CN106009941A - Environment-friendly natural stone paint for decoration and preparation method for natural stone paint - Google Patents
Environment-friendly natural stone paint for decoration and preparation method for natural stone paint Download PDFInfo
- Publication number
- CN106009941A CN106009941A CN201610597628.3A CN201610597628A CN106009941A CN 106009941 A CN106009941 A CN 106009941A CN 201610597628 A CN201610597628 A CN 201610597628A CN 106009941 A CN106009941 A CN 106009941A
- Authority
- CN
- China
- Prior art keywords
- minute
- natural stone
- decoration
- stone paint
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly natural stone paint for decoration and a preparation method for the natural stone paint. The natural stone paint is prepared from the following raw materials: natural color sand, sericite powder, nonylphenol polyoxyethylene ether, acetylated monostearin, modified urea-formaldehyde resin adhesive powder, carboxylic butadiene-styrene latex, polyvinyl acetate emulsion, carboxymethyl hydroxyethyl cellulose, glyceryl polyoxyethyl ether, zinc naphthenate, waxy corn steep liquor and water. Compared with the prior art, the natural stone paint and the preparation method for the same have the advantages that the natural color sand and the sericite powder are taken as main materials, colors can be selected according to practical requirements, and the natural stone paint is endowed with exquisite texture by fixed grading; after being used for the surface of a wooden board, the natural stone paint is high in cohesiveness, and can be dried without chalking within a short time under a normal-temperature condition, and does not fade after being used for a long time, and a formed pattern is stable, higher in pollution resistance and water resistance and high in color retention; compared with a conventional material, the natural stone paint has a good texture and higher applicability.
Description
Technical field
The invention belongs to furniture outer layer coating technology field, be specifically related to a kind of true mineral varnish of environment-friendly type for decoration and preparation method thereof.
Background technology
nullTrue mineral varnish is typically the natural rubbles such as the natural granite with different-grain diameter、Stone powder is primary raw material，With synthetic resin for main binding agent，And it is aided with the coating that several formulations is the most formulated，It is generally used for the imitative stone effect of external wall，True mineral varnish has fire prevention、Waterproof、Acid and alkali-resistance、Anti-pollution，Nontoxic、Tasteless、Cohesive force is strong，Will never fade feature，Can aid in the service life extending building，Along with updating of true mineral varnish performance and outward appearance，The most gradually apply in interior decoration now，Due to its construction solid after the hardest，It is generally used for the metope of indoor，Apply less elsewhere，And now with the raising of people's living standard，Requirement to furniture outward appearance is more and more diversified，While requiring monotone，Also begin to require that furniture outward appearance has the natural type pattern of top grade as decoration，But current true mineral varnish is in the more difficult bonding of board surface，Time one length is easy for coming off，Impact dicoration.
Summary of the invention
It is an object of the invention to for existing problem, it is provided that a kind of true mineral varnish of environment-friendly type for decoration and preparation method thereof.
The present invention is achieved by the following technical solutions: a kind of true mineral varnish of environment-friendly type for decoration; it is made up of the raw material of following weight portion: natural colour sand 28-32 part; sericite in powder 12-18 part; venamul 8-12 part; NPE 1-2 part; acetylation monoglyceride 2-5 part; modified urea-formaldehyde resin glue powder 5-8 part; carboxylic styrene butadiene latex 4-8 part; carboxymethyl hydroxyethyl cellulose 2-4 part, polyoxyethanyl glycerin ether 0.15-0.45 part, zinc naphthenate 0.55-0.85 part; Glutinous Semen Maydis serosity 12-16 part, water 8-12 part；
Wherein, the preparation method of described modified urea-formaldehyde resin glue powder is as follows: add the sodium laurylsulfate being equivalent to its weight portion 15% in urea formaldehyde resin adhesive powder, after stirring 10-15 minute, add the sodium hydroxide solution regulation that mass concentration is 15%, regulate its pH value and reach 8.2-8.6；After stirring 5-10 minute under conditions of 28-34 DEG C, add wherein and be equivalent to the tetraethyl orthosilicate of its gross weight 4% and the fatty bis-stearamides of 7%, continue to be heated to 55-60 DEG C, stir process 15-20 minute；Process complete after Temperature fall, with formic acid by its pH value regulate to 6.5-6.8, stir process 35-45 minute, then spray by centrifugal spray drying method, obtain the fine powder that fineness is 45-50.
As further improvement of these options, the preparation method of Glutinous Semen Maydis serosity is: collect the seed of Glutinous Semen Maydis, with blister 3-4 hour, it is then placed in being equivalent in the boiling water of its weight portion 5 times boiling 12-15 minute, natural cooling after completing, the soup of infusion Glutinous Semen Maydis seed and Glutinous Semen Maydis seed are put in beater and pulls an oar, to obtain final product.
