CN107200967A - 用于生产板材发泡层的组合物及包含此组合物的板材及其生产方法 - Google Patents

用于生产板材发泡层的组合物及包含此组合物的板材及其生产方法 Download PDF

Info

Publication number
CN107200967A
CN107200967A CN201710582639.9A CN201710582639A CN107200967A CN 107200967 A CN107200967 A CN 107200967A CN 201710582639 A CN201710582639 A CN 201710582639A CN 107200967 A CN107200967 A CN 107200967A
Authority
CN
China
Prior art keywords
layer
sheet material
lubricant
foaming
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710582639.9A
Other languages
English (en)
Inventor
周玉亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beneficial Plastics Machinery Co Ltd In Qingdao Three
Qingdao Sanyi Plastic Machinery Co Ltd
Original Assignee
Beneficial Plastics Machinery Co Ltd In Qingdao Three
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beneficial Plastics Machinery Co Ltd In Qingdao Three filed Critical Beneficial Plastics Machinery Co Ltd In Qingdao Three
Priority to CN201710582639.9A priority Critical patent/CN107200967A/zh
Priority to PCT/CN2017/097793 priority patent/WO2018113325A1/zh
Priority to MYPI2019007866A priority patent/MY189966A/en
Priority to KR1020177030359A priority patent/KR101986136B1/ko
Priority to EP17885269.5A priority patent/EP3617266B1/en
Publication of CN107200967A publication Critical patent/CN107200967A/zh
Priority to US15/811,628 priority patent/US10633503B2/en
Pending legal-status Critical Current

Abstract

