CN107382176A - 一种新型空心砖及其制备方法 - Google Patents

一种新型空心砖及其制备方法 Download PDF

Info

Publication number
CN107382176A
CN107382176A CN201710693065.2A CN201710693065A CN107382176A CN 107382176 A CN107382176 A CN 107382176A CN 201710693065 A CN201710693065 A CN 201710693065A CN 107382176 A CN107382176 A CN 107382176A
Authority
CN
China
Prior art keywords
parts
gangue
preparation
brick
hollow brick
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710693065.2A
Other languages
English (en)
Inventor
丁德峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XUZHOU HENGJI WEIYE BUILDING MATERIAL CO Ltd
Original Assignee
XUZHOU HENGJI WEIYE BUILDING MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XUZHOU HENGJI WEIYE BUILDING MATERIAL CO Ltd filed Critical XUZHOU HENGJI WEIYE BUILDING MATERIAL CO Ltd
Priority to CN201710693065.2A priority Critical patent/CN107382176A/zh
Publication of CN107382176A publication Critical patent/CN107382176A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种新型空心砖及其制备方法，包含如下重量份数的有效成分：煤矸石20‑40份、砂质页岩20‑30份、石灰岩10‑20份、水泥15‑30份、木屑5‑10份、竹纤维5‑10份，水余量。采用各种废弃料、取材方便、加工简单，节省能源、降低生产成本、能够有效减少对环境的污染，适合在市场中大量推广。

Description

一种新型空心砖及其制备方法
技术领域
本发明属于建筑墙体用砖及其制作方法，具体涉及一种新型空心砖及其制备方法。
背景技术
随着经济的高速发展使得建筑用砖的需求量成倍增长，尤其是城市中大量的拆建项目使得建筑用砖的需求量越来越大，空心砖是建筑行业常用的墙体主材，由于质轻、消耗原材少等优势，已经成为国家建筑部门首先推荐的产品。
发明内容
本发明提供了一种煤矸石保温砖及其制备方法，包含如下重量份数的有效成分：煤矸石20-40份、砂质页岩20-30份、石灰岩10-20份、水泥15-30份、木屑5-10份、竹纤维5-10份，水余量。
还包括以下步骤：
(1)将煤矸石20-40份、砂质页岩20-30份、石灰岩10-20份进行粉碎研磨，用搅拌机搅拌均匀成混合物料；
(2)将竹纤维5-10份浸泡1-2天，捞出放入粉碎机进行粉碎；
(3)将木屑5-10份加入步骤(2)中的原料放入搅拌机中混合；
(4)将水泥15-30份、水与步骤(1)和步骤(3)中的原料混合，得到制作空心砖的基础原料；
(5)将基础原料放入到空心砖模具中，进行压力成型以制备空心砖初胚；
(6)将空心砖初胚放置5-10小时后振动成型；
(7)自然冷却，即得。
所述步骤(2)中的浸泡液为醋与水的混合液。
本发明的有益之处在于：采用各种废弃料、取材方便、加工简单，节省能源、降低生产成本、能够有效减少对环境的污染，适合在市场中大量推广。
具体实施方式
为了加深对本发明的理解和认识，下面结合具体实施方式对本发明做出进一步的说明和介绍。
实施例1
一种煤矸石保温砖及其制备方法，包含如下重量份数的有效成分：煤矸石20份、砂质页岩20份、石灰岩10份、水泥15份、木屑5份、竹纤维5份，水余量。
还包括以下步骤：
(1)将煤矸石20份、砂质页岩20份、石灰岩10份进行粉碎研磨，用搅拌机搅拌均匀成混合物料；
(2)将竹纤维5份浸泡1天，捞出放入粉碎机进行粉碎；
(3)将木屑5份加入步骤(2)中的原料放入搅拌机中混合；
(4)将水泥15份、水与步骤(1)和步骤(3)中的原料混合，得到制作空心砖的基础原料；
(5)将基础原料放入到空心砖模具中，进行压力成型以制备空心砖初胚；
(6)将空心砖初胚放置5小时后振动成型；
(7)自然冷却，即得。
所述步骤(2)中的浸泡液为醋与水的混合液。
实施例2
一种煤矸石保温砖及其制备方法，包含如下重量份数的有效成分：煤矸石40份、砂质页岩30份、石灰岩20份、水泥30份、木屑10份、竹纤维10份，水余量。
还包括以下步骤：
(1)将煤矸石40份、砂质页岩30份、石灰岩20份进行粉碎研磨，用搅拌机搅拌均匀成混合物料；
(2)将竹纤维10份浸泡1-2天，捞出放入粉碎机进行粉碎；
(3)将木屑10份加入步骤(2)中的原料放入搅拌机中混合；
(4)将水泥30份、水与步骤(1)和步骤(3)中的原料混合，得到制作空心砖的基础原料；
(5)将基础原料放入到空心砖模具中，进行压力成型以制备空心砖初胚；
(6)将空心砖初胚放置10小时后振动成型；
(7)自然冷却，即得。
所述步骤(2)中的浸泡液为醋与水的混合液。

Claims (3)

1.一种新型空心砖及其制备方法，其特征在于：所述保温砖包含如下重量份数的有效成分：煤矸石20-40份、砂质页岩20-30份、石灰岩10-20份、水泥15-30份、木屑5-10份、竹纤维5-10份，水余量。
2.根据权利要求1所述的一种煤矸石保温砖及其制备方法，其特征在于还包括以下步骤：
(1)将煤矸石20-40份、砂质页岩20-30份、石灰岩10-20份进行粉碎研磨，用搅拌机搅拌均匀成混合物料；
(2)将竹纤维5-10份浸泡1-2天，捞出放入粉碎机进行粉碎；
(3)将木屑5-10份加入步骤(2)中的原料放入搅拌机中混合；
(4)将水泥15-30份、水与步骤(1)和步骤(3)中的原料混合，得到制作空心砖的基础原料；
(5)将基础原料放入到空心砖模具中，进行压力成型以制备空心砖初胚；
(6)将空心砖初胚放置5-10小时后振动成型；
(7)自然冷却，即得。
3.根据权利要求2所述的一种煤矸石保温砖及其制备方法，其特征在于所述步骤(2)中的浸泡液为醋与水的混合液。
CN201710693065.2A 2017-08-14 2017-08-14 一种新型空心砖及其制备方法 Pending CN107382176A (zh)