CN107325621A - A kind of high-strength environment-friendly powder of lacquer putty for use on and preparation method thereof - Google Patents
A kind of high-strength environment-friendly powder of lacquer putty for use on and preparation method thereof Download PDFInfo
- Publication number
- CN107325621A CN107325621A CN201710784060.0A CN201710784060A CN107325621A CN 107325621 A CN107325621 A CN 107325621A CN 201710784060 A CN201710784060 A CN 201710784060A CN 107325621 A CN107325621 A CN 107325621A
- Authority
- CN
- China
- Prior art keywords
- powder
- weight
- parts
- lacquer putty
- friendly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of high-strength environment-friendly powder of lacquer putty for use on and preparation method thereof, is related to building material field.A kind of high-strength environment-friendly powder of lacquer putty for use on, is mainly mixed, raw material includes by raw material：The parts by weight of white cement 20 40, the parts by weight of sierozem power 5 20, the parts by weight of ball clay 10 20, the parts by weight of talcum powder 5 20, the parts by weight of starch phosphate 28, the parts by weight of hydroxypropyl cellulose 15, the parts by weight of egg-shell meal 2 10 and the parts by weight of reinforcing fiber powder 0.5 2.It has the characteristics of intensity is high, adhesion property is good.A kind of preparation method of high-strength environment-friendly powder of lacquer putty for use on, including：Raw material is mixed high-strength environment-friendly powder of lacquer putty for use on is made.This method is simple, easy to operate.
Description
Technical field
The present invention relates to building material field, and more particularly to a kind of high-strength environment-friendly powder of lacquer putty for use on and preparation method thereof.
Background technology
Powder of lacquer putty for use on is a kind of ornament materials of smooth surface of wall, is, using inorganic gel materials as base material, to be equipped with and cohere material
Material and other auxiliary agent retrofits are formed, and are a kind of products essential before coating is painted.Powder of lacquer putty for use on generally applies and imposes on priming paint
Upper or directly painting is imposed on object, to remove the rugged defect in coated article surface.Powder of lacquer putty for use on is filled as interior wall, exterior wall
Material and be widely used.But when existing powder of lacquer putty for use on is as decorating inner and external walls, it is primarily present intensity is not enough, adhesive force is poor etc.
Defect.
The content of the invention
It is an object of the invention to provide a kind of high-strength environment-friendly powder of lacquer putty for use on, it has the spy that intensity is high, adhesion property is good
Point.
Another object of the present invention is to provide a kind of preparation method of high-strength environment-friendly powder of lacquer putty for use on, this method is simple, easy
Operation.
The present invention is solved its technical problem and realized using following technical scheme.
The present invention proposes a kind of high-strength environment-friendly powder of lacquer putty for use on, is mainly mixed by raw material, raw material includes：White cement 20-
40 parts by weight, sierozem power 5-20 parts by weight, ball clay 10-20 parts by weight, talcum powder 5-20 parts by weight, starch phosphate 2-8 weights
Measure part, hydroxypropyl cellulose 1-5 parts by weight, egg-shell meal 2-10 parts by weight and reinforcing fiber powder 0.5-2 parts by weight.
The present invention also proposes a kind of preparation method of high-strength environment-friendly powder of lacquer putty for use on, including：Raw material is mixed height is made
Intensity environmental friendly putty powder.
The beneficial effect of the embodiment of the present invention is：It is each in the high-strength environment-friendly powder of lacquer putty for use on of the embodiment of the present invention, its raw material
Component proportion is suitable, the high-strength environment-friendly powder of lacquer putty for use on by the use of white cement and sierozem power as main base and inorganic adhesive,
Using egg-shell meal, talcum powder as filler rise filling effect, in conjunction with high-ductility, high adhesiveness energy, polymolecularity can ball clay,
Starch phosphate and hydroxypropyl cellulose, can not only strengthen the intensity of high-strength environment-friendly powder of lacquer putty for use on, and cause high intensity
Powder of lacquer putty for use on is more preferable to the adhesive force of metope, further, since the addition of reinforcing fiber, also further enhancing high-strength environment-friendly putty
The intensity of powder.Without harmful substances, environmentally friendly nothing such as heavy metal, formaldehyde in the high-strength environment-friendly putty powder raw material of the embodiment of the present invention
Evil.
