CN107345088A - A kind of environment friendly mildew resistant powder of lacquer putty for use on and preparation method thereof - Google Patents
A kind of environment friendly mildew resistant powder of lacquer putty for use on and preparation method thereof Download PDFInfo
- Publication number
- CN107345088A CN107345088A CN201710784177.9A CN201710784177A CN107345088A CN 107345088 A CN107345088 A CN 107345088A CN 201710784177 A CN201710784177 A CN 201710784177A CN 107345088 A CN107345088 A CN 107345088A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- powder
- environment friendly
- lacquer putty
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of environment friendly mildew resistant powder of lacquer putty for use on and preparation method thereof, is related to building material field.A kind of environment friendly mildew resistant powder of lacquer putty for use on, is mainly made up, raw material includes of raw material：The parts by weight of white cement 30 40, the parts by weight of light calcium carbonate powder 10 20, the parts by weight of sierozem power 5 10, the parts by weight of ball clay 10 20, the parts by weight of talcum powder 5 20, the parts by weight of hydroxypropyl cellulose 3 10, the parts by weight of mould inhibitor 18, the parts by weight of flyash 5 12, modified montmorillonite used 3 10 parts by weight, the parts by weight of redispersable latex powder 5 10.It has preferable cementability and mould proof ability, and environment-protecting and non-poisonous.
Description
Technical field
The present invention relates to building material field, and more particularly to a kind of environment friendly mildew resistant powder of lacquer putty for use on and preparation method thereof.
Background technology
Powder of lacquer putty for use on is a kind of ornament materials of smooth surface of wall, is using inorganic gel materials as base material, is equipped with and coheres material
Material and other auxiliary agent retrofits form, and are a kind of products essential before coating paints.Powder of lacquer putty for use on generally applies and imposes on priming paint
Upper or directly painting is imposed on object, to remove the defects of coated article surface is uneven.Powder of lacquer putty for use on is filled as interior wall, exterior wall
Material and be widely used.But when existing powder of lacquer putty for use on is as decorating inner and external walls, it is frequently present of foaming, peels the shortcomings of mouldy.
The content of the invention
It is an object of the invention to provide a kind of environment friendly mildew resistant powder of lacquer putty for use on, and it has preferable cementability and mould proof energy
Power, and it is environment-protecting and non-poisonous.
Another object of the present invention is to provide a kind of preparation method of environment friendly mildew resistant powder of lacquer putty for use on, this method is simple, easily grasps
Make.
The present invention is solved its technical problem and realized using following technical scheme.
The present invention proposes a kind of environment friendly mildew resistant powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：White cement 30-40 weight
Part, light calcium carbonate powder 10-20 parts by weight, sierozem power 5-10 parts by weight, ball clay 10-20 parts by weight, talcum powder 5-20 parts by weight, hydroxypropyl
Base cellulose 3-10 parts by weight, mould inhibitor 1-8 parts by weight, flyash 5-12 parts by weight, modified montmorillonite used 3-10 parts by weight, can be again
Dispersed latex powder 5-10 parts by weight.
A kind of preparation method of environment friendly mildew resistant powder of lacquer putty for use on described above, including：Raw material is mixed environment friendly mildew resistant is made
Powder of lacquer putty for use on.
The beneficial effect of the embodiment of the present invention is：Each group distribution ratio in the raw material of environment friendly mildew resistant powder of lacquer putty for use on is suitable, environmental protection
Mildew-proof putty powder is by the use of white cement, sierozem power and light calcium carbonate powder as main base and inorganic adhesive, using talcum powder as filling out
Filling effect is expected, in conjunction with can dividing again for high-ductility, high cementability, the ball clay of high dispersive ability and high adhesiveness energy
Dissipate latex powder, hydroxypropyl cellulose；In addition, along with mould inhibitor is to the mildew-proof function of environment friendly mildew resistant powder of lacquer putty for use on, and flyash,
Modified montmorillonite used strong adsorption capacity, it can not only cause environment friendly mildew resistant powder of lacquer putty for use on that there is antimildew and antibacterial, and the environmental protection
Mildew-proof putty powder adhesive force is good, and intensity is high.Without heavy metal, formaldehyde etc. in the environment friendly mildew resistant putty powder raw material of the embodiment of the present invention
Harmful substance, it is environmentally friendly.
