CN105036676A - 一种添加石膏的多纤维混合保温砂浆及其制备方法 - Google Patents

一种添加石膏的多纤维混合保温砂浆及其制备方法 Download PDF

Info

Publication number
CN105036676A
CN105036676A CN201510382103.3A CN201510382103A CN105036676A CN 105036676 A CN105036676 A CN 105036676A CN 201510382103 A CN201510382103 A CN 201510382103A CN 105036676 A CN105036676 A CN 105036676A
Authority
CN
China
Prior art keywords
parts
gypsum
thermal insulation
insulation mortar
mortar
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510382103.3A
Other languages
English (en)
Inventor
方明珠
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zongyang County Tian Zhu New Building Materials Co Ltd
Original Assignee
Zongyang County Tian Zhu New Building Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zongyang County Tian Zhu New Building Materials Co Ltd filed Critical Zongyang County Tian Zhu New Building Materials Co Ltd
Priority to CN201510382103.3A priority Critical patent/CN105036676A/zh
Publication of CN105036676A publication Critical patent/CN105036676A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种添加石膏的多纤维混合保温砂浆，其特征在于，由下列重量份的原料制备制成：石蜡2-3、预胶化淀粉2-3、木质纤维2.5-4、剑麻短纤维2-3、聚丙烯纤维1-1.5、膨胀蛭石粉13-16、建筑废料11-14、普通硅酸盐水泥18-21、石膏10-13、玻化微珠20-24、酚醛泡沫颗粒11-13、增效剂8-10；本发明将石膏替代部分的水泥，具有一定的缓凝作用，延长使用时间；添加剑麻短纤维、聚丙烯纤维等多种纤维，增强了抗拉强度以及抗裂性；添加石蜡，具有一定的防水性，配合增效剂的添加，进一步增强了产品的防水防潮防蛀效果，同时减少了水泥用量；本发明性能优异，可广泛使用于建筑墙体的保温砂浆。

Description

一种添加石膏的多纤维混合保温砂浆及其制备方法
技术领域
本发明涉及建筑保温材料领域，特别是一种添加石膏的多纤维混合保温砂浆及其制备方法。
背景技术
石膏及其制品的微孔结构和加热脱水性，使之具优良的隔音、隔热和防火性能，将石膏与水泥混合使用还具有一定的缓凝效果，防止水泥使用时过快固化。本发明将石膏替代部分的水泥添加到保温砂浆中，使得保温砂浆具有一定的缓凝作用，延长使用时间；添加木质纤维、剑麻短纤维、聚丙烯纤维等多种纤维，增强了抗拉强度以及抗裂性；添加石蜡，具有一定的防水性，配合增效剂的添加，进一步增强了产品的防水防潮防蛀效果，同时减少了水泥用量，而且施工性能好。本发明能达到内外墙保温系统的理想强度标准，广泛使用于建筑墙体的保温砂浆。
发明内容
本发明的目的是提供一种添加石膏的多纤维混合保温砂浆及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种添加石膏的多纤维混合保温砂浆，由下列重量份的原料制备制成：石蜡2-3、预胶化淀粉2-3、木质纤维2.5-4、剑麻短纤维2-3、聚丙烯纤维1-1.5、膨胀蛭石粉13-16、建筑废料11-14、普通硅酸盐水泥18-21、石膏10-13、玻化微珠20-24、酚醛泡沫颗粒11-13、增效剂8-10；
所述增效剂由以下重量份的原料制备而成：农作物秸秆45-50、液体石蜡3-4、乳化沥青9-10、氧化钙3-4、甲基丙烯酸甲酯3-5、二甲基硅油2-3、丙烯酸羟乙酯2-3、正磷酸酯1-1.5、糖钙2-3、樟脑0.1-0.2、防老剂RD0.5-0.7、水20-25；制备方法如下：首先将农作物秸秆干燥后粉碎成100-200目粉末，与氧化钙混合均匀加入适量水研磨，再加入液体石蜡、二甲基硅油混合均匀，将甲基丙烯酸甲酯、丙烯酸羟乙酯混合，加热至75℃-85℃反应1-1.5小时，然后加入除樟脑油之外的其余剩余成分，保温反应60-90分钟，最后将所有物料混合，冷去至室温后加入樟脑油，以400-500转/分的速度搅拌20-30分钟得到混合浆料，最后将混合浆料泵入喷雾干燥设备中，控制进风温度120-150℃、出风温度80-100℃，即可制成增效剂。
本发明所述一种添加石膏的多纤维混合保温砂浆，由以下具体步骤制成：首先将建筑废料、石膏、石蜡混合后研磨30-40分钟，形成200-300目粉末，然后与其他剩余成分混合，加入到双轴卧式搅拌釜中，以300-400转/分钟匀速搅拌15-20分钟，包装即得到保温砂浆预拌料。
本发明的有益效果是：本发明将石膏替代部分的水泥，具有一定的缓凝作用，延长使用时间；添加木质纤维、剑麻短纤维、聚丙烯纤维等多种纤维，增强了抗拉强度以及抗裂性；添加石蜡，具有一定的防水性，配合增效剂的添加，进一步增强了产品的防水防潮防蛀效果，同时减少了水泥用量；本发明性能优异，可广泛使用于建筑墙体的保温砂浆。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种添加石膏的多纤维混合保温砂浆，由下列重量份（公斤）的原料制备制成：石蜡2、预胶化淀粉2、木质纤维2.5、剑麻短纤维2、聚丙烯纤维1、膨胀蛭石粉13、建筑废料11、普通硅酸盐水泥18、石膏10、玻化微珠20、酚醛泡沫颗粒11、增效剂8；
所述增效剂由以下重量份（公斤）的原料制备而成：农作物秸秆45、液体石蜡3、乳化沥青9、氧化钙3、甲基丙烯酸甲酯3、二甲基硅油2、丙烯酸羟乙酯2、正磷酸酯1、糖钙2、樟脑0.1、防老剂RD0.5、水20；制备方法如下：首先将农作物秸秆干燥后粉碎成100-200目粉末，与氧化钙混合均匀加入适量水研磨，再加入液体石蜡、二甲基硅油混合均匀，将甲基丙烯酸甲酯、丙烯酸羟乙酯混合，加热至75℃-85℃反应1-1.5小时，然后加入除樟脑油之外的其余剩余成分，保温反应60-90分钟，最后将所有物料混合，冷去至室温后加入樟脑油，以400-500转/分的速度搅拌20-30分钟得到混合浆料，最后将混合浆料泵入喷雾干燥设备中，控制进风温度120-150℃、出风温度80-100℃，即可制成增效剂。
本发明所述一种添加石膏的多纤维混合保温砂浆，由以下具体步骤制成：首先将建筑废料、石膏、石蜡混合后研磨30-40分钟，形成200-300目粉末，然后与其他剩余成分混合，加入到双轴卧式搅拌釜中，以300-400转/分钟匀速搅拌15-20分钟，包装即得到保温砂浆预拌料。
本发明保温砂浆采用现配现用的方式，使用时将保温砂浆加入0.8倍量的水搅拌均匀形成膏状物质即可使用。
经各种试验测定，本发明保温砂浆各项性能为：堆积密度为269kg/m3，导热系数为0.058W/m.K，抗压强度为0.41Mpa，线性收缩率为0.27%。

