CN107474978B - 皮革和/或乙烯基树脂清洁剂和润湿剂及其制造方法 - Google Patents
皮革和/或乙烯基树脂清洁剂和润湿剂及其制造方法 Download PDFInfo
- Publication number
- CN107474978B CN107474978B CN201710699209.5A CN201710699209A CN107474978B CN 107474978 B CN107474978 B CN 107474978B CN 201710699209 A CN201710699209 A CN 201710699209A CN 107474978 B CN107474978 B CN 107474978B
- Authority
- CN
- China
- Prior art keywords
- composition
- cleaning
- silicone
- leather
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供皮革和/或乙烯基树脂清洁剂和润湿剂及其制造方法。本发明包括具有温和表面活性剂的协同组合的硬表面清洁和处理组合物,该协同组合使得该组合物特别适于皮革、合成皮革、乙烯基树脂和不锈钢。该组合物是温和的,并且不会伤害皮革和合成皮革,并且不会留下粘性残余物。该组合物可以清洁食品污物如芥末、番茄酱、起酥油和油脂,并且在使用时无需个人保护设备。此外,公开了通过使所述表面与所述衬底接触来防护皮革表面或制品的方法,以及与制造该组合物以形成稳定的油包水乳液相关的特定方法。
Description
本申请是申请号为201380053565.X、申请日为2013年10月13日、发明名称为“皮革和/或乙烯基树脂清洁剂和润湿剂及其制造方法”的中国专利申请的分案申请。
发明领域
本发明涉及特别用于皮革和乙烯基树脂(vinyl)表面的硬表面清洁组合物的领域。本发明特别涉及皮革和乙烯基树脂表面清洁与处理组合物,其包含有机硅和有效清洁食品污渍的温和表面活性剂的特定组合,该表面活性剂不会破坏皮革或乙烯基树脂表面,并且无需使用防护设备来使用。
发明背景
由于正在全球范围内在店面重建和新建筑物中实施新的装饰类型,快餐店(QuickService Restaurants,QSR)中摊位表面(booth surface)的可清洁性变得越来越有挑战性。在深印花柔软乙烯基树脂装饰和室内装潢织物的黑色油烟污染提供了最大的清洁挑战。
许多商业产品目前可用于清洁和调理塑料、皮革和乙烯基树脂表面如家具覆盖物、衣物、鞋子、汽车内饰、马鞍和缰绳、时尚配饰如皮带和手袋等等。通常此类产品混入矿物油基皂,将其用刷子手工施加并加工至该表面中,并随后用水冲洗。这些皂类往往相当刺激使用者的皮肤,此外不是通常可生物降解的。需要用于乙烯基树脂、塑料和皮革的对使用者和环境更为友好的清洁剂和调理剂,特别是当此类表面在快餐店行业中使用时。
矿物油干扰皮革中存在的天然油,将其萃取;最终造成表面的开裂和干燥。硅油已经用于润滑此类材料并使其光泽或亮泽。硅油不会像其它油类如矿物油那样与皮革中存在的天然油或在乙烯基树脂中存在的合成油相互作用。除了用于润滑的硅油,需要其它成分以清洁该表面,因为皮革对pH和化学组合物如酸和碱、腐蚀性和苛性材料敏感,需要具有温和组成且不含苛性/碱性成分的表面活性剂以进行实施而清洁脂油,如在快餐店中会遇到的脂油,如起酥和汉堡油脂。
合意的是配制一种皮革、乙烯基树脂和塑料清洁剂与调理剂,其更容易施加,对使用者无毒且无刺激性,并且可生物降解,特别是用于快速服务行业。
发明概述
本发明包含具有使得该组合物特别适于皮革、合成皮革、乙烯基树脂和不锈钢的温和表面活性剂的协同组合的硬表面清洁和处理组合物。该组合物是温和的,并且不会破坏皮革和合成皮革,并且不会留下粘性残余物。该组合物可以清洁非反式脂肪污物和食品污物,如芥末、番茄酱、以及起酥油和油脂。该组合物在使用时还不需要个人保护设备。该组合物可以用于清洁皮革和乙烯基树脂表面如家具、室内装潢、服装、鞋子、皮带、汽车内部装潢等等。此外,公开了通过使所述表面与所述衬底(substrate)接触来防护皮革表面的方法。
该组合物使用有机硅以便与特定的温和表面活性剂组合和防止破坏皮革的对使用者安全的乳化剂/稳定剂一起进行保护和润湿,同时提供强有力的清洁性能。本发明中存在的表面活性剂包括椰油酰胺基丙基甜菜碱、聚氧乙烯(20)失水山梨糖醇单油酸酯和具有6摩尔乙氧基化物的C10-C12醇。其它组分包括作为乳化剂/稳定剂的胺和任选的防腐剂。该组合物还可以包括香料和增稠剂。
在另一个实施方案中,本发明是从诸如皮革、乙烯基树脂或不锈钢的表面上去除污物的方法。该方法包括用稀释水稀释清洁剂以形成使用溶液,并使所述表面与所述使用溶液接触。在一个实施方案中,该清洁剂包括清洁组合物,其具有有机硅和包含椰油酰胺基丙基甜菜碱与聚氧乙烯(20)失水山梨糖醇单油酸酯、具有3-6摩尔乙氧基化物的C10至C12醇的组合的表面活性剂、乳化剂或稳定剂以及防腐剂。该使用溶液能够去除食品和油质污物,同时润湿该表面,并且不会在干燥时留下粘性残余物。
在本发明的另一方面,提供了一种用于处理皮革制品的工艺,包括使所述皮革制品与处理组合物接触的步骤,所述处理组合物包含有机硅与包含椰油酰胺基丙基甜菜碱与聚氧乙烯(20)失水山梨糖醇单油酸酯的组合的表面活性剂、乳化剂或稳定剂以及防腐剂,其中与其在接触该处理组合物之前的原始外观相比,所述皮革制品的外观未被破坏。
在另一方面,本发明涉及清洁、防护和保护皮革表面的方法,包括以下步骤:使皮革表面与有效清洁量的清洁组合物接触,所述清洁组合物包含i)基于该清洁组合物重量的大约0.3%至大约20%的选自聚硅氧烷共聚物、有机硅-丙烯酸酯共聚物、硅油、氨基取代的有机硅共聚物衍生物及其混合物的有机硅衍生物;ii)基于该清洁组合物重量的大约0.027%至大约0.05%的至少一种稳定剂;iii)基于该清洁组合物重量的大约4%至大约20%的选自阳离子型、两性离子型、两性型、非离子型或其混合物的至少一种去污表面活性剂,其中所述表面活性剂对使用者是温和的和无刺激的;iv)基于该清洁组合物重量的大约0.12%至大约.17%的防腐剂,任何余量为水,并用布或一次性衬底擦拭所述表面。在一个优选实施方案中,该表面活性剂包含具有3-6摩尔环氧乙烷的C10-C12醇、椰油酰胺基丙基甜菜碱和聚氧乙烯(20)失水山梨糖醇单油酸酯的组合。该制剂也需要增稠剂如黄原胶以确保稳定配制。
本发明还包括使用该乳化剂/增稠剂以保持稳定乳液的特定工程工艺。首先,该增稠剂,优选黄原胶在与聚二甲基硅氧烷组合之前必须充分水合,第二聚二甲基硅氧烷在与水组合之前必须与表面活性剂、香料和缓冲剂共混。
实现此类稳定乳液是相当令人惊讶的,因为通常,粗乳状液是热力学不稳定的,并且可以化学计量地使用表面活性剂以便通过降低表面张力来使其稳定化。但是,为了在最终用途中提供额外的去垢力,该制剂中使用的表面活性剂的量超出了化学计量量。
申请人通过在内部乳化水实现了稳定的聚二甲基硅氧烷与表面活性剂预混料。出乎意料的是,制造油包水乳液首先制造了最稳定的成品。随后,水量降低至反相点(inversion point)的30%并仍实现稳定的油包水预混料,和稳定的最终产品。该乳液相当独特,在于最终配方中的油滴并未聚结,这在不具有高剪切的情况下产生了稳定的乳液,并在不具有表面活性剂:聚二甲基硅氧烷的化学计量比的情况下产生了稳定的乳液。
虽然公开了多个实施方案,由显示并描述本发明的示例性实施方案的下列详述,本发明的其它实施方案将对本领域技术人员将变得显而易见。因此,附图和详述应被认为本质上是示例性的而非限制性的。
附图概述
图1是显示筛选几种试验制剂的初始性能的照片。
图2A和2B是显示几种不同的试验制剂的清洁性能的单个照片。配方SC-3、SC-5、SC-6和SC-7显示具有令人满意的清洁。
图3是显示配方SC-3、SC-5、SC-6、SC-L、SC-8、SC-9、SC-10、SC-1、SC-12、H2O和SC-13的光泽性能的图。
图4包括显示清洁前后各种清洁剂的实地测试结果的几张照片。
图5包括显示清洁前后在皮革凳上测试的几张照片。
图6是显示在清洁布上的残留残余物的照片。
图7是显示本发明的组合物与市售清洁剂相比的ΔE值的图和显示在所用清洁布上残留残余物的照片。
图8显示黄色乙烯基树脂凳清洁的ΔE值的图和清洁前后该凳的照片。
图9显示褐色皮革凳(leather tan stool)清洁的ΔE值的图和清洁前后该凳的照片。
图10是用本发明的组合物处理以去除黑色划痕的高脚椅的之前和之后的照片。
发明详述
本专利或申请文件包含至少一张表现色彩的图。具有彩色附图的本专利或专利申请公开的副本将在请求并支付必要费用时由该局提供。
除了在操作实施例中之外,或另行说明,本文中所用的表示成分量或反应条件的所有数字理解为在所有情况下均被术语“大约”修饰。
术语“皮革制品”在本文中指的是完全或部分包含由皮张组成的材料的任何制品,所述皮张经鞣制或处理以使得该材料不会腐烂。皮革制品的实例是粒面皮革制品和/或绒面皮革制品。
术语“成品皮革制品”在本文中指的是已经以增加对消费者(即成品皮革制品的购买者)的价值的方式处理过(即整饰过)的皮革制品。成品皮革制品的非限制性实例包括皮革衣服(即裙子、外套、裤子)、皮革配件(即皮带、手套、箱包、皮包、鞋子)和皮革家具/内部装潢(即皮革椅子、皮革沙发、床品、帘子、家具罩)、防水布等等。此类成品皮革制品通常以常规洗衣工艺和/或以干洗工艺清洁。