Embodiment
, below will be in the embodiment of the present invention to make the purpose, technical scheme and advantage of the embodiment of the present invention clearer
Technical scheme be clearly and completely described.Unreceipted actual conditions person, builds according to normal condition or manufacturer in embodiment
The condition of view is carried out.Agents useful for same or the unreceipted production firm person of instrument, it is the conventional production that can be obtained by commercially available purchase
Product.
A kind of environment friendly mildew resistant powder of lacquer putty for use on of the embodiment of the present invention and preparation method thereof is specifically described below.
A kind of environment friendly mildew resistant powder of lacquer putty for use on, is mainly made up, raw material includes of raw material：White cement 30-40 parts by weight, light calcium carbonate powder
10-20 parts by weight, sierozem power 5-10 parts by weight, ball clay 10-20 parts by weight, talcum powder 5-20 parts by weight, hydroxypropyl cellulose
3-10 parts by weight, mould inhibitor 1-8 parts by weight, flyash 5-12 parts by weight, modified montmorillonite used 3-10 parts by weight, Redispersable latex
Powder 5-10 parts by weight.
White cement, it is the abbreviation of white portland cement, is a kind of hydraulic cementing materials.White cement is as powder of lacquer putty for use on
Raw material, its cementability is good, and intensity is high, is mainly used as base-material, can increase the later strength of environment friendly mildew resistant powder of lacquer putty for use on.
Ball clay is a kind of clay of high plasticity, and it has higher viscosity, rheological characteristic, can strengthen environment friendly mildew resistant putty
Powder to the adhesive force of metope, be not easy to peel off, and the intensity of high-strength environment-friendly powder of lacquer putty for use on can be strengthened.
Raw material of the sierozem power as environment friendly mildew resistant powder of lacquer putty for use on, bonding effect is primarily served, and waterproof, water-fast effect can be reached
Fruit.
Hydroxypropyl cellulose, it is a kind of nonionic cellulose derivative.Its thermoplasticity, filming performance, caking property, latex
Stability and dispersiveness are preferable, can strengthen adhesive force of the environment friendly mildew resistant powder of lacquer putty for use on to metope.
Flyash, is the fine ash that catching is got off from the flue gas after coal combustion, and flyash is the main of coal-burning power plant's discharge
Solid waste.Fly ash grain is in porous type cellular tissue, and specific surface area is larger, has higher adsorption activity.As ring
The raw material of mildew-proof putty powder, bacterium, germ during adsorbable air is heavy etc. are protected, plays the effect of antimildew and antibacterial.
Montmorillonite, there is stronger adsorption capacity, adsorbable toxic and harmful gas, and strengthen the attached of environment friendly mildew resistant powder of lacquer putty for use on
Put forth effort.The adsorption capacity and adhesive force of montmorillonite (i.e. modified montmorillonite used) after modified are more preferable.
The modified montmorillonite used of the embodiment of the present invention is mainly made by following methods：By condition of the montmorillonite at 120-140 DEG C
Lower preheating and drying 2-3h, titanate esters are diluted to 5-10wt% mixed solution with 60-90 DEG C of petroleum ether, after preheating and drying
Montmorillonite mixes with mixed solution.
Redispersable latex powder, it is water-soluble redispersible powder, and it has higher cementability and water-resistance
Energy, application property.It is used as the raw material of environment friendly mildew resistant powder of lacquer putty for use on, can strengthen environment friendly mildew resistant powder of lacquer putty for use on to the adhesive ability of metope and resist
Outlet capacity.In an embodiment of the present invention, redispersable latex powder is vinylacetate and ethylene copolymer rubber powder, vinylacetate
Any one in homopolymerization rubber powder, vinyl acetate/versatic acid ethylene copolymer and acrylic copolymer.
