CN107385928A - 一种防水透气新材料 - Google Patents
一种防水透气新材料 Download PDFInfo
- Publication number
- CN107385928A CN107385928A CN201710659367.8A CN201710659367A CN107385928A CN 107385928 A CN107385928 A CN 107385928A CN 201710659367 A CN201710659367 A CN 201710659367A CN 107385928 A CN107385928 A CN 107385928A
- Authority
- CN
- China
- Prior art keywords
- waterproof
- breathable
- new material
- silica gel
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防水透气新材料，材料的组成主要采用了布料与硅胶的结合,通过含浸工艺加工处理,主要功能可实现透气,不漏水。所述材料是首先将乙烯基硅油、气相法二氧化硅、乙烯基MQ树脂、含氢硅油、铂金催化剂、抑制剂经分散混合均匀后使用正庚烷稀释到20％的固含量，然后将涤纶纤维与氨纶混纺的针织织物含浸到上述的液体硅胶溶液中，取出后挤干，再使用热风烘道烤干即制得防水透气新材料。解决了目前市面上泳衣等大多不透气，硬度较大，使用时出现与身体相应部位不匹配的状况，与水接触的过程中出现滑脱的状况等的问题。本防水透气新材料具有防水性能好，舒适透气性好等的优点。
Description
技术领域
本发明涉及一种防水透气材料，尤其涉及游泳眼镜，泳帽,蛙鞋等所使用的材料。
背景技术
在服装行业里，服装的面料五花八门，日新月异。但是从总体上来讲，优质、高档的面料，大都具有穿着舒适、吸汗透气、视觉高贵、触觉柔美等几个方面的特点。泳衣的选择也看制作的面料以及具备的性能。好的泳衣面料柔软、耐穿、有弹性，布料的纹路相对较密。不仅泳衣如此，其他的泳帽、蛙鞋等在材质的选择上也要用弹性大、耐磨、安全、对皮肤无刺激、寿命长的材质。目前市售的游泳用品大多采用硅胶或塑胶材料，例如，公告号为CN1202886C的中国发明专利，公开了“游泳镜及其制备工艺”，其发明的游泳镜在权利要求中要求所用材质为硬质材料，该专利虽未限定何种硬质材料，但是可以知道硬质材料没有弹性，对身体有一定的压迫。这些材料在使用中，大多不透气且没有弹性，使使用者在使用的过程中出现轻微不适状况。另外，由于硬度等的问题，使用户在使用中会出现与脸型、头型、脚型，等不匹配的状况，从而对身体某些部位产生压迫，造成血液流通不畅，甚至发生危险，并且有些泳具在与水接触的过程中会出现滑脱等状况。因此，本发明研发了一种防水透气的新材料，既让人穿着安全舒适又能达到防水、透气作用，对于泳具行业具有重要的意义。
发明内容
本发明的目的，就是针对上述的游泳用品，采用大胆创新方案，将硅胶与布料进行结合，从而克服以上存在的问题。
为达到上述目的，本发明采用如下的技术方案：一种防水透气材料，材料的组成主要采用了布料与硅胶的结合,通过含浸工艺加工处理，主要功能可实现透气,不漏水。所述材料是首先将乙烯基硅油、气相法二氧化硅、乙烯基MQ树脂、含氢硅油、铂金催化剂、抑制剂经分散混合均匀后使用正庚烷稀释到20％的固含量，然后将涤纶纤维与氨纶混纺的针织织物含浸到上述的液体硅胶溶液中，取出后挤干，再使用热风烘道烤干即制得防水透气新材料。
所述的防水透气新材料，其特征在于透气(可通过呼气试验)，从材料的一面进行吹气,气息很容易透过材料从材料的另一面透出；不漏水(可进行漏水测试)，将水滴于材料表面2个小时内未见其渗透；舒适性，本材料具有一定的弹性，佩戴该材料所生产的产品，可根据佩戴者的佩戴部位进行伸缩。
所述的防水透气新材料，其特征在于表面布料粗糙度增加使产品的表面摩擦系数增大，继而使产品在使用过程中不易出现滑脱。
所述的防水透气新材料，其特征在于加工工艺是将布料含浸在液体硅胶的溶液中，再通过挤干，烘干而成。
所述的防水透气新材料，其特征在于液体硅胶的组成为20-60％的乙烯基硅油、10-30％的气相法二氧化硅、10-30％乙烯基MQ树脂、5-10％含氢硅油，0.5-2％铂金催化剂，以及为了实现材料的特殊性能适当添加一些抑制剂、增粘剂等。
所述的防水透气新材料，其特征在于使用溶剂将上述的液体硅胶稀释成5-30％的溶液进行含浸，溶剂可以是乙酸乙酯、乙酸丁酯、正庚烷、无味煤油等化学试剂。
所述的防水透气新材料，其特征在于布料的结构可以是双面弹的针织布或者四面弹的针织布。
所述的防水透气新材料，其特征在于布料的材质可以是纯棉、粘胶纤维、涤纶、氨纶以及它们之间相互的混纺。
附图说明
为了更清楚地说明本发明实施例或现有技术中的技术方案，下面将对实施例或现有技术描述中所需要使用的附图作简单地介绍，显而易见地，下面描述中的附图仅仅是本发明型的一些实施例，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他的附图。
图1是本发明部分材料的示意图；