本发明涉及用于生产板材发泡层的组合物，包括主要成分和辅助成分，其中，主要成分由聚氯乙烯(PVC)和碳酸钙组成，辅助成分包括调节剂、稳定剂、润滑剂、发泡剂；按照重量份数计，聚氯乙烯为75份，碳酸钙为75‑80份，调节剂为6‑8份，稳定剂为3‑5份，润滑剂为0.7‑1.4份；发泡剂为0.2‑0.7份。本用于生产板材的发泡层和实心层的组分中不含胶类物质，同时生产工艺中不含涂胶复合的过程，非常环保健康。通过本配方和本工艺生产得到的板材，通过聚氯乙烯发泡形成发泡层并且将聚氯乙烯未经发泡制得的实心层在发泡层的两侧共挤形成板材的核心层，具有优良的抗压、翘曲和收缩性能，并且防水、防潮、防虫，且工序简单。

Description

用于生产板材发泡层的组合物及包含此组合物的板材及其生 产方法
技术领域
本发明涉及板材领域，具体的说是用于生产板材发泡层的组合物及包含此组合物的板材及其生产方法。
背景技术
PVC塑胶板材由于其抗压、防水防潮、耐磨、环保等方面的优越性，越来越受消费者的青睐。但是，PVC塑胶板材性能的稳定性及优越性与其配方和加工工艺密不可分。
中国专利申请CN 103481517 A《一种PVC塑胶地板的生产工艺》，公开了将PVC混合粉、增塑剂、碳酸钙、稳定剂、石蜡、松香和碳粉经过混合、密炼、压延、冷却、裁片、入库养生、铺膜、烧制、养生、PU处理、物理处理、常温养生、成型、检测包装得到PVC塑胶地板。但是，此加工工艺非常复杂，材料消耗大，人工利用多，这无疑增加了产品的成本。
发明内容
根据上述不足之处，本发明的目的在于：提供一种用于生产板材发泡层的组合物及包含此组合物的板材及其生产方法。通过此配方生产出来的板材，操作工序简单，产品性能稳定。
为实现上述目的，本发明的技术方案在于：一种用于生产板材发泡层的组合物，包括主要成分和辅助成分，主要成分由聚氯乙烯和碳酸钙组成，辅助成分包括调节剂、稳定剂、润滑剂、发泡剂；按照重量份数计，聚氯乙烯为75份，碳酸钙为75-80份，调节剂为6-8份，稳定剂为3-5份，润滑剂为0.7-1.4份；发泡剂为0.2-0.7份。
优选的是：还包括回料，回料占发泡层组合物总质量的5-25％。
优选的是：润滑剂包括内润滑剂和外润滑剂。
优选的是：内润滑剂和外润滑剂的质量比为2:1-3:1。
优选的是：内润滑剂为硬脂酸、多元醇硬脂肪酸和氧化聚乙烯蜡中的一种或多种。
优选的是：外润滑剂为聚乙烯蜡。
优选的是：发泡剂包括白发泡剂和黄发泡剂。
优选的是：白发泡剂和黄发泡剂的质量比为1:1-3:7。
优选的是：白发泡剂为碳酸氢钠。
优选的是：黄发泡剂为偶氮二甲酰胺。
本发明还提供一种板材，包含有如前所述的组合物。
优选的是：板材包括位于中间层的发泡层和位于发泡层的两侧并与发泡层一体式挤出的实心层。
优选的是：发泡层一侧的实心层的表面设有防滑层。
优选的是：发泡层一侧的实心层的表面设有彩膜层。
优选的是：彩膜层的表面设有耐磨层。
优选的是：用于生产板材实心层的组合物，包括主要成分和辅助成分，主要成分由聚氯乙烯和碳酸钙组成，辅助成分包括调节剂、稳定剂、润滑剂；按重量份数计，聚氯乙烯为50份，碳酸钙为50-55份，调节剂为2-7份，稳定剂为2-4份、润滑剂为0.5-1.1份。
优选的是：还包括增塑剂，增塑剂占实心层组合物总质量的1-8％。
优选的是：增塑剂为邻苯二甲酸二辛酯或者环氧大豆油。
优选的是：润滑剂包括内润滑剂和外润滑剂。
优选的是：内润滑剂和外润滑剂的质量比为2:1-3:1。
优选的是：内润滑剂为硬脂酸、多元醇硬脂肪酸和氧化聚乙烯蜡中的一种或多种。
优选的是：外润滑剂为聚乙烯蜡。
本发明还提供一种生产如前所述的板材的方法，包括如下步骤：
(1)混料：将用于生产板材发泡层的组合物和用于生产板材实心层的组合物分别进行混料，先进行热混，当温度到达105-120℃时，再冷却搅拌；
