CN107555840A - 砂岩高档装饰品的制备方法 - Google Patents
砂岩高档装饰品的制备方法 Download PDFInfo
- Publication number
- CN107555840A CN107555840A CN201610500475.6A CN201610500475A CN107555840A CN 107555840 A CN107555840 A CN 107555840A CN 201610500475 A CN201610500475 A CN 201610500475A CN 107555840 A CN107555840 A CN 107555840A
- Authority
- CN
- China
- Prior art keywords
- top grade
- parts
- raw material
- preparation
- sandstone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种砂岩高档装饰品的制备方法,包括以下步骤:将191树脂、石英砂、甲乙酮固化剂以及工业化色浆按照重量比例进行混合,并混合均匀,得到原材料;铺设一定量的原材料至聚氯乙烯高温树脂膜具里,并拍振均匀,使铺设的物料厚度为0.9cm‑1.2cm;铺设一定量的原材料至上述铺设的物料上,并拍振均匀,使第二次铺设的物料厚度为1cm‑1.2cm;待聚氯乙烯高温树脂膜具里的物料凝固后,进行脱模,即可制备出砂岩高档装饰品。通过本发明提供的砂岩高档装饰品的制备方法,其制备出来的砂岩高档装饰品的硬度强,凝固快,档次高,耐腐蚀性能好,且可长时间保持美观,风吹雨淋都不褪色。
Description
技术领域
本发明涉及一种砂岩高档装饰品的制备方法,用于生产高档装饰品。
背景技术
现有的,通过水泥加工的工艺像和雕花,时间一久就容易坏掉,耐腐蚀性差;同时,水泥生产的成品强度和硬度达不到,还须去刮腻子,刷油漆,时间久就会脱落油漆,影响美观。
因此有必要设计一种砂岩高档装饰品的制备方法,以克服上述问题。
发明内容
本发明的目的在于克服现有技术之缺陷,提供了一种砂岩高档装饰品的制备方法,其制备出来的砂岩高档装饰品的硬度强,凝固快,档次高,耐腐蚀性能好,且可长时间保持美观,风吹雨淋都不褪色。
本发明是这样实现的:
本发明提供一种砂岩高档装饰品的制备方法,包括以下步骤:步骤一:将191树脂、石英砂、甲乙酮固化剂以及工业化色浆按照重量比例进行混合,并混合均匀,得到原材料,其中,191树脂、石英砂、甲乙酮固化剂以及工业化色浆的重量比为(800份-1000份):(5000份-6000份):(60份-100份):(220份-270份);步骤二:进行第一次铺料,铺设一定量的原材料至聚氯乙烯高温树脂膜具里,并拍振均匀,使铺设的物料厚度为0.9cm-1.2cm;步骤三:进行第二次铺料,铺设一定量的原材料至上述第一次铺设的物料上,并拍振均匀,使第二次铺设的物料厚度为1cm-1.2cm;步骤四:待聚氯乙烯高温树脂膜具里的物料凝固后,进行脱模,即可制备出砂岩高档装饰品。
进一步地,步骤一中,191树脂、石英砂、甲乙酮固化剂以及工业化色浆的重量分别为1000克、6000克、75克和250克。
进一步地,第一次铺料与第二次铺料的厚度相同。
本发明具有以下有益效果:
通过本发明提供的砂岩高档装饰品的制备方法,其制备出来的砂岩高档装饰品的硬度强,凝固快,档次高,耐腐蚀性能好,且可长时间保持美观,风吹雨淋都不褪色。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动的前提下所获得的所有其它实施例,都属于本发明保护的范围。
本发明实施例提供一种砂岩高档装饰品的制备方法,包括以下步骤:
