CN109665750A - Water-in-water multicolor coating and preparation method thereof, construction method and application - Google Patents
Water-in-water multicolor coating and preparation method thereof, construction method and application Download PDFInfo
- Publication number
- CN109665750A CN109665750A CN201811607748.2A CN201811607748A CN109665750A CN 109665750 A CN109665750 A CN 109665750A CN 201811607748 A CN201811607748 A CN 201811607748A CN 109665750 A CN109665750 A CN 109665750A
- Authority
- CN
- China
- Prior art keywords
- water
- agent
- continuous phase
- color grain
- multicolor coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides a kind of water-in-water multicolor coating and preparation method thereof, construction method and applications, are related to technical field of coatings, and the water-in-water multicolor coating includes color grain 7.5-30wt% and continuous phase 70-92.5wt%;The continuous phase includes white sand 30-50wt%, aqueous acrylic emulsion 30-50wt%, non-association type alkali swollen thickener 0.5-1.5wt%, hydroxyethyl ether cellulose 0.1-0.3wt% and water 10-25wt%, alleviates the technical issues of existing water-in-water multicolor coating can not be constructed using roller coating or by the way of batch scraping.Water-in-water multicolor coating viscosity stabilization provided by the invention, color grain is evenly dispersed in continuous phase, and no color grain is adhered and sedimentation phenomenon, can be constructed by roller coating or batch mode of scraping, the use scope for effectively expanding water-in-water multicolor coating, has broad application prospects.
Description
Technical field
The present invention relates to technical field of coatings, more particularly, to a kind of water-in-water multicolor coating and preparation method thereof, construction
Methods and applications.
Background technique
In aqueous, environmental protective, economize on resources, under the promotion of imitation stone demand true to nature, water-in-water multicolor coating is low with VOC content,
The decorative pattern figure effect of different marbles, granite can be prepared according to people's demand, market demand is increasing.Existing water
Packet water multicolor finish is substantially to be granulated in protective glue using base paint first, then use lotion as film forming matter and
It is made.
But existing most of water-in-water multicolor coating is using roller coating or when the forms of construction work such as batch scraping and being constructed, color grain
It is easy to cause color grain in construction surface to be unevenly distributed with construction tool movement, be unable to reach the effect for imitating stone material and decorative pattern figure.
Therefore, existing water-in-water multicolor coating needs the form pressurizeed using air pressure tank to be sprayed at building wall.And air pressure tank pressurizes
The harsh conditions of spraying are simply not proposed to the decoration of exterior wall such as household interior wall and cottage, to limit the colorful painting of water-water
The application range of material.
In view of this, the present invention is specifically proposed.
Summary of the invention
One of the objects of the present invention is to provide a kind of colorful paintings of water-water that can be constructed by roller coating or batch mode of scraping
Material, unstable to improve existing most of water-in-water multicolor coating system, color grain is easy to be adhered and settle, and needs using air pressure tank
Pressurized spray is in building wall, the technical issues of causing the application of water-in-water multicolor coating to be restricted.
Water-in-water multicolor coating provided by the invention, including following component: color grain 7.5-30wt% and continuous phase 70-
92.5wt%;Wherein, the continuous phase includes the following raw material: white sand 30-50wt%, aqueous acrylic emulsion 30-50wt%, non-
Association type alkali swollen thickener 0.5-1.5wt% and water 10-25wt%;
Preferably, the water-in-water multicolor coating includes color grain 10-25wt% and continuous phase 75-90wt%;
Preferably, the water-in-water multicolor coating includes color grain 15-25wt% and continuous phase 75-85wt%;
Preferably, in the continuous phase, white sand 35-45wt%, aqueous acrylic emulsion 35-45wt%, non-association
Type alkali swollen thickener is 0.5-1.5wt% and water 10-25wt%;
Preferably, in the continuous phase, white sand 38-42wt%, aqueous acrylic emulsion 38-42wt%, non-association
Type alkali swollen thickener is 0.8-1.2wt% and water 10-25wt%.
Further, the continuous phase further includes continuous phase auxiliary agent, continuous phase auxiliary agent the containing in the continuous phase
Amount is 1.5-5.5wt%;
Preferably, continuous phase auxiliary agent includes hydroxyethyl ether cellulose, defoaming agent, pH adjusting agent, film forming agent, antifreezing agent and kills
Bacterium at least one of the preservatives, preferably hydroxyethyl ether cellulose, non-association type alkali swollen thickener, defoaming agent, pH are adjusted
Agent, film forming agent, antifreezing agent and sterilization antiseptic mixture;
Preferably, the continuous phase auxiliary agent includes hydroxyethyl ether cellulose 0.1-0.3wt%, pH adjusting agent 0.1-
0.2wt%, defoaming agent 0.1-0.5wt%, film forming agent 0.5-1wt%, antifreezing agent 1-5wt% and sterilization antiseptic 0.1-
0.5wt%.
Further, the partial size of the color grain is 0.1-1.2cm;
And/or the partial size of the white sand is 80-120 mesh.
Further, the raw material of the color grain includes base paint and the first protection sol solution, and the base paint includes containing to form
Close acrylic emulsion 25-30wt%, the second protection the sol solution 8-10wt%, high molecular weight hydrophobically modified hydroxyethyl fiber of group
Plain ether 1-1.5wt% and water 50-60wt%.
Further, the mass ratio of the base paint and the first protection sol solution is (1-6): (1-3).
Further, the solute of the first protection sol solution and the second protection sol solution is lithium metasilicate magnalium soap;
Preferably, in the first protection sol solution, the concentration of the first protective glue is 3-7wt%;
Preferably, in the second protection sol solution, the concentration of the second protective glue is 5-10wt%;
Preferably, the lithium metasilicate magnalium soap is by water-soluble organic pyrophosphate salt organic matter processing.
Further, the base paint further includes base paint auxiliary agent, base paint auxiliary agent the containing in the base paint
Amount is 2.5-5wt%;
Preferably, the base paint auxiliary agent includes filler, pH adjusting agent, defoaming agent, film forming agent, antifreezing agent and sterilization and anticorrosion
At least one of agent, preferably filler, pH adjusting agent, defoaming agent, film forming agent, antifreezing agent and sterilization antiseptic mixture;
Preferably, the base paint auxiliary agent includes filler 0.5-1wt%, defoaming agent 0.1-0.5wt%, pH adjusting agent 0.1-
0.2wt%, film forming agent 1-2wt%, antifreezing agent 0.5-1.5wt% and sterilization antiseptic 0.1-0.5wt%.
Further, the preparation method of the color grain includes the following steps: base paint to be added in the first protection sol solution
It is uniformly mixed, obtains color grain;
The second object of the present invention is to provide the preparation method of above-mentioned water-in-water multicolor coating, include the following steps:
Color grain and continuous phase are uniformly mixed, water-in-water multicolor coating is obtained;
Preferably, high molecular weight hydrophobically modified hydroxyethyl cellulose ether, the acrylic emulsion containing associative groups, second are protected
It protects sol solution, water and optional base paint auxiliary agent to be uniformly mixed, obtains base paint.
Preferably, by aqueous acrylic emulsion, white sand, non-association type alkali swollen thickener, water and optional continuous help
Agent is uniformly mixed, and obtains continuous phase.