术语对皮革制品的“不利影响”和/或“破坏”在本文中指的是成品皮革制品的物理和/或美学特性受到了负面影响。此类不利影响可以发生在成品皮革制品的结构和/或完整性中和/或发生在成品皮革制品的整饰表面上。在成品皮革制品上的不利影响的非限制性实例包括收缩、开裂、褪色、柔软性丧失和/或感觉丧失。一旦对成品皮革制品产生不利影响,该成品皮革制品通常失去对该成品皮革制品所有者的价值,因为所有者可能停止或减少使用该成品皮革制品。
本文中使用的术语“皮革制品清洁组合物”和/或“皮革制品处理组合物”意在指任何组合物,尤其是含有亲脂性流体的组合物,其与待清洁和/或待处理的皮革制品直接接触。要理解的是,该术语涵盖了除清洁之外的用途,如调理和定型。
此外,任选的清洁助剂如上述那些表面活性剂之外的另外的表面活性剂、漂白剂等等可以添加到所述“处理组合物”中。也就是说,清洁助剂可以任选与该亲脂性流体组合。这些任选的清洁助剂在下文中更详细地描述。此类清洁助剂可以以本发明的处理组合物重量的0.01%至大约10%的水平存在于该处理组合物中。
术语“污物”指的是期望被除去的在皮革制品上的任何不合意的物质。在餐饮服务领域,这可以包括芥末、番茄酱、来自食品物质的油脂和脂肪、烹饪油脂、蛋白质等等。
如本文中所用的重量百分比(wt-%)、按重量计的百分比、重量%等等是同义词,指的是该物质重量除以该组合物总重量并乘以100所得的物质浓度。
本文中所用的修饰本发明的组合物中成分量或在本发明的方法中使用的术语“大约”指的是例如通过用于在现实世界中制造浓缩液或使用溶液的典型测量与液体处理程序;通过这些程序中的无意误差;通过用于制造该组合物或实施该方法的成分的制造、来源或纯度方面的差异等等而可能发生的数值量的变化。术语大约还涵盖来自特定初始混合物的组合物的不同的平衡条件所造成的相异量。无论是否被术语“大约”修饰,权利要求包括该量的等效量。
术语“烷基”指的是具有规定碳原子数的直链或支链的一价烃基团。烷基可以是未取代的,或被不会干扰该组合物的指定功能的取代基取代,并可以被相同或不同的基团取代一次或两次。取代基可以包括例如烷氧基、羟基、巯基、氨基、烷基取代的氨基、硝基、羧基、羰基(carbanyl)、羰氧基(carbanyloxy)、氰基、甲基磺酰基氨基或卤素。“烷基”的实例包括但不限于甲基、乙基、正丙基、异丙基、正丁基、仲丁基、叔丁基、正戊基、正己基、3-甲基戊基等等。
术语“表面活性剂”或“表面活性试剂”指的是当加入到液体中时能改变表面处该液体的特性的有机化学品。
“清洁”指的是进行或帮助去除污物、漂白、微生物群落减少、冲洗或其组合。
本文中所用的术语“基本不含”指的是完全缺乏该组分或具有小到致使该组分不会影响该组合物的效力的量的该组分的组合物。该组分可以作为杂质或作为污染物存在,并应小于0.5重量%。在另一个实施方案中,该组分的量小于0.1重量%,在又一实施方案中,该组分的量小于0.01重量%。
本文中所用的术语“硬表面”包括淋浴设备、水池、马桶、浴缸、台面、窗户、镜子、运输车辆、地板等等。这些表面可以是作为“硬表面”典型的那些(如墙壁、地板、便盆)。
要注意的是,如在本说明书和所附权利要求中所用那样,单数形式“一”、“一个/一种”和“该/所述”包括复数对象,除非该内容另有明确说明。由此,例如,提到组合物含有“一种化合物”包括两种或多种化合物的混合物。还要注意的是,术语“或”通常以其包括“和/或”的含义使用,除非该内容另有明确说明。
术语“活性物质”或“百分比活性物质”或“活性物质重量百分比”或“活性物质浓度”在本文中互换使用并且指的是清洁中涉及的那些成分的浓度,其表示为减去惰性成分的百分比,如水或盐。
术语“基本类似的清洁性能”通常指的是当使用代用清洁产品或代用清洁体系而非含有烷基酚乙氧基化物的清洁以解决在典型基底上的典型污染状况时,通过通常相同的清洁度(或至少并非明显更低的程度)或以通常同样的努力付出(或至少并非明显更少的付出)或这两者的代用清洁产品或代用清洁体系所实现的结果。取决于特定清洁产品和特定衬底,该清洁度可能对应于通常不存在可见污物,或对应于一定的较低清洁度,如前面的段落中所解释的那样。
本发明的组合物
本发明的组合物使用有机硅以便与特定的温和表面活性剂组合和防止破坏皮革的乳化剂/稳定剂一起进行保护和润湿。该组合物对使用者安全,同时提供强有力的清洁特性。存在于本发明中的表面活性剂优选包含椰油酰胺基丙基甜菜碱、聚氧乙烯(20)失水山梨糖醇单油酸酯和具有6摩尔乙氧基化物的C10-C12醇。其它组分包括作为乳化剂/稳定剂的胺、增稠剂和任选的防腐剂。该组合物还可以包括香料。
在一个实施方案中,本发明是从表面如皮革、乙烯基树脂或不锈钢上去除污物的方法。该方法包括如果需要的话用稀释水稀释清洁剂,以形成使用溶液,并使该表面与该使用溶液接触。在一个实施方案中,该清洁剂包含清洁组合物,其具有有机硅和包含椰油酰胺基丙基甜菜碱与聚氧乙烯(20)失水山梨糖醇单油酸酯、具有6摩尔乙氧基化物的C10至C12醇的组合的表面活性剂组合、乳化剂或稳定剂以及防腐剂。该使用溶液能够去除食品和油质污物,同时还润湿该表面,并且不会在干燥时留下粘性残余物。
在本发明的另一方面,提供了一种用于处理皮革制品的工艺,包括将所述皮革制品与处理组合物接触的步骤,所述处理组合物包含有机硅与包含椰油酰胺基丙基甜菜碱与聚氧乙烯(20)失水山梨糖醇单油酸酯的组合的表面活性剂、乳化剂或稳定剂以及防腐剂,其中与其在接触该处理组合物之前的原始外观相比,所述皮革制品的外观未被破坏。
在另一方面,本发明涉及清洁、防护和保护皮革表面的方法,包括以下步骤:使皮革表面与预润湿的可随意处理清洁衬底接触,所述可随意处理衬底中引入了有效清洁量的b)清洁组合物,所述清洁组合物包含i)基于该清洁组合物重量的大约0.3%至大约20%的选自聚硅氧烷共聚物、有机硅-丙烯酸酯共聚物、硅油、氨基取代的有机硅共聚物衍生物及其混合物的有机硅衍生物;ii)基于该清洁组合物重量的大约0.027%至大约0.05%的至少一种稳定剂;iii)基于该清洁组合物重量的大约4%至大约20%的选自阳离子型、两性离子型、两性型、非离子型或其混合物的至少一种去污表面活性剂,其中所述表面活性剂对使用者是温和的和无刺激的;iv)基于该清洁组合物重量的大约0.12%至大约.17%的防腐剂,和任选的增稠试剂,任何余量为水。在一个优选实施方案中,该表面活性剂包括具有3摩尔环氧乙烷的C10-C12醇、椰油酰胺基丙基甜菜碱和聚氧乙烯(20)失水山梨糖醇单油酸酯的组合。该制剂也需要增稠剂如黄原胶以确保稳定配制。
有机硅组分
部件的清洁/处理组合物包含有机硅组分,所述有机硅组分选自聚硅氧烷共聚物、有机硅-丙烯酸酯共聚物、硅油、氨基取代的有机硅衍生物及其混合物。
部件的清洁组合物的有机硅组分可以是硅油,并区别于有机硅弹性体和树脂(其与硅油相比更彻底地交联)。合适的硅油包括基于有机聚硅氧烷的那些,它们可以选自具有通式(RnSiO((4-n)/2))m(I)的聚合物类别,其中n为0至3,m为2或更大,R是烷基或芳基,如Silicone Compounds Register and Review,第5版,R.Anderson,G.L.Larson和C.Smith编辑,Huls America Inc.,Piscataway,N.J.,第247页(1991)中所定义,该出版物在此通过引用并入本文。m的值可以大到一百万或更大,但是更通常具有大约5至1000的值,它们是具有良好操作特性与性能特征的易于流动的液体。这些示例性硅油可以是直链或支链的。基本等效于该示例性硅油类别的各种命名规范和命名法包括但不限于:二烷基聚硅氧烷水解产物;α-烷基-ω-甲氧基聚二烷基硅氧烷;聚二烷基硅油;聚(二烷基硅氧烷);烷基封端的聚二烷基硅氧烷;聚氧(二烷基亚甲硅基),α-(三烷基甲硅烷基)-ω-羟基;聚[氧(二烷基亚甲硅基)],α-[三烷基甲硅烷基]-ω-[(三烷基甲硅烷基)氧基];和α-(三烷基甲硅烷基)聚[氧(二烷基亚甲硅基)]-ω-烷基。一些另外的合适的实例还包括聚二甲基硅氧烷共聚醇、二甲基聚硅氧烷、二乙基聚硅氧烷、高分子量聚二甲基硅氧烷(dimethicone)、混合的C1-C30烷基聚硅氧烷、苯基聚二甲基硅氧烷、聚二甲基硅氧烷醇及其混合物。在本文中可用的硅油的非限制性实例还描述在授予Ciotti等人的美国专利号5,011,681中,该专利在此通过引用并入本文。
部件的清洁组合物的有机硅衍生物b)i)可以是聚硅氧烷共聚物。本文中可用的聚硅氧烷共聚物还包括聚烷基或聚芳基硅氧烷。在该硅氧烷链上或在硅氧烷链末端取代的烷基或芳基(R)可以具有任何结构,只要形成的有机硅在室温或大致室温下保持为液体。合适的R基团包括羟基、甲基、甲氧基、乙基、乙氧基、丙基、丙氧基、苯基、甲基苯基、苯基苯基、芳基和芳氧基。硅原子上的一个或多个R基团可以代表相同基团或不同基团,或其任意组合。合适的有机硅化合物是聚二甲基硅氧烷、聚二乙基硅氧烷和聚甲基苯基硅氧烷。聚二甲基硅氧烷(也称为聚二甲硅氧烷(dimethicone))是合适的并可以容易地以多种形式和等级获得,包括例如适用于食品接触用途的组合物的可食用等级。可以使用的聚烷基硅氧烷包括例如聚二甲基硅氧烷。这些有机硅化合物例如可以以他们的和SF 96系列获自General Electric Company,和以他们的Dow Corning 200系列获自Dow Corning。例如含有一个或多个烷基或烷基芳基取代基的聚烷基芳基硅氧烷流体也可以使用,并且包括但不限于聚甲基苯基硅氧烷、聚[(二甲基硅氧烷)/(甲基乙烯基硅氧烷)]、聚[(二甲基硅氧烷)/(二苯基硅氧烷)]、聚[(二甲基硅氧烷)/(苯基甲基硅氧烷)]和聚[(二甲基硅氧烷)/(二苯基硅氧烷)/(甲基乙烯基硅氧烷)]。这些硅氧烷例如可以作为SF 1075MethylPhenylFluid获自General Electric Company,或作为556Cosmetic Grade Fluid获自DowCorning,作为RHODORSIL 763获自Rhne-Poulenc,作为SILBIONE 70641V 30和70641V 200获自Rhone-Poulenc,作为PK系列的有机硅获自Bayer,如PK20,作为PN和PH系列的有机硅获自Bayer,如PN 1000和PH 1000,并作为SF系列的某些油获自General Electric,如SF1250、SF 1265、SF 1154和SF 1023。