图2是本发明材料在拉伸前后的对比图，其中a是拉伸前，b是拉伸后；
图3是本发明材料漏水测试前后的对比图，其中a是漏水前，b是漏水后；
具体实施方式
下面将结合本发明实施例中的附图，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明型一部分实施例，而不是全部的实施例。基于本发明型中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于发明保护的范围。
【实施例1】
步骤1：将52.5wt％乙烯基硅油、25wt％的气相法二氧化硅、15wt％乙烯基MQ树脂、6wt％含氢硅油、1wt％铂金催化剂、0.5wt抑制剂进行分散、混合均匀；
步骤2：将步骤1中的混合物用正庚烷稀释到20％的固含量；
步骤3：将涤纶纤维与氨纶混纺的针织织物含浸到步骤2中的液体硅胶溶液中；
步骤4：将浸胶后的针织织物取出、挤干，并使用热风烘道烤干即制得防水透气新材料样品A。
【实施例2】
步骤1：将50wt％乙烯基硅油、20wt％的气相法二氧化硅、23wt％乙烯基MQ树脂、5.5wt％含氢硅油、1wt％铂金催化剂、0.5wt抑制剂进行分散、混合均匀；
步骤2：将步骤1中的混合物用正庚烷稀释到20％的固含量；
步骤3：将纯棉与氨纶混纺的针织织物含浸到步骤2中的液体硅胶溶液中；
步骤4：将浸胶后的针织织物取出、挤干，并使用热风烘道烤干即制得防水透气新材料样品B。
【实施例3】
步骤1：将47.5wt％乙烯基硅油、15wt％的气相法二氧化硅、30wt％乙烯基MQ树脂、6wt％含氢硅油、1wt％铂金催化剂、0.5wt抑制剂进行分散、混合均匀；
步骤2：将步骤1中的混合物用正庚烷稀释到20％的固含量；
步骤3：将粘胶纤维与氨纶混纺的针织织物含浸到步骤2中的液体硅胶溶液中；
步骤4：将浸胶后的针织织物取出、挤干，并使用热风烘道烤干即制得防水透气新材料样品C。
【实施例4】
步骤1：将47.5wt％乙烯基硅油、10wt％的气相法二氧化硅、35wt％乙烯基MQ树脂、6wt％含氢硅油、1wt％铂金催化剂、0.5wt抑制剂进行分散、混合均匀；
步骤2：将步骤1中的混合物用正庚烷稀释到20％的固含量；
步骤3：将粘胶纤维与氨纶混纺的针织织物含浸到步骤2中的液体硅胶溶液中；
步骤4：将浸胶后的针织织物取出、挤干，并使用热风烘道烤干即制得防水透气新材料样品D。
根据实施例1-4，制造出防水透气新材料样品A、样品B、样品C、样品D，并使用以下方法对防水透湿性能进行测试：
抗水压的测试方法：按照GB/T4744-2013《防水性能的检测和评价静水压法》方法测试。
透湿性的测试方法：按照GB/T12704.1-2009《织物透湿性试验方法第1部分吸湿性》方法测试。
测试结果如下：
| 样品 | 抗静水压(kpa) | 透湿性(g/m2.day) |
| 样品A | 50 | 5100 |
| 样品B | 43 | 5523 |
| 样品C | 48 | 5151 |
| 样品D | 38 | 5682 |
测试结果表面，本发明所提供的防水透气新材料具有非常好的防水、透气、透湿性能。
综上，本发明具有的优点和积极效果是：本发明一种防水透气的新材料，具有一定的弹性，既能让人穿着安全舒适又能达到防水、透气作用，解决了目前市售的游泳用品大多采用硅胶或塑胶材料，这些材料在使用中，大多不透气且没有弹性，使用户在使用中会出现与脸型、头型、脚型，等不匹配的状况，从而对身体某些部位产生压迫，造成血液流通不畅，甚至发生危险，滑脱等状况的问题。
Claims (9)
1.一种防水透气新材料，其特征在于材料的组成主要采用了布料与硅胶的结合,通过含浸工艺加工处理,主要功能可实现透气,不漏水，具有防水、透气性能，同时具有较高的舒适性。
2.如权利要求1所述的防水透气新材料，适用于除泳镜镜片之外的所有配件，及泳帽，蛙鞋等。
3.如权利要求1所述的防水透气新材料，其特征在于：透气(可通过呼气试验),从材料的一面进行吹气,气息很容易透过材料从材料的另一面透出；不漏水(抗静水压测试),将水滴于材料表面2个小时内未见其渗透；舒适性,本材料具有一定的弹性,佩戴该材料所生产的产品,可根据佩戴者的佩戴部位进行伸缩。
4.如权利要求1所述的防水透气新材料，由于表面布料粗糙度增加做成的产品表面摩擦系数增大，使佩戴该材料的产品不易在使用过程中出现滑脱。
5.如权利要求1所述的防水透气新材料，其特征在于加工工艺是通过将布料含浸在液体硅胶的溶液中，再通过挤干，烘干而成。
6.如权利要求1所述的防水透气新材料，其特征在于液体硅胶的组成为20-50％的乙烯基硅油、10-30％的白炭黑、10-30％乙烯基MQ树脂、5-10％含氢硅油，0.5-2％铂金催化剂，以及为了实现材料的特殊性能适当添加一些抑制剂、增粘剂等。
7.如权利要求1所述的防水透气新材料，其特征在于使用溶剂将上述的液体硅胶稀释成5-30％的溶液进行含浸，溶剂可以是乙酸乙酯、乙酸丁酯、正庚烷、无味煤油等有机化学试剂。
8.如权利要求1所述的防水透气新材料，其特征在于布料的结构可以是双面弹的针织布或者四面弹的针织布。
9.如权利要求1所述的防水透气新材料，其特征在于布料的材质可以是纯棉、粘胶纤维、涤纶、氨纶以及它们之间相互的混纺。