竖直”、“水平”、“顶”、“底”、“内”、“外”等指示的方位或位置关系为基于附图所示的方位或位置关系,仅是为了便于描述本发明和简化描述,并不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作,因此不能理解为对本发明的限制。
参照图1至图11,本优选实施例中,一种砌筑墙体裂缝的处理方法,包括以下步骤:
步骤S10,沿砌筑墙体裂缝将其两侧的抹灰层铲除直至露出砌筑墙体;
步骤S20,沿砌筑墙体裂缝切割多个V形槽1,多个槽在砌筑墙体裂缝长度方向均匀分布,V形槽1与裂缝垂直,V形槽1的两端钻定位孔以插入U形拉结筋2;
步骤S30,在V形槽1的两端定位孔中注入水泥浆,将U形拉结筋2两侧弯起部分插入裂缝两侧的定位孔内,使U形拉结筋2插入孔内部分与水泥浆形成锚固,U形拉结筋2主体埋入V形槽1内,采用砂浆嵌补裂缝并覆盖V形槽1,并初步抹平;
步骤S40,沿裂缝范围铺贴钢丝网3以覆盖整个砌筑墙体裂缝,通过水泥砂浆找平后,采用乳胶腻子将修补部位抹平至与原有墙面一样平。
步骤S10中,沿砌筑墙体裂缝将其两侧的抹灰层铲除时,铲除宽度为墙体裂缝两侧180mm-220mm范围,铲除表面抹灰层直至露出砌筑墙体后,对铲除抹灰层后的外露部分砌体进行充分浇水湿润。
本实施例中,参照图11,采用Ф6热轧钢筋制作U形拉结筋2,U形拉结筋2的数量按裂缝长度300~400mm间距均匀布置计算数量,U形拉结筋2的拉结长度300mm,两端弯起长度60mm,用于裂缝两端砌体拉结。
步骤S20中,采用小型便携式切割机在砌筑墙体裂缝长度方向每间隔300~400mm切280-320mm(本实施例中为300mm,下同)长的V型槽,槽深不小于10mm,定位孔直径为8-12mm(10mm),孔深为70-90mm(80mm)。V形槽1两侧的定位孔以裂缝为中心,两定位孔间距离与U形拉结筋2长度相等以便于其插入。两定位孔距裂缝约150mm,两定位孔间距离为300mm,
步骤S30中,采用比原砌筑砂浆高一等级的砂浆嵌补裂缝并覆盖V形槽1。U形拉结筋2的钢筋主体埋入V形槽1内时,不高于V形槽1高度。
步骤S40中,参照图7,钢丝网3的铺贴宽度不小于200mm。钢丝网3网格面积为15mm×15mm。沿裂缝范围铺贴钢丝网3以覆盖整个砌筑墙体裂缝,通过水泥砂浆找平后,满贴尼龙网格布4(采用高强度尼龙网格布4),再用乳胶腻子将修补部位抹平。
本实施例提出的砌筑墙体裂缝的处理方法,其有益效果如下。
1.采用U形拉结筋2拉结对裂缝墙体加固,类似于在墙面上钉订书钉的方式加固墙体,使墙体裂缝部位强度增大,恢复裂缝墙体整体性。此加固形式在墙体裂缝较大,裂缝发展趋势不明的情况下使裂缝墙体重新恢复整体性,对裂缝的发展趋势有抑制作用。
2.采用U形拉结筋2对裂缝墙体对拉加固,采用钢丝网3沿裂缝范围铺贴,满贴高强尼龙网格布4这三种裂缝加强措施,能有效地防止裂缝的再产生。
3.采用垂直于裂缝用便携式切割机切V型槽,在V型槽两端等同于拉结筋长度位置钻孔,在孔内注入水泥浆,将U形拉结筋2插入孔内,形成锚固拉结。此方法处理复杂裂缝操作性强,无需拆除裂缝墙体即能达到处理效果,能有效避免重复施工,其施工成本低。
以上仅为本发明的优选实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书及附图内容所作的等效结构变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (9)
1.一种砌筑墙体裂缝的处理方法,其特征在于,包括以下步骤:
沿砌筑墙体裂缝将其两侧的抹灰层铲除直至露出砌筑墙体;
沿砌筑墙体裂缝切割多个V形槽,多个槽在砌筑墙体裂缝长度方向均匀分布,V形槽与裂缝垂直,V形槽的两端钻定位孔以插入U形拉结筋;
在V形槽的两端定位孔中注入水泥浆,将U形拉结筋两侧弯起部分插入裂缝两侧的定位孔内,使U形拉结筋插入孔内部分与水泥浆形成锚固,U形拉结筋主体埋入V形槽内,采用砂浆嵌补裂缝并覆盖V形槽,并初步抹平;
沿裂缝范围铺贴钢丝网以覆盖整个砌筑墙体裂缝,通过水泥砂浆找平后,采用乳胶腻子将修补部位抹平至与原有墙面一样平。
2.如权利要求1所述的砌筑墙体裂缝的处理方法,其特征在于,沿砌筑墙体裂缝将其两侧的抹灰层铲除时,铲除宽度为墙体裂缝两侧180mm-220mm范围,铲除表面抹灰层直至露出砌筑墙体后,对铲除抹灰层后的外露部分砌体进行充分浇水湿润。
3.如权利要求1所述的砌筑墙体裂缝的处理方法,其特征在于,在砌筑墙体裂缝长度方向每间隔300~400mm切280-320mm长的V型槽,槽深不小于10mm,定位孔直径为8-12mm,孔深为70-90mm。
4.如权利要求1所述的砌筑墙体裂缝的处理方法,其特征在于,V形槽两侧的定位孔以裂缝为中心,两定位孔间距离与U形拉结筋长度相等以便于其插入。
5.如权利要求1所述的砌筑墙体裂缝的处理方法,其特征在于,采用比原砌筑砂浆高一等级的砂浆嵌补裂缝并覆盖V形槽。
6.如权利要求1所述的砌筑墙体裂缝的处理方法,其特征在于,U形拉结筋的钢筋主体埋入V形槽内时,不高于V形槽高度。
7.如权利要求1所述的砌筑墙体裂缝的处理方法,其特征在于,钢丝网的铺贴宽度不小于200mm。
8.如权利要求7所述的砌筑墙体裂缝的处理方法,其特征在于,钢丝网网格面积为15mm×15mm。
9.如权利要求1至8中任意一项所述的砌筑墙体裂缝的处理方法,其特征在于,沿裂缝范围铺贴钢丝网以覆盖整个砌筑墙体裂缝,通过水泥砂浆找平后,满贴尼龙网格布,再用乳胶腻子将修补部位抹平。