更高分子量有机硅衍生物,包括硅橡胶和树脂,根据本发明可以使用,并包括分子质量为200,000至5,000,000的聚二有机硅氧烷,单独或与选自挥发性有机硅、聚二甲基硅氧烷(PDMS)油、聚苯基甲基硅氧烷(PPMS)油、异链烷烃、二氯甲烷、戊烷、十二烷、十三烷和十四烷或其混合物的溶剂混合使用。
该有机硅衍生物可以是直链或支链的,并且可以被化学基团改性以提供另外的特性。例如,合适的有机硅衍生物还包括氨基取代的有机硅衍生物,其中R是胺、酰胺或烷基、二烷基或三烷基衍生的胺成分。通过用其它有机或官能化有机基团如乙烯基、苯基、羧酸衍生物、羧基酯和季铵衍生物取代一个或多个R基团,可以制造其它有机聚硅氧烷。
包括在内的是这些材料的混合物,例如但不限于:1)由在链末端处羟基化的聚二甲基硅氧烷(根据CTFA命名法为聚二甲基硅氧烷醇)和由环状聚二甲基硅氧烷(根据CTFA命名法为环聚二甲基硅氧烷)形成的混合物,如由Dow Corning公司出售的产品Q2 1401;2)由聚二甲基硅氧烷胶与环状有机硅形成的混合物,如来自General Electric的产品SF1214Silicone Fluid,其是溶解在SF 1202Silicone Fluid(十甲基环五硅氧烷)中的MW500,000的SE 30胶;3)不同粘度的两种PDMS材料的混合物,例如PDMS胶和PDMS油,如来自General Electric公司的产品SF 1236和CF 1241。产品“SF 1236”是上面定义的SE 30胶(粘度为20m2/s)和SF 96油(粘度为5×l0-5m2/s)的混合物(15%SE 30胶和85%SF 96油)。产品“CF 1241”是SE 30胶(33%)和粘度为10-2m2/s的PDMS(67%)的混合物。根据本发明的有机改性的有机硅是如上定义的有机硅,在其一般结构中含有一个或多个直接连接到该硅氧烷链或经由烃基基团连接的有机官能团。实例包括含有以下基团的有机硅:a)聚乙烯氧和/或聚丙烯氧基团,任选含有烷基,如:由Dow Corning公司以名称“DC 1248”出售的作为聚二甲基硅氧烷共聚醇已知的产品,和由Dow Corning公司以名称“Q2 5200”出售的烷基(C12)聚二甲基硅氧烷共聚醇,来自General Electric公司的油“SILWET”L 722、L 7500、L77和L 711,聚二甲基硅氧烷共聚醇和环聚二甲基硅氧烷的混合物,如由Dow Corning公司以名称“Q2-3225C”出售的产品;由Rhone-Poulenc出售的产品“MIRASIL DMCO”;b)羟酰基氨基,如欧洲专利申请EP-A-0,342,834中描述的那些,特别是由Dow Corning公司以名称“Q2-8413”出售的有机硅;c)硫醇基团,如在来自Dow Corning的有机硅“X 2-8360”或来自Genesee的“GP 72A”和“GP 71”中;Union Carbide或在CTFA词典中称为“氨端聚二甲基硅氧烷(Amodimethicone)”的有机硅;d)羧酸根基团,如在来自Chisso Corporation的欧洲专利EP 186,507(在此通过引用并入本文)中所描述的产品;e)羟基化基团,如在专利申请FR-A-2,589,476(其在此通过引用并入本文)中描述的含有羟基烷基官能的聚有机硅氧烷,特别是含有γ-羟基-丙基官能的聚有机硅氧烷;f)含有至少12个碳原子的烷氧基化基团,如来自SWS Silicones的产品“Silicone Copolymer F 7551”和来自Goldschmidt公司的产品“ABILWAX 2428”、“ABILWAX 2434”和“ABILWAX 2440”;g)含有至少12个碳原子的酰氧基烷基基团,如专利申请FR-A-2,641,185(其在此通过引用并入本文)中描述的聚有机硅氧烷,特别是含有硬脂酰氧基丙基官能的聚有机硅氧烷;h)季铵基团,如在来自Goldschmidt公司的产品“X2 81 08”和“X2 81 09”和产品“ABIL K 3270”中;i)两性或甜菜碱基团,如在由Goldschmidt公司以名称“ABIL B 9950”出售的产品中;和j)亚硫酸氢根基团,如在由Goldschmidt公司以名称“ABIL S 201”和“ABIL S 255”出售的产品中。具有聚硅氧烷-聚氧化烯直链嵌段作为重复单元的嵌段共聚物(其用于本发明的上下文中)包括具有下列通式的那些:([Y(R2SiO)aR'2SiYO][CnH2nO--)b])c(II),其中R和R',其可以相同或不同,代表不含有脂族不饱和的一价烃基基团,n是2至4的整数,a是大于或等于5的整数,特别是5至200且甚至更特别为5至100,b是大于或等于4的整数,特别是4至200且甚至更特别为5至100,c是大于或等于4的整数,特别是4至1000且甚至更特别为5至300,Y代表二价有机基团,其经由碳-硅键连接到相邻的硅原子上并经由氧原子连接到聚氧化烯嵌段上,各硅氧烷嵌段的平均分子量为大约400至大约10,000,各聚氧化烯嵌段的平均分子量为大约300至大约10,000,该硅氧烷嵌段占该嵌段共聚物重量的大约10%至大约95%,该嵌段共聚物的平均分子量为至少3000,特别为5000至1,000,000且甚至更特别为10,000至200,000。R和R'适宜地选自烷基基团如甲基、乙基、丙基、丁基、戊基、己基、辛基、癸基和十二烷基基团,芳基基团如苯基和萘基,芳烷基基团如苄基和苯乙基,以及甲苯基、二甲苯基和环己基基团。Y适宜地选自包括--R"--、--R"--CO--、--R"--NHCO--、--R"--NH--CO--NH--R"--NHCO或--R"--OCONH--R'"—NHCO--,其中R"是二价亚烷基,如亚乙基、亚丙基或亚丁基,并且R'"是二价亚烷基或二价亚芳基,如--C6H4、--C6H4C6H4-、C6H4-CH2-C6H4、C6H4-C(CH3)2C6H4。甚至更特别地,Y代表二价亚烷基基团,更特别为--CH2-CH2-CH2-基团或--C4H8-基团。用于本发明的上下文的所述嵌段共聚物的制备描述在欧洲申请EP 0,492,657 Al(其在此通过引用并入本文)中。
同样合适的是使用一种或多种挥发性硅油,即具有足以在将本发明的组合物涂施到皮革表面的过程中和/或之后至少部分或完全蒸发到大气中的足够的蒸汽压或挥发性的硅油。本发明的组合物在一个实施方案中可以仅含有挥发性有机硅流体作为该硅油,或在一个替代实施方案中可以任选组合地含有一种或多种挥发性有机硅流体,或在又一实施方案中可以任选组合地含有一种或多种挥发性有机硅流体和一种或多种非挥发性有机硅流体。挥发性硅油通常是在环境温度下具有相当的蒸汽压的低粘度有机硅流体。通常,可用于本发明的挥发性有机硅流体具有在25℃下小于大约10厘沲和在25℃下任选小于大约5厘沲的粘度。
合适的挥发性硅油包括聚二甲基环硅氧烷。可用于本发明的聚二甲基环硅氧烷流体可以通过通式[(CH3)2SiO]x来定义,其中x具有3至8的值。
通常,可用于本发明的聚二甲基环硅氧烷流体是一种或多种由上式所示的不同物类的混合物。市售聚二甲基环硅氧烷是由上式所示的各种物类的混合物,并视为在本发明的范围内。用于本发明的一些适宜的聚二甲基环硅氧烷流体是其中主要为八甲基环四硅氧烷、十甲基环五硅氧烷和十二甲基环六硅氧烷(即其中x为4至6)的那些。其中主要为十甲基环五硅氧烷和十二甲基环六硅氧烷的流体是特别适宜的。根据另一个实施方案,使用由DowCorning Corporation制造的那些挥发性有机硅流体。据信Dow Corning 245和345挥发性有机硅流体主要由十甲基环戊硅氧烷组成,含有较少量的十二甲基环六硅氧烷和次要量的八甲基环四硅氧烷。其它合适的挥发性有机硅包括“DC 244”、“DC 245”、“DC 246”、“DC344”、“DC 345”和“DC 346”(由Dow Corning制造);SILICONE 7207和SILICONE 7158(由Union Carbide Corp.制造);SF 1202(由General Electric制造);和SWS-03314(由SWSSilicones,Inc.制造)。
同样适于使用且特别是与其它硅油组合的是下面描述的改性有机硅衍生物。实例还包括但不限于可以作为SILWET 7650获自General Electric的聚环氧烷(polyalkyleneoxide)改性的聚二甲基硅氧烷,可以作为SILWET 7280和SILWET 7608也获自General Electric的聚环氧烷改性七甲基三硅氧烷,以及可以作为DC 57获自DowCorning的有机硅二醇共聚物表面活性剂,和称为Q2-5211的Dow Corning有机硅聚醚表面活性剂。
