CN105017837A - Internal wall putty powder - Google Patents
Internal wall putty powder Download PDFInfo
- Publication number
- CN105017837A CN105017837A CN201510458279.2A CN201510458279A CN105017837A CN 105017837 A CN105017837 A CN 105017837A CN 201510458279 A CN201510458279 A CN 201510458279A CN 105017837 A CN105017837 A CN 105017837A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- wall putty
- zine oxide
- nano zine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an internal wall putty powder, relating to the field of paints. The internal wall putty powder is prepared from 40-70 parts of gypsum powder, 10-30 parts of kaolin, 10-30 parts of ash calcium powder, 1.5-2.5 parts of hydroxypropyl methylcellulose, 10-15 parts of nano zinc oxide, 5-10 parts of japonica rice gel powder, 2-3 parts of rubber powder, 0.5-1 part of titanium white and 0.1-0.3 part of triclosan. Compared with the prior art, the internal wall putty powder adopts the gypsum powder as the base material and the japonica rice gel powder as the adhesive, and thus, has the advantages of high adhesive force with the base wall, no peeling, white and smooth surface and high quality stability.
Description
Technical field
The present invention relates to technical field of coatings, especially a kind of inner wall putty powder.
Background technology
Inner wall putty is between body of wall leveling mortar and dope layer, and main purpose is the curve deviation of filling the space of construction surface and the space of rectification construction surface and rectification construction surface, lays a solid foundation for obtaining even, level and smooth lacquer painting.
Traditional inner wall putty powder is often base-material with inorganic gel materials, is equipped with matrix material and other auxiliary combination forms, and such inner wall putty powder also exists water-wash resistance difference, causes construction in later period to occur powder phenomenon-tion, and whiteness and texture are all inadequate.
Summary of the invention
Problem to be solved by this invention is to provide a kind of water-tolerant, inner wall putty powder that whiteness is high.
In order to solve the problems of the technologies described above, scheme of the present invention is:
It is made up of the raw material of following weight part:
Terra alba 40-70 part, kaolin 10-30 part, sierozem power 10-30 part, Vltra tears 1.5-2.5 part, nano zine oxide 10-15 part, polished rice gel powder 5-10 part, rubber powder 2-3 part, titanium dioxide 0.5-1 part, triclosan 0.1-0.3 part.
In technique scheme, scheme can also be more specifically: the particle size range of described nano zine oxide is 2 ~ 40 nanometers, specific surface area be 51.5 squares of faces/gram, described rubber powder is any one or two kinds of mixtures in acrylic resin, polyvinyl alcohol rubber powder; Described Vltra tears viscosity was not less than for 50,000 milli handkerchief seconds.
Further: described parts by weight of raw materials is as follows:
Terra alba 40 parts, kaolin 30 parts, sierozem power 30 parts, Vltra tears 1.5 parts, nano zine oxide 10 parts, polished rice gel powder 5 parts, rubber powder 2 parts, titanium dioxide 0.5 part, triclosan 0.1 part.
Further: described parts by weight of raw materials is as follows:
Terra alba 70 parts, kaolin 10 parts, sierozem power 10 parts, Vltra tears 2 parts, nano zine oxide 12 parts, polished rice gel powder 7 parts, rubber powder 2 parts, titanium dioxide 0.7 part, triclosan 0.2 part.
Further: described parts by weight of raw materials is as follows:
Terra alba 60 parts, kaolin 20 parts, sierozem power 20 parts, Vltra tears 2.5 parts, nano zine oxide 15 parts, polished rice gel powder 10 parts, rubber powder 3 parts, titanium dioxide 1 part, triclosan 0.3 part.
The present invention compared with prior art, has following beneficial effect:
1, adopt terra alba to be base-material in this inner wall putty powder, adopt polished rice gel powder as caking agent, make this putty powder and base course wall strong adhesion, do not peel off, the tenderly white bright and clean exquisiteness in surface, quality stability is good.
2, with the addition of nano zine oxide in this inner wall putty powder, the specific surface area of its super large, can, by the moisture absorption in air, storage also release in good time, automatically surge chamber humidity, make putty powder can not occur the phenomenons such as peeling, hollowing and cracking because of damp atmosphere; Simultaneously they can the generation of mould fungus inhibition, prevents the generation of mildew phenomena.