The third object of the present invention is to provide the construction method of above-mentioned water-in-water multicolor coating, using roller coating or batch scrapes
Mode is constructed.
The fourth purpose provided by the invention is to provide application of the water-in-water multicolor coating in interior wall or decoration of exterior wall.
In water-in-water multicolor coating provided by the invention, color grain and white sand, aqueous acrylic emulsion and non-association type alkali soluble
Swollen thickener mutually cooperates with, and forms thixotropic system, effectively color grain can be avoided to be dragged by construction tool, so that water-water coating
It can be constructed by roller coating or batch mode of scraping, effectively expand the use scope of water-in-water multicolor coating, had wide
Application prospect.
The preparation method simple process of water-in-water multicolor coating provided by the invention, it is easy to operate, industry can be suitable for
Change mass production, improve production efficiency, reduces production cost.
Specific embodiment
Embodiment of the present invention is described in detail below in conjunction with embodiment, but those skilled in the art will
Understand, the following example is merely to illustrate the present invention, and is not construed as limiting the scope of the invention.It is not specified in embodiment specific
Condition person carries out according to conventional conditions or manufacturer's recommended conditions.Reagents or instruments used without specified manufacturer is
The conventional products that can be obtained by commercially available purchase.
It should be understood that
In the present invention, if without particularly illustrating, all embodiments mentioned in this article and preferred implementation method
It can be combined with each other to form new technical solution.
In the present invention, if percentage (%) or part refer to the weight relative to composition without particularly illustrating
Percentage or parts by weight.
In the present invention, if related each component or its preferred ingredient can be combined with each other shape without particularly illustrating
The technical solution of Cheng Xin.
In the present invention, unless otherwise indicated, numberical range " a~b " indicates the contracting of any real combinings between a to b
Sketch form shows that wherein a and b is real number.Such as numberical range " 6~22 " indicate herein all listed " 6~22 " it
Between whole real numbers, " 6~22 " be these combinations of values breviary indicate.
" range " disclosed in this invention can be respectively one or more lower limits and one in the form of lower and upper limit
A or multiple upper limits.
In the present invention, unless otherwise indicated, it is each reaction or operating procedure can sequentially carry out, can also in sequence into
Row.Preferably, reaction method herein is that sequence carries out.
Unless otherwise indicated, profession used herein and meaning phase known to scientific term and one skilled in the art
Together.In addition, any method similar to or equal to what is recorded or material can also be applied in the present invention.
According to an aspect of the present invention, the present invention provides a kind of water-in-water multicolor coatings
Including following component: color grain 7.5-30wt% and continuous phase 70-92.5wt%;Wherein, the continuous phase includes such as
Lower raw material: white sand 30-50wt%, aqueous acrylic emulsion 30-50wt%, non-association type alkali swollen thickener 0.5-1.5wt%
With water 10-25wt%.
In the present invention, the sum of color grain and continuous phase are 100wt%, and the content of color grain is 7.5-30wt%, continuous phase
Content is 70-92.5wt%.
In water-in-water multicolor coating provided by the invention, color grain and white sand, the non-association type alkali soluble of aqueous acrylic emulsion agent
Swollen thickener mutually cooperates with, and forms thixotropic system, effectively color grain can be avoided to be dragged by construction tool, so that water-water coating
It can be constructed by roller coating or batch mode of scraping, effectively expand the use scope of water-in-water multicolor coating, had wide
Application prospect.
Inventors have found that being not easy to form thixotropic when the content of color grain in water-in-water multicolor coating is more than 30wt%
System can not be unable to reach decorative pattern figure effect by batch scraping or the construction of roll coating model, when the content of color grain is lower than 7.5wt%
Fruit.It is typical but non-limiting, in water-in-water multicolor coating provided by the invention, the content of color grain for example 7.5wt%,
10wt%, 12wt%, 15wt%, 18wt%, 20wt%, 25wt% or 30wt%;The content of continuous phase for example 70wt%,
72wt%, 75wt%, 78wt%, 80wt%, 82wt%, 85wt%, 90wt% or 92.5wt%.
Typical but non-limiting, in the continuous phase of water-in-water multicolor coating provided by the invention, the content of white sand is for example
30wt%, 32wt%, 35wt%, 38wt%, 40wt%, 42wt%, 45wt%, 48wt% or 50wt%.
In the raw material of the continuous phase of water-in-water multicolor coating provided by the invention, the content of white sand is 30-50wt%, water
The content of property acrylic emulsion is 30-50wt%, the content of non-association type alkali swollen thickener is 0.5-1.5wt% and water contains
Amount is 10-25wt%.
Continuous phase of the present invention can only include (specific) these components, can also organize exceptionally except these, including its
His component, these other components assign the continuous phase different characteristics.May be replaced by enclosed " for " or " by ...
Composition ".Regardless of which kind of ingredient is continuous phase of the present invention include, the sum of each component of the continuous phase is 100wt%.
In the continuous phase of water-in-water multicolor coating provided by the invention the content of white sand be 30-50wt%, make ground white sand with
Aqueous acrylic emulsion and non-association type alkali swollen thickener mutually cooperate with, in addition, when carrying out roller coating or batch scraping construction, white sand
Addition on the one hand improve the surface roughness for painting sample, to prevent color grain from being dragged away by construction tool, there is color grain point after construction
Cloth is uneven, the problem of plate face effect difference, on the other hand by the addition of white sand so that white sand is evenly distributed on after paint sample is dry
Surface of the paint film not only will not influence the form and aspect of color grain, but also have certain sand sense, guarantee the same of paint film decorative effect
When, also add touch sense.
In addition, on the one hand the continuous phase of water-in-water multicolor coating provided by the invention passes through the white sand that 30-50wt% is added
It is improved continuous phase thickening efficiency, improves the dispersion stabilization of color grain, color grain is avoided to be adhered and settle, it is on the other hand continuous
By selecting non-association type alkali swollen thickener to be thickened in phase, glued so that being prepared into paint sample rheology system and being more biased towards low sheraing
Degree, thixotropy is good, is not easy to be adhered between continuous phase and color grain together, construct more smooth, batch scrapes or when roller application, color
Grain is evenly distributed, to realize roller coating or criticize the construction requirement for scraping multicolor finish.
It is typical but non-limiting, in the continuous phase of water-in-water multicolor coating, the content of white sand for example 30wt%,
32wt%, 35wt%, 38wt%, 40wt%, 42wt%, 45wt%, 48wt% or 50wt%.
In the preferred embodiment of the present invention, the partial size of white sand is 80-120 mesh.By the partial size for controlling white sand
For 80-120 mesh, in order to white sand uniform and stable dispersion in continuous phase, to guarantee paint film plate made of water-in-water multicolor coating
Face effect is more preferable.
In water-in-water multicolor coating continuous phase provided by the invention, the content of aqueous acrylic emulsion is 30-50wt%.
By the way that in control continuous phase, the content of aqueous acrylic emulsion is 30-50wt%, to guarantee the viscosity of continuous phase.It is typical but non-
It is restrictive, in water-in-water multicolor coating continuous phase, the content of aqueous acrylic emulsion for example 30wt%, 32wt%, 35wt%,
38wt%, 40wt%, 42wt%, 45wt% or 50wt%.