As further improvement of these options, described sericite in powder fineness is 800 mesh, and whiteness is 80%, and water content is 2-4%.
As further improvement of these options, the distribution of particles situation that described natural colour sand is as the criterion with particle diameter is as follows: particle diameter, as 0.058-0.074mm, accounts for the 65-70% of its gross weight；Particle diameter is 0.075-0.180mm, accounts for the 18-24% of its gross weight；Particle diameter is 0.181-0.250mm, accounts for the 6-17% of its gross weight.
As further improvement of these options, the color of described natural colour sand be white, grey, black, yellow, red, green in any one or a few mixing.
The preparation method of a kind of true mineral varnish of environment-friendly type for decoration, comprises the following steps:
(1) in container, it is sequentially added into the water of corresponding weight portion, Glutinous Semen Maydis serosity, carboxylic styrene butadiene latex, venamul, carboxymethyl hydroxyethyl cellulose and NPE, processes 12-15 minute with dispersion machine dispersion under the rotating speed of 600-800r/min；
(2) in above-mentioned compound, it is sequentially added into acetylation monoglyceride, sericite in powder and the natural colour sand of corresponding weight portion; process 3-5 minute with dispersion machine dispersion under the rotating speed of 1200-1500r/min, then with the microwave device of 400-600MHz frequency, above-mentioned compound is processed the 15-20 second；
(3) in above-mentioned compound, surplus stock is added, process 8-10 minute with dispersion machine dispersion under the rotating speed of 300-500r/min, with the pH value of ammonia regulation compound to 7.2-7.5, in heated and stirred to compound, the percentage by weight of contained humidity is 8-12%, then discharging and get final product after Temperature fall.
Heretofore described decoration refers to the decoration on wood furniture or Indoor Wooden sheet material.
The present invention has the advantage that in the present invention compared to existing technology with natural colour sand and sericite in powder as major ingredient, selects color according to actual needs, and its fixing grating makes true mineral varnish keep fine and smooth texture, behind wooden boards surface, caking property is good, can be dried in a short time, not efflorescence after drying under normal temperature condition, become pattern is stable, having preferable resistance to soiling and resistance to water, color keeps, and life-time service is colour-fast, comparing conventional material and have good texture, the suitability is stronger.
Detailed description of the invention
Embodiment 1
A kind of true mineral varnish of environment-friendly type for decoration, is made up of the raw material of following weight portion: natural colour sand 30 parts, sericite in powder 14 parts; venamul 10 parts; NPE 2 parts, acetylation monoglyceride 4 parts, 6 parts of modified urea-formaldehyde resin glue powder; carboxylic styrene butadiene latex 8 parts; carboxymethyl hydroxyethyl cellulose 3 parts, polyoxyethanyl glycerin ether 0.35 part, zinc naphthenate 0.65 part; 14 parts of Glutinous Semen Maydis serosity, 8 parts of water；
Wherein, the preparation method of described modified urea-formaldehyde resin glue powder is as follows: add the sodium laurylsulfate being equivalent to its weight portion 15% in urea formaldehyde resin adhesive powder, after stirring 10-15 minute, add the sodium hydroxide solution regulation that mass concentration is 15%, regulate its pH value and reach 8.2-8.6；After stirring 5-10 minute under conditions of 28-34 DEG C, add wherein and be equivalent to the tetraethyl orthosilicate of its gross weight 4% and the fatty bis-stearamides of 7%, continue to be heated to 55-60 DEG C, stir process 15-20 minute；Process complete after Temperature fall, with formic acid by its pH value regulate to 6.5-6.8, stir process 35-45 minute, then spray by centrifugal spray drying method, obtain the fine powder that fineness is 45-50.
Wherein, the preparation method of Glutinous Semen Maydis serosity was: collect the seed of Glutinous Semen Maydis, with blister 3-4 hour, it is then placed in being equivalent in the boiling water of its weight portion 5 times boiling 12-15 minute, natural cooling after completing, puts into the soup of infusion Glutinous Semen Maydis seed and Glutinous Semen Maydis seed in beater and pulls an oar, to obtain final product.
Wherein, described sericite in powder fineness is 800 mesh, and whiteness is 80%, and water content is 2-4%.
Wherein, the distribution of particles situation that described natural colour sand is as the criterion with particle diameter is as follows: particle diameter, as 0.058-0.074mm, accounts for the 65-70% of its gross weight；Particle diameter is 0.075-0.180mm, accounts for the 18-24% of its gross weight；Particle diameter is 0.181-0.250mm, accounts for the 6-17% of its gross weight.
