CN107629408A - 一种温度传感器用环氧树脂的制造工艺 - Google Patents
一种温度传感器用环氧树脂的制造工艺 Download PDFInfo
- Publication number
- CN107629408A CN107629408A CN201710829582.8A CN201710829582A CN107629408A CN 107629408 A CN107629408 A CN 107629408A CN 201710829582 A CN201710829582 A CN 201710829582A CN 107629408 A CN107629408 A CN 107629408A
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- temperature sensor
- manufacturing process
- polyurethane modified
- modified epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种温度传感器用环氧树脂的制造工艺,按重量份计,在反应釜中,加入聚氨酯改性环氧树脂,双酚A型环氧丙烯酸酯,甲基丙烯酸缩水甘油酯,乙烯基三(二甲基硅氧烷基)硅烷,金属镍螯合琼脂糖凝胶6FF,(2‑甲烷酰苯基)(1R,2S)‑1‑氨基‑2‑乙烯基环丙烷甲酸甲酯4‑甲基苯磺酸盐,混合均匀,在65‑90℃温度下反应4‑10h,得环氧树脂产品。
Description
技术领域
本发明涉及一种环氧树脂的制造工艺,尤其是一种温度传感器用环氧树脂的制造工艺。
背景技术
温度传感器(temperature transducer)是指能感受温度并转换成可用输出信号的传感器。温度传感器是温度测量仪表的核心部分,品种繁多。按测量方式可分为接触式和非接触式两大类,按照传感器材料及电子元件特性分为热电阻和热电偶两类。
环氧树脂可与多种类型的固化剂发生交联反应而形成不溶的具有三向网状结构的高聚物。凡分子结构中含有环氧基团的高分子化合物统称为环氧树脂。固化后的环氧树脂具有良好的物理、化学性能,它对金属和非金属材料的表面具有优异的粘接强度,介电性能良好,变形收缩率小,制品尺寸稳定性好,硬度高,柔韧性较好,对碱及大部分溶剂稳定,因而广泛应用于国防、国民经济各部门,作浇注、浸渍、层压料、粘接剂、涂料等用途。在温度传感器的制备中,环氧树脂大多覆盖于表面,有着封装,保护,绝缘的作用。
CN106461366A 公开了一种环氧树脂组合物,其用于形成构成静电电容型指纹传感器的绝缘膜,所述静电电容型指纹传感器具备基板、设置在所述基板上的检测电极和将所述检测电极密封的所述绝缘膜,所述环氧树脂组合物的特征在于,含有:环氧树脂(A);和无机填充剂(B)。
CN103328530B 公开了一种环氧树脂组合物,其特征是:由(A)环氧树脂、(B)1,4-环己烷二甲醇二缩水甘油醚、(C)咪唑类潜在性硬化剂、及(D)酚醛树脂组成;所述(B)1,4-环己烷二甲醇二缩水甘油醚的含量相对于所述(A)环氧树脂及所述(B)1,4-环己烷二甲醇二缩水甘油醚的合计质量为0.5~80质量%,所述(C)咪唑类潜在性硬化剂的含量相对于环氧树脂组合物的全部成分的合计质量为5~25质量%,所述(D)酚醛树脂的含量相对于环氧树脂组合物的全部成分的合计质量为0.5~25质量%。
温度传感器处于温度变化范围较大的使用环境中,测量物质并不限定于中性环境,同时可能应用于酸碱性环境中,因此容易产生开裂现象,影响测量数据的精确度和传感器的使用寿命,因此,研发一种耐化学性强,不易开裂的环氧树脂产品是有必要的。
发明内容
本发明的目的是:提供一种温度传感器用环氧树脂的制造工艺,克服上述缺点,其特征在于以下步骤:
按重量份计,在反应釜中,加入聚氨酯改性环氧树脂,双酚A型环氧丙烯酸酯,甲基丙烯酸缩水甘油酯,乙烯基三(二甲基硅氧烷基)硅烷,金属镍螯合琼脂糖凝胶6FF,(2-甲烷酰苯基)(1R,2S)-1-氨基-2-乙烯基环丙烷甲酸甲酯4-甲基苯磺酸盐,混合均匀,在65-90℃温度下反应4-10h,得环氧树脂产品。
所述的双酚A型环氧丙烯酸酯,其质量用量为聚氨酯改性环氧树脂的30-60%。
所述的甲基丙烯酸缩水甘油酯,其质量用量为聚氨酯改性环氧树脂的2-8%。