另外的实例包括但不限于可获自Dow Corning的烷基甲基硅氧烷DC 56,和可获自General Electric的称为FORMASIL 433的有机改性二甲基硅氧烷。
所述部件的清洁组合物的有机硅衍生物b)i)可以是有机硅-丙烯酸酯共聚物。这种共聚物的有机硅部分构成基于该共聚物总重量的大约10%至大约95%。在本发明的另一个实施方案中,该共聚物的有机硅部分构成基于该共聚物总重量的大约20%至大约65%。在本发明的另一个实施方案中,该共聚物的有机硅部分构成基于该共聚物总重量的大约20%至大约35%。该共聚物的有机硅部分由大约88摩尔%至大约97摩尔%、优选92至97摩尔%的二甲基硅氧烷单元和大约3%至大约12%、优选大约3摩尔%至大约8摩尔%的甲基乙烯基硅氧烷单元组成。基于该有机硅-丙烯酸酯共聚物重量的剩余5%至大约95%、优选大约35%至大约80%和更优选大约65%至大约80%由丙烯酸酯部分组成。该丙烯酸酯部分是选自丙烯酸乙酯、丙烯酸甲酯、丙烯酸、甲基丙烯酸乙酯、甲基丙烯酸甲酯、甲基丙烯酸和丙烯腈的丙烯酸酯单体。
在本发明中使用的有机硅-丙烯酸酯共聚物可以通过乳液聚合法制备。在法国专利号1,491,782中叙述了适于制备这些共聚物的乳液聚合工艺。
基本上,在优选实施方案中,制备该共聚物的工艺包括首先在乳液中聚合该硅氧烷部分,随后向其中添加适当的丙烯酸酯单体并在该乳液中共聚合该有机硅与丙烯酸酯单体。或者,该有机硅和丙烯酸酯单体可以一起乳化,然后首先聚合该有机硅单体,并随后添加催化剂并造成所形成的硅氧烷与丙烯酸酯单体的聚合以形成所需的有机硅-丙烯酸酯共聚物。
本文中例示的任何组分的有机硅衍生物的混合物与组合,例如具有不同分子量、不同粘度、不同官能化衍生物、不同挥发性和/或蒸汽压、不同特性和益处及其组合的硅油可以有利地在本发明的清洁组合物中组合。例如,“较轻质”或更低粘度的聚有机硅氧烷可以与“较重质”或更高粘度的硅油、和/或硅橡胶和/或有机硅弹性体组合以便分散在本发明的组合物中,其中否则如果单独或在不包含“较轻质”有机硅的情况下组合的话,所述“较重质”材料将难以处理和分散。或者,挥发性硅油可以与更低挥发性或基本非挥发性的硅油组合。
组分b)i)的有机硅衍生物还可用于赋予处理表面光亮或光泽涂层,从而改善外观和与入射光改变相关的其它审美益处,如对有助于感知改进的色彩与色调,并减少对表面缺陷如刮痕、应力裂纹、条纹和通常随正常老化与磨损在表面上显露的其它表面缺陷的感知的镜面反射的折射或散射助益。因此,组分b)i)的有机硅衍生物当用在老化和磨损的皮革表面上时因其恢复效果而是有用的。
本发明的另一个实施方案是作为该组分的聚硅氧烷共聚物与氨基取代的有机硅共聚物的混合物。该混合物的所述聚硅氧烷共聚物描述在式(III)中。
其中
z是1至大约5000的整数,并且
该混合物的所述氨基取代的有机硅共聚物描述在式(IV)中
其中
R、R1、R2和R3彼此独立地为CH3、OH或OC1-C4烷基,x是1至2000的整数,并且
y是1至2000的整数。
本发明的另一个实施方案是作为b)i)的组分的聚硅氧烷共聚物与氨基取代的有机硅共聚物的混合物。该混合物的所述聚硅氧烷共聚物描述在式(III)中。
其中
z是1至大约2000的整数,并且
该混合物的所述氨基取代的有机硅共聚物描述在式(IV)中
其中
R、R1、R2和R3彼此独立地为CH3、OH或OC1-C4烷基,x是1至200的整数,并且
y是1至500的整数。
本发明的另一个实施方案是作为b)i)的组分的聚硅氧烷共聚物与氨基取代的有机硅共聚物的混合物。该混合物的所述聚硅氧烷共聚物描述在式(III)中。
其中
z是10至大约500的整数,并且
该混合物的所述氨基取代的有机硅共聚物描述在式(IV)中
其中
R、R1、R2和R3彼此独立地为CH3、OH或OC1-C4烷基,x是1至100的整数,并且
y是10至300的整数。
本发明的另一个实施方案是作为b)i)的组分的聚硅氧烷共聚物与氨基取代的有机硅共聚物的混合物,其中该混合物的所述氨基取代的有机硅共聚物描述在式(IV)中
其中
R、R1、R2和R3是CH3,并且x和y是如上所述的整数。
本发明的另一个实施方案是式(III)的化合物的分子量为大约200至大约200,000道尔顿。本发明的另一个实施方案是式(III)的化合物的分子量为大约500至大约150,000道尔顿。本发明的另一个实施方案是式(III)的化合物的分子量为大约1000至大约100,000道尔顿。
本发明的另一个实施方案是式(IV)的化合物的分子量为大约200至大约200,000道尔顿。本发明的另一个实施方案是式(IV)的化合物的分子量为大约500至大约150,000道尔顿。本发明的另一个实施方案是式(IV)的化合物的分子量为大约1000至大约100,000道尔顿。
在合适的实施方案中,该有机硅/组分或衍生物占本发明组合物重量的0.001重量%至大约25重量%,或0.01重量%至大约20重量%,或可选地0.05重量%至大约18重量%,或可选地占本发明组合物重量的0.1重量%至大约15重量%。
水
本发明的组合物任选可以含有水。应当理解的是,所述水可以以去离子水或软化水的形式提供。作为浓缩物一部分提供的水可以相对不具有硬度。可以预期的是,可以将所述水去离子以去除一部分溶解的固体。也就是说,可以用包含溶解的固体的水配制该浓缩物,也可以用可表征为硬水的水配制该浓缩物。
水,当存在于本发明的皮革制品处理/清洁组合物中时,优选占该皮革制品处理组合物重量的大约0.001重量%至大约5重量%、更优选大约0.005重量%至大约5重量%、甚至更优选大约0.01重量%至大约1重量%。
水,当存在于本发明的可消耗皮革制品处理/清洁组合物中时,优选占该可消耗皮革制品处理/清洁组合物重量的大约0重量%至大约99重量%、更优选大约40重量%至大约95重量%、甚至更优选大约50重量%至大约90重量%。
水,如果存在的话,可以单独添加到该皮革制品处理装置中以形成该皮革制品处理组合物,而不是存在于该可消耗皮革制品处理组合物中。
防腐剂
本发明的保护剂组合物可以任选包含一种或多种防腐剂和/或杀生物剂。许多不同类型的防腐剂和/或杀生物剂可用于该保护剂组合物。此外,一种或多种防腐剂和/或杀生物剂可用于该保护剂组合物。可用于该保护剂组合物的防腐剂的非限制性实例包括但不限于mildewstat或抑菌剂,对羟基苯甲酸甲酯、对羟基苯甲酸乙酯和对羟基苯甲酸丙酯,短链有机酸(例如乙酸、乳酸和/或乙醇酸),双胍化合物(例如Dantogard和/或Glydant)和/或短链醇(例如乙醇和/或IPA)。mildewstat或抑菌剂的非限制性实例包括但不限于mildewstats(包括非异噻唑啉酮化合物),包括来自Avecia Corporation的Proxel GXL和Vantocil IB,Kathon GC(一种5-氯-2-甲基-4-异噻唑啉-3-酮),KATHON ICP(一种2-甲基-4-异噻唑啉-3-酮)及其共混物,以及KATHON 886(一种5-氯-2-甲基-4-异噻唑啉-3-酮)和Neolone M-10,均可获自Rohm and Haas Company;来自Boots Company Ltd.的BRONOPOL(一种2-溴-2-硝基丙烷-1,3-二醇),来自ICI PLC的PROXEL CRL(一种对羟基苯甲酸丙酯);来自Nipa Laboratories Ltd.的NIPASOL M(一种邻苯基苯酚,钠盐),均来自Dow ChemicalCo.的DOWICIDE A(一种1,2-苯并异噻唑啉-3-酮)、Dowacil 75和Bioban,和来自Ciba-Geigy A.G的IRGASAN DP 200(一种2,4,4'-三氯-2-羟基二苯基醚),以及来自SuretyLaboratories的Surcide P,可购自Lonza的Dantogard Plus(例如l,3-双(羟基甲基)-5,5-二甲基乙内酰脲和羟基甲基-5,5-二甲基乙内酰脲),可购自Angus的Bioban DXN(例如乙酰二甲二噁烷(dimethoxane))等等。杀生物剂的非限制性实例包括季铵化合物和酚类化合物(phenolics)。这些季铵化合物的非限制性实例包括苯扎氯铵和/或取代的苯扎氯铵,二(C6-C14)烷基二短链(C1-4烷基和/或羟基烷基)季铵盐,N-(3-氯代烯丙基)氯化六亚甲基四胺(hexaminium)、氯化苄乙氧铵、氯化甲苄乙氧铵和氯化十六烷基吡啶鎓。其它季铵化合物包括二烷基二甲基氯化铵、烷基二甲基苄基氯化铵、二烷基甲基苄基氯化铵及其混合物,其中该烷基基团可以是C1至C24。
双胍抗微生物活性物质包括但不限于聚六亚甲基双胍盐酸盐、对氯苯基双胍;4-氯二苯甲基双胍,二卤代苯双胍己烷(halogenated hexidine),例如但不限于氯己定(1,1’-六亚甲基-双-5-(4-氯苯基双胍)及其盐也在此类别中。当在该保护剂组合物中包含一种或多种防腐剂和/或杀生物剂时,防腐剂和/或杀生物剂的量为至少大约0.001重量%和小于大约1重量%,通常为大约0.04-0.8重量%,更通常为大约0.04-0.6重量%,再更通常为大约0.05-0.5重量%,甚至更通常为大约0.05-0.3重量%。
表面活性剂/乳化剂共混物
