CN106947413B - A kind of dedicated filleting glue squeegeeed for house ornamentation seam and preparation method - Google Patents
A kind of dedicated filleting glue squeegeeed for house ornamentation seam and preparation method Download PDFInfo
- Publication number
- CN106947413B CN106947413B CN201710204534.XA CN201710204534A CN106947413B CN 106947413 B CN106947413 B CN 106947413B CN 201710204534 A CN201710204534 A CN 201710204534A CN 106947413 B CN106947413 B CN 106947413B
- Authority
- CN
- China
- Prior art keywords
- filleting
- filleting glue
- seam
- dedicated
- squeegeeed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of dedicated filleting glue squeegeeed for house ornamentation seam and preparation method, the component including following weight content：Vinyl acetate-ethylene copolymerization emulsions 55%-60%, powdered whiting 12%-15%, precipitated calcium carbonate 20%-25%, lignocellulosic particle 1.5%, dioctyl phthalate 1.5%, chlorinated paraffin -52 accounts for 1.5%；The beneficial effects of the present invention are：Filleting glue has high tenacity after parching, and arbitrarily folds indeformable, does not crack；Environmental protection, non-volatile object is pollution-free；High adhesion force, subordinate cover not delamination；Construction is simple changes tradition and repeats to drape over one's shoulders to scrape method of attaching, one-pass molding.
Description
Technical field
The invention belongs to glue field more particularly to a kind of dedicated filleting glue squeegeeed for house ornamentation seam.
Background technique
During interior decoration, when plaster tablet suspended ceiling, partition wall, junction usually will appear gap, for beauty, need
Gap is smoothed out with glue, has a kind of filleting glue for being seam king that repetition is needed to smear repetition currently on the market and scrapes and could smooth out, and two
It is secondary to be also easy to fall off when smearing, it also cracks often in the drying process, there is peculiar smell, using effect is bad.
The capital equipment that the preparation of filleting glue of the present invention is used is dispersion machine, and dispersion machine is broadly one kind of blender.
Since using high speed agitator very strong turbulent flow can be partially formed, usually there is very strong dispersion and emulsion effect to material.Point
It is strong to dissipate machine continuous production, rapid dispersion and dissolution can be carried out to material, dispersion effect is good, high production efficiency, smooth running, peace
Dress is easy.There are many dispersion machines, the present invention using stirring dispersion machine, stirring dispersion machine be suitable for coating, dyestuff, ink,
The liquid and liquid in the fields such as pigment, cosmetics, resin, adhesive, lotion, medicine, petroleum-powder phase materials carry out stirring for high speed
It mixes, dissolve and disperses, speed can be adjusted arbitrarily（0-1440 revs/min）.Stirring dispersion machine uses stepless speed regulation：There is electromagnetic speed-adjusting, become
Frequency modulation speed（Such as it is used for water paint）And explosion-proof variable frequency variable speed（Such as it is used for oil paint）Etc. diversified forms.Function of stepless speed regulation energy
Sufficiently meet technique requirement different in each technical process, different revolving speeds can be selected according to different operation stages.Powder
Not adding assistant, not applicable to the brilliant higher material of packet integrity demands.The zigzag circular dispersion of working principle high speed disperser
Disk high speed dispersion in container completes solid-liquid dispersing, wet, depolymerization, stabilization process.Make slurries in annular flow is rolled, generates strong rotation
Whirlpool, slurry surface particle drop to vortex bottom in the shape of a spiral；Form turbulent area at dispersion plate edge 2.5-5mm, slurry and
Particle is by intensive shear and impact；Two lines above and below being formed outside region, slurry are sufficiently recycled and are stirred；Dispersion machine
It is laminar state below dispersion impeller, pulp layer different in flow rate, which diffuses into one another, plays peptizaiton.High speed disperser has hydraulic
Lifting, the multiple functions such as 360 degree of revolution, stepless speed regulation, can configure 2-4 container simultaneously, 1000 millimeters of hydraulic lifting stroke,
360 degree of revolute functions can better meet a tractor serves several purposes, can in a short period of time from a cylinder transform to another cylinder into
Row operation greatly improves working efficiency, while also reducing labor intensity.