Wherein, the color of described natural colour sand be white, grey, black, yellow, red, green in any one or a few mixing.
The preparation method of a kind of true mineral varnish of environment-friendly type for decoration, comprises the following steps:
(1) in container, it is sequentially added into the water of corresponding weight portion, Glutinous Semen Maydis serosity, carboxylic styrene butadiene latex, venamul, carboxymethyl hydroxyethyl cellulose and NPE, processes 12-15 minute with dispersion machine dispersion under the rotating speed of 600-800r/min；
(2) in above-mentioned compound, it is sequentially added into acetylation monoglyceride, sericite in powder and the natural colour sand of corresponding weight portion; process 3-5 minute with dispersion machine dispersion under the rotating speed of 1200-1500r/min, then with the microwave device of 400-600MHz frequency, above-mentioned compound is processed the 15-20 second；
(3) in above-mentioned compound, surplus stock is added, process 8-10 minute with dispersion machine dispersion under the rotating speed of 300-500r/min, with the pH value of ammonia regulation compound to 7.2-7.5, in heated and stirred to compound, the percentage by weight of contained humidity is 8-12%, then discharging and get final product after Temperature fall.
In the present embodiment, true mineral varnish is 126 minutes in the drying time of furniture surface, adhesion strength is 1.35MPa, resistance to water experiment is carried out with the plank scribbling true mineral varnish under normal temperature condition, soak time is 3 days, after experiment terminates, scribble the plank of true mineral varnish without variable color, foaming, wrinkling, the phenomenon such as come off, its wearability is preferable, and impact flexibility is 2.18KJ/cm.
Embodiment 2
A kind of true mineral varnish of environment-friendly type for decoration, is made up of the raw material of following weight portion: natural colour sand 28 parts, sericite in powder 18 parts; venamul 12 parts; NPE 2 parts, acetylation monoglyceride 4 parts, 5 parts of modified urea-formaldehyde resin glue powder; carboxylic styrene butadiene latex 6 parts; carboxymethyl hydroxyethyl cellulose 2 parts, polyoxyethanyl glycerin ether 0.15 part, zinc naphthenate 0.85 part; 12 parts of Glutinous Semen Maydis serosity, 10 parts of water；
Wherein, the preparation method of described modified urea-formaldehyde resin glue powder is as follows: add the sodium laurylsulfate being equivalent to its weight portion 15% in urea formaldehyde resin adhesive powder, after stirring 10-15 minute, add the sodium hydroxide solution regulation that mass concentration is 15%, regulate its pH value and reach 8.2-8.6；After stirring 5-10 minute under conditions of 28-34 DEG C, add wherein and be equivalent to the tetraethyl orthosilicate of its gross weight 4% and the fatty bis-stearamides of 7%, continue to be heated to 55-60 DEG C, stir process 15-20 minute；Process complete after Temperature fall, with formic acid by its pH value regulate to 6.5-6.8, stir process 35-45 minute, then spray by centrifugal spray drying method, obtain the fine powder that fineness is 45-50.
Its preparation method is in the same manner as in Example 1.
In the present embodiment, true mineral varnish is 135 minutes in the drying time of furniture surface, adhesion strength is 1.38MPa, resistance to water experiment is carried out with the plank scribbling true mineral varnish under normal temperature condition, soak time is 3 days, after experiment terminates, scribble the plank of true mineral varnish without variable color, foaming, wrinkling, the phenomenon such as come off, its wearability is preferable, and impact flexibility is 2.15KJ/cm.
Embodiment 3
A kind of true mineral varnish of environment-friendly type for decoration, is made up of the raw material of following weight portion: natural colour sand 32 parts, sericite in powder 12 parts; venamul 8 parts; NPE 2 parts, acetylation monoglyceride 2 parts, 5 parts of modified urea-formaldehyde resin glue powder; carboxylic styrene butadiene latex 8 parts; carboxymethyl hydroxyethyl cellulose 3 parts, polyoxyethanyl glycerin ether 0.25 part, zinc naphthenate 0.75 part; 15 parts of Glutinous Semen Maydis serosity, 12 parts of water；
Wherein, the preparation method of described modified urea-formaldehyde resin glue powder is as follows: add the sodium laurylsulfate being equivalent to its weight portion 15% in urea formaldehyde resin adhesive powder, after stirring 10-15 minute, add the sodium hydroxide solution regulation that mass concentration is 15%, regulate its pH value and reach 8.2-8.6；After stirring 5-10 minute under conditions of 28-34 DEG C, add wherein and be equivalent to the tetraethyl orthosilicate of its gross weight 4% and the fatty bis-stearamides of 7%, continue to be heated to 55-60 DEG C, stir process 15-20 minute；Process complete after Temperature fall, with formic acid by its pH value regulate to 6.5-6.8, stir process 35-45 minute, then spray by centrifugal spray drying method, obtain the fine powder that fineness is 45-50.