In the preferred embodiment of the present invention, aqueous acrylic emulsion is carboxylic aqueous acrylic emulsion,
Preferably Changshu Ahmedabad richness Science and Technology Ltd., the aqueous acrylic emulsion containing carboxyl of model RS-6733.
In water-in-water multicolor coating continuous phase provided by the invention, the non-swollen amount of thickener of association type alkali soluble is 0.5-
1.5wt%.
It is thickened by using non-association type alkali swollen thickener, on the one hand makes the colorful painting of the water-water being prepared
Material system is more biased towards low-shear viscosity, and coating does not settle during storage, not sagging, while system inclined thixotroping when construction
Property, it is not easy to be adhered between continuous phase and color grain, keeps construction more smooth, batch scrapes or color grain is more evenly distributed when roller coating;It is another
Aspect, water-in-water multicolor coating are biased to low-shear viscosity, and thixotropy is presented, so that coating can show after roller coating film forming
Certain decorative pattern, so that water-in-water multicolor coating more has artistic feeling, visual effect more has relative to common water-in-water multicolor coating
New meaning.
In a preferred embodiment of the invention, non-association type alkali swollen thickener is selected from Rhom and Hass's model
The product of ASE-60, the product of BASF AG trade mark HV-30, the production that Gao Tai auxiliary agent Co., Ltd's trade mark is Viscoatex730
Product.
It is typical but non-limiting, in continuous phase, the content for example 0.5wt% of non-association type alkali swollen thickener,
0.6wt%, 0.7wt%, 0.8wt%, 0.9wt%, 1wt%, 1.1wt%, 1.2wt%, 1.3wt%, 1.4wt% or
1.5wt%.
White sand that water-in-water multicolor coating continuous phase provided by the invention is matched by extra fine quality, non-association type alkali soluble is swollen
Thickener and aqueous acrylic emulsion mutually cooperate with, so that will not be adhered and settle between continuous phase and color grain, water-water
Multicolor finish forms thixotropic system, so that water-in-water multicolor coating construction is more smooth, by batch scraping or roller coating
Color grain is evenly distributed in continuous phase, obtains the uniform and stable paint film being dispersed in continuous phase of color grain.
In the preferred embodiment of the present invention, continuous phase further includes continuous phase auxiliary agent 1.5-5.5wt%, i.e., white
The sum of sand, aqueous acrylic emulsion, non-association type alkali swollen thickener, water and continuous phase auxiliary agent are 100wt%.By continuous
Continuous phase auxiliary agent is added in phase to improve the performance of continuous phase.
In present invention further optimization embodiment, continuous phase auxiliary agent includes hydroxyethyl ether cellulose, defoaming agent, pH
One or more of regulator, film forming agent, antifreezing agent and sterilization antiseptic.
It include hydroxyethyl ether cellulose 0.1- in continuous phase in still more preferably embodiment of the invention
0.3wt%, pH adjusting agent 0.1-0.2wt%, defoaming agent 0.1-0.5wt%, film forming agent 0.5-1wt%, antifreezing agent 1-5wt% and
Sterilization antiseptic 0.1-0.5wt%, the sum of above-mentioned various auxiliary agents are 1.5-5.5wt%.
In a kind of preferred embodiment of the invention, water-in-water multicolor coating continuous phase, hydroxyethyl ether cellulose contains
Amount is 0.1-0.3wt%.By the way that hydroxy ethyl fiber ether is added in continuous phase, certain viscosity side can either be provided for continuous phase
Just it constructs, and moisture-keeping function can be played, prevent coating skinning, increase the shelf-life of coating.
It is typical but non-limiting, content of the hydroxyethyl ether cellulose in water-in-water multicolor coating for example 0.1wt%,
0.15wt%, 0.2wt%, 0.25wt% or 0.3wt%.Selected from Chemical Co., Ltd., sub- Silan, board in hydroxyethyl ether cellulose
Number be 250HBR or 250MHBR product;Or it is selected from Shin-Etsu Chemial Co., Ltd, the trade mark is the production of HS-30000-PY2
Product;Or it is selected from Akzo Nobel's coating Co., Ltd, the trade mark is the product of EBS-451FQ.
In the continuous phase of water-in-water multicolor coating provided by the invention, pH adjusting agent is selected from more function of Dow Chemical
It can auxiliary agent A MP-95;Defoaming agent is selected from the SN-154 of San Nopco K.K.;Film forming agent is selected from Eastman Chemical Co., Ltd.
Texanol, antifreezing agent be commercially available ethylene glycol, sterilization antiseptic be De Lan Chemical Co., Ltd. GT-50.
Typical but non-limiting, in water-in-water multicolor coating, the typical but non-limiting content of pH adjusting agent is for example
0.1wt%, 0.11wt%, 0.12wt%, 0.13wt%, 0.14wt%, 0.15wt%, 0.16wt%, 0.17wt%,
0.18wt%, 0.19wt% or 0.2wt%;Typical but non-limiting content for example 0.1wt%, 0.15wt% of defoaming agent,
0.2wt%, 0.25wt%, 0.3wt%, 0.35wt%, 0.4wt%, 0.45wt% or 0.5wt%;Film forming agent it is typical but non-
Restrictive content for example 0.5wt%, 0.55wt%, 0.6wt%, 0.65wt%, 0.7wt%, 0.75wt%, 0.8wt%,
0.85wt%, 0.9wt%, 0.95wt% or 1wt%;The typical but non-limiting content for example 1wt% of antifreezing agent,
1.5wt%, 2wt%, 2.5wt%, 3wt%, 3.5wt%, 4wt%, 4.5wt% or 5wt%;Sterilization antiseptic it is typical but non-
Restrictive content for example 0.1wt%, 0.15wt%, 0.2wt%, 0.25wt%, 0.3wt%, 0.35wt%, 0.4wt%,
0.45wt% or 0.5wt%.
In the preferred embodiment of the present invention, the partial size of color grain is 0.1-1.2cm.By the way that the partial size of color grain is set
It is set to 0.1-1.2cm, in favor of color grain uniform and stable dispersion in continuous phase.Typical but non-limiting, the partial size of color grain is such as
For 0.1,0.2,0.3,0.4,0.5,0.6,0.7,0.8,0.9,1,1.1 or 1.2cm.
In the preferred embodiment of the present invention, the raw material of color grain includes base paint and the first protection sol solution, institute
Stating base paint includes that acrylic emulsion 25-30wt% containing associative groups, the second protection sol solution 8-10wt%, high molecular weight are dredged
Water modified hydroxyethylcellulosadsorbing ether 1-1.5wt% and water 50-60wt%.
In a preferred embodiment of the invention, protection is provided to base paint by the first protection sol solution, effectively to mention
The intensity and colour stability of high color grain.
In a preferred embodiment of the invention, high molecular weight hydrophobically modified hydroxyethyl cellulose ether is in 25 DEG C of environment,
The high molecular weight hydrophobically modified hydroxyethyl cellulose ether solution viscosity of 1wt% is 9000-16000cps.It is typical but non-limiting
, the viscosity of the high molecular weight hydrophobically modified hydroxyethyl cellulose ether aqueous solution of 1wt% for example 9000,10000,11000,
1200,13000,14000,15000 or 16000cps.