本发明包括以协同方式起作用以保护脆弱的皮革表面并同时还提供清洁的表面活性剂/乳化剂的共混物。该表面活性剂共混物包括非离子型表面活性剂,如醇烷氧基化物。优选的醇乙氧基化物是具有6摩尔乙氧基化物的C10至1C12醇。另外的醇烷氧基化物包括烷基酚乙氧基化物、支链醇乙氧基化物、仲醇乙氧基化物(例如来自Dow Chemical的Tergitol 15-S-7)、蓖麻油乙氧基化物、烷基胺乙氧基化物、牛脂胺乙氧基化物、脂肪酸乙氧基化物、山梨糖醇(sorbital)油酸酯乙氧基化物、封端的乙氧基化物、或其混合物。
该表面活性剂/乳化剂共混物还包括两性表面活性剂。合适的两性表面活性剂包括衍生自椰子产品如椰油或椰子脂肪酸的那些。另外的合适的椰子衍生的表面活性剂包含作为其结构的一部分的乙二胺部分、链烷醇酰胺部分、氨基酸部分(例如甘氨酸)或其组合;以及大约8至18个(例如12个)碳原子的脂族取代基。此类表面活性剂还可以考虑烷基两性二羧酸。这些两性表面活性剂可以包括表示为以下的化学结构:C12-烷基-C(O)-NH-CH2-CH2-N+(CH2-CH2-CO2Na)2-CH2-CH2-OH或C12-烷基-C(O)-N(H)-CH2-CH2-N+(CH2-CO2Na)2-CH2-CH2-OH。椰油酰(cocoampho)两性二丙酸二钠是一种合适的两性表面活性剂,并可以以商品名Miranol FBS购自Rhodia Inc.,Cranbury,N.J。化学名称为椰油酰两性二乙酸二钠的另一种合适的椰子衍生的两性表面活性剂以商品名Mirataine JCHA出售,也来自于RhodiaInc.,Cranbury,N.J。在1975年12月30日授予Laughlin和Heuring的美国专利号3,929,678中给出了两性类的典型列表以及这些表面活性剂的物类。在“Surface Active Agents andDetergents”(卷I和II,Schwartz,Perry和Berch)中给出了进一步的实例,其内容在此通过引用全文并入本文。优选的两性表面活性剂是椰油酰胺基丙基甜菜碱。
该表面活性剂乳化剂共混物中的第三组分是失水山梨糖醇酯(也称为SPANs),特别是失水山梨糖醇单硬脂酸酯;山梨糖醇;聚山梨酸酯(聚氧乙烯失水山梨糖醇酯,在工业上也称为TWEENs),特别是聚山梨酸酯20、聚山梨酸酯60、聚山梨酸酯65和聚山梨酸酯80;硬脂酰基丙烯酸酯;卵磷脂与衍生物;聚乙二醇脂肪酸酯;对伞花烃;季铵化合物;烷基磺酸钠;三乙醇胺;和烷基多糖。在一个优选的实施方案中,该聚山梨酸酯20(聚氧乙烯失水山梨糖醇单油酸酯)。
该表面活性剂共混物基于该清洁组合物重量占整个组合物的大约4%至大约20%,优选大约6%至大约18%和更优选大约8%至大约15%。所述失水山梨糖醇酯、椰子衍生物和醇乙氧基化物的比可以包括2:1:1至大约1:1:1的比。
水溶助剂(Hydrotope)/增溶剂
该组合物包括水溶助剂/增溶剂。这通常是胺化合物。可用于本发明的胺化合物的具体实例可以包括单乙醇胺、二乙醇胺、三乙醇胺、N-甲基乙醇胺、Ν,Ν-二甲基乙醇胺、N-乙基乙醇胺、N,N-二乙基乙醇胺、N-异丙基乙醇胺、N,N-二异丙基乙醇胺、单异丙醇胺、二异丙醇胺、三异丙醇胺、N-甲基异丙醇胺、Ν,Ν-二甲基异丙醇胺、N-乙基异丙醇胺、Ν,Ν-二乙基异丙醇胺、N-异丙基异丙醇胺、Ν,Ν-二异丙基异丙醇胺、单正丙醇胺、二正丙醇胺、三正丙醇胺、N-甲基正丙醇胺、N,N-二甲基正丙醇胺、N-乙基正丙醇胺、N,N-二乙基正丙醇胺、N-异丙基正丙醇胺、N,N-二异丙基正丙醇胺、单丁醇胺、二丁醇胺、三丁醇胺、N-甲基丁醇胺、Ν,Ν-二甲基丁醇胺、N-乙基丁醇胺、N,N-二乙基丁醇胺、N-异丙基丁醇胺和N,N-二异丙基丁醇胺。可用的水溶助剂/增溶剂的其它实例包括诸如二甲苯磺酸钠或丙二醇的化合物。该水溶助剂/增溶剂以组合物重量的大约0.001重量%至大约0.10重量%、优选大约0.005重量%至大约0.08重量%和更优选大约0.01重量%至大约0.05重量%的量存在。
增稠剂
该清洁/处理组合物包含增稠剂。该清洁组合物的粘度随增稠试剂的量而提高,粘性组合物可用于其中清洁组合物附着到表面上的用途。合适的增稠剂可以包括不会在待处理表面上留下污染残余物的那些。通常,可用于本发明的增稠剂包括天然胶如黄原胶、瓜尔胶、改性瓜尔胶或来自植物粘液的其它胶;多糖基增稠剂,如藻酸盐、淀粉和纤维素聚合物(例如羧甲基纤维素、羟乙基纤维素等等);聚丙烯酸酯增稠剂;以及水胶体增稠剂,如果胶。通常,在本组合物或方法中使用的增稠剂的浓度将由最终组合物中的所需粘度来决定。但是,作为一般参考,本发明的组合物中增稠剂的粘度为大约0.1重量%至大约3重量%、大约0.1重量%至大约2重量%或大约0.1重量%至大约0.5重量%。
另外的功能材料
该清洁/处理组合物可以包含另外的组分或试剂,如另外的功能材料。因此,在一些实施方案中,该清洁/处理组合物可以提供大量、或甚至该清洁组合物总重量的全部,例如在具有极少或不具有设置在其中的另外的功能材料的实施方案中。该功能材料向该清洁组合物提供所需的特性和功能。对本申请的目的而言,术语“功能材料”包括当分散或溶解在使用溶液和/或浓缩溶液,如水溶液中时,提供特定用途中的有益特性的材料。该清洁/处理制剂可以任选含有其它污物消化组分、另外的表面活性剂、消毒剂、消毒杀菌剂、酸化剂、络合剂、缓蚀剂、染料和芳香剂,如美国专利号7,341,983(在此通过引用并入本文)中所述。在下面更详细地讨论了功能材料的一些特定实例,但是本领域技术人员以及其他人应当理解,讨论的特定材料仅作为例子给出,可以使用多种多样的其它功能材料。例如,下面讨论的许多功能材料涉及在清洁应用中使用的材料,但是要理解的是,其它实施方案可能包括用于其它应用的功能材料。
另外的表面活性剂
该清洁/处理组合物可以含有另外的阴离子型表面活性剂组分,其包括去污量的阴离子型表面活性剂或阴离子型表面活性剂的混合物。阴离子型表面活性剂因其湿润和去污特性在清洁组合物中是合意的。根据本发明可以使用的阴离子型表面活性剂包括清洁行业中可获得的任何阴离子型表面活性剂。合适的阴离子型表面活性剂组包括磺酸盐和硫酸盐。可以在该阴离子型表面活性剂组分中提供的合适的表面活性剂包括烷基芳基磺酸盐、仲烷烃磺酸盐、烷基甲基酯磺酸盐、α烯烃磺酸盐、烷基醚硫酸盐、烷基硫酸盐和醇硫酸盐。
可用于该清洁组合物的合适的烷基芳基磺酸盐可以具有含6至24个碳原子的烷基,并且芳基可以是苯、甲苯和二甲苯的至少一种。合适的烷基芳基磺酸盐包括直链烷基苯磺酸盐。合适的直链烷基苯磺酸盐包括直链十二烷基苄基磺酸盐,其可以以中和形成磺酸盐的酸形式提供。另外合适的烷基芳基磺酸盐包括二甲苯磺酸盐和异丙苯磺酸盐。
可用于该清洁组合物的合适的烷烃磺酸盐可以具有含6至24个碳原子的烷烃。可以使用的合适的烷烃磺酸盐包括仲烷烃磺酸盐。合适的仲烷烃磺酸盐包括作为HostapurSAS购自Clariant的C14-C17仲烷基磺酸钠。
可用于该清洁组合物的合适的烷基甲基酯磺酸盐包括具有含6至24个碳原子的烷基的那些。
可用于该清洁组合物的合适的α烯烃磺酸盐包括具有含6至24个碳原子的α烯烃基团的那些。
可用于该清洁组合物的合适的烷基醚硫酸盐包括具有大约1至大约10个重复的烷氧基、大约1至大约5个重复的烷氧基的那些。通常,该烷氧基含有大约2至大约4个碳原子。合适的烷氧基是乙氧基。合适的烷基醚硫酸盐是月桂基醚硫酸钠,并可以以名称Steol CS-460获得。
可用于该清洁组合物的合适的烷基硫酸盐包括具有含6至24个碳原子的烷基的那些。合适的烷基硫酸盐包括但不限于月桂基硫酸钠和月桂基/肉豆蔻基硫酸钠。
可用于该清洁组合物的合适的醇硫酸盐包括具有含大约6至大约24个碳原子的醇基团的那些。
该阴离子型表面活性剂可以用碱性金属盐、胺或其混合物中和。合适的碱性金属盐包括钠、钾和镁。合适的胺包括单乙醇胺、三乙醇胺和单异丙醇胺。如果使用盐的混合物,合适的碱性金属盐的混合物可以是钠和镁,钠对镁的摩尔比可以为大约3:1至大约1:1。
该清洁组合物可以以用水稀释后足以提供具有所需湿润和去污特性的使用组合物的量包含该另外的阴离子型表面活性剂组分。该浓缩物可以含有大约0.1重量%至大约0.5重量%、大约0.1重量%至大约1.0重量%、大约1.0重量%至大约5重量%、大约5重量%至大约10重量%、大约10重量%至大约20重量%、30重量%、大约0.5重量%至大约25重量%和大约1重量%至大约15重量%,以及类似中间浓度的所述阴离子型表面活性剂。
该清洁组合物可以含有非离子型表面活性剂组分,其包含去污量的非离子型表面活性剂或非离子型表面活性剂的混合物。非离子型表面活性剂可以包括在该清洁组合物中以提高油脂去除特性。尽管该表面活性剂组分可以包括非离子型表面活性剂组分,应当理解的是,可以从该去污剂/处理组合物中排除该非离子型表面活性剂组分。
可用于该组合物的非离子型表面活性剂包括聚环氧烷表面活性剂(也称为聚氧化烯表面活性剂或聚烷撑二醇表面活性剂)。合适的聚环氧烷表面活性剂包括聚氧丙烯表面活性剂和聚氧乙烯二醇表面活性剂。合适的这种类型的表面活性剂是合成的有机聚氧丙烯(PO)-聚氧乙烯(EO)嵌段共聚物。这些表面活性剂包括二嵌段聚合物,其包含EO嵌段和PO嵌段,聚氧丙烯单元(PO)的中心嵌段,并具有接枝到聚氧丙烯单元上的聚氧乙烯嵌段,或具有连接的PO嵌段的EO中心嵌段。
此外,该表面活性剂在分子中可以具有聚氧乙烯或聚氧丙烯的其它嵌段。可用的表面活性剂的合适的平均分子量范围可以是大约1,000至大约40,000,环氧乙烷的重量%含量可以是大约10-80重量%。