(2)熔融：当物料温度降低至30-40℃时，将两种混合后的物料分别上料至挤出机的料斗，两种物料分别经事先预热至150-180℃的挤出机进行加热挤压成为熔体；
(3)分配成型：两种物料的熔体按照中间层为发泡层，发泡层的两侧为实心层的形式经过分配器进入160-180℃的模具腔内进行成型；
(4)定型复合：首先将成型的实心层和发泡层一起在20-50℃下冷却压平，随后温度逐渐升高；然后将需要复合的彩膜层或/和防滑层分别通过传输设备置于两层实心层的两侧，在130-180℃下进行压实复合，最后将耐磨层通过传输设备置于彩膜层的表面，在130-180℃下进行压实复合，形成板材；
(5)裁剪：对板材进行冷却，裁剪。
优选的是：防滑层或/和彩膜层复合后，分别在130-180℃下，对彩膜层的表面或/和防滑层的表面进行压纹。
本发明的有益效果在于：本用于生产板材的发泡层和实心层的组分中不含胶类物质，同时生产工艺中不含涂胶复合的过程，非常环保健康。通过本配方和本工艺生产得到的板材，通过聚氯乙烯发泡形成发泡层并且将聚氯乙烯未经发泡制得的实心层在发泡层的两侧共挤形成板材的核心层，使得生产得到的板材既轻便，又具有优于传统板材性能的特点，即具有优良的抗压、翘曲和收缩性能，并且防水、防潮、防虫。本生产工艺较传统的生产工艺节省了好几个步骤，不仅节约了设备投入，并且节约耗电量和人工费，本工艺不需要砂光，就没有粉尘，更加环保，且产能成品率高。
附图说明
图1是本发明的结构示意图
图中，1-耐磨层；2-彩膜层；3-实心层；4-发泡层；5-防滑层；6-锁扣；7-槽。
具体实施方式
下面结合具体实施例对本发明做进一步说明。
本发明涉及一种用于生产板材发泡层的组合物，包括主要成分和辅助成分，其中，主要成分由聚氯乙烯(PVC)和碳酸钙组成，辅助成分包括调节剂、稳定剂、润滑剂、发泡剂；按照重量份数计，聚氯乙烯为75份，碳酸钙为75-80份，调节剂为6-8份，稳定剂为3-5份，润滑剂为0.7-1.4份；发泡剂为0.2-0.7份。
本发泡层中通过将聚氯乙烯进行发泡，整体降低板材的重量，但是发泡后的板材中间会出现不规则的空隙，这些空隙会导致板材的抗压性较弱，通过碳酸钙的填充，可以起到支撑的作用，也就是说通过聚氯乙烯和碳酸钙的相互配合，既能节约聚氯乙烯的用量，同时又能确保板材具有足够的抗压性能及良好的翘曲和收缩性能。
本用于生产板材发泡层中所采用的碳酸钙为活性轻质碳酸钙。
本用于生产板材发泡层中所采用的调节剂为市售的化工助剂，其主要作用是调节发泡，增加塑化效果，使得聚氯乙烯可以呈现更好的发泡效果，促进塑化提高熔体强度，防止气泡合并或破裂，高分子量粘度熔体，保证充足的发泡熔体，提高流动性和表面光洁度。
本用于生产板材发泡层中所采用的稳定剂为市售的化工助剂，可以是钙锌稳定剂或者复合稳定剂，其主要作用是加工中抑制聚氯乙烯提前分解，使得配方体系拥有足够的稳定性。
作为一种优选的实施例，本用于生产板材发泡层的组合物中还包括回料，回料占发泡层组合物总质量的5-25％。回料就是在生产过程中产生的边角料废板破碎回收后的料。通过采用回料，可以在一定程度上降低原料的使用，降低成本。
作为一种优选的实施例，润滑剂包括内润滑剂和外润滑剂。外润滑剂的作用主要是改善聚合物熔体与加工设备的热金属表面的摩擦，它与聚合物相容性较差，容易从熔体内往外迁移，所以能在塑料熔体与金属的交界面形成润滑的薄层。内润滑剂与聚合物有良好的相容性，它在聚合物内部起到降低聚合物分子间内聚力的作用，从而改善塑料熔体的内摩擦生热和熔体的流动性。