Embodiment
, below will be in the embodiment of the present invention to make the purpose, technical scheme and advantage of the embodiment of the present invention clearer
Technical scheme be clearly and completely described.Unreceipted actual conditions person, builds according to normal condition or manufacturer in embodiment
The condition of view is carried out.Agents useful for same or the unreceipted production firm person of instrument, are the conventional production that can be obtained by commercially available purchase
Product.
A kind of high-strength environment-friendly powder of lacquer putty for use on of the embodiment of the present invention and preparation method thereof is specifically described below.
A kind of high-strength environment-friendly powder of lacquer putty for use on, is mainly mixed, raw material includes by raw material：White cement 20-40 parts by weight, ash
Calcium powder 5-20 parts by weight, ball clay 10-20 parts by weight, talcum powder 5-20 parts by weight, starch phosphate 2-8 parts by weight, hydroxypropyl
Cellulose 1-5 parts by weight, egg-shell meal 2-10 parts by weight and reinforcing fiber powder 0.5-2 parts by weight.
White cement, is the abbreviation of white portland cement, is a kind of hydraulic cementing materials.White cement is used as powder of lacquer putty for use on
Raw material, its cementability is good, and intensity is high, is mainly used as base-material, can increase the later strength of high-strength environment-friendly powder of lacquer putty for use on.
Ball clay is a kind of clay of high plasticity, and it has higher viscosity, rheological characteristic, can strengthen high-strength environment-friendly greasy
Sub- powder to the adhesive force of metope, be difficult to peel off, and the intensity of high-strength environment-friendly powder of lacquer putty for use on can be strengthened.
Starch phosphate is easily gelatinized, with the high grade of transparency, high viscosity, high gumminess.It is used as the raw material of powder of lacquer putty for use on, can
The cementability of its powder of lacquer putty for use on is improved, and its dispersiveness is preferably, is conducive to strengthening adhesive force of the high-strength environment-friendly powder of lacquer putty for use on to metope.
Hydroxypropyl cellulose, is a kind of nonionic cellulose derivative.Its thermoplasticity, filming performance, caking property, latex
Stability and dispersiveness are preferable, can strengthen adhesive force of the high-strength environment-friendly powder of lacquer putty for use on to metope.
Egg-shell meal is the powder product after eggshell is ground, and its main component is calcium carbonate, is mainly used as high-strength environment-friendly greasy
The filler of sub- powder.
Reinforcing fiber, it can strengthen the intensity of high-strength environment-friendly powder of lacquer putty for use on as the raw material of high-strength environment-friendly powder of lacquer putty for use on.
Each group distribution ratio in the high-strength environment-friendly powder of lacquer putty for use on of the embodiment of the present invention, its raw material is suitable, the high-strength environment-friendly
Powder of lacquer putty for use on is risen by the use of white cement and sierozem power as main base and inorganic adhesive using egg-shell meal, talcum powder as filler
Filling effect, in conjunction with high-ductility, high adhesiveness energy, polymolecularity can ball clay, starch phosphate and hydroxy propyl cellulose
Element, can not only strengthen the intensity of high-strength environment-friendly powder of lacquer putty for use on, and make it that high-strength putty powder is more preferable to the adhesive force of metope,
Further, since the addition of reinforcing fiber, also further enhancing the intensity of high-strength environment-friendly powder of lacquer putty for use on.The height of the embodiment of the present invention
It is environmentally friendly without harmful substances such as heavy metal, formaldehyde in intensity environmental friendly putty powder raw material.