另外的非离子型表面活性剂包括醇烷氧基化物。合适的醇烷氧基化物包括直链醇乙氧基化物,如TomadolTM 1-5,其是含有具有11个碳原子的烷基和5摩尔环氧乙烷的表面活性剂。另外的醇烷氧基化物包括烷基酚乙氧基化物、支链醇乙氧基化物、仲醇乙氧基化物(例如来自Dow Chemical的Tergitol 15-S-7)、蓖麻油乙氧基化物、烷基胺乙氧基化物、牛脂胺乙氧基化物、脂肪酸乙氧基化物、山梨糖醇油酸酯乙氧基化物、封端的乙氧基化物、或其混合物。另外的非离子型表面活性剂包括酰胺,如脂肪链烷醇酰胺、烷基二乙醇酰胺、椰油酸二乙醇酰胺、月桂酸二乙醇酰胺、聚乙二醇椰油酰胺(例如PEG-6椰油酰胺)、油酸二乙醇酰胺或其混合物。另外的合适的非离子型表面活性剂包括聚烷氧基化脂族碱、聚烷氧基化酰胺、乙二醇酯、甘油酯、胺氧化物、磷酸酯、醇磷酸盐、脂肪酸甘油三酯、脂肪酸甘油三酯酯、烷基醚磷酸盐、烷基酯、烷基酚乙氧基化物磷酸酯、烷基多糖、嵌段共聚物、烷基聚葡糖苷或其混合物。
当非离子型表面活性剂包含在该组合物中时,它们可以以至少大约0.1重量%的量包含,并且可以以最多大约15重量%的量包含。该浓缩物可以包括大约0.1至1.0重量%、大约0.5重量%至大约12重量%或大约2重量%至大约10重量%的该非离子型表面活性剂。
两性表面活性剂也可用于提供所需去污性质。可以使用的合适的两性表面活性剂包括但不限于:甜菜碱、咪唑啉和丙酸盐。合适的两性表面活性剂包括但不限于:甜菜碱(sultaines)、两性丙酸盐、两性二丙酸盐、氨基丙酸盐、氨基二丙酸盐、两性乙酸盐、两性二乙酸盐和两性羟丙基磺酸盐。
当该去污剂组合物包含两性表面活性剂时,可以以大约0.1重量%至大约15重量%的量包含该两性表面活性剂。该浓缩物可以包含大约0.1重量%至大约1.0重量%、0.5重量%至大约12重量%或大约2重量%至大约10重量%的该两性表面活性剂。
该清洁/处理组合物可以含有阳离子型助表面活性剂组分,其包括去污量的阳离子型表面活性剂或阳离子型表面活性剂的混合物。可用于该清洁组合物的阳离子型助表面活性剂包括但不限于:胺类,如具有C18烷基或链烯基链的伯、仲和叔单胺,乙氧基化的烷基胺、乙二胺的烷氧基化物、咪唑类如l-(2-羟基乙基)-2-咪唑啉、2-烷基-l-(2-羟基乙基)-2-咪唑啉等等;以及季铵盐,如烷基氯化季铵表面活性剂,如正烷基(C12-C18)二甲基苄基氯化铵、正十四烷基二甲基苄基氯化铵一水合物和亚萘基取代的氯化季铵,如二甲基-1-萘基甲基氯化铵。
去污剂填料
该清洁组合物可以包括有效量的去污剂填料,其本身不起清洁试剂的作用,但是与清洁试剂配合而提高该组合物的整体清洁能力。
适用于本清洁组合物的去污剂填料的实例包括硫酸钠、氯化钠、淀粉、糖、C1-C10亚烷基二醇如丙二醇等等。当该浓缩物包含去污剂填料时,其可以以大约1重量%至大约20重量%和大约3重量%至大约15重量%的量包含。
消泡试剂
该清洁组合物可以包含消泡试剂以降低泡沫的稳定性并减少起泡。当该浓缩物包含消泡试剂时,该消泡试剂可以以大约0.01重量%至大约3重量%的量提供。
可以用于该组合物的消泡试剂的实例包括环氧乙烷/环氧丙烷嵌段共聚物,如可以以名称Pluronic N3获得的那些,有机硅化合物如分散在聚二甲基硅氧烷中的二氧化硅、聚二甲基硅氧烷以及官能化聚二甲基硅氧烷,如可以以名称Abil B9952获得的那些,脂肪酰胺,烃蜡,脂肪酸,脂肪酯,脂肪醇,脂肪酸皂,乙氧基化物,矿物油,聚乙二醇酯,烷基磷酸酯,如磷酸单硬脂酯,等等。例如可以在授予Martin等人的美国专利号3,048,548、授予Brunelle等人的美国专利号3,334,147和授予Rue等人的美国专利号3,442,242中找到消泡试剂的讨论,其公开内容出于所有目的在此通过引用并入本文。
抗再沉积试剂
该清洁组合物可以包含抗再沉积试剂以促进污物持续悬浮在清洁溶液中并防止去除的污物重新沉积到被清洁的基底上。合适的抗再沉积试剂的实例包括脂肪酸酰胺、氟碳化合物表面活性剂、络合磷酸酯、苯乙烯-马来酸酐共聚物和纤维素衍生物,如羟乙基纤维素、羟丙基纤维素等等。当该浓缩物包含抗再沉积试剂时,可以以大约0.5重量%至大约10重量%和大约1重量%至大约5重量%的量包含该抗再沉积试剂
稳定试剂
可用于该清洁组合物的稳定试剂包括但不限于:脂族伯胺、甜菜碱、硼酸盐、钙离子、柠檬酸钠、柠檬酸、甲酸钠、丙三醇、丙二酸、有机二酸、多元醇、丙二醇及其混合物。该浓缩物不必包含稳定试剂,但是当该浓缩物包含稳定试剂时,其可以以提供该浓缩物所需稳定水平的量包含该稳定剂。稳定试剂的例示性范围包括最高大约20重量%、大约0.5重量%至大约15重量%和大约2重量%至大约10重量%。
水溶助剂
本发明的组合物可以任选包含有助于组成稳定性和含水制剂的水溶助剂。从功能上来说,可以使用的合适的水溶偶联剂(hydrotrope couplers)是无毒的,并在浓缩物或任何使用溶液暴露于其下的整个温度范围和浓度内将所述活性成分保持在水溶液中。
可以使用任何水溶偶联剂,只要其不与该组合物的其它组分反应或负面影响该组合物的性能特性。可以使用的水溶偶联试剂或增溶剂的代表性类别包括阴离子型表面活性剂如烷基硫酸盐和烷烃磺酸盐,直链烷基苯或萘磺酸盐,仲烷烃磺酸盐,烷基醚硫酸盐或磺酸盐,烷基磷酸盐或膦酸盐,二烷基磺基琥珀酸酯,糖酯(例如失水山梨糖醇酯),胺氧化物(单-、二-或三烷基)和C8-C10烷基葡糖苷。用于本发明的优选的偶联剂包括可以作为NAS 8D获自Ecolab Inc.的正辛烷磺酸盐,正辛基二甲基氧化胺,和通常可获得的芳族磺酸盐,如烷基苯磺酸盐(例如二甲苯磺酸盐)或萘磺酸盐,芳基或烷芳基磷酸酯或其具有1至大约40个环氧乙烷、环氧丙烷或环氧丁烷单元的烷氧基化类似物,或其混合物。其它优选的水溶助剂包括以下的非离子型表面活性剂:具有1至大约15个环氧烷基团(优选大约4至大约10个环氧烷基团)的C6-C24醇烷氧基化物(烷氧基化物指的是乙氧基化物、丙氧基化物、丁氧基化物及其共聚物或三聚物混合物)(优选C6-C14醇烷氧基化物);具有1至大约15个环氧烷基团(优选大约4至大约10个环氧烷基团)的C6-C24烷基酚烷氧基化物;具有1至大约15个糖苷基团(优选大约4至大约10个糖苷基团)的C6-C24烷基多糖苷(优选C6-C20烷基多糖苷);C6-C24脂肪酸酯乙氧基化物、丙氧基化物或甘油酯;以及C4-C12单或二烷醇酰胺。优选的水溶助剂是二甲苯磺酸钠(SXS)。
任选的水溶助剂的组合物可以以大约0至大约25重量%存在。
染料和香料
各种染料、添味剂(包括芳香剂)和其它美学增强试剂也可以包括在该清洁组合物中。可以包括染料以改变该组合物的外观,如多种FD&C染料、D&C染料等等的任一种。另外的合适的染料包括直接蓝86(Miles)、Fastusol Blue(Mobay Chemical Corp.)、酸性橙7(American Cyanamid)、碱性紫10(Sandoz)、酸性黄23(GAF)、酸性黄17(Sigma Chemical)、Sap Green(Keystone Aniline and Chemical)、间胺黄(Keystone Aniline andChemical)、酸性蓝9(Hilton Davis)、Sandolan Blue/酸性蓝182(Sandoz)、Hisol FastRed(Capitol Color and Chemical)、荧光黄(Capitol Color and Chemical)、酸性绿25(BASF)、Pylakor Acid Bright Red(Pylam)等等。
可以包含在该组合物中的香料或芳香剂包括例如萜类化合物如香茅醇,醛类如戊基肉桂醛,茉莉(jasmine)如顺式-茉莉或茉莉吡喃(jasmal),香草醛等等。
佐剂
本发明的组合物还可以包括任意数量的佐剂。
具体而言,该清洁组合物在可以添加到该组合物中的任意数量的其它成分中可以包含稳定试剂、湿润试剂、增稠剂、发泡试剂、缓蚀剂、杀生物剂、过氧化氢、颜料或染料。此类佐剂可以与本发明的组合物一起预先配制,或同时添加到该体系中,或甚至在添加本组合物后。该清洁组合物还可以含有任意数量的用途所需的其它成分,其是已知的并有利于本组合物的活性。
本组合物的实施方案
本发明的清洁组合物有效地去除含有蛋白质、猪油和油类的污物。在一个实施方案中,该清洁组合物有效去除含有高达大约20%的蛋白质的污物。在下表中提供了几种合适的例示性浓缩液组合物。
表1.例示性组成
在RTU组合物的情况下,要注意的是,如果需要的话,上面公开的清洁组合物可以用基于该清洁组合物重量的最多大约96重量%的水进一步稀释。
使用方法
本发明的保护剂组合物具有多种应用,例如但不限于汽车护理应用、家庭护理应用、个人护理应用、工业和机构应用、制药应用、纺织品应用等等。所述保护剂组合物可用于处理众多无生命表面,包括但不限于遍及家庭和汽车领域的内部与外部的硬质和柔软表面。该保护剂组合物可用于其上的家庭表面包括但不限于地板、台面、家具、墙壁和玻璃、塑料、玻璃纤维、层压材料如Formica.TM.和Corian.TM.、瓷砖、瓷、砖、混凝土、石灰石、水泥浆、大理石、花岗岩构成的表面以及金属表面如铝、钢、不锈钢、铁、铬、铜、黄铜等等。其它家庭表面包括地毯、室内装潢、乙烯基树脂、皮革、纺织品、织物、地板、墙壁、天花板和墙壁饰面,如壁纸、涂漆面和面板。该保护剂组合物可用于其上的汽车表面包括轮胎、橡胶、乙烯基树脂、织物、塑料和在船只、车辆、汽车、公共汽车、轿车、飞机、摩托车等等的外部和内部发现的通常的弹性体表面。