In a preferred embodiment of the invention, high molecular weight hydrophobically modified hydroxyethyl cellulose ether is Ya Shilan company,
The product of model HE-10K.
In a preferred embodiment of the invention, on the one hand, base paint passes through high molecular weight hydrophobically modified hydroxyethyl fiber
With the acrylic emulsion containing associative groups better association occurs for plain ether, forms space network, provides for color grain
Good intensity makes the water-in-water multicolor coating being prepared in roller coating or color grain is not destroyed by construction tool and dyed when batch scraping,
Guarantee the integrality of color grain after constructing.On the other hand, high molecular weight hydrophobically modified hydroxyethyl fiber ether due to molecular weight it is big,
Better crosslinked action can occur with the protective glue in base paint, the structure of formation is similar to " card room structure ", makes color grain more
Add secured and stablize, the component inside color grain is not easy to ooze out, while the component outside color grain is also not easily penetrated into, to ensure that water
The viscosity stability in packet water multicolor finish later period, while good cohesive force also is provided for color grain, it is provided centainly for color grain
Toughness, further ensure construction after colorful grain integrality.In addition, due to using high molecular weight hydrophobic in base paint
Modified cellulose ethers are avoided and are absorbed water because of color grain to the first protection sol solution and continuous phase so that the hydrophobic performance of color grain is more preferably
The case where causing viscosity to rise, to effectively increase the viscosity stability of water-in-water multicolor coating, while high molecular weight is hydrophobic
Modified hydroxyethylcellulosadsorbing can also form physical crosslinking between the second protective glue, enable color grain resistance to bleed more preferably.
In a preferred embodiment of the invention, the acrylic emulsion containing associative groups is not protected with second in base paint
Sol solution reacts, so that the color grain for effectively avoiding color grain from occurring in the water-in-water multicolor coating storage later period is swollen to be adhered etc. and be asked
Topic.
In a preferred embodiment of the invention, the acrylic emulsion containing associative groups is rich selected from but not limited to Changshu Ahmedabad
The RS-2788 of Science and Technology Ltd. need to contain carboxyl-content in the acrylic acid of associative groups very when choosing the product of other companies
It is few, it reacts to avoid it with the second protection sol solution.
It is typical but non-limiting, the content of the acrylic emulsion in base paint containing associative groups for example 25wt%,
26wt%, 27wt%, 28wt%, 29wt% or 30wt%;Content for example 8.2wt%, 8.5wt% of second protection sol solution,
8.8wt%, 9wt%, 9.2wt%, 9.5wt%, 9.8wt% or 10wt%;High molecular weight hydrophobically modified hydroxyethyl cellulose ether
Content for example 1wt%, 1.1wt%, 1.2wt%, 1.3wt%, 1.4wt% or 1.5wt%;The content of water for example 50wt%,
52wt%, 54wt%, 55wt%, 56wt%, 58wt% or 60wt%.
It in the preferred embodiment of the present invention, further include mill base 0.01-5wt% in base paint.By on basis
Middle addition mill base, is made required color for color grain.Typical but non-limiting, in base paint, the content of mill base is for example
0.01wt%, 0.02wt%, 0.05wt%, 0.1wt%, 0.2wt%, 0.5wt%, 0.8wt%, 1wt%, 1.2wt%,
1.5wt%, 1.8wt%, 2wt%, 3wt%, 4wt% or 5wt%.
In the preferred embodiment of the present invention, the mass ratio of base paint and the first protection sol solution is (1-6):
(1-3).By the mass ratio of control base paint and the first protection sol solution, so that manufactured color grain has good intensity
With impervious color and anti-performance of swelling.It is typical but non-limiting, the mass ratio for example 2:1 of base paint and the first protection sol solution,
1:1,3:1,7:3,8:3,10:3,1:2,2:3,4:1,5:1,6:1.
In the preferred embodiment of the present invention, the solute of the first protection sol solution and the second protection sol solution is
Lithium metasilicate magnalium soap.Select lithium metasilicate magnesium lithium soap as the solute of the first protection sol solution and the second protection sol solution, to guarantee
Color grain has good intensity and impervious color and prevents swollen performance.
In present invention further optimization embodiment, the lithium metasilicate magnalium soap is by water-soluble organic pyrophosphate salt
Organic matter processing.
Lithium metasilicate magnalium soap of the present invention by water-soluble organic pyrophosphate salt organic matter processing is complete
The product of gram chemical company model S-482.
In the preferred embodiment of the present invention, the concentration of the first protection sol solution is 3-7wt%.Pass through control the
The concentration of one protection sol solution is 3-7wt%, occurs phenomenon of swelling during storage to avoid color grain.It is typical but non-limiting
, first protection concentration for example 3wt%, 3.5wt% of sol solution, 4wt%, 4.5wt%, 5wt%, 5.5wt%, 5.8wt%,
6wt%, 6.2wt%, 6.5wt%, 6.8wt% or 7wt%.
In the preferred embodiment of the present invention, the concentration of the second protection sol solution is 5-10wt%.Pass through control
The concentration of second protection sol solution is 5-10wt%, so that it is uniformly mixed with other components in base paint, and improves coloured silk
The intensity of grain and prevents swollen performance at resistance to bleed energy.It is typical but non-limiting, the concentration for example 5wt% of the second protection sol solution,
5.5wt%, 6wt%, 6.5wt%, 7wt%, 7.5wt%, 8wt%, 8.5wt%, 9wt%, 9.5wt% or 10wt%.
In the preferred embodiment of the present invention, base paint further includes base paint auxiliary agent 2.5-5wt%, i.e., containing association
The acrylic emulsion of group, high molecular weight hydrophobically modified hydroxyethyl cellulose ether, the second protection sol solution and base paint auxiliary agent it
With for 100wt%.By base paint auxiliary agent being added in base paint phase to improve the performance of color grain.
In the preferred embodiment of the present invention, base paint auxiliary agent includes filler, pH adjusting agent, defoaming agent, film forming
One or more of agent, antifreezing agent and sterilization antiseptic.
In the base paint auxiliary agent of water-in-water multicolor coating provided by the invention, pH adjusting agent is selected from Dow Chemical
Multifunctional assistant AMP-95;Defoaming agent is selected from the SN-154 of San Nopco K.K.;Film forming agent is selected from antifreezing agent and is selected from her scholar
The Texanol of graceful Chemical Co., Ltd., antifreezing agent are commercially available ethylene glycol, and sterilization antiseptic is the GT- of De Lan Chemical Co., Ltd.
50。
In present invention further optimization embodiment, base paint auxiliary agent includes filler 0.5-1wt%, defoaming agent 0.1-
0.5wt%, pH adjusting agent 0.1-0.2wt%, film forming agent 1-2wt%, antifreezing agent 0.5-1.5wt% and sterilization antiseptic 0.1-
0.5wt%, the 2.5-5wt% of Qi Hanliang based on the sum of above-mentioned various basic agent aids.