Preferably, the white cement in raw material is 25-35 parts by weight, and sierozem power is 10-15 parts by weight, and ball clay is 12-18
Parts by weight, talcum powder is 10-15 parts by weight, and starch phosphate is 3-5 parts by weight, hydroxypropyl cellulose 2-4 parts by weight, egg-shell meal
For 3-8 parts by weight, reinforcing fiber powder is 1-1.5 parts by weight.The high-strength environment-friendly powder of lacquer putty for use on of the proportioning is the wound by inventor
The property made thinking and empirical preferred value, the intensity of high-strength environment-friendly powder of lacquer putty for use on are higher.
Further, the reinforcing fiber powder in raw material is in glass fiber powder, basalt fibre powder and polypropylene fibre powder
At least one.
In some embodiments of the invention, it is 1~3 that reinforcing fiber powder, which includes weight ratio,:1 glass fiber powder and poly- third
Alkene fiber powder.Glass fiber powder and polypropylene fibre powder mix to cause the intensity of high-strength environment-friendly powder of lacquer putty for use on higher.In this hair
In bright embodiment, the particle diameter of reinforcing fiber powder is 50-100 μm.
Further, in an embodiment of the present invention, the particle diameter of sierozem power is 320-400 mesh；The particle diameter of ball clay is
200-400 mesh.The particle diameter of talcum powder is 200-400 mesh.The particle diameter of hydroxypropyl cellulose is 200-300 mesh.
A kind of preparation method of high-strength environment-friendly powder of lacquer putty for use on, including：Raw material is mixed high-strength environment-friendly putty is made
Powder.This method is simple, easy to operate.
The feature and performance to the present invention are described in further detail with reference to embodiments.
Embodiment 1
The present embodiment provides a kind of high-strength environment-friendly powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The weight of white cement 20
Part, the parts by weight of sierozem power 10, the parts by weight of ball clay 15, the parts by weight of talcum powder 12, the parts by weight of starch phosphate 3, hydroxy propyl cellulose
Plain 2 parts by weight, the parts by weight of egg-shell meal 5, weight ratio are 1:3 glass fiber powder and polypropylene fibre powder totally 1 parts by weight.Wherein,
The particle diameter of glass fiber powder and polypropylene fibre powder is 50 μm；The particle diameter of sierozem power is 400 mesh；The particle diameter of ball clay is 300
Mesh；The particle diameter of talcum powder is 300 mesh；The particle diameter of hydroxypropyl cellulose is 200 mesh.
The preparation method of the high-strength environment-friendly powder of lacquer putty for use on, including：Raw material is weighed according to said ratio, raw material is mixed
Produce high-strength environment-friendly powder of lacquer putty for use on.
Embodiment 2
The present embodiment provides a kind of high-strength environment-friendly powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The weight of white cement 25
Part, the parts by weight of sierozem power 8, the parts by weight of ball clay 18, the parts by weight of talcum powder 15, the parts by weight of starch phosphate 7, hydroxypropyl cellulose
4 parts by weight, the parts by weight of egg-shell meal 7, weight ratio are 1:2 glass fiber powder and polypropylene fibre powder totally 1.5 parts by weight.Wherein,
The particle diameter of glass fiber powder and polypropylene fibre powder is 70 μm；The particle diameter of sierozem power is 350 mesh；The particle diameter of ball clay is 400
Mesh；The particle diameter of talcum powder is 400 mesh；The particle diameter of hydroxypropyl cellulose is 200 mesh.
The preparation method of the high-strength environment-friendly powder of lacquer putty for use on, including：Raw material is weighed according to said ratio, raw material is mixed
Produce high-strength environment-friendly powder of lacquer putty for use on.
Embodiment 3
The present embodiment provides a kind of high-strength environment-friendly powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The weight of white cement 40
Part, the parts by weight of sierozem power 12, the parts by weight of ball clay 10, the parts by weight of talcum powder 8, the parts by weight of starch phosphate 8, hydroxypropyl cellulose
1 parts by weight, the parts by weight of egg-shell meal 10, weight ratio are 1:1 glass fiber powder and polypropylene fibre powder totally 1 parts by weight.Wherein, glass
The particle diameter of glass fiber powder and polypropylene fibre powder is 80 μm；The particle diameter of sierozem power is 360 mesh；The particle diameter of ball clay is 300 mesh；
The particle diameter of talcum powder is 400 mesh；The particle diameter of hydroxypropyl cellulose is 300 mesh.