Embodiment
Below in conjunction with specific examples, the invention will be further described:
Embodiment 1:
The raw material that the present embodiment adopts is:
Terra alba 40 parts, kaolin 30 parts, sierozem power 30 parts, Vltra tears 1.5 parts, nano zine oxide 10 parts, polished rice gel powder 5 parts, rubber powder 2 parts, titanium dioxide 0.5 part, triclosan 0.1 part,
Wherein rubber powder is polyvinyl alcohol rubber powder, and the particle diameter of nano zine oxide is 2 nanometers, specific surface area be 51.5 squares of faces/gram, hydroxyethylcellulose viscosity was 50,000 milli handkerchief seconds;
Preparation method is:
Terra alba, kaolin, sierozem power, nano zine oxide are added in stirrer, stir after within 20 minutes, mixing, then add carboxymethyl cellulose, polished rice gel powder, rubber powder, titanium dioxide and triclosan in stirrer, continue stirring 10 minutes, make it fully mix, to obtain final product.
Embodiment 2:
The raw material that the present embodiment adopts is:
Terra alba 70 parts, kaolin 10 parts, sierozem power 10 parts, Vltra tears 2 parts, nano zine oxide 12 parts, polished rice gel powder 7 parts, rubber powder 2 parts, titanium dioxide 0.7 part, triclosan 0.2 part;
Wherein, rubber powder is acrylic resin rubber powder, and the particle diameter of nano zine oxide is 15 nanometers, specific surface area be 51.5 squares of faces/gram, hydroxyethylcellulose viscosity was 5.1 ten thousand milli handkerchief seconds;
Its preparation method is identical with embodiment 1.
Embodiment 3:
The raw material that the present embodiment adopts is:
Terra alba 60 parts, kaolin 20 parts, sierozem power 20 parts, Vltra tears 2.5 parts, nano zine oxide 15 parts, polished rice gel powder 10 parts, rubber powder 3 parts, titanium dioxide 1 part, triclosan 0.3 part;
Wherein, rubber powder is acrylic resin rubber powder and polyvinyl alcohol rubber powder, and the particle diameter of nano zine oxide is 40 nanometers, specific surface area be 51.5 squares of faces/gram, hydroxyethylcellulose viscosity was 5.2 ten thousand milli handkerchief seconds;
Its preparation method is identical with embodiment 1.
measure of merit:
Water tolerance test
Criticized respectively by the putty powder that embodiment 1-3 is obtained and scrape on three interior walls, putty thickness is about 2mm, and after putty drying, to metope trickle, keep metope moist in 96 hours, wall surface putty is without exception.
Claims (5)
1. an inner wall putty powder, is characterized in that being made up of the raw material of following weight part:
Terra alba 40-70 part, kaolin 10-30 part, sierozem power 10-30 part, Vltra tears 1.5-2.5 part, nano zine oxide 10-15 part, polished rice gel powder 5-10 part, rubber powder 2-3 part, titanium dioxide 0.5-1 part, triclosan 0.1-0.3 part.
2. inner wall putty powder according to claim 1, it is characterized in that: the particle size range of described nano zine oxide is 2 ~ 40 nanometers, specific surface area be 51.5 squares of faces/gram, described rubber powder is any one or two kinds of mixtures in acrylic resin, polyvinyl alcohol rubber powder; Described Vltra tears viscosity was not less than for 50,000 milli handkerchief seconds.
3. inner wall putty powder according to claim 1 and 2, is characterized in that described parts by weight of raw materials is as follows:
Terra alba 40 parts, kaolin 30 parts, sierozem power 30 parts, Vltra tears 1.5 parts, nano zine oxide 10 parts, polished rice gel powder 5 parts, rubber powder 2 parts, titanium dioxide 0.5 part, triclosan 0.1 part.
4. inner wall putty powder according to claim 1 and 2, is characterized in that described parts by weight of raw materials is as follows:
Terra alba 70 parts, kaolin 10 parts, sierozem power 10 parts, Vltra tears 2 parts, nano zine oxide 12 parts, polished rice gel powder 7 parts, rubber powder 2 parts, titanium dioxide 0.7 part, triclosan 0.2 part.
5. inner wall putty powder according to claim 1 and 2, is characterized in that described parts by weight of raw materials is as follows:
Terra alba 60 parts, kaolin 20 parts, sierozem power 20 parts, Vltra tears 2.5 parts, nano zine oxide 15 parts, polished rice gel powder 10 parts, rubber powder 3 parts, titanium dioxide 1 part, triclosan 0.3 part.