CN107384106A - A kind of preparation of exterior wall reflective thermal insulation texture coating with degraded haze function and construction method - Google Patents
A kind of preparation of exterior wall reflective thermal insulation texture coating with degraded haze function and construction method Download PDFInfo
- Publication number
- CN107384106A CN107384106A CN201710642093.1A CN201710642093A CN107384106A CN 107384106 A CN107384106 A CN 107384106A CN 201710642093 A CN201710642093 A CN 201710642093A CN 107384106 A CN107384106 A CN 107384106A
- Authority
- CN
- China
- Prior art keywords
- exterior wall
- thermal insulation
- reflective
- degraded
- texture coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of exterior wall reflective thermal insulation texture coating with degraded haze function disclosed by the invention, is made up of water, cellulose, wetting agent, dispersant, defoamer, propane diols, coalescents, reflective insulation titanium dioxide, nano titanium oxide, blanc fixe, silicone acrylic emulsion, bactericide, preservative, white quartz sand and reflective insulation cool colour slurry.The invention also discloses the preparation method and construction method of the exterior wall reflective thermal insulation texture coating with degraded haze function.The invention has the characteristics that：1st, by doing film forming matter from silicone acrylic emulsion, it is low to overcome commercially available texture coating quality, the drawbacks of light shine easy xanthochromia；2nd, by using photocatalyst agent nano titanium oxide, under illumination condition, harmful machine thing in air effectively can be degraded into CO2And H2O, to reach the purpose of purification air；3rd, by adding reflective insulation powder, indoor heat conduction, the consumable purpose of electricity-saving are reduced, into air, to have been reached effectively by the infrared reflection in sunshine.
Description
Technical field
The present invention relates to coating preparation and technical field of construction, more particularly to a kind of exterior wall with degraded haze function is anti-
Penetrate preparation and the construction method of heat-insulated texture coating.
Background technology
At present, with the development of national economy, there is large area haze phenomenon in many cities；Meanwhile town dweller makes a living
Living and working environment improves, and causes waste of energy huge.Existing commercially available exterior coating, sand textured coating substantially occupies leading excellent
Gesture.Conventional people manufacture texture coating by glue and river sand, and single varieties are water-fast poor with weatherability.Sent out later from America and Europe etc.
Styrene-acrylic emulsion is have developed up to country, then different colors is presented by adding color stuffing, so as to improve above-mentioned drawback, gradually
Form texture coating popular in the market.But due to the easy xanthochromia of styrene-acrylic emulsion, it is only capable of playing decoration and defencive function.Especially
It, haze aggravated in recent years, and electric consumption increase, there is in the market the texture coating of reflection function to have research, but be provided simultaneously with dropping
Solution haze and the texture coating of reflective insulation function have no and reported.
The content of the invention
One of technical problems to be solved by the invention be for above-mentioned technical problem present in existing texture coating and
A kind of exterior wall reflective thermal insulation texture coating with degraded haze function is provided, it does film forming matter by using silicone acrylic emulsion,
Using the photocatalysis of photocatalyst auxiliary agent come haze in air of degrading, using reflective insulation additive come reflected sunlight energy, with up to
Arrival has the function that to purify air and saves electric energy.
The two of the technical problems to be solved by the invention be to provide the above-mentioned exterior wall reflection with degraded haze function every
The preparation method of hot texture coating.
The two of the technical problems to be solved by the invention be to provide the above-mentioned exterior wall reflection with degraded haze function every
The construction method of hot texture coating.
As a kind of exterior wall reflective thermal insulation texture coating with degraded haze function of first aspect present invention, by following
The raw material of parts by weight is prepared：
In a preferred embodiment of the invention, the blanc fixe is 1250 mesh blanc fixes.
In a preferred embodiment of the invention, the nano titanium oxide is Nano Titanium Oxide as Photocatalyst.
In a preferred embodiment of the invention, the reflective insulation cool colour slurry produces reflective insulation for gram Lay benefactor department
Cool colour is starched, and has auxiliary reflective insulation titanium dioxide, plays a part of reflecting infrared ray.
In a preferred embodiment of the invention, the white quartz sand is 20-120 mesh white quartz sands.