The preparation method of the high-strength environment-friendly powder of lacquer putty for use on, including：Raw material is weighed according to said ratio, raw material is mixed
Produce high-strength environment-friendly powder of lacquer putty for use on.
Embodiment 4
The present embodiment provides a kind of high-strength environment-friendly powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The weight of white cement 40
Part, the parts by weight of sierozem power 12, the parts by weight of ball clay 10, the parts by weight of talcum powder 8, the parts by weight of starch phosphate 8, hydroxypropyl cellulose
1 parts by weight, the parts by weight of egg-shell meal 10, weight ratio are 1:1 glass fiber powder and polypropylene fibre powder totally 1 parts by weight.Wherein, glass
The particle diameter of glass fiber powder and polypropylene fibre powder is 100 μm；The particle diameter of sierozem power is 320 mesh；The particle diameter of ball clay is 300
Mesh；The particle diameter of talcum powder is 400 mesh；The particle diameter of hydroxypropyl cellulose is 300 mesh.
The preparation method of the high-strength environment-friendly powder of lacquer putty for use on, including：Raw material is weighed according to said ratio, raw material is mixed
Produce high-strength environment-friendly powder of lacquer putty for use on.
Embodiment 5
The present embodiment provides a kind of high-strength environment-friendly powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The weight of white cement 35
Part, the parts by weight of sierozem power 5, the parts by weight of ball clay 12, the parts by weight of talcum powder 17, the parts by weight of starch phosphate 4, hydroxypropyl cellulose
3 parts by weight, the parts by weight of egg-shell meal 8, the parts by weight of polypropylene fibre powder 0.5.Wherein, the particle diameter of polypropylene fibre powder is 60 μm；
The particle diameter of sierozem power is 380 mesh；The particle diameter of ball clay is 400 mesh；The particle diameter of talcum powder is 400 mesh；The grain of hydroxypropyl cellulose
Footpath is 300 mesh.
The preparation method of the high-strength environment-friendly powder of lacquer putty for use on, including：Raw material is weighed according to said ratio, raw material is mixed
Produce high-strength environment-friendly powder of lacquer putty for use on.
Embodiment 6
The present embodiment provides a kind of high-strength environment-friendly powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The weight of white cement 38
Part, the parts by weight of sierozem power 18, the parts by weight of ball clay 15, the parts by weight of talcum powder 20, the parts by weight of starch phosphate 5, hydroxy propyl cellulose
Plain 2 parts by weight, the parts by weight of egg-shell meal 6, the parts by weight of glass fiber powder 1.2.Wherein, the particle diameter of glass fiber powder is 90 μm；Ash
The particle diameter of calcium powder is 350 mesh；The particle diameter of ball clay is 300 mesh；The particle diameter of talcum powder is 300 mesh；The particle diameter of hydroxypropyl cellulose
For 300 mesh.
The preparation method of the high-strength environment-friendly powder of lacquer putty for use on, including：Raw material is weighed according to said ratio, raw material is mixed
Produce high-strength environment-friendly powder of lacquer putty for use on.
Embodiment 7
The present embodiment provides a kind of high-strength environment-friendly powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The weight of white cement 28
Part, the parts by weight of sierozem power 20, the parts by weight of ball clay 10, the parts by weight of talcum powder 5, the parts by weight of starch phosphate 2, hydroxypropyl cellulose
4 parts by weight, the parts by weight of egg-shell meal 2, the parts by weight of basalt fibre powder 1.8.Wherein, the particle diameter of basalt fibre powder is 80 μm；
The particle diameter of sierozem power is 400 mesh；The particle diameter of ball clay is 200 mesh；The particle diameter of talcum powder is 300 mesh；The grain of hydroxypropyl cellulose
Footpath is 200 mesh.