所述的乙烯基三(二甲基硅氧烷基)硅烷,其质量用量为聚氨酯改性环氧树脂的0.1-0.5%。
所述的金属镍螯合琼脂糖凝胶6FF,其质量用量为聚氨酯改性环氧树脂的0.5-1.5%。
所述的(2-甲烷酰苯基)(1R,2S)-1-氨基-2-乙烯基环丙烷甲酸甲酯4-甲基苯磺酸盐,其质量用量为聚氨酯改性环氧树脂的的0.01-0.1%。
所述的聚氨酯改性环氧树脂为市售产品,如东莞市雅德树脂新材料有限公司;双酚A型环氧丙烯酸酯为市售产品,如上海帅科化工有限公司生产的产品;甲基丙烯酸缩水甘油酯为市售产品,如湖南恒湖化工有限公司生产的产品;乙烯基三(二甲基硅氧烷基)硅烷为市售产品,如美西精细化工有限公司生产的产品;金属镍螯合琼脂糖凝胶6FF为市售产品,如上海抚生实业有限公司生产的产品;(2-甲烷酰苯基)(1R,2S)-1-氨基-2-乙烯基环丙烷甲酸甲酯4-甲基苯磺酸盐为市售产品,如石家庄斯迪亚诺精细化工有限公司生产的产品。
本发明的产品具有以下有益效果:
本发明所生产的环氧树脂组合物,其韧性较强,不易产生开裂的现象,耐化学性和耐热性优良,可以适应作为温度传感器封装的工作环境。
具体实施方式
实施例1
在反应釜中,加入聚氨酯改性环氧树脂100Kg,双酚A型环氧丙烯酸酯45Kg,甲基丙烯酸缩水甘油酯5Kg,乙烯基三(二甲基硅氧烷基)硅烷0.3Kg,金属镍螯合琼脂糖凝胶6FF1Kg,(2-甲烷酰苯基)(1R,2S)-1-氨基-2-乙烯基环丙烷甲酸甲酯4-甲基苯磺酸盐0.05Kg,混合均匀,在75℃温度下反应7h,得环氧树脂产品。
实施例2
在反应釜中,加入聚氨酯改性环氧树脂100Kg,双酚A型环氧丙烯酸酯30Kg,甲基丙烯酸缩水甘油酯2Kg,乙烯基三(二甲基硅氧烷基)硅烷0.1Kg,金属镍螯合琼脂糖凝胶6FF0.5Kg,(2-甲烷酰苯基)(1R,2S)-1-氨基-2-乙烯基环丙烷甲酸甲酯4-甲基苯磺酸盐0.01Kg,混合均匀,在65℃温度下反应4h,得环氧树脂产品。
实施例3
在反应釜中,加入聚氨酯改性环氧树脂100Kg,双酚A型环氧丙烯酸酯60Kg,甲基丙烯酸缩水甘油酯8Kg,乙烯基三(二甲基硅氧烷基)硅烷0.5Kg,金属镍螯合琼脂糖凝胶6FF1.5Kg,(2-甲烷酰苯基)(1R,2S)-1-氨基-2-乙烯基环丙烷甲酸甲酯4-甲基苯磺酸盐0.1Kg,混合均匀,在90℃温度下反应10h,得环氧树脂产品。
对比例1
不加入乙烯基三(二甲基硅氧烷基)硅烷,其他条件同实施例1。
对比例2
不加入金属镍螯合琼脂糖凝胶,其他条件同实施例1。
对比例3
不加入(2-甲烷酰苯基)(1R,2S)-1-氨基-2-乙烯基环丙烷甲酸甲酯4-甲基苯磺酸盐,其他条件同实施例1。
对比例4
直接采用聚氨酯改性环氧树脂。
实施例4
分别将实施例1-3与对比例1-4所生产的环氧树脂,参照标准GB/T7193-2008检验其延伸断裂率和冲击强度,并检验其耐热性。
表1 实施例1-3与对比例1-4所生产的环氧树脂性能指标。
Claims (6)
1.一种温度传感器用环氧树脂的制造工艺,其特征在于:在反应釜中,加入聚氨酯改性环氧树脂,双酚A型环氧丙烯酸酯,甲基丙烯酸缩水甘油酯,乙烯基三(二甲基硅氧烷基)硅烷,金属镍螯合琼脂糖凝胶6FF,(2-甲烷酰苯基)(1R,2S)-1-氨基-2-乙烯基环丙烷甲酸甲酯4-甲基苯磺酸盐,混合均匀,在65-90℃温度下反应4-10h,得环氧树脂产品。
2.根据权利要求1所述的一种温度传感器用环氧树脂的制造工艺,其特征在于:所述的双酚A型环氧丙烯酸酯,其质量用量为聚氨酯改性环氧树脂的30-60%。
3.根据权利要求1所述的一种温度传感器用环氧树脂的制造工艺,其特征在于:所述的甲基丙烯酸缩水甘油酯,其质量用量为聚氨酯改性环氧树脂的2-8%。
4.根据权利要求1所述的一种温度传感器用环氧树脂的制造工艺,其特征在于:所述的乙烯基三(二甲基硅氧烷基)硅烷,其质量用量为聚氨酯改性环氧树脂的0.1-0.5%。
5.根据权利要求1所述的一种温度传感器用环氧树脂的制造工艺,其特征在于:所述的金属镍螯合琼脂糖凝胶6FF,其质量用量为聚氨酯改性环氧树脂的0.5-1.5%。
6.根据权利要求1所述的一种温度传感器用环氧树脂的制造工艺,其特征在于:所述的(2-甲烷酰苯基)(1R,2S)-1-氨基-2-乙烯基环丙烷甲酸甲酯4-甲基苯磺酸盐,其质量用量为聚氨酯改性环氧树脂的的0.01-0.1%。