Typical but non-limiting, in base paint auxiliary agent, filler is titanium dioxide, the content of titanium dioxide for example 0.5,0.6,
0.7wt%, 0.8wt%, 0.9wt% or 1wt%;The content of defoaming agent for example 0.1wt%, 0.2wt%, 0.3wt%,
0.4wt% or 0.5wt%;The content of pH adjusting agent for example 0.1wt%, 0.11wt%, 0.12wt%, 0.13wt%,
0.14wt%, 0.15wt%, 0.16wt%, 0.17wt%, 0.18wt%, 0.19wt% or 0.2wt%;The content of film forming agent is such as
For 1wt%, 1.1wt%, 1.2wt%, 1.3wt%, 1.4wt%, 1.5wt%, 1.6wt%, 1.7wt%, 1.8wt%,
1.9wt% or 2wt%;The content of sterilization antiseptic for example 0.1wt%, 0.15wt%, 0.2wt%, 0.25wt%, 0.3wt%,
0.35wt%, 0.4wt%, 0.45wt% or 0.5wt%.
In the preferred embodiment of the present invention, the preparation method of color grain includes the following steps: base paint and appoints
After the mill base of choosing mixes, it is added in the first protection sol solution and is uniformly mixed, obtain color grain.Wherein specific granulation mode passes through granulation
The equipment such as machine, dispersion impeller carry out.The size and shape of color grain can be adjusted by the way that Granulation Equipments parameter is arranged.
In present invention further optimization embodiment, the preparation method of base paint includes the following steps: macromolecule
Measure hydrophobically modified hydroxyethyl cellulose ether, the acrylic emulsion containing associative groups, the second protection sol solution, water and optional basis
It paints auxiliary agent to be uniformly mixed, obtains base paint.
Typical but non-limiting, the preparation of base paint carries out in accordance with the following steps:
(1) it first adds water in container, the hydrophobically modified hydroxyethyl cellulose ether of high molecular weight is then added, part defoams
Agent, titanium dioxide stir 5-10min with the revolving speed of 500-800r/min;
(2) pH adjusting agent is added, continues to stir 10-15min with the revolving speed of 800-1200r/min;
(3) film forming agent, antifreezing agent, the acrylic emulsion containing associative groups, surplus defoaming agent, the second protection sol solution is added
And base paint is made with the revolving speed high-speed stirred 30min of 1200-1600r/min in sterilization antiseptic.
According to the second aspect of the invention, the present invention provides the preparation methods of above-mentioned water-in-water multicolor coating, including
Following steps: color grain and continuous phase are uniformly mixed, and obtain water-in-water multicolor coating.
The preparation method simple process of water-in-water multicolor coating provided by the invention, it is easy to operate, life can be effectively improved
Efficiency is produced, production cost is reduced.
In the preferred embodiment of the present invention, the preparation method of continuous phase includes the following steps:
By aqueous acrylic emulsion, white sand, hydroxyethyl ether cellulose, non-association type alkali swollen thickener, water and optional
Continuous phase auxiliary agent is uniformly mixed, and obtains continuous phase.
Typical but non-limiting, the preparation method of continuous phase includes the following steps:
(1) it adds water in container, is slowly added to hydroxyethyl ether cellulose, part defoaming agent and sterilization antiseptic, with
The revolving speed of 800-1200r/min stirs 5-10min;
(2) pH adjusting agent is added, continues to stir 10-15min with the revolving speed of 800-1200r/min;
(3) white sand, antifreezing agent, film forming agent, aqueous acrylic emulsion, surplus defoaming agent, the non-swollen increasing of association type alkali soluble is added
Thick dose, with the revolving speed high-speed stirred 30min of 1200-1600r/min, obtain continuous phase.
According to the third aspect of the present invention, the present invention provides above-mentioned water-in-water multicolor coatings in interior wall or decoration of exterior wall
In application.
Water-in-water multicolor coating provided by the invention can construct roller coating or by way of batch scraping, and operate simpler
It is single, it constructs more smooth, can be applied not only to decoration of exterior wall, and inner wall decoration can be suitable for, be significantly expanded water-water
The scope of application of multicolor finish, has broad application prospects.
Technical solution provided by the invention is further described below with reference to embodiment and comparative example.
Embodiment 1
Present embodiments provide a kind of water-in-water multicolor coating comprising partial size 0.5cm color grain 7.5wt% and continuous phase
92.5wt%;Wherein continuous phase includes 80-120 mesh snowflake white sand 30wt%, aqueous acrylic emulsion 50wt%, non-association type alkali
Swollen thickener 1wt%, hydroxyethyl ether cellulose 0.2wt%, defoaming agent 0.3wt%, pH adjusting agent 0.1wt%, antifreezing agent
2.5wt%, film forming agent 0.6wt%, sterilization antiseptic 0.3wt% and water 15wt%;The raw material of color grain includes base paint and first
Sol solution is protected, it is 3:1 that base paint and first, which protect the mass ratio of sol solution, and base paint includes acrylic emulsion containing associative groups
28wt%, high molecular weight hydrophobically modified hydroxyethyl cellulose ether 1.2wt%, the second protection sol solution 9wt%, titanium dioxide
0.8wt%, defoaming agent 0.3wt%, pH adjusting agent 0.1wt%, film forming agent 1.5wt%, antifreezing agent 1wt% and sterilization antiseptic
0.3wt% and water 57.8wt%;The solute of first protection sol solution and the second protection sol solution is water-soluble organic pyrophosphoric acid
The lithium metasilicate magnalium soap of ester salt organic matter processing;The concentration of first protection sol solution is 5wt%, the concentration of the second protection sol solution
For 7wt%.
In the present embodiment, aqueous acrylic emulsion is carboxylic aqueous acrylic emulsion, is purchased in Changshu Ahmedabad richness
Science and Technology Ltd., model RS-6733;High molecular weight hydrophobically modified hydroxyethyl cellulose ether is company, sub- Silan, model
The product of HE-10K;Acrylic emulsion containing associative groups is selected from the RS-2788 product of Changshu Ahmedabad richness Science and Technology Ltd.;It is non-
Association type alkali swollen thickener is selected from the product of Rhom and Hass's model ASE-60;PH adjusting agent is selected from Dow Chemical
Multifunctional assistant AMP-95;Defoaming agent is selected from the SN-154 of San Nopco K.K.;Film forming agent has selected from Eastman Chemical
The Texanol of limit company, antifreezing agent are commercially available ethylene glycol, and sterilization antiseptic is the GT-50 of De Lan Chemical Co., Ltd..
In the present embodiment, the preparation method of color grain includes the following steps:
(1) it first adds water in container, the hydrophobically modified hydroxyethyl cellulose ether of high molecular weight is then added, part defoams
Agent, titanium dioxide stir 5-10min with the revolving speed of 500-800r/min;
(2) pH adjusting agent is added, continues to stir 10-15min with the revolving speed of 800-1200r/min;
(3) film forming agent, antifreezing agent, the acrylic emulsion containing associative groups, surplus defoaming agent, the second protection sol solution is added
And base paint is made with the revolving speed high-speed stirred 30min of 1200-1600r/min in sterilization antiseptic;
(4) base paint is added in the first protection sol solution and is uniformly mixed, obtain color grain.
Embodiment 2
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 30wt% that partial size is 0.1cm and continuous
Phase 70wt%;Wherein for color grain with color grain in embodiment 1, continuous phase includes 80-120 mesh snowflake white sand 50wt%, water soluble acrylic acid
Lotion 30wt%, non-association type alkali swollen thickener 1wt%, hydroxyethyl ether cellulose 0.2wt%, defoaming agent 0.3wt%, pH tune
Save agent 0.1wt%, antifreezing agent 2.5wt%, film forming agent 0.6wt%, sterilization antiseptic 0.3wt% and water 15wt%.The present embodiment
In it is raw materials used with raw material in embodiment 1 be with the same batch of producer, details are not described herein.
