CN107325310A - 一种塑料表面的处理工艺 - Google Patents

一种塑料表面的处理工艺 Download PDF

Info

Publication number
CN107325310A
CN107325310A CN201710469405.3A CN201710469405A CN107325310A CN 107325310 A CN107325310 A CN 107325310A CN 201710469405 A CN201710469405 A CN 201710469405A CN 107325310 A CN107325310 A CN 107325310A
Authority
CN
China
Prior art keywords
coating
plastics
frosting
parts
handling process
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710469405.3A
Other languages
English (en)
Inventor
袁孝菊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHUCHENG ANTAI PLASTIC PRODUCTS CO Ltd
Original Assignee
SHUCHENG ANTAI PLASTIC PRODUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHUCHENG ANTAI PLASTIC PRODUCTS CO Ltd filed Critical SHUCHENG ANTAI PLASTIC PRODUCTS CO Ltd
Priority to CN201710469405.3A priority Critical patent/CN107325310A/zh
Publication of CN107325310A publication Critical patent/CN107325310A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种塑料表面的处理工艺，包括如下步骤：打磨，用砂纸对塑料表面进行打磨处理；清洁，将塑料浸在工业酒精中进行去油污处理；水洗，将塑料经由流水的冲刷，进行表面的清洁；烘干，在40‑50℃的温度下，干燥10‑20min，去除水分；涂料，烘干将干燥之后的塑料包装、库存；本发明通过在塑料基体表面涂布一层致密的涂层，改善了塑料基本本身的韧性，延长其使用时间，同时可改变涂料本身的颜色，以搭配出不同风格，不同品味的外观，更加迎合市场的需要。

Description

一种塑料表面的处理工艺
技术领域
本发明属于塑料加工技术领域，尤其涉及一种塑料表面的处理工艺。
背景技术
塑料是以单体为原料，通过加聚或缩聚反应聚合而成的高分子化合物，俗称塑料或树脂，可以自由改变成分及形体样式，由合成树脂及填料、增塑剂、稳定剂、润滑剂、色料等添加剂组成。
塑料的主要成分是树脂。树脂这一名词最初是由动植物分泌出的脂质而得名，如松香、虫胶等，树脂是指尚未和各种添加剂混合的高分子化合物。树脂约占塑料总重量的40％～100％。塑料的基本性能主要决定于树脂的本性，但添加剂也起着重要作用。有些塑料基本上是由合成树脂所组成，不含或少含添加剂，如有机玻璃、聚苯乙烯等。大多数塑料质轻，化学性稳定，不会锈蚀；耐冲击性好；具有较好的透明性和耐磨耗性；绝缘性好，导热性低；一般成型性、着色性好，加工成本低，塑料给人们生活带来巨大便利；但塑料在使用过程中会出现韧性下降，容易折损，如空调机箱外壳、油烟机的外壳等等，在使用一段时间后需要对其更换，因其韧性低，损坏几率大，这样使用增加了投入成本，而且更换过程复杂，操作不便。
发明内容
本发明的目的在于提供一种塑料表面的处理工艺，以改善塑料的韧性，延长其使用寿命，降低投入成本。
为实现上述目的，本发明提供如下技术方案：一种塑料表面的处理工艺，包括如下步骤：
1)、打磨，用砂纸对塑料表面进行打磨处理；
2)、清洁，将塑料浸在工业酒精中进行去油污处理；
3)、水洗，将塑料经由流水的冲刷，进行表面的清洁；
4)、烘干，在40-50℃的温度下，干燥10-20min，去除水分；
5)、涂料，涂料其组分按其重量配比如下：聚氨酸丙烯酸5-10份、聚丙烯酸钠3-8份、酚醛树脂1.8-3.5份、醋丙乳液0.8-2.3份、己二醇丁醚醋酸钠0.2-0.6份，将涂料均匀的涂布在塑料的表面上。
6)烘干、将涂料之后的塑料在50-60℃的环境下，干燥10-20min；
7)成品、将干燥之后的塑料包装、库存。
优选的，所述步骤2)中可有次氯酸钠溶液代替工业酒精对塑料表面的油污进行处理。
优选的，所述步骤5)的涂料过程中可在其中加入不同颜色的颜料，使之与涂料混合均匀，涂布在塑料表面，以增强塑料整体的美观性，使之有更好的审美效果。
优选的，所述步骤5)中可加入硅藻土份5-7份，以增强涂料的吸附效果，使涂料与塑料集体结合更加牢固。
优选的，所述步骤5)中的涂料中可加入苯酐1-3份、顺酐0.5-2份，以改善涂料的整体柔韧性，使之更容易涂布在塑料基体至上。
本发明的有益效果：本发明通过在塑料基体表面涂布一层致密的涂层，改善了塑料基本本身的韧性，延长其使用时间，同时可改变涂料本身的颜色，以搭配出不同风格，不同品味的外观，更加迎合市场的需要；并且改变涂料本身的柔韧性，使之更容易贴合，不易剥落，延长塑料的使用寿命，使之不易损坏，更加符合大众的需求。
具体实施方式
为了使本领域的技术人员更好地理解本发明的技术方案，下面将结合具体实施例对本发明作进一步的详细介绍。
实施例1
一种塑料表面的处理工艺，包括如下步骤：
1)、打磨，用砂纸对塑料表面进行打磨处理；
2)、清洁，将塑料浸在工业酒精中进行去油污处理；
3)、水洗，将塑料经由流水的冲刷，进行表面的清洁；
4)、烘干，在40-50℃的温度下，干燥10-20min，去除水分；
5)、涂料，涂料其组分按其重量配比如下：聚氨酸丙烯酸5份、聚丙烯酸钠8份、酚醛树脂1.8份、醋丙乳液2.3份、己二醇丁醚醋酸钠0.2份，将涂料均匀的涂布在塑料的表面上。
6)、烘干，将涂料之后的塑料在50-60℃的环境下，干燥10-20min；
7)、成品，将干燥之后的塑料包装、库存。
所述步骤2)中可有次氯酸钠溶液代替工业酒精对塑料表面的油污进行处理。
实施例2
一种塑料表面的处理工艺，包括如下步骤：
1)、打磨，用砂纸对塑料表面进行打磨处理；
2)、清洁，将塑料浸在工业酒精中进行去油污处理；
3)、水洗，将塑料经由流水的冲刷，进行表面的清洁；
4)、烘干，在40-50℃的温度下，干燥10-20min，去除水分；
5)、涂料，涂料其组分按其重量配比如下：颜料5份、聚氨酸丙烯酸10份、聚丙烯酸钠3份、酚醛树脂3.5份、醋丙乳液0.8份、己二醇丁醚醋酸钠0.6份，将涂料均匀的涂布在塑料的表面上
6)、烘干，将涂料之后的塑料在50-60℃的环境下，干燥10-20min；
7)、成品，将干燥之后的塑料包装、库存。
在涂料中加入不同的颜料，可使得塑料制品在外观上更佳的观赏性，更能符合大众的审美。
实施例3
一种塑料表面的处理工艺，包括如下步骤：
1)、打磨，用砂纸对塑料表面进行打磨处理；
2)、清洁，将塑料浸在工业酒精中进行去油污处理；
3)、水洗，将塑料经由流水的冲刷，进行表面的清洁；
4)、烘干，在40-50℃的温度下，干燥10-20min，去除水分；
5)、涂料，涂料其组分按其重量配比如下：颜料5份、聚氨酸丙烯酸8份、聚丙烯酸钠5份、酚醛树脂2.7份、醋丙乳液1.5份、己二醇丁醚醋酸钠0.4份，硅藻土份5-7份、苯酐1-3份、顺酐0.5-2份，将涂料均匀的涂布在塑料的表面上。
6)、烘干，将涂料之后的塑料在50-60℃的环境下，干燥10-20min；
7)、成品，将干燥之后的塑料包装、库存。
在涂料过程中不仅加入颜料配比，同时改变涂料的柔韧性，提高其附着力，使其效果更佳。
本发明通过在塑料基体表面涂布一层致密的涂层，改善了塑料基本本身的韧性，延长其使用时间，同时可改变涂料本身的颜色，以搭配出不同风格，不同品味的外观，更加迎合市场的需要；并且改变涂料本身的柔韧性，使之更容易贴合，不易剥落，延长塑料的使用寿命，使之不易损坏，更加符合大众的需求。
经过上述步骤处理后的塑料保光保色性好，耐候性佳。对上述经过喷涂处理的塑料进行拉伸试验，三组实施例中的塑料的拉伸结果分别为35MPa、36MPa、和43MPa，均高于普通塑料的韧性，效果更佳。
以上只通过说明的方式描述了本发明的某些示范性实施例，毋庸置疑，对于本领域的普通技术人员，在不偏离本发明的精神和范围的情况下，可以用各种不同的方式对所描述的实施例进行修正。因此，上述实施例中的描述在本质上是说明性的，不应理解为对本发明权利要求保护范围的限制。