The preparation method of the high-strength environment-friendly powder of lacquer putty for use on, including：Raw material is weighed according to said ratio, raw material is mixed
Produce high-strength environment-friendly powder of lacquer putty for use on.
Comparative example 1
A kind of powder of lacquer putty for use on, is mainly made up of raw material, and raw material includes：The parts by weight of white cement 20, the parts by weight of sierozem power 10, talcum
The parts by weight of powder 12, the parts by weight of starch phosphate 3, the parts by weight of hydroxypropyl cellulose 2, the parts by weight of egg-shell meal 5, weight ratio are 1:3
Glass fiber powder and polypropylene fibre powder totally 1 parts by weight.Wherein, the particle diameter of glass fibre and polypropylene fibre is 50 μm；Ash
The particle diameter of calcium powder is 400 mesh；The particle diameter of talcum powder is 300 mesh；The particle diameter of hydroxypropyl cellulose is 200 mesh.
The preparation method of the powder of lacquer putty for use on, including：Raw material is weighed according to said ratio, raw material is mixed and produces putty
Powder.
Comparative example 2
The present embodiment provides a kind of powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The parts by weight of white cement 18, sierozem power 3
Parts by weight, the parts by weight of ball clay 21, the parts by weight of talcum powder 6, the parts by weight of starch phosphate 1, the parts by weight of hydroxypropyl cellulose 6, egg
The parts by weight of shell powder 11, weight ratio are 1:2 glass fiber powder and polypropylene fibre powder totally 0.3 parts by weight.Wherein, glass fibre and
The particle diameter of polypropylene fibre is 50 μm；The particle diameter of sierozem power is 400 mesh；The particle diameter of ball clay is 300 mesh；The particle diameter of talcum powder
For 300 mesh；The particle diameter of hydroxypropyl cellulose is 200 mesh.
The preparation method of the powder of lacquer putty for use on, including：Raw material is weighed according to said ratio, raw material is mixed and produces putty
Powder.
Comparative example 3
The present embodiment provides a kind of powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The parts by weight of white cement 42, sierozem power
21 parts by weight, the parts by weight of ball clay 8, the parts by weight of talcum powder 21, the parts by weight of starch phosphate 9, the weight of hydroxypropyl cellulose 0.8
Part, the parts by weight of egg-shell meal 1, weight ratio are 1:1 glass fiber powder and polypropylene fibre powder totally 2.2 parts by weight.Wherein, glass fibers
The particle diameter of peacekeeping polypropylene fibre is 50 μm；The particle diameter of sierozem power is 400 mesh；The particle diameter of ball clay is 300 mesh；Talcum powder
Particle diameter is 300 mesh；The particle diameter of hydroxypropyl cellulose is 200 mesh.
The preparation method of the powder of lacquer putty for use on, including：Raw material is weighed according to said ratio, raw material is mixed and produces putty
Powder.
Test example
High-strength environment-friendly powder of lacquer putty for use on of reference JG/T-298-2010 (architecture indoor putty) standard to embodiment 1-7
And comparative example 1-3 powder of lacquer putty for use on carries out the performances such as application property, adhesive strength, drying time, grinability, rupture strength and surveyed
Examination, its result is recorded in table 1.
The embodiment 1-7 of table 1 and comparative example 1-3 test result
From table 1 it follows that the high-strength environment-friendly powder of lacquer putty for use on of embodiment 1 than comparative example 1 powder of lacquer putty for use on adhesive strength and
Rupture strength is all more preferable, illustrates, add the ball clay in the embodiment of the present invention can improve powder of lacquer putty for use on adhesive strength and
Rupture strength.By each performance of comparative example 1-7 high-strength environment-friendly powder of lacquer putty for use on and comparative example 2-3 powder of lacquer putty for use on, find
Either adhesive strength, rupture strength, or grinability and drying time performance, embodiment 1-7 high-strength environment-friendly powder of lacquer putty for use on
Powder of lacquer putty for use on performance all than comparative example 2-3 is more excellent, illustrates each raw material proportioning of high-strength environment-friendly powder of lacquer putty for use on of the embodiment of the present invention
Properly, be conducive to preparing the more excellent high-strength environment-friendly powder of lacquer putty for use on of performance.