Preparation as a kind of exterior wall reflective thermal insulation texture coating with degraded haze function of the second invention of the invention
Method, comprise the following steps：
The exterior wall reflective thermal insulation texture coating manufacturing process with degraded haze function of invention is divided into two parts,
It is specific as follows：
1. mashing：Water is added by formula ratio in stirred tank, under 600r/min~800r/min speed conditions, by proportioning
Successively by cellulose, wetting agent, dispersant, defoamer, propane diols and coalescents, disperse 10~15 minutes to uniform nothing
Grain；Then reflective insulation titanium dioxide, nano titanium oxide and blanc fixe are sequentially added by formula ratio, improves rotating speed extremely
Under the conditions of 1400r/min, disperse 30min, fineness to below 50um at a high speed；
2. paint：Silicone acrylic emulsion, bactericide and preservative are sequentially added by formula ratio, in 800-1000r/min rotating speed bars
It is texture base-material to disperse about 10min under part；White quartz sand is subsequently added into, is mixed under 800-1000r/min speed conditions
It is uniformly base paint, adds a certain amount of reflective insulation cool colour slurry as needed.
Construction as a kind of exterior wall reflective thermal insulation texture coating with degraded haze function of the 3rd invention of the invention
Method, comprise the following steps：
1. base treatment：It is required that basal plane it is smooth, it is solid, cleaning, dry, fastness is good, alkalescence it is low；
2. batch scrape insulation putty for architectural exterior wall：General batch is scraped 2, and thickness is 1.4~1.6cm, and maintenance is qualified；
3. batch scrape plastering putty；General batch is scraped 2, and thickness is 0.9~1.1mm, and maintenance is qualified；
4. reflective insulation priming paint of constructing：General roller coat 1-2 roads, thin and thick is uniform, no holiday；
5. batch scrape the exterior wall reflective thermal insulation texture coating with degraded haze function：Typically applied using batch, criticize and scrape 2, thickness
Spend 1.0-1.5mm.
As a result of technical scheme as above, the invention has the characteristics that：
1st, by doing film forming matter from silicone acrylic emulsion, overcome that commercially available texture coating quality is low, and the easy xanthochromia of light shine is resistance to
The drawbacks of scale and polluting proofing property difference；
2nd,, can be effectively by harmful machine thing in air under illumination condition by using photocatalyst agent nano titanium oxide
It is degraded into CO2And H2O, to reach the purpose of purification air；
3rd, by adding reflective insulation powder, into air, to have reached reduction effectively by the infrared reflection in sunshine
Indoor heat conduction, the consumable purpose of electricity-saving.
Brief description of the drawings
Fig. 1 is the exterior wall reflective thermal insulation texture coating preparation technology flow chart that the present invention has degraded haze function.
Embodiment
Embodiment 1
A kind of exterior wall reflective thermal insulation texture coating with degraded haze function, by the raw material preparation of following parts by weight
Into：
Above-mentioned blanc fixe is 1250 mesh blanc fixes, and nano titanium oxide is Nano Titanium Oxide as Photocatalyst, instead
Penetrate heat-insulated cool colour slurry and produce reflective insulation cool colour slurry for gram Lay benefactor department, there is auxiliary reflective insulation titanium dioxide, it is red to play reflection
The effect of outside line, white quartz sand are 20-120 mesh white quartz sands.
The above-mentioned exterior wall reflective thermal insulation texture coating manufacturing process with degraded haze function is divided into two parts, specifically such as
Under：
1. mashing：Water is added by formula ratio in stirred tank, under 600r/min~800r/min speed conditions, by proportioning
Successively by cellulose, wetting agent, dispersant, defoamer, propane diols and coalescents, disperse 10~15 minutes to uniform nothing
Grain；Then reflective insulation titanium dioxide, nano titanium oxide and blanc fixe are sequentially added by formula ratio, improves rotating speed extremely
Under the conditions of 1400r/min, disperse 30min, fineness to below 50um at a high speed；
2. paint：Silicone acrylic emulsion, bactericide and preservative are sequentially added by formula ratio, in 800-1000r/min rotating speed bars
It is texture base-material to disperse about 10min under part；White quartz sand is subsequently added into, is mixed under 800-1000r/min speed conditions
It is uniformly base paint, adds a certain amount of reflective insulation cool colour slurry as needed.