Claims (5)

1.一种塑料表面的处理工艺，包括如下步骤：
1)、打磨，用砂纸对塑料表面进行打磨处理；
2)、清洁，将塑料浸在工业酒精中进行去油污处理；
3)、水洗，将塑料经由流水的冲刷，进行表面的清洁；
4)、烘干，在40-50℃的温度下，干燥10-20min，去除水分；
5)、涂料，涂料其组分按其重量配比如下：聚氨酸丙烯酸5-10份、聚丙烯酸钠3-8份、酚醛树脂1.8-3.5份、醋丙乳液0.8-2.3份、己二醇丁醚醋酸钠0.2-0.6份，将涂料均匀的涂布在塑料的表面上。
6)、烘干，将涂料之后的塑料在50-60℃的环境下，干燥10-20min；
7)、成品，将干燥之后的塑料包装、库存。
2.根据权利要求1所述的一种塑料表面的处理工艺，其特征在于：所述步骤2)中可有次氯酸钠溶液代替工业酒精对塑料表面的油污进行处理。
3.根据权利要求1所述的一种塑料表面的处理工艺，其特征在于：所述步骤5)的涂料过程中可在其中加入不同颜色的颜料，使之与涂料混合均匀，涂布在塑料表面，以增强塑料整体的美观性，使之有更好的审美效果。
4.根据权利要求1所述的一种塑料表面的处理工艺，其特征在于：所述步骤5)中可加入硅藻土份5-7份，以增强涂料的吸附效果，使涂料与塑料集体结合更加牢固。
5.根据权利要求1所述的一种塑料表面的处理工艺，其特征在于：所述步骤5)中的涂料中可加入苯酐1-3份、顺酐0.5-2份，以改善涂料的整体柔韧性，使之更容易涂布在塑料基体至上。
CN201710469405.3A 2017-06-20 2017-06-20 一种塑料表面的处理工艺 Pending CN107325310A (zh)