The raw material dioctyl phthalate that the present invention uses, abbreviation dioctyl ester（DOP）, it is a kind of organosilane ester chemical combination
Object is a kind of common plasticiser.
Summary of the invention
In order to develop it is a kind of it is easy to operate, adhesive force is strong, free from extraneous odour filleting glue, the invention discloses one kind to be used for house
The dedicated filleting glue and preparation method of seam sews and mend in attaching, and the present invention is achieved by the following technical solutions.
A kind of dedicated filleting glue squeegeeed for house ornamentation seam, the component including following weight content：
Vinyl acetate-ethylene copolymerization emulsions 55%-60%
Powdered whiting 12%-16%
Precipitated calcium carbonate 20%-26%
Lignocellulosic particle 1.5%
Dioctyl phthalate 1.5%
Chlorinated paraffin -52 1.5%
The filleting glue is grouped as by above group；
The preparation method of the dedicated filleting glue squeegeeed for house ornamentation seam, includes the following steps：
The first step：Prepare filleting collagen material, separately prepares by following raw material and proportion
Vinyl acetate-ethylene copolymerization emulsions 55%-60%
Powdered whiting 12%-16%
Precipitated calcium carbonate 20%-26%
Lignocellulosic particle 1.5%
Dioctyl phthalate 1.5%
Chlorinated paraffin -52 1.5%；
Second step：The stirring point that revolving speed is 80r/min is added in the vinyl acetate-ethylene copolymerization emulsions that the first step is prepared
It dissipates and is stirred in machine；Powdered whiting, precipitated calcium carbonate are sequentially added in whipping process, are stirred to react 5 minutes；It adds wooden
Fiber grain stirs 3 minutes；Dioctyl phthalate, chlorinated paraffin -52 are sequentially added, stirs 15 minutes, keeps product equal
It is even without condensation particle, it is hydraulic go out tank up to filleting glue.
Preferably, when preparing above-mentioned filleting glue, environment temperature just produces when being higher than 3 °C.
The beneficial effects of the present invention are：Filleting glue has high tenacity after parching, and arbitrarily folds indeformable, does not crack；Ring
It protects, non-volatile object is pollution-free；High adhesion force, subordinate cover not delamination；Construction is simple changes tradition and repeats to drape over one's shoulders to scrape method of attaching,
One-pass molding.
Specific embodiment
The present invention will be further described combined with specific embodiments below, gives the present embodiment, ordinary skill people
The embodiment that member is made without making creative work is all within the scope of the present invention.
Embodiment 1：
A kind of dedicated filleting glue squeegeeed for house ornamentation seam, the component including following weight content：
Vinyl acetate-ethylene copolymerization emulsions 55.5%
Powdered whiting 15.5%
Precipitated calcium carbonate 24.5%
Lignocellulosic particle 1.5%
Dioctyl phthalate 1.5%
Chlorinated paraffin -52 1.5%
The filleting glue is grouped as by above group；
The preparation method of the dedicated filleting glue squeegeeed for house ornamentation seam, includes the following steps：
The first step：Prepare filleting collagen material, separately prepares by following raw material and proportion
Vinyl acetate-ethylene copolymerization emulsions 55.5%
Powdered whiting 15.5%
Precipitated calcium carbonate 24.5%
Lignocellulosic particle 1.5%
Dioctyl phthalate 1.5%
Chlorinated paraffin -52 1.5%
Second step：The stirring point that revolving speed is 80r/min is added in the vinyl acetate-ethylene copolymerization emulsions that the first step is prepared
It dissipates and is stirred in machine；Powdered whiting, precipitated calcium carbonate are sequentially added in whipping process, are stirred to react 5 minutes；It adds wooden
Fiber grain stirs 3 minutes；Dioctyl phthalate, chlorinated paraffin -52 are sequentially added, stirs 15 minutes, keeps product equal
It is even without condensation particle, it is hydraulic go out tank up to filleting glue.