Embodiment 3
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 10wt% that partial size is 1.2cm and continuous
Phase 90wt%;Wherein for color grain with color grain in embodiment 1, continuous phase includes 80-120 mesh snowflake white sand 45wt%, water soluble acrylic acid
Lotion 35wt%, non-association type alkali swollen thickener 1wt%, hydroxyethyl ether cellulose 0.2wt%, defoaming agent 0.3wt%, pH tune
Save agent 0.1wt%, antifreezing agent 2.5wt%, film forming agent 0.6wt%, sterilization antiseptic 0.3wt% and water 15wt%.The present embodiment
In it is raw materials used with raw material in embodiment 1 be with the same batch of producer, details are not described herein.
Embodiment 4
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 15wt% and continuous phase 85wt%;Wherein
For color grain with color grain in embodiment 1, continuous phase includes 80-120 mesh snowflake white sand 42wt%, aqueous acrylic emulsion 38wt%, non-
Association type alkali swollen thickener 1wt%, hydroxyethyl ether cellulose 0.2wt%, defoaming agent 0.3wt%, pH adjusting agent 0.1wt%,
Antifreezing agent 2.5wt%, film forming agent 0.6wt%, sterilization antiseptic 0.3wt% and water 15wt%.It is raw materials used equal in the present embodiment
It is with the same batch of producer with raw material in embodiment 1, details are not described herein.
Embodiment 5
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 25wt% and continuous phase 75wt%;Wherein
For color grain with color grain in embodiment 1, continuous phase includes 80-120 mesh snowflake white sand 38wt%, aqueous acrylic emulsion 42wt%, non-
Association type alkali swollen thickener 1wt%, hydroxyethyl ether cellulose 0.2wt%, defoaming agent 0.3wt%, pH adjusting agent 0.1wt%,
Antifreezing agent 2.5wt%, film forming agent 0.6wt%, sterilization antiseptic 0.3wt% and water 15wt%.It is raw materials used equal in the present embodiment
It is with the same batch of producer with raw material in embodiment 1, details are not described herein.
Embodiment 6
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 25wt% and continuous phase 75wt%;Wherein
For color grain with color grain in embodiment 1, continuous phase includes 80-120 mesh snowflake white sand 40wt%, aqueous acrylic emulsion 40wt%, non-
Association type alkali swollen thickener 1wt%, hydroxyethyl ether cellulose 0.2wt%, defoaming agent 0.3wt%, pH adjusting agent 0.1wt%,
Antifreezing agent 2.5wt%, film forming agent 0.6wt%, sterilization antiseptic 0.3wt% and water 15wt%.It is raw materials used equal in the present embodiment
It is with the same batch of producer with raw material in embodiment 1, details are not described herein.
Embodiment 7
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 15wt% and continuous phase 85wt%;Wherein
For color grain with color grain in embodiment 1, continuous phase includes 80-120 mesh snowflake white sand 40wt%, aqueous acrylic emulsion 40wt%, non-
Association type alkali swollen thickener 1wt%, hydroxyethyl ether cellulose 0.2wt%, defoaming agent 0.3wt%, pH adjusting agent 0.1wt%,
Antifreezing agent 2.5wt%, film forming agent 0.6wt%, sterilization antiseptic 0.3wt% and water 15wt%.It is raw materials used equal in the present embodiment
It is with the same batch of producer with raw material in embodiment 1, details are not described herein.
Embodiment 8
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 15wt% and continuous phase 85wt%;Wherein
Continuous phase in consecutive identical embodiment 7, color grain include base paint and the first protection sol solution, and base paint and first protects sol solution
Mass ratio be 2:1, base paint and first protection sol solution it is in the same manner as in Example 1, details are not described herein.
Embodiment 9
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 15wt% and continuous phase 85wt%;Wherein
Continuous phase in consecutive identical embodiment 7, color grain include base paint and the first protection sol solution, and base paint and first protects sol solution
Mass ratio be 1:3, base paint and first protection sol solution it is in the same manner as in Example 1, details are not described herein.
Embodiment 10
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 15wt% and continuous phase 85wt%;Wherein
Continuous phase in consecutive identical embodiment 7, color grain include base paint and the first protection sol solution, and base paint and first protects sol solution
Mass ratio be 6:1, base paint and first protection sol solution it is in the same manner as in Example 1, details are not described herein.
Embodiment 11
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 15wt% and continuous phase 85wt%;Wherein
Continuous phase in consecutive identical embodiment 7, color grain include base paint and the first protection sol solution, and base paint and first protects sol solution
Mass ratio be 1:5, base paint and first protection sol solution it is in the same manner as in Example 1, details are not described herein.
Embodiment 12
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 15wt% and continuous phase 85wt%;Wherein
Continuous phase in consecutive identical embodiment 7, color grain include base paint and the first protection sol solution, and base paint and first protects sol solution
Mass ratio be 12:1, base paint and first protection sol solution it is in the same manner as in Example 1, details are not described herein.
Embodiment 13
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 15wt% and continuous phase 85wt%;Wherein
Continuous phase in consecutive identical embodiment 7, color grain include base paint and the first protection sol solution, and base paint and first protects sol solution
Mass ratio be 3:1, the base paint that base paint and embodiment 1 provide the difference is that, using aqueous acrylic emulsion generation
For the acrylic emulsion containing associative groups, which is same with batch with the aqueous acrylic emulsion in continuous phase
Model, details are not described herein.
Embodiment 14
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 15wt% and continuous phase 85wt%;Wherein
Continuous phase in consecutive identical embodiment 7, color grain include base paint and the first protection sol solution, and base paint and first protects sol solution
Mass ratio be 3:1, the base paint that base paint and embodiment 1 provide the difference is that, using hydroxyethyl ether cellulose generation
For high molecular weight hydrophobically modified hydroxyethyl cellulose ether, which is same with hydroxyethyl ether cellulose in continuous phase
The same model of batch, details are not described herein.
Embodiment 15
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 15wt% and continuous phase 85wt%;Wherein
Continuous phase in consecutive identical embodiment 7, color grain include base paint and the first protection sol solution, and base paint and first protects sol solution
Mass ratio be 3:1, the base paint that base paint and embodiment 1 provide the difference is that, second is free of in the base paint
Sol solution is protected, and the content of the acrylic emulsion containing associative groups is 33wt%, the content 61.8wt% of water, other components and is contained
Amount is with embodiment 1, and details are not described herein.
Embodiment 16
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 15wt% and continuous phase 85wt%;Wherein
Continuous phase in consecutive identical embodiment 7, color grain include base paint and the first protection sol solution, and base paint and first protects sol solution
Mass ratio be 3:1, the base paint that base paint and embodiment 1 provide the difference is that, in the base paint, the base containing association
Content 60wt%, the water content 25.8wt% of group's acrylic emulsion, other components and content are same
Embodiment 1, details are not described herein.
Embodiment 17
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 15wt% and continuous phase 85wt%;Wherein
Color grain is with color grain in embodiment 7, the difference of continuous phase and embodiment 7, and the partial size of white sand is 20-40 mesh, other components and
Content is with embodiment 7, and details are not described herein.