使用方法
本发明的保护剂组合物可以通过多种方式施加到目标表面上,包括通过喷雾、泵或气雾剂分配装置的直接涂施,或通过其它方式,包括使用载体,或稀释系统,例如但不限于洗涤、浸渍或浸泡工艺。关于通过使用载体的涂施,此类合适的载体包括例如浸渍的擦拭物、泡沫、海绵、布、毛巾、纸巾或纸毛巾或能够通过直接物理接触涂施本发明的组合物并将其由载体转移到目标表面(通常在铺展、填充、摩擦或擦拭操作过程中)的类似可释放吸收性载体。直接涂施与随后借助泡沫、海绵、布、毛巾、纸巾或纸毛巾、刮板或类似的擦拭器具进行的铺展、填充、摩擦或擦拭操作的组合也适于涂施本发明的保护剂组合物。
该保护剂组合物还可以直接喷到目标表面上,因此通常包装在喷雾分配器中。该喷雾分配器可以是本领域已知的用于制造液滴喷雾的手动激活装置的任意一种,例如扳机型、泵型、电喷雾、液压喷嘴、声波雾化器、高压喷雾嘴、非气雾剂自加压式和气雾剂型喷雾装置。在本文中也可以使用自动激活装置。这些类型的自动装置类似于手动激活装置,除了推进剂被压缩机取代。该喷雾分配器可以是气雾剂分配器。所述气雾剂分配器包含可由任何用于制造气雾剂容器的常规材料构造的容器。市售气雾剂喷雾分配器的更完整的描述出现在美国专利号3,436,772和3,600,325中,二者均在此通过引用全文并入本文。或者,该喷雾分配器可以是具有盘绕衬里(convoluted liner)和弹性套筒的自加压式非气雾剂容器。自加压式喷雾分配器的更完整的描述可以在美国专利号4,260,110;5,111,971和5,232,126中找到,其均在此通过引用全文并入本文。该容器与泵机构可以由任何用于制造泵-喷雾分配器的常规材料构造,所述材料包括但不限于:聚乙烯;聚丙烯;聚对苯二甲酸乙二醇酯;聚乙烯、乙酸乙烯酯和橡胶弹性体的共混物。其它材料可包括不锈钢。市售分配装置的更完整的公开出现在:美国专利号4,082,223;4,161,288;4,274,560;4,434,917;4,735,347;4,819,835;4,895,279和5,303,867;其均在此通过引用全文并入本文。
形成本发明的组合物
混合系统提供成分在高剪切下的连续混合以形成基本均匀的液体或半固体混合物,其中该成分分布在其整个质量中。混合系统包括用于混合该成分的装置以提供有效地将该混合物保持在可流动稠度下的剪切,且在处理过程中的粘度为大约1,000-1,000,000cP、优选大约50,000-200,000cP。该混合系统可以是连续流混合机或单螺杆或双螺杆挤出机设备。
该混合物可以在一定温度下处理以保持成分的物理和化学稳定性,如在大约20-80℃,和大约25-55℃的环境温度下。尽管可以对该混合物施加有限的外部热,由于摩擦、在环境条件下的变动和/或通过成分间的放热反应,该混合物达到的温度可以在加工过程中升高。任选地,混合物的温度可以在例如混合系统的入口或出口处提高。
成分可以为液体或固体如干燥颗粒的形式,并可以单独或作为与另一成分的预混料的一部分添加到该混合物中,例如,防垢组分可以与餐具洗涤去污剂的其余部分分离。可以将一种或多种预混料添加到该混合物中。
将该成分混合以形成基本均匀的稠度,其中该成分在其整个质量中基本均匀地分布。
该浓缩物可以以液体的形式提供。各种液体形式包括凝胶和糊料。当然,当该浓缩物以液体形式提供时,不必硬化该组合物以形成固体。事实上,期待该组合物中的水量将足以阻止固化。此外,分散剂和其他组分可引入该浓缩物中以保持组分的所需分布。
该包装接受器或容器可以是刚性或柔性的,并由适于包含根据本发明制得的组合物的任何材料组成,例如玻璃、金属、塑料膜或片、纸板、纸板复合材料、纸张等等。该组合物在大约150-170℉下处理,并通常在包装前冷却至100-150℉,使得处理的混合物可以直接浇铸或挤出到该容器或其它包装系统中,而不会在结构上破坏该材料。结果,与用于在熔融条件下处理和分散的组合物的那些材料相比,可以使用更多种多样的材料来制造该容器。
该包装材料可以作为水溶性包装材料如水溶性包装膜来提供。例示性水溶性包装膜公开在美国专利号6,503,879;6,228,825;6,303,553;6,475,977;和6,632,785中,其公开内容在此通过引用并入本文。可以提供可用于包装该浓缩物的包装材料的例示性水溶性聚合物包括聚乙烯醇。该包装的浓缩物可以以单位剂量包装形式或多剂量包装形式提供。在单位剂量包装的情况下,期待将单个包装单位放置在洗碗机中,如洗碗机的去污剂隔室中,并在单个洗涤周期中用完。在多剂量包装的情况下,期待将该单位放置在料斗中,水流将侵蚀浓缩物表面以提供将要引入到该洗碗机中的液体浓缩物。
形成稳定乳液的步骤
该有机硅制剂可以相当快速地分离为两相。为了确保初始制剂的两相的一致与正确的比例,增稠试剂将油滴悬浮在水中。
一旦该制剂包括用于液滴悬浮的黄原胶,该工艺需要进一步限定,需要满足两个标准:
1)该增稠剂(如黄原胶)必须在与聚二甲基硅氧烷组合前充分水合,和
2)该聚二甲基硅氧烷必须在与水组合前与表面活性剂、任何香料和任何缓冲剂共混。
要求两种预混料达到两种工艺限定标准。在主混合罐中制造该黄原胶预混料,而预混料罐用于该有机硅预混料。选择这种安排以匹配现有的混合设备。尽管混合有机硅预混料直至均匀,其随时间推移分离为两相。期望有机硅预混料的稳定性以确保与水组合时获得均匀的乳液。
通常,粗乳状液是热力学不稳定的,并且可以化学计量地使用表面活性剂以便通过降低表面张力来使其稳定化。但是,为了在最终用途中提供额外的去污力,该制剂中使用的表面活性剂的量超出了化学计量量。
我们通过在内部乳化一点水实现了稳定的PDMS+表面活性剂预混料。这使得油包水乳液成为最稳定的成品。随后,水量降低至反相点的30%并实现了稳定的油包水预混料,和稳定的最终产品。所得乳液在不具有高剪切的情况下是稳定的,并且油滴通常并不聚结。该工艺还能够在不具有表面活性剂和有机硅的化学计量比的情况下产生稳定的乳液。
在仅旨在作为示例的下列实施例中更具体地描述本发明,因为在本发明范围内的多种修改和变化将对本领域技术人员显而易见。除非另行说明,下面实施例中报道的所有份数、百分比和比率以重量为基础,该实施例中使用的所有试剂获自或可获自下面描述的化学品供应商,或可以通过常规技术合成。
实施例1
由于正在全球范围内在店面重建和新建筑物中实施新的装饰类型,快餐店(QSR)中摊位表面的可清洁性变得越来越有挑战性。
摊位表面清洁度是在整个连锁店与全球各个位置中最普遍的装饰担忧。其中之前的摊位表面在历史上均为硬质乙烯基树脂,新的装饰向着更高端的材料变化,包括皮革、软质乙烯基树脂和室内装潢织物。这些更柔软的装饰因其更重的纹理表面及其更柔软的设计而更易被污物侵染,产生现有清洁溶液和程序无法达到的藏污纳垢的所在。深印花柔软乙烯基树脂装饰和内部装潢织物的黑色油烟污染提供了最大的清洁挑战。
本发明涉及开发用于这些目的的清洁产品。
第一原型:
制剂SC-2、SC-3、SC-5、SC-7、SC-9、SC-11和SC-12是不稳定的并作为选项丢弃。制剂SC-1、SC-4、SC-6、SC-8、SC-10和SC-13是可能的制剂,但是不满足全球组合物的制剂要求。
增稠剂制剂:
上述制剂是开发以测试增稠剂特性的第一批制剂:Custopoly GL不像黄原胶那样与该组合物良好地起作用。
优化的制剂:
RM | SC-14 | SC-15 | SC-16 | SC-17 | |
290287 | ADC Silicone 200FL | 3 | 5.418 | 13.6 | 8.751 |
116178 | 三乙醇胺99%DRM | 0.05 | 0.04 | 0.04 | 0.027 |
170575 | C10-12合成醇和3摩尔乙烯 | 4 | 6 | 2 | 3 |
172452 | 月桂基二甲胺氧化物30%DRM | 7.38 | 3.20 | 3.20 | 4.17 |
177035 | 椰油酰胺基丙基甜菜碱 | 4.00 | 2.00 | 6.00 | 3.00 |
830845 | 黄原胶 | ||||
100016 | 水沸石软化的TNK | 81.425 | 83.197 | 75.015 | 80.906 |
300148 | 2-甲基-4-异噻唑啉-3-酮DRM | 0.15 | 0.15 | 0.15 | 0.15 |
制剂SC-14至SC-17是开发的。
更好的乳化和无PPE制剂:
通过添加原材料170654聚氧乙烯失水山梨糖醇单油酸酯,该制剂具有更好的乳化。上面的制剂无需个人保护设备。随后在配制过程中重新考虑了添加增稠剂,并选择了黄原胶。
最终制剂:
任何残余部分为水、香料或其它另外的组分:
230115 | 20 | 黄原胶 | 0.37 |
177056 | 30 | 椰油酰胺基丙基甜菜碱 | 2 |
300148 | 40 | 2-甲基-4-异噻唑啉-3-酮DRM | 0.15 |
290287 | 50 | ADC Silicone 200FL | 8.62 |
170654 | 60 | 聚氧乙烯(20)失水山梨糖醇单油酸酯 | 6.7 |
170270 | 70 | C10-12合成醇和3摩尔乙烯 | 3.2 |
116178 | 80 | 三乙醇胺99%DRM | 0.04 |
对污物进行的原型实验台性能测试
o将污物施加到基底上并静置干燥24小时。所用污物是存在于QSR环境中的那些,如番茄酱、芥末、红色食品污物和黑色食品污物。后二者作为Ecolab制造的标准污物而提及。