Embodiment 2：
A kind of dedicated filleting glue squeegeeed for house ornamentation seam, the component including following weight content：
Vinyl acetate-ethylene copolymerization emulsions 57.0%
Powdered whiting 14.0%
Precipitated calcium carbonate 24.5%
Lignocellulosic particle 1.5%
Dioctyl phthalate 1.5%
Chlorinated paraffin -52 1.5%
The filleting glue is grouped as by above group；
The preparation method of the dedicated filleting glue squeegeeed for house ornamentation seam, includes the following steps：
The first step：Prepare filleting collagen material, separately prepares by following raw material and proportion
Vinyl acetate-ethylene copolymerization emulsions 57.0%
Powdered whiting 14.0%
Precipitated calcium carbonate 24.5%
Lignocellulosic particle 1.5%
Dioctyl phthalate 1.5%
Chlorinated paraffin -52 1.5%
Second step：The stirring point that revolving speed is 80r/min is added in the vinyl acetate-ethylene copolymerization emulsions that the first step is prepared
It dissipates and is stirred in machine；Powdered whiting, precipitated calcium carbonate are sequentially added in whipping process, are stirred to react 5 minutes；It adds wooden
Fiber grain stirs 3 minutes；Dioctyl phthalate, chlorinated paraffin -52 are sequentially added, stirs 15 minutes, keeps product equal
It is even without condensation particle, it is hydraulic go out tank up to filleting glue.
Embodiment 3：
A kind of dedicated filleting glue squeegeeed for house ornamentation seam, the component including following weight content：
Vinyl acetate-ethylene copolymerization emulsions 60.0%
Powdered whiting 12.0%
Precipitated calcium carbonate 23.5%
Lignocellulosic particle 1.5%
Dioctyl phthalate 1.5%
Chlorinated paraffin -52 1.5%
The filleting glue is grouped as by above group；
The preparation method of the dedicated filleting glue squeegeeed for house ornamentation seam, includes the following steps：
The first step：Prepare filleting collagen material, separately prepares by following raw material and proportion
Vinyl acetate-ethylene copolymerization emulsions 60.0%
Powdered whiting 12.0%
Precipitated calcium carbonate 23.5%
Lignocellulosic particle 1.5%
Dioctyl phthalate 1.5%
Chlorinated paraffin -52 1.5%
Second step：The stirring point that revolving speed is 80r/min is added in the vinyl acetate-ethylene copolymerization emulsions that the first step is prepared
It dissipates and is stirred in machine；Powdered whiting, precipitated calcium carbonate are sequentially added in whipping process, are stirred to react 5 minutes；It adds wooden
Fiber grain stirs 3 minutes；Dioctyl phthalate, chlorinated paraffin -52 are sequentially added, stirs 15 minutes, keeps product equal
It is even without condensation particle, it is hydraulic go out tank up to filleting glue.
Claims (1)
1. a kind of dedicated filleting glue squeegeeed for house ornamentation seam, the component including following weight content：
Vinyl acetate-ethylene copolymerization emulsions 55%-60%
Powdered whiting 12%-15%
Precipitated calcium carbonate 20%-25%
Lignocellulosic particle 1.5%
Dioctyl phthalate 1.5%
Chlorinated paraffin -52 1.5%
The filleting glue is grouped as by above group；
The preparation method of the dedicated filleting glue squeegeeed for house ornamentation seam, includes the following steps：
The first step：Prepare filleting collagen material, separately prepares by following raw material and proportion
Vinyl acetate-ethylene copolymerization emulsions 55%-60%
Powdered whiting 12%-15%
Precipitated calcium carbonate 20%-25%
Lignocellulosic particle 1.5%
Dioctyl phthalate 1.5%
Chlorinated paraffin -52 1.5%；
Second step：The vinyl acetate-ethylene copolymerization emulsions that the first step is prepared are added in the stirring dispersion machine that revolving speed is 80rpm
Stirring；Powdered whiting, precipitated calcium carbonate are sequentially added in whipping process, are stirred to react 5 minutes；Add wood fibre
Grain stirring 3 minutes；Dioctyl phthalate, chlorinated paraffin -52 are sequentially added, is stirred 15 minutes, makes product uniformly without solidifying
Particle is tied, hydraulic tank out is up to filleting glue.