其中，润滑剂包括内润滑剂和外润滑剂，内润滑剂和外润滑剂的质量比为2:1-3:1。
作为一种优选的实施例，内润滑剂为硬脂酸、多元醇硬脂肪酸和氧化聚乙烯蜡中的一种或多种；所述的外润滑剂为聚乙烯蜡。
作为一种优选的实施例，发泡剂包括白发泡剂和黄发泡剂，白发泡剂和黄发泡剂均为市售的化工助剂，白发泡剂和黄发泡剂的质量比为1:1-3:7。
本用于生产板材发泡层的组合物中发泡剂需要由白发泡剂和黄发泡剂共同作用，才能对聚氯乙烯起到很好的发泡的效果，单一一种发泡剂都不能达到理想的发泡效果，即，既要有传统木质地板相似的重量，又要有理想的抗压、翘曲和收缩性能。
作为一种优选的实施例，白发泡剂为碳酸氢钠；黄发泡剂为偶氮二甲酰胺。
本发明还提供一种板材，包含有如前所述的组合物。
本发明提供的板材包括位于中间层的发泡层和位于发泡层的两侧并与发泡层一体式挤出的实心层，如图1所示。
作为一种优选的实施例，发泡层4一侧的实心层3设有防滑层5。当板材需要与墙面或者地面进行安装时，防滑层是设置在板材靠近墙面或者地面的一侧，起到防止板材滑动的作用。
作为一种优选的实施例，发泡层4一侧的实心层3设有彩膜层2。因审美的需要，板材面对使用者的一侧复合上彩膜层，彩膜层的图案和色彩可以自行调整，以配合消费者的喜好以及建筑装饰的搭配。当板材需要双面都面对使用者时，可以在两层实心层的表面均附上彩膜层，并且彩膜层的图案和色彩可以不一样。
作为一种优选的实施例，彩膜层2的表面设有耐磨层1。耐磨层1可以起到保护彩膜层和板材本身的作用，具有防止彩膜层的图案磨损或是色彩流失，放水防潮防虫蛀等作用。
作为一种优选的实施例，用于生产板材实心层的组合物，包括主要成分和辅助成分，主要成分由聚氯乙烯和碳酸钙组成，辅助成分包括调节剂、稳定剂、润滑剂；按重量份数计，聚氯乙烯为50份，碳酸钙为50-55份，调节剂为2-7份，稳定剂为2-4份、润滑剂为0.5-1.1份。
实心层在发泡层的两侧，这是并且不含发泡剂，即不经过发泡的过程，这是因为实心层需要对发泡层起到一个保护和支撑的作用。当发泡层和实心层一体式寄出后成为板材的主体结构，使得板材兼具传统木制板材的轻便性和传统石塑材料的结实程度。
实心层中的调节剂为两种，一种是调节剂401，一种是调节剂CPE，均为市售的化工助剂。调节剂401促使物料前期塑化，属ACR系列抗冲类塑化助剂。CPE属增韧抗冲类料，增加制品的强度及柔韧性，提高表面硬度。
作为一种优选的实施例，还包括增塑剂，塑化剂为市售的化工助剂，增塑剂占实心层组合物总质量的1-8％，可以提高塑化的效果。
作为一种优选的实施例，增塑剂为邻苯二甲酸二辛酯(DOP)或者环氧大豆油。
作为一种优选的实施例，润滑剂包括内润滑剂和外润滑剂，内润滑剂和外润滑剂的作用如前所述。其中，内润滑剂和外润滑剂的质量比为2:1-3:1。
作为一种优选的实施例，内润滑剂为硬脂酸、多元醇硬脂肪酸和氧化聚乙烯蜡中的一种或多种；外润滑剂为聚乙烯蜡。
本发明还提供一种生产如前所述的板材的方法，包括如下步骤：
(1)混料：将用于生产板材发泡层的组合物和用于生产板材实心层的组合物分别进行混料，先进行热混，当温度到达105-120℃时，再冷却搅拌；
(2)熔融：当物料温度降低至30-40℃时，将两种混合后的物料分别上料至挤出机的料斗，两种物料分别经事先预热至150-180℃的挤出机进行加热挤压成为熔体；
(3)分配成型：两种物料的熔体按照中间层为发泡层，所述发泡层的两侧为实心层的形式经过分配器进入160-180℃的模具腔内进行成型；
