CN107285808A - 一种高强保温建筑板材 - Google Patents
一种高强保温建筑板材 Download PDFInfo
- Publication number
- CN107285808A CN107285808A CN201710634355.XA CN201710634355A CN107285808A CN 107285808 A CN107285808 A CN 107285808A CN 201710634355 A CN201710634355 A CN 201710634355A CN 107285808 A CN107285808 A CN 107285808A
- Authority
- CN
- China
- Prior art keywords
- parts
- magnesium
- building board
- agricultural crop
- crop straw
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种建筑板材,其组分包括:其组分包括:按重量份数计,镁质胶凝材料80‑100份、农作物秸秆粉末8‑12份、粉煤灰空心微珠6‑10份、玻璃纤维3‑5份、钛酸镁11‑15份、钛酸钙5‑8份、聚苯乙烯5‑11份、丙酸丁酯15‑21份和石英砂15‑19份;其中,所述镁质胶凝材料的粒径为70‑80微米;在所述镁质胶凝材料中,包括氯化镁和氧化镁,且所述氯化镁和所述氧化镁的重量比例在5/6‑5/3 之间进一步地,所述农作物秸秆粉末的粒径≤260微米;其水分含量≤10%;所述农作物秸秆粉末的杂质含量≤10%。本发明的优点在于:本发明的建筑板材,具有较高强度且具有保温性能。
Description
技术领域
本发明属于建筑材料领域,特别涉及一种高强保温建筑板材。
背景技术
目前,在建筑领域中,通常以红砖、多孔砖、空心砖等作为筑墙的主体 材料;红砖、多孔砖、空心砖等多以粘土、页岩、煤矸石作为原料粉碎后在 高温条件下烧制而成;将砖块规划堆砌后,再外加水泥固定成型,就形成了 建筑物的墙体;但是,这种传统原料本身不具备保温效果,导致砌成的墙体 保温较差,而为了达到房屋墙体的保温,需要在墙体的表面再单独外加一层 保温隔热层才能使得墙体具有保温的效果,但是,外加单独的隔热层不但增 加了建筑施工繁杂,劳动力施工强度增大,而且还形成了原料的浪费。
针对上述现象,专利CN103073262B公开了一种建筑板材,其组份包括:镁质胶凝材料70-90份、农作物秸秆粉末6-10份、粉煤灰空心微珠6-10份、玻璃纤维2-4份,具体的,按重量份数计,包括:镁质胶凝材料80份、农作物秸秆粉末8份、粉煤灰空心微珠8份、玻璃纤维2份;本发明还公开了一种该建筑板材的制作方法,包括制成镁质胶凝材料溶液;将粉煤灰空心微珠和农作物秸秆粉末加入到所述镁质胶凝材料中,均匀搅拌后倒入磨具;得到初成品;对所述初成品植入玻璃纤维固化成型,得到成品。该建筑板材的配方组成中,由于粉煤灰空心微珠其自身结构组成的特殊性,与多种原料混合之后就可以使得制成的板材本身具有多种微小的细孔,因而,该建筑板材具有保温的作用;但其由于其较为单一的组成成分,制备的建筑板材的性能较差,不能满足实际生产和应用。
发明内容
本发明要解决的技术问题是提供一种具有高强度且具有保温性能的建筑板材。
为解决上述技术问题,本发明的技术方案为:一种高强保温建筑板材,其创新点在于:其组分包括:按重量份数计,镁质胶凝材料80-100份、农作物秸秆粉末8-12份、粉煤灰空心微珠6-10份、玻璃纤维3-5份、钛酸镁11-15份、钛酸钙5-8份、聚苯乙烯5-11份、丙酸丁酯15-21份和石英砂15-19份;其中,所述镁质胶凝材料的粒径为70-80微米;在所述镁质胶凝材料中, 包括氯化镁和氧化镁,且所述氯化镁和所述氧化镁的重量比例在5/6-5/3 之间进一步地,所述农作物秸秆粉末的粒径≤260微米;其水分含量≤10%;所述农作物秸秆粉末的杂质含量≤10%。