In summary, high-strength environment-friendly powder of lacquer putty for use on of the embodiment of the present invention and preparation method thereof, high-strength environment-friendly powder of lacquer putty for use on
Raw material in each group distribution ratio it is suitable, the high-strength environment-friendly powder of lacquer putty for use on using white cement conjunction sierozem power as main base, with
Egg-shell meal, talcum powder play filling effect as filler, in conjunction with high-ductility, high adhesiveness energy, the ball clay of polymolecularity energy, shallow lake
Powder phosphate and hydroxypropyl cellulose, can not only strengthen the intensity of high-strength environment-friendly powder of lacquer putty for use on, and make it that high intensity is greasy
Sub- powder is more preferable to the adhesive force of metope, further, since the addition of reinforcing fiber, also further enhancing high-strength environment-friendly powder of lacquer putty for use on
Intensity.Without harmful substances, environmentally friendly nothing such as heavy metal, formaldehyde in the high-strength environment-friendly putty powder raw material of the embodiment of the present invention
Evil.
Embodiments described above is a part of embodiment of the invention, rather than whole embodiments.The reality of the present invention
The detailed description for applying example is not intended to limit the scope of claimed invention, but is merely representative of the selected implementation of the present invention
Example.Based on the embodiment in the present invention, what those of ordinary skill in the art were obtained under the premise of creative work is not made
Every other embodiment, belongs to the scope of protection of the invention.
Claims (10)
1. a kind of high-strength environment-friendly powder of lacquer putty for use on, is mainly mixed by raw material, it is characterised in that
The raw material includes：White cement 20-40 parts by weight, sierozem power 5-20 parts by weight, ball clay 10-20 parts by weight, talcum powder
5-20 parts by weight, starch phosphate 2-8 parts by weight, hydroxypropyl cellulose 1-5 parts by weight, egg-shell meal 2-10 parts by weight and enhancing
Fiber powder 0.5-2 parts by weight.
2. high-strength environment-friendly powder of lacquer putty for use on according to claim 1, it is characterised in that the white cement is 25-35 parts by weight,
The sierozem power is 10-15 parts by weight, and the ball clay is 12-18 parts by weight, and the talcum powder is 10-15 parts by weight, described
Starch phosphate is 3-5 parts by weight, and the hydroxypropyl cellulose 2-4 parts by weight, the egg-shell meal is 3-8 parts by weight, the increasing
Strong fiber powder is 1-1.5 parts by weight.
3. high-strength environment-friendly powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that the reinforcing fiber powder is glass
At least one of fiber powder, basalt fibre powder and polypropylene fibre powder.
4. high-strength environment-friendly powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that the reinforcing fiber powder includes weight
Amount is than being 1~3:1 glass fiber powder and polypropylene fibre powder.
5. high-strength environment-friendly powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that the particle diameter of the reinforcing fiber powder
For 50-100 μm.
6. high-strength environment-friendly powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that the particle diameter of the sierozem power is
320-400 mesh.
7. high-strength environment-friendly powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that the particle diameter of the ball clay is
200-400 mesh.
8. high-strength environment-friendly powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that the particle diameter of the talcum powder is
200-400 mesh.
9. high-strength environment-friendly powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that the grain of the hydroxypropyl cellulose
Footpath is 200-300 mesh.
10. a kind of preparation method of high-strength environment-friendly powder of lacquer putty for use on as described in claim any one of 1-9, it is characterised in that bag
Include：The raw material is mixed the high-strength environment-friendly powder of lacquer putty for use on is made.