o在使污物静置而在表面上干燥后,待测试区域用原型溶液擦拭并记录观察结果。
o在清洁之前、过程中和之后拍摄显微照片。
o根据照片看起来如何来分析性能。
在名为皮革清洁剂的附件中讨论了照片和结论。
红色食品污物
猪油3
玉米油,100%
整个干蛋(dry egg)
氧化铁III,粉末
黑色食品污物
低气味溶剂油
矿物油
机油:10/30W(SM级)
Oil Dag(石墨润滑剂)
Black Charm球状粘土
程序
基底和污物识别:
1.摊位基底获自Ecolab QSR Request for Technical Information(RTI)项目档案。表面类型包括:
i.皮革
ii.软质乙烯基树脂,略微带有印花至无印花
iii.软质乙烯基树脂,重印花(皮革状)
iv.硬质乙烯基树脂
v.织物室内装潢
2.获得可以带来家庭环境的QSR前沿(QSR front)中的潜在的清洁挑战的代表性污物
i.番茄酱
ii.芥末
iii.苏打
iv.油脂/起酥油
v.鞋子痕迹
vi.尘土污物(Gardner Abrasion SOP配方)
vii.食品污物(Gardner Abrasion SOP配方)
3.将基底污染并清洁
i.污物沿基底宽度以水平图案施加
ii.令污物空气干燥并老化24小时
iii.将清洁剂喷到纸毛巾上,并随后用于穿过污物清洁以获得最佳可能清洁。产品未再涂施。
结果与讨论
经由上述规程将基底样品污染并清洁。
图1显示了初始性能筛选。将皮革件污染并随后用不同的皮革与乙烯基树脂清洁剂原型清洗。在污染前、污染后和在清洁后拍摄显微照片。标有星号的那些照片是表现最好的。这里显示的照片仅针对黑色污物。
图2A和2B显示了不同制剂的清洁性能。配方SC-3、SC-5、SC-6和SC-7显示具有令人满意的清洁。
图3是显示配方SC-3、SC-5、SC-6、SC-L、SC-8、SC-9、SC-10、SC-1、SC-12、H2O和SC-13的光泽性能的图。
图4显示了各种清洁剂的实地测试结果。5次测量的平均值取为各读数。本发明的组合物和微纤维除去100%的表面污物和80%的嵌入污物,留下清洁的表面。APSC(一种市售多用途表面清洁剂,不含任何润湿剂或表面活性剂)和食品服务巾除去几乎所有表面污物,但是仅除去大约30%的嵌入污物,并在表面上留下微珠形式的污物。
在下面的照片中,通过使用本发明的组合物和微纤维布前后擦洗而产生十字形。该链的其余部分已经用APSC和毛巾预先清洁过。结果表明,本发明的组合物除去90%的表面和嵌入污物,而APSC仅除去25%的表面和嵌入污物。
图5显示了在皮革凳上的测试。本发明的组合物与在皮革上表现非常好的微纤维布结合使用,令表面湿润但又不过分闪亮,触感柔软,无油腻残余物,并显示从皮革裂纹和缝隙中除去95%的污物。
在下面的照片中,本发明的组合物与微纤维除去比APSC和毛巾更多的污物,但是由于乙烯基树脂的独特质地,两种产品的表现均不是特别出色。本发明的组合物除去大约60%的表面和嵌入污物,而APSC除去大约35%的污物。
图6显示在清洁布上的残留残余物。如可以看到的那样,即使表面看上去干净,仍然存在可以去除的大量污物。下表1显示了采用本发明的清洁剂的试验的现场效果。ΔE值越高,从座位的表面上去除的污物越多(颜色变化越大)。由该结果可以看出,本发明的组合物具有优于不具有本发明的表面活性剂组合或任何润湿剂的市售多种表面清洁剂的清洁。
现场筛选ΔE结果:
*备注-ΔE值越高,从座位的表面上去除的污物越多(颜色变化越大)。5次测量的平均值取为各读数。
图7是显示本发明的组合物与市售皮革/乙烯基树脂清洁剂相比的ΔE值的图。可以看出,本发明的组合物清洁得要比市售清洁剂好得多。这一发现也可以在该图旁显示的布料照片中看出。
图8显示了黄色乙烯基树脂凳清洁的ΔE值的图。同样,本发明的组合物的ΔE值更高。照片也显示了这一点。
图9是显示褐色皮革凳上的污渍去除的图。本发明的组合物显示出高得多的ΔE值,因此本发明的组合物显然除去最多污物。这也图画地显示在照片中。
图10显示了快餐店高脚椅的照片。本发明的组合物在这里用在椅子底部上的黑色划痕上。本发明的组合物除去最多划痕,显示本发明的清洁组合物的进一步用途。
实施例2
本发明还包括使用该乳化剂/增稠剂以保持稳定乳液的特定工程工艺。首先,该增稠剂,优选黄原胶在与有机硅组合之前必须充分水合,其次,有机硅在与水组合之前必须与表面活性剂、香料和缓冲剂共混。
首先通过在预混料罐中添加香料、表面活性剂、水溶助剂和有机硅来制备有机硅预混料。该组分混合大约10分钟以形成乳液。接着,加入少量的水。随后用黄原胶和足以水合该胶的水制造第二预混料。该组分混合15分钟的时间间隔并取样用于分析粘度。粘度可以通过型号LVDV1P115的布氏粘度计(小量样品适配器主轴21,30RPM和77F)来测定。粘度范围对于最终配方为106-372,期望粘度为239。
当达到足够粘度时,加入防腐剂和任何另外的表面活性剂并混合。最后,加入第一预混料,将组分混合15分钟,将该批料取样,如果需要的话再混合一定的时间,直到获得合意的乳液。
实现此类稳定乳液时相当令人惊讶的,因为通常,粗乳状液是热力学不稳定的,并且可以化学计量地使用表面活性剂以便通过降低表面张力来使其稳定化。但是,为了在最终用途中提供额外的去污力,该制剂中使用的表面活性剂的量超出了化学计量量。
申请人通过在内部乳化水实现了稳定的聚二甲基硅氧烷与表面活性剂的预混料。出乎意料的是,制造油包水乳液首先制造了最稳定的成品。随后,水量降低至反相点的30%并仍实现了稳定的油包水预混料,和稳定的最终产品。该乳液相当独特,在于最终配方中的油滴并未聚结,这在不具有高剪切的情况下产生了稳定的乳液,并在不具有表面活性剂:聚二甲基硅氧烷的化学计量比的情况下产生了稳定的乳液。
Claims (18)
1.用于皮革、乙烯基树脂和类似表面的清洁/处理组合物,包含:
(a)有机硅组分;
(b)胺分散剂;
(c)防腐剂;
(d)基于该清洁/处理组合物重量的4%至20%的包含醇烷氧基化物、椰油酰胺丙基甜菜碱和失水山梨糖醇酯的组合的表面活性剂组分,其中所述椰油酰胺丙基甜菜碱的量为该清洁/处理组合物重量的约2%;
(e)增稠剂;任何余量为水或其它功能组分。
2.权利要求1的组合物,其中所述醇烷氧基化物是具有3-6摩尔乙氧基化物的C10至C12醇。
3.权利要求1的组合物,其中所述失水山梨糖醇酯是聚氧乙烯(20)失水山梨糖醇单油酸酯。
4.权利要求1的组合物,其中所述胺分散剂是三乙醇胺。
5.权利要求1的组合物,其中所述有机硅组分以所述组合物重量的0.01%至10%的量存在。
6.权利要求1的组合物,其中所述表面活性剂组分包含椰油酰胺基丙基甜菜碱、具有3-6摩尔乙氧基化物的C10至C12醇和聚氧乙烯(20)失水山梨糖醇单油酸酯的组合。
7.权利要求6的组合物,其中所述三种组分以表面活性剂组分重量的1:1:2的比存在。
8.清洁、防护和保护皮革表面的方法,包括以下步骤:使皮革表面与有效清洁量的清洁组合物接触,所述清洁组合物包含:
i)基于该清洁组合物重量的0.3%至20%的选自聚硅氧烷共聚物、有机硅-丙烯酸酯共聚物、硅油、氨基取代的有机硅共聚物衍生物及其混合物的有机硅衍生物;
ii)基于该清洁组合物重量的0.027%至0.05%的至少一种稳定剂;
iii)基于该清洁组合物重量的4%至20%的选自醇烷氧基化物、椰油酰胺丙基甜菜碱和失水山梨糖醇酯的组合的去污表面活性剂,其中所述表面活性剂对使用者是温和的和无刺激的,和所述椰油酰胺丙基甜菜碱的量为该清洁组合物重量的约2%;
iv)基于该清洁组合物重量的0.12%至0.17%的防腐剂,任何余量为水,
并用布或一次性衬底擦拭所述皮革表面。
9.权利要求8的方法,其中所述组合物是稳定乳液。
10.权利要求8的方法,其中所述接触不会留下粘性残余物。
11.权利要求8的方法,其中所述组合物能够从所述表面除去芥末、非反式脂肪、来自食品产品的油脂、烹饪油脂或番茄酱。
12.制造清洁/处理组合物的方法,包括:
用水水合增稠剂组分以便形成第一预混料溶液;
将表面活性剂组分与有机硅共混以形成第二预混料溶液,其中所述表面活性剂组分包含醇烷氧基化物、椰油酰胺丙基甜菜碱和失水山梨糖醇酯的组合,其中所述椰油酰胺丙基甜菜碱的量为该清洁/处理组合物重量的约2%;和
之后将所述第一和第二预混料与包括防腐剂、稳定剂和其它非功能组分的其它组分混合以形成稳定的乳液。
13.权利要求12的方法,其中所述表面活性剂组分占所述预混料的70%,且10%为水,余量为有机硅。
14.权利要求12的方法,其中所述增稠剂是黄原胶。
15.权利要求12的方法,其中该清洁/处理组合物包含:
i)基于该清洁/处理组合物重量的0.3%至20%的选自聚硅氧烷共聚物、有机硅-丙烯酸酯共聚物、硅油、氨基取代的有机硅共聚物衍生物及其混合物的有机硅;
ii)基于该清洁/处理组合物重量的0.027%至0.05%的至少一种稳定剂;
iii)基于该清洁/处理组合物重量的4%至20%的包含椰油酰胺基丙基甜菜碱、具有3-6摩尔乙氧基化物的C10至C12醇和聚氧乙烯(20)失水山梨糖醇单油酸酯的组合的表面活性剂组分,其中所述表面活性剂组分对使用者是温和的且无刺激的,和所述椰油酰胺基丙基甜菜碱的量为该清洁/处理组合物重量的约2%;
iv)基于该清洁/处理组合物重量的0.12%至0.17%的防腐剂,任何余量为水。
16.权利要求12的方法,其中所述有机硅是聚二甲基硅氧烷。
17.权利要求15的方法,其中所述混合持续一小时。
18.权利要求15的方法,其中所述乳液是不具有高剪切的稳定乳液。