(4)定型复合：首先将成型的实心层和发泡层一起在20-50℃下冷却压平，随后温度逐渐升高；然后将需要复合的彩膜层或/和防滑层分别通过传输设备置于两层实心层的两侧，在130-180℃下进行压实复合，最后将耐磨层通过传输设备置于彩膜层的表面，在130-180℃下进行压实复合，形成板材；
(5)裁剪：对板材进行冷却，裁剪。
其中，定型复合的过程中，首先需要对成型的实心层和发泡层进行冷却压平，这是因为中间层是发泡层，虽然挤出模具后就已经形成三层共挤层了，但是中间层由于是发泡层，出料后的中间层会出现波浪的形状，同时发泡层两侧的实心层也会随着发泡层出现波浪的形状，因此先用定型装置瞬间冷却压平，可以将板材的共挤层更为平坦，对于保证产品质量至关重要。冷却压平后进入成型机，成型机温度由低到高，刚开始如果温度太高会出现二次发泡的现象，所以先低温冷却一会成型后再加温复合。
定型复合的过程中，先压平后是边定型边复合的过程，随着板材的输送，前面的辊子温度较低，后面的辊子温度较高，一般情况下，前面的辊子温度为40-80℃，后面的辊子温度为100-160℃，当达到复合温度时，通过别的输送设备，将其他复合层输送至与共挤层进行复合。
复合的过程根据产品的需要进行调整，可以是先复合防滑层，再复合彩膜层，也可以是先复合彩膜层，再复合防滑层，或者两者同时复合。
当双面都需要彩膜层的情况下，可以将防滑层替换为彩膜层。
彩膜层的表面需要复合耐磨层，即通过传输设备将耐磨层置于彩膜层的表面，在130-180℃下进行压实复合，形成板材。
当不需要彩膜层时，也可以对彩膜层进行省略。
当不需要防滑层时，也可以对防滑层进行省略。
作为一种优选的实施例，耐磨层或/和彩膜层复合后，分别在130-180℃下，对彩膜层的表面或/和耐磨层的表面进行压纹。压纹的过程可选可不选，根据产品需求进行定制，当不需要压纹时，可以将花辊换为光辊即可。
传统的木塑板材的加工过程为挤出基材—砂光表面—涂胶—贴合—堆码—冷压—养生—分切—开槽—检测包装—打托—入库装箱。
本发明一步法加工过程为一步成型—养生—分切—开槽—检测包装—打托—入库装箱。
本发明的一步法生产工艺省掉五个工序的同时也省掉了以下的投入：
1、省掉了五个工序的设备的同时也省掉的设备占地面积的空间；
2、省掉了设备就省掉了钱和电费；
3、省掉了大量的人工(五个环节都需要工人)；
4、省掉了材料，比如说贴合前需要用胶水；同时胶水的成分不利于身体健康；
5、不需要砂光就没有粉尘，更加环保。
本产品具有非常优越的特点：
1、板材质地柔软，弹性很好，在重物冲击下有着良好的弹性恢复，能大大减少人员的滑到摔伤，同时对重物的冲击破坏也有良好的弹性恢复，不会造成损坏；
2、绿色环保、无毒无害、无放射性污染、属绿色环保产品，可资源回收利用；
3、板材有与水即涩的特性，同时都做了防滑处理(耐磨层花纹)；
4、安全性高、绝缘、阻燃、耐腐蚀、耐酸碱、表面无异状、离开明火能自熄；
5、防水、防潮、遇水不变形；
6、板材的吸音可达20分贝，所以在需要安静的环境如医院病房、图书馆、报告厅等地选用本发明的板材，就不用再为高跟鞋的响声而烦恼；
7、板材可以加工成众多的颜色和花纹，使用者的花纹的可选择范围更广泛，可以实现个性化定制；
8、施工安装简便；
9、超高性价比：比专业木地板价格便宜很多，但性能更卓越；
10、成品密度可在0.9T/m3-1.2T/m3内任意控制；
11、收缩率比传统的木塑板材低一到二倍之间；
12、基材部分可实现模内多层复合，再像SPC(石塑)地板一样，将彩膜和耐磨层材料同步复合成型，产品下线后直接开槽UV等即可成品销售；