The environment friendly mildew resistant powder of lacquer putty for use on of the embodiment of the present invention, each group distribution ratio in its raw material is suitable, environment friendly mildew resistant powder of lacquer putty for use on
By the use of white cement, sierozem power and light calcium carbonate powder as main base and inorganic adhesive, filling is played using talcum powder as filler and is made
With, in conjunction with high-ductility, high cementability, the ball clay of high dispersive ability and high adhesiveness can redispersable latex powder,
Hydroxypropyl cellulose；In addition, along with mould inhibitor takes off to the mildew-proof function of environment friendly mildew resistant powder of lacquer putty for use on, and flyash, modified cover
The strong adsorption capacity of stone, it can not only cause environment friendly mildew resistant powder of lacquer putty for use on that there is antimildew and antibacterial, and the environment friendly mildew resistant putty
Powder adhesive force is good, and intensity is high.Without nuisances such as heavy metal, formaldehyde in the environment friendly mildew resistant putty powder raw material of the embodiment of the present invention
Matter, it is environmentally friendly.
Preferably, the white cement in raw material is 32-37 parts by weight, and light calcium carbonate powder is 12-15 parts by weight, and sierozem power is 5-8 weights
Part is measured, ball clay is 12-15 parts by weight, and talcum powder is 10-15 parts by weight, and hydroxypropyl cellulose is 5-8 parts by weight, and mould inhibitor is
2-5 parts by weight, flyash are 8-10 parts by weight, and modified montmorillonite used is 5-8 parts by weight, and redispersable latex powder is 6-8 parts by weight.
The environment friendly mildew resistant powder of lacquer putty for use on of the proportioning is the creative thinking and empirical preferred value by inventor, environment friendly mildew resistant putty
The adhesive force of powder is more preferable.
Further, mould inhibitor is at least one of Nano Silver, Nanometer Copper, Nano-Zinc or nano zine oxide.
Nano Silver, Nanometer Copper, Nano-Zinc or nano zine oxide are inorganic material, and it can just press down without bio-toxicity medicine
Mildew making grows, environment-protecting and non-poisonous, and has preferable waterproof effect.
In some embodiments of the invention, it is 1~3 that mould inhibitor, which includes weight ratio,:1 Nano Silver and Nano-Zinc.
Further, in an embodiment of the present invention, the particle diameter of ball clay is 200-400 mesh；The particle diameter of talcum powder is
200-400 mesh；The particle diameter of hydroxypropyl cellulose is 200-300 mesh；The particle diameter of flyash is 200-400 mesh.
A kind of environment friendly mildew resistant powder of lacquer putty for use on described above, including：Raw material is mixed environment friendly mildew resistant powder of lacquer putty for use on is made.The party
Method is simple, easy to operate.
The feature and performance of the present invention are described in further detail with reference to embodiments.
Embodiment 1
The present embodiment provides a kind of environment friendly mildew resistant powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The weight of white cement 35
Part, the parts by weight of light calcium carbonate powder 12, the parts by weight of sierozem power 5, the parts by weight of ball clay 12, the parts by weight of talcum powder 18, the weight of hydroxypropyl cellulose 5
Measure part, the parts by weight of mould inhibitor 3, the parts by weight of flyash 12, modified montmorillonite used 4 parts by weight, the parts by weight of redispersable latex powder 6.Its
In, the particle diameter of ball clay is 400 mesh；The particle diameter of talcum powder is 300 mesh；The particle diameter of hydroxypropyl cellulose is 200 mesh；Flyash
Particle diameter is 300 mesh.
It is modified montmorillonite used to be mainly made by following methods：By montmorillonite under conditions of 120 DEG C preheating and drying 3h, use 60-
Titanate esters are diluted to 5wt% mixed solution by 90 DEG C of petroleum ethers, and the montmorillonite after preheating and drying is mixed with mixed solution.