Embodiment 18
Present embodiments provide a kind of water-in-water multicolor coating comprising color grain 15wt% and continuous phase 85wt%;Wherein
Color grain is that the partial size of white sand is 140-180 mesh, other components with color grain in embodiment 7, the difference of continuous phase and embodiment 7
And content, with embodiment 7, details are not described herein.
Embodiment 19
The preparation method for present embodiments providing a kind of water-in-water multicolor coating, includes the following steps:
(1) it adds water in container, is slowly added to hydroxyethyl ether cellulose, part defoaming agent and sterilization antiseptic, with
The revolving speed of 800-1200r/min stirs 5-10min;
(2) pH adjusting agent is added, continues to stir 10-15min with the revolving speed of 800-1200r/min;
(3) snowflake white sand, antifreezing agent, film forming agent, aqueous acrylic emulsion, surplus defoaming agent, non-association type alkali soluble is added
Swollen thickener obtains continuous phase with the revolving speed high-speed stirred 10-15min of 1200-1600r/min.
(4) color grain is added in continuous phase, is stirred evenly to get water-in-water multicolor coating is arrived.
Comparative example 1
This comparative example provides a kind of water-in-water multicolor coating, this comparative example and embodiment 3 the difference is that, color grain
Content be 5wt%, the content of continuous phase is 95wt%.
Comparative example 2
This comparative example provides a kind of water-in-water multicolor coating, this comparative example and embodiment 3 the difference is that, color grain
Content be 50wt%, the content of continuous phase is 50wt%
Comparative example 3
This comparative example provides a kind of water-in-water multicolor coating, this comparative example and embodiment 3 the difference is that, continuously
Non- association type alkali swollen thickener is not added in phase, and the content of water is 16wt%.
Comparative example 4
This comparative example provides a kind of water-in-water multicolor coating, this comparative example and embodiment 3 the difference is that, continuously
Hydroxyethyl ether cellulose is not added in phase, and the content of water is 15.2wt%.
Comparative example 5
This comparative example provides a kind of water-in-water multicolor coating, this comparative example and embodiment 3 the difference is that, continuously
Mutually include 80-120 mesh snowflake white sand 10wt%, aqueous acrylic emulsion 60wt%, non-association type alkali swollen thickener 1wt%,
Hydroxyethyl ether cellulose 0.2wt%, defoaming agent 0.3wt%, pH adjusting agent 0.1wt%, antifreezing agent 2.5wt%, film forming agent
0.6wt%, sterilization antiseptic 0.3wt% and water 25wt%.Raw material is same in raw materials used equal and embodiment 1 in this comparative example
The same batch of producer, details are not described herein.
Comparative example 6
This comparative example provides a kind of water-in-water multicolor coating, this comparative example and embodiment 3 the difference is that, continuously
Mutually include 80-120 mesh snowflake white sand 20wt%, aqueous acrylic emulsion 50wt%, non-association type alkali swollen thickener 1wt%,
Hydroxyethyl ether cellulose 0.2wt%, defoaming agent 0.3wt%, pH adjusting agent 0.1wt%, antifreezing agent 2.5wt%, film forming agent
0.6wt%, sterilization antiseptic 0.3wt% and water 25wt%.Raw material is same in raw materials used equal and embodiment 1 in this comparative example
The same batch of producer, details are not described herein.
The preparation method is the same as that of Example 13 for the water-in-water multicolor coating that above-mentioned comparative example 1-6 is provided, and details are not described herein.
Embodiment 1-18 and comparative example the 1-6 water-in-water multicolor coating provided are tested for the property, as a result such as 1 institute of table
Show:
Wherein, 1. color grain intensity ratings are 1-5 points, specific standards of grading are as follows: 5 points of expression color grain intensity are fine, normally apply
Working hour will not be destroyed, and 4 points of expression color grain intensity are preferable, and color grain has minimal amount to be destroyed and becomes smaller when normal construction, but basic
Do not influence form and aspect, 3 points of expression color grain intensity are general, when normal construction color grain have it is a certain amount of be destroyed, color grain becomes smaller more serious, table
Now small for template overall color point, 2 points of expression color grain intensity are poor, and color grain is largely destroyed when normal construction, and color grain becomes smaller seriously,
Color grain part colours mix, and show as that template form and aspect are uneven, and 1 point of expression intensity is very poor.2. colorful water-water coating lacquer
The test method of the roughness of film is to take a small amount of water-in-water multicolor coating, and the water of equivalent is added, abundant using oscillator after tinning
It after shaking 3-5min, is filtered using the sieve of different meshes, record can just be by the mixture mistake of all paint samples and water
Complete sieve is filtered, and tests and the mixture of all paint samples and water can just be filtered complete sieve particle size, will be surveyed
Try sieve particle size is denoted as the roughness of hygrometric state paint sample.
3. the sand sense of paint film is characterized with coefficient of friction, the test method of paint film sand sense are as follows: take the water-water of equivalent more
Color coating material is carried out criticizing on the smooth no asbestos fibre cement plate of same area and be scraped, and after paint film is dry, is surveyed using coefficient of friction
Determine instrument measurement dynamic friction coefficient μ value, μ value is bigger, and it is better to represent sand sense.4. viscosity: being measured using stormer viscosity meter;
5. thixotroping value use rotary viscosity design determining, test method are as follows: will paint sample No. 6 rotor (6#) revolving speeds be 6rmp and
Viscosity number when 60rmp, then measure viscosity number ratio 6#60rmp with 6#6rmp and measure viscosity number to get to thixotroping value.
6. the color grain form of color grain after roller application: being divided into 1-5 points: 5 points representatives according to the integrated degree of color spot after construction
Color grain is complete after construction;Color grain minimal amount destroys after 4 points of representative constructions, does not influence form and aspect;Color grain is a certain amount of after 3 points of representative constructions
It destroys, color grain becomes smaller seriously, and it is small to show as template overall color point;Color grain is largely destroyed after 2 points of representative constructions, and color grain becomes smaller sternly
Weight, color grain part colours mix, and it is uneven to show as template form and aspect;Color grain is all destroyed after 1 point of representative construction,
Color grain mixes, and loses original form and aspect completely.
7. the uniform distribution of forces of color grain after roller application: the degree of being evenly distributed of color grain is commented after according to construction
Point, it is divided into 1-4 points, 4 points represent color grain and are evenly distributed, and form and aspect uniformly achieve the effect that imitate stone material;3 points represent color grain distribution compared with
Uniformly, the place for having a small amount of color grain on the low side, but whole form and aspect are not influenced;2 points represent color grain and are distributed more uneven, whole top
Divide local color spot more, part color spot is less, influences form and aspect;1 point represents that color grain distribution is very uneven, and color dot is with applying on the whole
Work tool is dragged away, and color spot is caused to be accumulated.
1 water-water coating property tables of data of table
Note: in upper table --- it is poor to represent effect of decorative patterns, is unable to reach water-water coating imitation stone effect.
As it can be seen from table 1 the comparison of embodiment 1-18 and comparative example 2-6 can be seen that embodiment 1-18 by specific
The color grain of quality proportioning is mutually cooperateed with white sand, aqueous acrylic emulsion and non-association type alkali swollen thickener, obtained water packet
The thixotroping value of water paint is above 5.5, is more likely to thixotropic system, can construct using roller coating or by the way of batch scraping.