13、大幅度的降低了设备成本、材料成本、人工成本及多步法成本，自动化程度高；
14、产量高，重量轻，涨缩率低，不开裂，不变形，零污染。
实施例1
按照表1准备原材料，表1为一个批次的用量。
表1实施例1的配方成分表
其中，青岛阳光嘉恒国际贸易有限公司德国巴斯夫在中国的唯一总代理。
OA6(氧化聚乙烯蜡)是一种高密度氧化聚乙烯蜡，前期起促进塑化、增大电流作用，后期起润滑作用。它的内润滑效果大于外润滑。
PE蜡为PVC加工的外润滑剂，调节塑化时间，增加制品表面光洁度，过少则塑化时间短，粘附严重，热稳定性差；过量则出现析出，模具内结垢。
60为内润滑剂，调节PVC物料内滑动性,减少熔体内摩擦，降低电流，协助物料均匀塑化，使用过量则破坏熔体黏度。
按照表1进行材料的准备，进行地板的生产，具体步骤如下：
(1)混料：将用于生产板材发泡层的组合物和用于生产板材实心层的组合物分别进行混料，先进行热混，当温度到达105-110℃时，再冷却搅拌；
其中，实心层物料搅拌的同时将DOP(因为是液体)慢慢的倒入旋转的搅拌机内，这样搅拌的比较均匀；
(2)熔融：当物料温度降低至30-35℃时，将两种混合后的物料分别上料至挤出机的料斗，两种物料分别经事先预热至150-160℃的挤出机进行加热挤压成为熔体；
(3)分配成型：两种物料的熔体按照中间层为发泡层，发泡层的两侧为实心层的形式经过分配器进入160-180℃的模具腔内进行成型；
(4)定型复合：首先将成型的实心层和发泡层一起在20-25℃下冷却压平，随后温度逐渐升高；然后将需要复合的彩膜层和防滑层分别通过传输设备置于两层实心层的两侧，在130-150℃下进行压实复合，最后将耐磨层通过传输设备置于彩膜层的表面，在130-150℃下进行压实复合，形成板材；防滑层和彩膜层复合后，分别在130-150℃下，对彩膜层的表面或/和防滑层的表面进行压纹；
(5)裁剪：对板材进行冷却，裁剪。
实施例2
按照表2准备原材料，表2为一个批次的用量。
表2实施例2的配方成分表
按照表2进行材料的准备，进行地板的生产，具体步骤如下：
(1)混料：将用于生产板材发泡层的组合物和用于生产板材实心层的组合物分别进行混料，先进行热混，当温度到达110-115℃时，再冷却搅拌；
(2)熔融：当物料温度降低至30-40℃时，将两种混合后的物料分别上料至挤出机的料斗，两种物料分别经事先预热至160-170℃的挤出机进行加热挤压成为熔体；
(3)分配成型：两种物料的熔体按照中间层为发泡层，发泡层的两侧为实心层的形式经过分配器进入165-170℃的模具腔内进行成型；
(4)定型复合：首先将成型的实心层和发泡层一起在35-40℃下冷却压平，随后温度逐渐升高；然后将需要复合的彩膜层或/和防滑层分别通过传输设备置于两层实心层的两侧，在150-160℃下进行压实复合，最后将耐磨层通过传输设备置于彩膜层的表面，在150-160℃下进行压实复合，形成板材；防滑层和彩膜层复合后，分别在150-160℃下，对彩膜层的表面或/和防滑层的表面进行压纹；
(5)裁剪：对板材进行冷却，裁剪。
实施例3
按照表3准备原材料，表3为一个批次的用量。
表3实施例3的配方成分表
按照表3进行材料的准备，进行地板的生产，具体步骤如下：
(1)混料：将用于生产板材发泡层的组合物和用于生产板材实心层的组合物分别进行混料，先进行热混，当温度到达115-120℃时，再冷却搅拌；
(2)熔融：当物料温度降低至35-40℃时，将两种混合后的物料分别上料至挤出机的料斗，两种物料分别经事先预热至170-180℃的挤出机进行加热挤压成为熔体；