The preparation method of the environment friendly mildew resistant powder of lacquer putty for use on, including：Raw material is weighed according to said ratio, raw material is mixed and made
Obtain environment friendly mildew resistant powder of lacquer putty for use on.
Embodiment 2
The present embodiment provides a kind of environment friendly mildew resistant powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The weight of white cement 32
Part, the parts by weight of light calcium carbonate powder 10, the parts by weight of sierozem power 7, the parts by weight of ball clay 15, the parts by weight of talcum powder 8, the weight of hydroxypropyl cellulose 6
Measure part, the parts by weight of mould inhibitor 2, the parts by weight of flyash 8, modified montmorillonite used 5 parts by weight, the parts by weight of redispersable latex powder 5.Its
In, the particle diameter of ball clay is 300 mesh；The particle diameter of talcum powder is 200 mesh；The particle diameter of hydroxypropyl cellulose is 300 mesh；Flyash
Particle diameter is 400 mesh.
It is modified montmorillonite used to be mainly made by following methods：By montmorillonite under conditions of 140 DEG C preheating and drying 2h, use 60-
Titanate esters are diluted to 10wt% mixed solution by 90 DEG C of petroleum ethers, and the montmorillonite after preheating and drying is mixed with mixed solution.
The preparation method of the environment friendly mildew resistant powder of lacquer putty for use on, including：Raw material is weighed according to said ratio, raw material is mixed and made
Obtain environment friendly mildew resistant powder of lacquer putty for use on.
Embodiment 3
The present embodiment provides a kind of environment friendly mildew resistant powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The weight of white cement 37
Part, the parts by weight of light calcium carbonate powder 20, the parts by weight of sierozem power 6, the parts by weight of ball clay 10, the parts by weight of talcum powder 20, the weight of hydroxypropyl cellulose 4
Measure part, the parts by weight of mould inhibitor 1, the parts by weight of flyash 10, modified montmorillonite used 8 parts by weight, the parts by weight of redispersable latex powder 7.Its
In, the particle diameter of ball clay is 200 mesh；The particle diameter of talcum powder is 300 mesh；The particle diameter of hydroxypropyl cellulose is 300 mesh；Flyash
Particle diameter is 200 mesh.
It is modified montmorillonite used to be mainly made by following methods：By montmorillonite under conditions of 130 DEG C preheating and drying 2h, use 60-
Titanate esters are diluted to 7wt% mixed solution by 90 DEG C of petroleum ethers, and the montmorillonite after preheating and drying is mixed with mixed solution.
The preparation method of the environment friendly mildew resistant powder of lacquer putty for use on includes：Raw material is weighed according to said ratio, raw material is mixed and made
Obtain environment friendly mildew resistant powder of lacquer putty for use on.
Embodiment 4
The present embodiment provides a kind of environment friendly mildew resistant powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The weight of white cement 40
Part, the parts by weight of light calcium carbonate powder 15, the parts by weight of sierozem power 5, the parts by weight of ball clay 13, the parts by weight of talcum powder 5, the weight of hydroxypropyl cellulose 3
Measure part, the parts by weight of mould inhibitor 5, the parts by weight of flyash 5, modified montmorillonite used 3 parts by weight, the parts by weight of redispersable latex powder 8.Its
In, the particle diameter of ball clay is 400 mesh；The particle diameter of talcum powder is 300 mesh；The particle diameter of hydroxypropyl cellulose is 200 mesh；Flyash
Particle diameter is 300 mesh.Modified montmorillonite used preparation method is same as Example 1.
The preparation method of the environment friendly mildew resistant powder of lacquer putty for use on includes：Raw material is weighed according to said ratio, raw material is mixed and made
Obtain environment friendly mildew resistant powder of lacquer putty for use on.