The construction method of the above-mentioned exterior wall reflective thermal insulation texture coating with degraded haze function, comprises the following steps：
1. base treatment：It is required that basal plane it is smooth, it is solid, cleaning, dry, fastness is good, alkalescence it is low；
2. batch scrape insulation putty for architectural exterior wall：General batch is scraped 2, and thickness is 1.4~1.6cm, and maintenance is qualified；
3. batch scrape plastering putty；General batch is scraped 2, and thickness is 0.9~1.1mm, and maintenance is qualified；
4. reflective insulation priming paint of constructing：General roller coat 1-2 roads, thin and thick is uniform, no holiday；
5. batch scrape the exterior wall reflective thermal insulation texture coating with degraded haze function：Typically applied using batch, criticize and scrape 2, thickness
Spend 1.0-1.5mm.
Embodiment 2
A kind of exterior wall reflective thermal insulation texture coating with degraded haze function, by the raw material preparation of following parts by weight
Into：
Above-mentioned blanc fixe is 1250 mesh blanc fixes, and nano titanium oxide is Nano Titanium Oxide as Photocatalyst, instead
Penetrate heat-insulated cool colour slurry and produce reflective insulation cool colour slurry for gram Lay benefactor department, there is auxiliary reflective insulation titanium dioxide, it is red to play reflection
The effect of outside line, white quartz sand are 20-120 mesh white quartz sands.
The above-mentioned exterior wall reflective thermal insulation texture coating manufacturing process with degraded haze function is divided into two parts, specifically such as
Under：
1. mashing：Water is added by formula ratio in stirred tank, under 600r/min~800r/min speed conditions, by proportioning
Successively by cellulose, wetting agent, dispersant, defoamer, propane diols and coalescents, disperse 10~15 minutes to uniform nothing
Grain；Then reflective insulation titanium dioxide, nano titanium oxide and blanc fixe are sequentially added by formula ratio, improves rotating speed extremely
Under the conditions of 1400r/min, disperse 30min, fineness to below 50um at a high speed；
2. paint：Silicone acrylic emulsion, bactericide and preservative are sequentially added by formula ratio, in 800-1000r/min rotating speed bars
It is texture base-material to disperse about 10min under part；White quartz sand is subsequently added into, is mixed under 800-1000r/min speed conditions
It is uniformly base paint, adds a certain amount of reflective insulation cool colour slurry as needed.
The construction method of the above-mentioned exterior wall reflective thermal insulation texture coating with degraded haze function, comprises the following steps：
1. base treatment：It is required that basal plane it is smooth, it is solid, cleaning, dry, fastness is good, alkalescence it is low；
2. batch scrape insulation putty for architectural exterior wall：General batch is scraped 2, and thickness is 1.4~1.6cm, and maintenance is qualified；
3. batch scrape plastering putty；General batch is scraped 2, and thickness is 0.9~1.1mm, and maintenance is qualified；
4. reflective insulation priming paint of constructing：General roller coat 1-2 roads, thin and thick is uniform, no holiday；
5. batch scrape the exterior wall reflective thermal insulation texture coating with degraded haze function：Typically applied using batch, criticize and scrape 2, thickness
Spend 1.0-1.5mm.
Embodiment 3
A kind of exterior wall reflective thermal insulation texture coating with degraded haze function, by the raw material preparation of following parts by weight
Into：
Above-mentioned blanc fixe is 1250 mesh blanc fixes, and nano titanium oxide is Nano Titanium Oxide as Photocatalyst, instead
Penetrate heat-insulated cool colour slurry and produce reflective insulation cool colour slurry for gram Lay benefactor department, there is auxiliary reflective insulation titanium dioxide, it is red to play reflection
The effect of outside line, white quartz sand are 20-120 mesh white quartz sands.