(3)分配成型：两种物料的熔体按照中间层为发泡层，发泡层的两侧为实心层的形式经过分配器进入170-180℃的模具腔内进行成型；
(4)定型复合：首先将成型的实心层和发泡层一起在40-50℃下冷却压平，随后温度逐渐升高；然后将需要复合的彩膜层或/和防滑层分别通过传输设备置于两层实心层的两侧，在170-180℃下进行压实复合，最后将耐磨层通过传输设备置于彩膜层的表面，在170-180℃下进行压实复合，形成板材；防滑层和彩膜层复合后，分别在170-180℃下，对彩膜层的表面或/和防滑层的表面进行压纹；
(5)裁剪：对板材进行冷却，裁剪。
实施例4
按照表4准备原材料，表4为一个批次的用量。
表4实施例4的配方成分表
按照表4进行材料的准备，进行地板的生产，具体步骤如下：
(1)混料：将用于生产板材发泡层的组合物和用于生产板材实心层的组合物分别进行混料，先进行热混，当温度到达105-120℃时，再冷却搅拌；
(2)熔融：当物料温度降低至30-40℃时，将两种混合后的物料分别上料至挤出机的料斗，两种物料分别经事先预热至150-180℃的挤出机进行加热挤压成为熔体；
(3)分配成型：两种物料的熔体按照中间层为发泡层，发泡层的两侧为实心层的形式经过分配器进入160-180℃的模具腔内进行成型；
(4)定型复合：首先将成型的实心层和发泡层一起在20-50℃下冷却压平，随后温度逐渐升高；然后将需要复合的彩膜层和防滑层分别通过传输设备置于两层实心层的两侧，在130-180℃下进行压实复合，最后将耐磨层通过传输设备置于彩膜层的表面，在130-180℃下进行压实复合，形成板材；防滑层和彩膜层复合后，分别在130-180℃下，对彩膜层的表面或/和防滑层的表面进行压纹。
(5)裁剪：对板材进行冷却，裁剪。
实施例5
按照表5准备原材料。
表5实施例5的配方成分表
按照表5进行材料的准备，进行非地板用板材的生产，具体步骤如下：
(1)混料：将用于生产板材发泡层的组合物和用于生产板材实心层的组合物分别进行混料，先进行热混，当温度到达105-120℃时，再冷却搅拌；
(2)熔融：当物料温度降低至30-40℃时，将两种混合后的物料分别上料至挤出机的料斗，两种物料分别经事先预热至150-180℃的挤出机进行加热挤压成为熔体；
(3)分配成型：两种物料的熔体按照中间层为发泡层，发泡层的两侧为实心层的形式经过分配器进入160-180℃的模具腔内进行成型；
(4)定型复合：首先将成型的实心层和发泡层一起在20-50℃下冷却压平，随后温度逐渐升高；然后将需要复合的彩膜层通过传输设备置于两层实心层的两侧，在130-180℃下进行压实复合，最后将耐磨层通过传输设备置于彩膜层的表面，在130-180℃下进行压实复合，形成板材；彩膜层复合后，分别在130-180℃下，对彩膜层的表面或/和防滑层的表面进行压纹；
(5)裁剪：对板材进行冷却，裁剪。
对于实施例1-5生产的板材与传统板材进行性能测试，测试结果如表6所示。
表6本发明生产的板材与传统板材各性能指标对比表
通过表6可以知道，本发明生产得到的板材各项指标均优于传统板材。

Claims (17)

1.一种用于生产板材发泡层的组合物，其特征在于：包括主要成分和辅助成分，所述的主要成分由聚氯乙烯和碳酸钙组成，所述的辅助成分包括调节剂、稳定剂、润滑剂、发泡剂；按照重量份数计，所述的聚氯乙烯为75份，所述的碳酸钙为75-80份，所述的调节剂为6-8份，所述的稳定剂为3-5份，所述的润滑剂为0.7-1.4份；所述的发泡剂为0.2-0.7份。