Embodiment 5
The present embodiment provides a kind of environment friendly mildew resistant powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The weight of white cement 30
Part, the parts by weight of light calcium carbonate powder 18, the parts by weight of sierozem power 8, the parts by weight of ball clay 18, the parts by weight of talcum powder 12, the weight of hydroxypropyl cellulose 8
Measure part, the parts by weight of mould inhibitor 6, the parts by weight of flyash 6, modified montmorillonite used 9 parts by weight, the parts by weight of redispersable latex powder 10.Its
In, the particle diameter of ball clay is 300 mesh；The particle diameter of talcum powder is 400 mesh；The particle diameter of hydroxypropyl cellulose is 200 mesh；Flyash
Particle diameter is 200 mesh.Modified montmorillonite used preparation method is same as Example 1.
The preparation method of the environment friendly mildew resistant powder of lacquer putty for use on includes：Raw material is weighed according to said ratio, raw material is mixed and made
Obtain environment friendly mildew resistant powder of lacquer putty for use on.
Embodiment 6
The present embodiment provides a kind of environment friendly mildew resistant powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The weight of white cement 35
Part, the parts by weight of light calcium carbonate powder 16, the parts by weight of sierozem power 10, the parts by weight of ball clay 16, the parts by weight of talcum powder 10, hydroxypropyl cellulose 10
Parts by weight, the parts by weight of mould inhibitor 8, the parts by weight of flyash 7, modified montmorillonite used 10 parts by weight, the parts by weight of redispersable latex powder 9.
Wherein, the particle diameter of ball clay is 200 mesh；The particle diameter of talcum powder is 200 mesh；The particle diameter of hydroxypropyl cellulose is 300 mesh；Flyash
Particle diameter be 400 mesh.Modified montmorillonite used preparation method is same as Example 1.
The preparation method of the environment friendly mildew resistant powder of lacquer putty for use on includes：Raw material is weighed according to said ratio, raw material is mixed and made
Obtain environment friendly mildew resistant powder of lacquer putty for use on.
Embodiment 7
The present embodiment provides a kind of environment friendly mildew resistant powder of lacquer putty for use on, is mainly made up of raw material, raw material includes：The weight of white cement 38
Part, the parts by weight of light calcium carbonate powder 15, the parts by weight of sierozem power 9, the parts by weight of ball clay 20, the parts by weight of talcum powder 15, the weight of hydroxypropyl cellulose 5
Measure part, the parts by weight of mould inhibitor 4, the parts by weight of flyash 9, modified montmorillonite used 6 parts by weight, the parts by weight of redispersable latex powder 8.Its
In, the particle diameter of ball clay is 300 mesh；The particle diameter of talcum powder is 400 mesh；The particle diameter of hydroxypropyl cellulose is 300 mesh；Flyash
Particle diameter is 300 mesh.Modified montmorillonite used preparation method is same as Example 1.
The preparation method of the environment friendly mildew resistant powder of lacquer putty for use on includes：Raw material is weighed according to said ratio, raw material is mixed and made
Obtain environment friendly mildew resistant powder of lacquer putty for use on.
Comparative example 1
A kind of mould powder of lacquer putty for use on, is mainly made up, raw material includes of raw material：The parts by weight of white cement 35, the parts by weight of light calcium carbonate powder 12, ash
The parts by weight of calcium powder 5, the parts by weight of ball clay 12, the parts by weight of talcum powder 18, the parts by weight of hydroxypropyl cellulose 5, the parts by weight of flyash 12,
Modified montmorillonite used 4 parts by weight, the parts by weight of redispersable latex powder 6.Wherein, the particle diameter of ball clay is 400 mesh；The particle diameter of talcum powder
For 300 mesh；The particle diameter of hydroxypropyl cellulose is 200 mesh；The particle diameter of flyash is 300 mesh.Modified montmorillonite used preparation method with
Embodiment 1 is identical.
The preparation method of the mould powder of lacquer putty for use on includes：Raw material is weighed according to said ratio, raw material is mixed putty is made
Powder.