The water-in-water multicolor coating that comparative example 1 provides, can not since its color grain content is too low although also forming thixotropic system
Reach the effect of decorative patterns of imitation stone.
It can be seen that from the comparison of embodiment 1-10 and embodiment 11-12 when preparing color grain, base paint and the first protection
The mass ratio of glue is (1-6): when (1-3), the intensity of the color grain being prepared is high, more preferably with the synergistic effect of continuous phase, makes
It obtains and keeps complete when being more conducive to construct while the colorful painting coating of water-water forms high thixotroping value thixotropic system.
It can be seen that from the comparison of embodiment 1-10 and embodiment 13 by using the acrylic emulsion containing associative groups and be
The raw material of base paint can effectively improve the intensity of color grain, more conducively keep complete in the construction process.
It can be seen that from the comparison of embodiment 1-10 and embodiment 14 fine by using high molecular weight hydrophobically modified hydroxyethyl
It ties up plain ether and replaces the raw material painted based on hydroxyethyl ether cellulose, the intensity for the color grain being prepared is higher, is more conducively applying
It is kept during work complete.
From the comparison of embodiment 1-10 and embodiment 15-16 as can be seen that base paint passes through the acrylic acid containing associative groups
Lotion 25-30wt%, the second protection sol solution 8-10wt%, high molecular weight hydrophobically modified hydroxyethyl cellulose ether 1-1.5wt%
It is mutually cooperateed with water 50-60wt%, the performance for the color grain being prepared is more excellent, and more complete after construction, dispersion is more evenly.
From the comparison of embodiment 1-10 and embodiment 17-18 as can be seen that the partial size of the white sand used in the continuous phase for
When 80-120 mesh, more evenly, decorative pattern imitation stone effect is more for color grain distribution in the paint film for the water-in-water multicolor coating being prepared
It is true to nature.
Finally, it should be noted that the above embodiments are only used to illustrate the technical solution of the present invention., rather than its limitations;To the greatest extent
Pipe present invention has been described in detail with reference to the aforementioned embodiments, those skilled in the art should understand that: its according to
So be possible to modify the technical solutions described in the foregoing embodiments, or to some or all of the technical features into
Row equivalent replacement;And these are modified or replaceed, various embodiments of the present invention technology that it does not separate the essence of the corresponding technical solution
The range of scheme.
Claims (10)
1. a kind of water-in-water multicolor coating, which is characterized in that including following component: color grain 7.5-30wt% and continuous phase 70-
92.5wt%;Wherein, the continuous phase includes the following raw material: white sand 30-50wt%, aqueous acrylic emulsion 30-50wt%, non-
Association type alkali swollen thickener 0.5-1.5wt% and water 10-25wt%;
Preferably, the water-in-water multicolor coating includes color grain 10-25wt% and continuous phase 75-90wt%;
Preferably, the water-in-water multicolor coating includes color grain 15-25wt% and continuous phase 75-85wt%;
Preferably, in the continuous phase, white sand 35-45wt%, aqueous acrylic emulsion 35-45wt%, non-association type alkali
Swollen thickener is 0.5-1.5wt% and water 10-25wt%;
Preferably, in the continuous phase, white sand 38-42wt%, aqueous acrylic emulsion 38-42wt%, non-association type alkali
Swollen thickener is 0.5-1.5wt% and water 10-25wt%.
2. water-in-water multicolor coating according to claim 1, which is characterized in that the continuous phase further includes continuously aiding
Agent, content of the continuous phase auxiliary agent in the continuous phase are 1.5-5.5wt%;Preferably, continuous phase auxiliary agent includes hydroxyl second
At least one of base cellulose ether, defoaming agent, pH adjusting agent, film forming agent, antifreezing agent and sterilization antiseptic, preferably ethoxy
Cellulose ether, defoaming agent, pH adjusting agent, film forming agent, antifreezing agent and sterilization antiseptic mixture;
Preferably, the continuous phase auxiliary agent includes hydroxyethyl ether cellulose 0.1-0.3wt%, pH adjusting agent 0.1-0.2wt%, disappears
Infusion 0.1-0.5wt%, film forming agent 0.5-1wt%, antifreezing agent 1-5wt% and sterilization antiseptic 0.1-0.5wt%.
3. water-in-water multicolor coating according to claim 1, which is characterized in that the partial size of the color grain is 0.1-1.2cm;
And/or the partial size of the white sand is 80-120 mesh.
4. water-in-water multicolor coating according to claim 1-3, which is characterized in that the raw material of the color grain includes
Base paint and the first protection sol solution, the base paint include acrylic emulsion 25-30wt% containing associative groups, the second protection
Sol solution 8-10wt%, high molecular weight hydrophobically modified hydroxyethyl cellulose ether 1-1.5wt% and water 50-60wt%.
5. water-in-water multicolor coating according to claim 4, which is characterized in that the base paint and first protective glue
The mass ratio of solution is (1-6): (1-3).
6. water-in-water multicolor coating according to claim 4, which is characterized in that the first protection sol solution and second is protected
The solute for protecting sol solution is lithium metasilicate magnalium soap;
Preferably, in the first protection sol solution, the concentration of the first protective glue is 3-7wt%;Preferably, second protection
In sol solution, the concentration of the second protective glue is 5-10wt%;
Preferably, the lithium metasilicate magnalium soap is by water-soluble organic pyrophosphate salt organic matter processing.
7. water-in-water multicolor coating according to claim 4, which is characterized in that the base paint further includes that base paint helps
Agent, content of the base paint auxiliary agent in the base paint are 2.5-5wt%;
Preferably, the base paint auxiliary agent includes in filler, pH adjusting agent, defoaming agent, film forming agent, antifreezing agent and sterilization antiseptic
At least one, the preferably mixture of filler, pH adjusting agent, defoaming agent, film forming agent, antifreezing agent and sterilization antiseptic;
Preferably, the base paint auxiliary agent includes filler 0.5-1wt%, defoaming agent 0.1-0.5wt%, pH adjusting agent 0.1-
0.2wt%, film forming agent 1-2wt%, antifreezing agent 0.5-1.5wt% and sterilization antiseptic 0.1-0.5wt%.
8. the preparation method of water-in-water multicolor coating according to claim 1-7, which is characterized in that including as follows
Step:
Color grain and continuous phase are uniformly mixed, water-in-water multicolor coating is obtained;
Preferably, base paint is added in the first protection sol solution and is uniformly mixed, obtain color grain;
Preferably, by high molecular weight hydrophobically modified hydroxyethyl cellulose ether, the acrylic emulsion containing associative groups, the second protective glue
Solution, water and optional base paint auxiliary agent are uniformly mixed, and obtain base paint;
Preferably, aqueous acrylic emulsion, white sand, non-association type alkali swollen thickener, water and optional continuous phase auxiliary agent are mixed
It closes uniformly, obtains continuous phase.
9. the construction method of water-in-water multicolor coating according to claim 1-7, which is characterized in that use roller coating
Or batch mode scraped is constructed.
10. application of the water-in-water multicolor coating according to claim 1-7 in interior wall or decoration of exterior wall.