2.根据权利要求1所述的组合物，其特征在于：还包括回料，所述的回料占发泡层组合物总质量的5-25％。
3.根据权利要求1或2所述的组合物，其特征在于：所述的润滑剂包括内润滑剂和外润滑剂，所述的内润滑剂和外润滑剂的质量比为2:1-3:1。
4.根据权利要求3所述的组合物，其特征在于：所述的内润滑剂为硬脂酸、多元醇硬脂肪酸和氧化聚乙烯蜡中的一种或多种；所述的外润滑剂为聚乙烯蜡。
5.根据权利要求3所述的组合物，其特征在于：所述的发泡剂包括白发泡剂和黄发泡剂，所述的白发泡剂和黄发泡剂的质量比为1:1-3:7。
6.一种板材，其特征在于：包含有如权利要求1-5任意一项所述的组合物。
7.根据权利要求6所述的板材，其特征在于：包括位于中间层的发泡层(4)和位于所述发泡层(4)的两侧并与所述发泡层(4)一体式挤出的实心层(3)。
8.根据权利要求7所述的板材，其特征在于：所述发泡层(4)一侧的实心层(3)的表面设有防滑层(5)。
9.根据权利要求7或8所述的板材，其特征在于：所述发泡层(4)一侧的实心层(3)的表面设有彩膜层(2)。
10.根据权利要求9所述的板材，其特征在于：所述彩膜层(2)的表面设有耐磨层(1)。
11.根据权利要求9所述的板材，其特征在于：用于生产板材实心层的组合物，包括主要成分和辅助成分，所述的主要成分由聚氯乙烯和碳酸钙组成，所述的辅助成分包括调节剂、稳定剂、润滑剂；按重量份数计，所述的聚氯乙烯为50份，所述的碳酸钙为50-55份，所述的调节剂为2-7份，所述的稳定剂为2-4份、所述的润滑剂为0.5-1.1份。
12.根据权利要求11所述的板材，其特征在于：还包括增塑剂，所述增塑剂占实心层组合物总质量的1-8％。
13.根据权利要求12所述的板材，其特征在于：所述的增塑剂为邻苯二甲酸二辛酯或者环氧大豆油。
14.根据权利要求11或12所述的组合物，其特征在于：所述的润滑剂包括内润滑剂和外润滑剂，所述的内润滑剂和外润滑剂的质量比为2:1-3:1。
15.根据权利要求14所述的组合物，其特征在于：所述的内润滑剂为硬脂酸、多元醇硬脂肪酸和氧化聚乙烯蜡中的一种或多种；所述的外润滑剂为聚乙烯蜡。
16.一种生产如权利要求6-15任意一项所述的板材的方法，其特征在于：包括如下步骤：
(1)混料：将用于生产板材发泡层的组合物和用于生产板材实心层的组合物分别进行混料，先进行热混，当温度到达105-120℃时，再冷却搅拌；
(2)熔融：当物料温度降低至30-40℃时，将两种混合后的物料分别上料至挤出机的料斗，两种物料分别经事先预热至150-180℃的挤出机进行加热挤压成为熔体；
(3)分配成型：两种物料的熔体按照中间层为发泡层，发泡层的两侧为实心层的形式经过分配器进入160-180℃的模具腔内进行成型；
(4)定型复合：首先将成型的实心层和发泡层一起在20-50℃下冷却压平，随后温度逐渐升高；然后将需要复合的耐磨层或/和防滑层分别通过传输设备置于两层实心层的两侧，在130-180℃下进行压实复合，最后将耐磨层通过传输设备置于彩膜层的表面，在130-180℃下进行压实复合，形成板材；
(5)裁剪：对板材进行冷却，裁剪。
17.根据权利要求16所述的生产板材的方法，其特征在于：所述的防滑层或/和彩膜层复合后，分别在130-180℃下，对彩膜层的表面或/和防滑层的表面进行压纹。
CN201710582639.9A 2017-07-17 2017-07-17 用于生产板材发泡层的组合物及包含此组合物的板材及其生产方法 Pending CN107200967A (zh)