Claims (2)

1.一种添加石膏的多纤维混合保温砂浆，其特征在于，由下列重量份的原料制备制成：石蜡2-3、预胶化淀粉2-3、木质纤维2.5-4、剑麻短纤维2-3、聚丙烯纤维1-1.5、膨胀蛭石粉13-16、建筑废料11-14、普通硅酸盐水泥18-21、石膏10-13、玻化微珠20-24、酚醛泡沫颗粒11-13、增效剂8-10；
所述增效剂由以下重量份的原料制备而成：农作物秸秆45-50、液体石蜡3-4、乳化沥青9-10、氧化钙3-4、甲基丙烯酸甲酯3-5、二甲基硅油2-3、丙烯酸羟乙酯2-3、正磷酸酯1-1.5、糖钙2-3、樟脑0.1-0.2、防老剂RD0.5-0.7、水20-25；制备方法如下：首先将农作物秸秆干燥后粉碎成100-200目粉末，与氧化钙混合均匀加入适量水研磨，再加入液体石蜡、二甲基硅油混合均匀，将甲基丙烯酸甲酯、丙烯酸羟乙酯混合，加热至75℃-85℃反应1-1.5小时，然后加入除樟脑油之外的其余剩余成分，保温反应60-90分钟，最后将所有物料混合，冷去至室温后加入樟脑油，以400-500转/分的速度搅拌20-30分钟得到混合浆料，最后将混合浆料泵入喷雾干燥设备中，控制进风温度120-150℃、出风温度80-100℃，即可制成增效剂。
2.根据权利要求1所述一种添加石膏的多纤维混合保温砂浆，其特征在于，由以下具体步骤制成：首先将建筑废料、石膏、石蜡混合后研磨30-40分钟，形成200-300目粉末，然后与其他剩余成分混合，加入到双轴卧式搅拌釜中，以300-400转/分钟匀速搅拌15-20分钟，包装即得到保温砂浆预拌料。
CN201510382103.3A 2015-07-03 2015-07-03 一种添加石膏的多纤维混合保温砂浆及其制备方法 Pending CN105036676A (zh)