步骤一:将191树脂、石英砂、甲乙酮固化剂以及工业化色浆按照重量比例进行混合,并混合均匀,得到原材料,其中,191树脂、石英砂、甲乙酮固化剂以及工业化色浆的重量比为(800份-1000份):(5000份-6000份):(60份-100份):(220份-270份)。在本较佳实施例中,191树脂、石英砂、甲乙酮固化剂以及工业化色浆的重量分别为1000克、6000克、75克和250克。
步骤二:进行第一次铺料,铺设一定量的原材料至聚氯乙烯高温树脂膜具里,并拍振均匀,使铺设的物料厚度为0.9cm-1.2cm。其中,聚氯乙烯高温树脂膜软膜不用刷进口蜡脱模剂,此模具本身就起到光洁自动脱模的效果,所以此聚氯乙烯高温树脂膜具不必刷进口蜡,使得制备工艺更加简单化。
步骤三:进行第二次铺料,铺设一定量的原材料至上述第一次铺设的物料上,并拍振均匀,使第二次铺设的物料厚度为1cm-1.2cm。在本较佳实施例中,第一次铺料与第二次铺料的厚度相同,均为1cm。
步骤四:待聚氯乙烯高温树脂膜具里的物料凝固后,进行脱模,即可制备出砂岩高档装饰品。
以下采用一个具体的实施例进行说明:
各种原料按比例来配比:191树脂1000克、石英砂6000克、甲乙酮固化剂75克、工业化色浆250克。其中,工业化色浆的液体具有各种颜色,可以根据实际需求进行选择。
按照上面的比例把原材料放入一胶盆里,用手带上胶手套,把放入胶盆里的原材料反复拌均匀即可用,把拌均匀的原材料放入聚氯乙烯高温树脂膜具里面,用手弄均匀,第一次铺的厚度在1公分厚就行,铺好在用手把原材料反复拍几次,因为必须拍好,起到震动,把空气排出来,倒出的成品就没有沙眼,没有缺陷现象,所以必须第一次要用手拍好。
当第一层拍好后,在开始接着铺盖第二层调好的原材料,用手弄均匀,接着用手拍好,拍光滑,拍紧,可增加成品的硬度,铺第二层的厚度为1公分厚,倒出的成品总厚度在2公分左右即可,倒一个成品基本铺盖2次原材料就可以成功。
等待聚氯乙烯高温树脂膜具里的物料凝固,一般夏天气温凝固时间在4个小时左右,就可以脱模,当然在生产砂岩成品是脱模的时间可根据气温来加配原材料,因为以上的比例是夏天的配比,如果在冬天气温低,可以把甲乙酮固化剂在配比原材料时适当的稍微多加点,起到凝固要快一些,原材料比例有时是根据天气的高温或者低温来配原料的,按照以上的程序和序号做,加工一个工艺装饰产品就倒成功。
脱膜下来的砂岩高档装饰品的线条、图案、花纹、清晰度强,仿天然色泽,古朴典雅,回归大自然,此产品适用于宾馆,酒店。别墅。酒吧,等高档装修用,代替普通的GRC水泥产品,用砂岩生产的成品即环保有事防火材料,又高雅,是现代高档装修的替代品。
综上所述,通过本发明提供的砂岩高档装饰品的制备方法,其制备出来的砂岩高档装饰品的硬度强,凝固快,档次高,耐腐蚀性能好,且可长时间保持美观,风吹雨淋都不褪色。
以上所述仅为本发明的较佳实施例而已,并不用以限制本发明,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (3)
1.一种砂岩高档装饰品的制备方法,其特征在于,包括以下步骤:
步骤一:将191树脂、石英砂、甲乙酮固化剂以及工业化色浆按照重量比例进行混合,并混合均匀,得到原材料,其中,191树脂、石英砂、甲乙酮固化剂以及工业化色浆的重量比为(800份-1000份):(5000份-6000份):(60份-100份):(220份-270份);
步骤二:进行第一次铺料,铺设一定量的原材料至聚氯乙烯高温树脂膜具里,并拍振均匀,使铺设的物料厚度为0.9cm-1.2cm;
步骤三:进行第二次铺料,铺设一定量的原材料至上述第一次铺设的物料上,并拍振均匀,使第二次铺设的物料厚度为1cm-1.2cm;
步骤四:待聚氯乙烯高温树脂膜具里的物料凝固后,进行脱模,即可制备出砂岩高档装饰品。
2.如权利要求1所述的砂岩高档装饰品的制备方法,其特征在于:步骤一中,191树脂、石英砂、甲乙酮固化剂以及工业化色浆的重量分别为1000克、6000克、75克和250克。
3.如权利要求1或2所述的砂岩高档装饰品的制备方法,其特征在于:第一次铺料与第二次铺料的厚度相同。