Comparative example 2
A kind of mould powder of lacquer putty for use on, is mainly made up, raw material includes of raw material：The parts by weight of white cement 35, the parts by weight of light calcium carbonate powder 12, ash
The parts by weight of calcium powder 5, the parts by weight of talcum powder 18, the parts by weight of hydroxypropyl cellulose 5, the parts by weight of flyash 12, the parts by weight of mould inhibitor 3,
Modified montmorillonite used 4 parts by weight, the parts by weight of redispersable latex powder 6.Wherein the particle diameter of talcum powder is 300 mesh；Hydroxypropyl cellulose
Particle diameter be 200 mesh；The particle diameter of flyash is 300 mesh.Modified montmorillonite used preparation method is same as Example 1.
The preparation method of the powder of lacquer putty for use on includes：Raw material is weighed according to said ratio, raw material is mixed powder of lacquer putty for use on is made.
Comparative example 3
A kind of mould powder of lacquer putty for use on, is mainly made up, raw material includes of raw material：The parts by weight of white cement 28, the parts by weight of light calcium carbonate powder 21, ash
The parts by weight of calcium powder 3, the parts by weight of ball clay 8, the parts by weight of talcum powder 21, the parts by weight of hydroxypropyl cellulose 2, the parts by weight of mould inhibitor 9, powder
The parts by weight of coal ash 22, modified montmorillonite used 2 parts by weight, the parts by weight of redispersable latex powder 11.Wherein, the particle diameter of ball clay is 300
Mesh；The particle diameter of talcum powder is 400 mesh；The particle diameter of hydroxypropyl cellulose is 300 mesh；The particle diameter of flyash is 300 mesh.Modified cover takes off
The preparation method of stone is same as Example 1.
The preparation method of the powder of lacquer putty for use on includes：Raw material is weighed according to said ratio, raw material is mixed powder of lacquer putty for use on is made.
Test example
1. reference JG/T-298-2010 (architecture indoor putty) standard is to embodiment 1-7 high-strength environment-friendly putty
Powder and comparative example 1-3 powder of lacquer putty for use on carry out the performances such as application property, adhesive strength, drying time, grinability, rupture strength and surveyed
Examination, its result are recorded in table 1.
2. mould proof experiment：By embodiment 1-7 environment friendly mildew resistant powder of lacquer putty for use on and comparative example 1-3 powder of lacquer putty for use on and water according to 1:
0.3 weight ratio is mixed, and is scratched on the wall of long mould, and record mould removes the time and mould removes degree,
Its result is recorded in table 1.
The embodiment 1-7 of table 1 and comparative example 1-3 test result
From table 1 it follows that embodiment 1-7 environment friendly mildew resistant powder of lacquer putty for use on than comparative example 1 powder of lacquer putty for use on anti-mold effect compared with
It is good, illustrate that mould inhibitor is added in the embodiment of the present invention can effectively strengthen the antimildew function of powder of lacquer putty for use on.
In addition, the environment friendly mildew resistant powder of lacquer putty for use on of embodiment 1 than the powder of lacquer putty for use on of comparative example 2 adhesive strength and rupture strength all more
It is good, illustrate, the adhesive strength and rupture strength of powder of lacquer putty for use on can be improved by adding the ball clay in the embodiment of the present invention.
By each performance of comparative example 1-7 environment friendly mildew resistant powder of lacquer putty for use on and the powder of lacquer putty for use on of comparative example 3, find either
Adhesive strength, rupture strength, or grinability and drying time performance, embodiment 1-7 environment friendly mildew resistant powder of lacquer putty for use on all compare ratio
The powder of lacquer putty for use on performance of example 3 is more excellent, illustrates that each raw material proportioning of environment friendly mildew resistant powder of lacquer putty for use on of the embodiment of the present invention is suitable, is advantageous to make
It is standby to obtain the more excellent environment friendly mildew resistant powder of lacquer putty for use on of performance.
