CN107324804A - 无铅压电陶瓷及其制备方法 - Google Patents
无铅压电陶瓷及其制备方法 Download PDFInfo
- Publication number
- CN107324804A CN107324804A CN201710566793.7A CN201710566793A CN107324804A CN 107324804 A CN107324804 A CN 107324804A CN 201710566793 A CN201710566793 A CN 201710566793A CN 107324804 A CN107324804 A CN 107324804A
- Authority
- CN
- China
- Prior art keywords
- preparation
- zro
- piezoelectric ceramics
- time
- leadless piezoelectric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (15)