Its preparation method is in the same manner as in Example 1.
In the present embodiment, true mineral varnish is 129 minutes in the drying time of furniture surface, adhesion strength is 1.37MPa, resistance to water experiment is carried out with the plank scribbling true mineral varnish under normal temperature condition, soak time is 3 days, after experiment terminates, scribble the plank of true mineral varnish without variable color, foaming, wrinkling, the phenomenon such as come off, its wearability is preferable, and impact flexibility is 2.24KJ/cm.
Claims (6)
1. the true mineral varnish of environment-friendly type for decoration, it is characterised in that be made up of the raw material of following weight portion: natural colour sand 28-32 part; sericite in powder 12-18 part, venamul 8-12 part, NPE 1-2 part; acetylation monoglyceride 2-5 part; modified urea-formaldehyde resin glue powder 5-8 part, carboxylic styrene butadiene latex 4-8 part, carboxymethyl hydroxyethyl cellulose 2-4 part; polyoxyethanyl glycerin ether 0.15-0.45 part; zinc naphthenate 0.55-0.85 part, Glutinous Semen Maydis serosity 12-16 part, water 8-12 part；
Wherein, the preparation method of described modified urea-formaldehyde resin glue powder is as follows: add the sodium laurylsulfate being equivalent to its weight portion 15% in urea formaldehyde resin adhesive powder, after stirring 10-15 minute, add the sodium hydroxide solution regulation that mass concentration is 15%, regulate its pH value and reach 8.2-8.6；After stirring 5-10 minute under conditions of 28-34 DEG C, add wherein and be equivalent to the tetraethyl orthosilicate of its gross weight 4% and the fatty bis-stearamides of 7%, continue to be heated to 55-60 DEG C, stir process 15-20 minute；Process complete after Temperature fall, with formic acid by its pH value regulate to 6.5-6.8, stir process 35-45 minute, then spray by centrifugal spray drying method, obtain the fine powder that fineness is 45-50.
A kind of true mineral varnish of environment-friendly type for decoration, it is characterized in that, the preparation method of Glutinous Semen Maydis serosity is: collect the seed of Glutinous Semen Maydis, with blister 3-4 hour, it is then placed in being equivalent in the boiling water of its weight portion 5 times boiling 12-15 minute, natural cooling after completing, puts into the soup of infusion Glutinous Semen Maydis seed and Glutinous Semen Maydis seed in beater and pulls an oar, to obtain final product.
A kind of true mineral varnish of environment-friendly type for decoration, it is characterised in that described sericite in powder fineness is 800 mesh, and whiteness is 80%, and water content is 2-4%.
A kind of true mineral varnish of environment-friendly type for decoration, it is characterised in that the distribution of particles situation that described natural colour sand is as the criterion with particle diameter is as follows: particle diameter, as 0.058-0.074mm, accounts for the 65-70% of its gross weight；Particle diameter is 0.075-0.180mm, accounts for the 18-24% of its gross weight；Particle diameter is 0.181-0.250mm, accounts for the 6-17% of its gross weight.
A kind of for decoration the true mineral varnish of environment-friendly type, it is characterised in that the color of described natural colour sand be white, grey, black, yellow, red, green in any one or a few mixing.
6. the preparation method of the true mineral varnish of environment-friendly type being used for decoration as claimed in claim 1, it is characterised in that comprise the following steps:
(1) in container, it is sequentially added into the water of corresponding weight portion, Glutinous Semen Maydis serosity, carboxylic styrene butadiene latex, venamul, carboxymethyl hydroxyethyl cellulose and NPE, processes 12-15 minute with dispersion machine dispersion under the rotating speed of 600-800r/min；
(2) in above-mentioned compound, it is sequentially added into acetylation monoglyceride, sericite in powder and the natural colour sand of corresponding weight portion; process 3-5 minute with dispersion machine dispersion under the rotating speed of 1200-1500r/min, then with the microwave device of 400-600MHz frequency, above-mentioned compound is processed the 15-20 second；
(3) in above-mentioned compound, surplus stock is added, process 8-10 minute with dispersion machine dispersion under the rotating speed of 300-500r/min, with the pH value of ammonia regulation compound to 7.2-7.5, in heated and stirred to compound, the percentage by weight of contained humidity is 8-12%, then discharging and get final product after Temperature fall.