The above-mentioned exterior wall reflective thermal insulation texture coating manufacturing process with degraded haze function is divided into two parts, specifically such as
Under：
1. mashing：Water is added by formula ratio in stirred tank, under 600r/min~800r/min speed conditions, by proportioning
Successively by cellulose, wetting agent, dispersant, defoamer, propane diols and coalescents, disperse 10~15 minutes to uniform nothing
Grain；Then reflective insulation titanium dioxide, nano titanium oxide and blanc fixe are sequentially added by formula ratio, improves rotating speed extremely
Under the conditions of 1400r/min, disperse 30min, fineness to below 50um at a high speed；
2. paint：Silicone acrylic emulsion, bactericide and preservative are sequentially added by formula ratio, in 800-1000r/min rotating speed bars
It is texture base-material to disperse about 10min under part；White quartz sand is subsequently added into, is mixed under 800-1000r/min speed conditions
It is uniformly base paint, adds a certain amount of reflective insulation cool colour slurry as needed.
The construction method of the above-mentioned exterior wall reflective thermal insulation texture coating with degraded haze function, comprises the following steps：
1. base treatment：It is required that basal plane it is smooth, it is solid, cleaning, dry, fastness is good, alkalescence it is low；
2. batch scrape insulation putty for architectural exterior wall：General batch is scraped 2, and thickness is 1.4~1.6cm, and maintenance is qualified；
3. batch scrape plastering putty；General batch is scraped 2, and thickness is 0.9~1.1mm, and maintenance is qualified；
4. reflective insulation priming paint of constructing：General roller coat 1-2 roads, thin and thick is uniform, no holiday；
5. batch scrape the exterior wall reflective thermal insulation texture coating with degraded haze function：Typically applied using batch, criticize and scrape 2, thickness
Spend 1.0-1.5mm.
Claims (7)
1. a kind of exterior wall reflective thermal insulation texture coating with degraded haze function, it is characterised in that by the original of following parts by weight
Material is prepared：
A kind of 2. exterior wall reflective thermal insulation texture coating with degraded haze function as claimed in claim 1, it is characterised in that
The blanc fixe is 1250 mesh blanc fixes.
A kind of 3. exterior wall reflective thermal insulation texture coating with degraded haze function as claimed in claim 1, it is characterised in that
The nano titanium oxide is Nano Titanium Oxide as Photocatalyst.
A kind of 4. exterior wall reflective thermal insulation texture coating with degraded haze function as claimed in claim 1, it is characterised in that
The reflective insulation cool colour slurry produces reflective insulation cool colour slurry for gram Lay benefactor department, has auxiliary reflective insulation titanium dioxide, plays
Reflect the effect of infrared ray.
A kind of 5. exterior wall reflective thermal insulation texture coating with degraded haze function as claimed in claim 1, it is characterised in that
The white quartz sand is 20-120 mesh white quartz sands.
A kind of 6. exterior wall reflective thermal insulation texture with degraded haze function described in any one of claim 1 to 5 claim
The preparation method of coating, it is characterised in that comprise the following steps：
1) it is beaten：Water is added by formula ratio in stirred tank, under 600r/min~800r/min speed conditions, by proportioning successively
By cellulose, wetting agent, dispersant, defoamer, propane diols and coalescents, disperse 10~15 minutes to uniformly without particle；Connect
And sequentially add reflective insulation titanium dioxide, nano titanium oxide and blanc fixe by formula ratio, improve rotating speed to 1400r/min
Under the conditions of, disperse 30min, fineness to below 50um at a high speed；
2) paint：Silicone acrylic emulsion, bactericide and preservative are sequentially added by formula ratio, under 800-1000r/min speed conditions
Scattered about 10min is texture base-material；White quartz sand is subsequently added into, is well mixed under 800-1000r/min speed conditions
As base paint, a certain amount of reflective insulation cool colour slurry is added as needed.
A kind of 7. exterior wall reflective thermal insulation texture with degraded haze function described in any one of claim 1 to 5 claim
The construction method of coating, comprises the following steps：
1) base treatments：It is required that basal plane it is smooth, it is solid, cleaning, dry, fastness is good, alkalescence it is low；
2) insulation putty for architectural exterior wall is scraped for batches：General batch is scraped 2, and thickness is 1.4~1.6cm, and maintenance is qualified；
3) plastering putty is scraped for batches；General batch is scraped 2, and thickness is 0.9~1.1mm, and maintenance is qualified；
4) constructions reflective insulation priming paint：General roller coat 1-2 roads, thin and thick is uniform, no holiday；
5) the exterior wall reflective thermal insulation texture coating with degraded haze function is scraped for batches：It is general to criticize using painting is criticized and scrape 2, thickness
1.0-1.5mm。