In summary, environment friendly mildew resistant powder of lacquer putty for use on of the embodiment of the present invention and preparation method thereof, the original of environment friendly mildew resistant powder of lacquer putty for use on
Each group distribution ratio in material is suitable, and environment friendly mildew resistant powder of lacquer putty for use on is used as main base and nothing by the use of white cement, sierozem power and light calcium carbonate powder
Machine adhesives, using talcum powder as filler rise filling effect, in conjunction with high-ductility, high cementability, high dispersive ability ball
Redispersable latex powder, the hydroxypropyl cellulose of clay and high adhesiveness energy；In addition, along with mould inhibitor is greasy to environment friendly mildew resistant
The mildew-proof function of sub- powder, and flyash, modified montmorillonite used strong adsorption capacity, environment friendly mildew resistant powder of lacquer putty for use on can be not only caused to have
There is antimildew and antibacterial, and the environment friendly mildew resistant powder of lacquer putty for use on adhesive force is good, intensity is high.The environment friendly mildew resistant putty of the embodiment of the present invention
It is environmentally friendly without harmful substances such as heavy metal, formaldehyde in powder raw material.
Embodiments described above is part of the embodiment of the present invention, rather than whole embodiments.The reality of the present invention
The detailed description for applying example is not intended to limit the scope of claimed invention, but is merely representative of the selected implementation of the present invention
Example.Based on the embodiment in the present invention, what those of ordinary skill in the art were obtained under the premise of creative work is not made
Every other embodiment, belongs to the scope of protection of the invention.
Claims (10)
1. a kind of environment friendly mildew resistant powder of lacquer putty for use on, is mainly made up of raw material, it is characterised in that the raw material includes：White cement 30-40 weights
Measure part, light calcium carbonate powder 10-20 parts by weight, sierozem power 5-10 parts by weight, ball clay 10-20 parts by weight, talcum powder 5-20 parts by weight, hydroxyl
Propyl cellulose 3-10 parts by weight, mould inhibitor 1-8 parts by weight, flyash 5-12 parts by weight, modified montmorillonite used 3-10 parts by weight, can
Redisperse latex powder 5-10 parts by weight.
2. environment friendly mildew resistant powder of lacquer putty for use on according to claim 1, it is characterised in that the white cement is 32-37 parts by weight, institute
It is 12-15 parts by weight to state light calcium carbonate powder, and the sierozem power is 5-8 parts by weight, and the ball clay is 12-15 parts by weight, the talcum
Powder is 10-15 parts by weight, and the hydroxypropyl cellulose is 5-8 parts by weight, and the mould inhibitor is 2-5 parts by weight, the flyash
For 8-10 parts by weight, it is described it is modified montmorillonite used be 5-8 parts by weight, the redispersable latex powder is 6-8 parts by weight.
3. environment friendly mildew resistant powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that the mould inhibitor is Nano Silver, nanometer
At least one of copper, Nano-Zinc or nano zine oxide.
4. environment friendly mildew resistant powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that it is 1 that the mould inhibitor, which includes weight ratio,
~3:1 Nano Silver and Nano-Zinc.
5. environment friendly mildew resistant powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that it is described it is modified montmorillonite used mainly by with
Lower section method is made：By montmorillonite under conditions of 120-140 DEG C preheating and drying 2-3h, it is with 60-90 DEG C of petroleum ether that titanate esters are dilute
5-10wt% mixed solution is interpreted into, the montmorillonite after preheating and drying is mixed with mixed solution.
6. environment friendly mildew resistant powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that the particle diameter of the ball clay is 200-
400 mesh.
7. environment friendly mildew resistant powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that the particle diameter of the talcum powder is 200-
400 mesh.
8. environment friendly mildew resistant powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that the particle diameter of the hydroxypropyl cellulose
For 200-300 mesh.
9. environment friendly mildew resistant powder of lacquer putty for use on according to claim 1 or 2, it is characterised in that the particle diameter of the flyash is 200-
400 mesh.
A kind of 10. preparation method of environment friendly mildew resistant powder of lacquer putty for use on as described in claim any one of 1-9, it is characterised in that including：
The raw material is mixed the environment friendly mildew resistant powder of lacquer putty for use on is made.