进一步地,所述粉煤灰空心微珠的硅含量≥40%,且所述粉煤灰空心微珠的粒径≤800微米。
本发明的优点在于:本发明的建筑板材,在本配方中,镁质胶凝材料为本配方的主要原料,镁质胶凝材料主要起到粘合和固化的作用,当所有的原料混合之后镁质胶凝材料可以将各组份粘合并且易 于固化,是制成板材制成作用的主要贡献因素,此外,由于农作物秸秆粉末 可以起到填充和连筋的作用,成型之后,其可以有效的改变板材结构体的裂痕和密度,从而具有防震坚固的特点;粉煤灰空心微珠是从粉煤灰中筛选出 来的玻璃微珠,其多以微小的空心环形颗粒存在,应用到本配方中后,由于粉煤灰空心微珠其自身结构组成的特殊性,与多种原料混合之后就可以使得 制成的建筑板材本身具有多种微小的细孔,进而其建筑板材具有保温隔热的作用;此外,该配方中,加入了一些增强组分,使得本发明的建筑板材还具有非常好的抗压强度和抗折强度,抗压强度达到了15MPa以上,抗折强度达到了 14MPa以上,提高了常规的建筑板材的抗压强度和抗折强度,解决了常规的建筑板材的强度较低的问题。
具体实施方式
下面的实施例可以使本专业的技术人员更全面地理解本发明,但并不因此将本发明限制在所述的实施例范围之中。
实施例1
本实施例建筑板材,其组分包括:按重量份数计,镁质胶凝材料80份、农作物秸秆粉末12份、粉煤灰空心微珠10份、玻璃纤维5份、钛酸镁15份、钛酸钙8份、聚苯乙烯11份、丙酸丁酯21份和石英砂19份;其中,所述镁质胶凝材料的粒径为70-80微米;在所述镁质胶凝材料中, 包括氯化镁和氧化镁,且所述氯化镁和所述氧化镁的重量比例在5/6-5/3 之间;所述农作物秸秆粉末的粒径≤260微米;其水分含量≤10%;所述农作物秸秆粉末的杂质含量≤10%;所述粉煤灰空心微珠的硅含量≥40%,且所述粉煤灰空心微珠的粒径≤800微米。
实施例2
本实施例建筑板材,其组分包括:按重量份数计,镁质胶凝材料100份、农作物秸秆粉末8份、粉煤灰空心微珠6份、玻璃纤维3份、钛酸镁11份、钛酸钙5份、聚苯乙烯5份、丙酸丁酯15份和石英砂15份;其中,所述镁质胶凝材料的粒径为70微米;在所述镁质胶凝材料中, 包括氯化镁和氧化镁,且所述氯化镁和所述氧化镁的重量比例在5/6-5/3 之间;所述农作物秸秆粉末的粒径≤260微米;其水分含量≤10%;所述农作物秸秆粉末的杂质含量≤10%;所述粉煤灰空心微珠的硅含量≥40%,且所述粉煤灰空心微珠的粒径≤800微米。
实施例3
本实施例建筑板材,其组分包括:按重量份数计,镁质胶凝材料90份、农作物秸秆粉末10份、粉煤灰空心微珠8份、玻璃纤维4份、钛酸镁13份、钛酸钙7份、聚苯乙烯8份、丙酸丁酯18份和石英砂17份;其中,所述镁质胶凝材料的粒径为70-80微米;在所述镁质胶凝材料中,包括氯化镁和氧化镁,且所述氯化镁和所述氧化镁的重量比例在5/6-5/3 之间;所述农作物秸秆粉末的粒径≤260微米;其水分含量≤10%;所述农作物秸秆粉末的杂质含量≤10%;所述粉煤灰空心微珠的硅含量≥40%,且所述粉煤灰空心微珠的粒径≤800微米。
以上显示和描述了本发明的基本原理和主要特征以及本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (3)
1.一种高强保温建筑板材,其特征在于:其组分包括:按重量份数计,镁质胶凝材料80-100份、农作物秸秆粉末8-12份、粉煤灰空心微珠6-10份、玻璃纤维3-5份、钛酸镁11-15份、钛酸钙5-8份、聚苯乙烯5-11份、丙酸丁酯15-21份和石英砂15-19份;其中,所述镁质胶凝材料的粒径为70-80微米;在所述镁质胶凝材料中, 包括氯化镁和氧化镁,且所述氯化镁和所述氧化镁的重量比例在5/6-5/3 之间。
2.根据权利要求1所述的高强保温建筑板材,其特征在于:所述农作物秸秆粉末的粒径≤260微米;其水分含量≤10%;所述农作物秸秆粉末的杂质含量≤10%。
3.根据权利要求1所述的高强保温建筑板材,其特征在于:所述粉煤灰空心微珠的硅含量≥40%,且所述粉煤灰空心微珠的粒径≤800微米。