CN106497209A - A kind of putty powder for exterior wall - Google Patents
A kind of putty powder for exterior wall Download PDFInfo
- Publication number
- CN106497209A CN106497209A CN201611232256.0A CN201611232256A CN106497209A CN 106497209 A CN106497209 A CN 106497209A CN 201611232256 A CN201611232256 A CN 201611232256A CN 106497209 A CN106497209 A CN 106497209A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- exterior wall
- putty
- putty powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of putty powder for exterior wall, is related to paint field, it is made up of following raw material：White portland cement, precipitated calcium carbonate powder, Pulvis Talci, sierozem power, silica flour, 1008 glue powders of GN, efficient general dispersant P 30A, polyacrylamide, organic silicon solid defoaming agent, easily antifungus agent BJ 75, dispersion fiber, nano zine oxide.The putty powder for exterior wall of the present invention with the addition of precipitated calcium carbonate powder, sierozem power and anion surfactant, can interpenetrate and react, so as to improve the stability and hardness of putty bisque；With the addition of silica flour simultaneously, more effectively enhance the hardness of powder of lacquer putty for use on.
Description
Technical field
The present invention relates to technical field of coatings, and in particular to a kind of putty powder for exterior wall.
Background technology
Putty is a kind of decoration gel material of smooth surface of wall, is a kind of thick slurry coating material, and being must not before coating is painted
A kind of product that can lack；The main purpose of brushing putty is the curve deviation of the hole and correction construction surface for filling construction surface, is
Obtain uniform, smooth lacquer painting to lay a solid foundation.And often there is peeling, opens due to residing outdoor environment in conventional outer wall powder of lacquer putty for use on
The phenomenon such as split, come off.
Content of the invention
Problem to be solved by this invention is to provide a kind of waterproof, hardness height, the putty powder for exterior wall of anticracking.
In order to solve above-mentioned technical problem, the technical solution adopted in the present invention is：A kind of putty powder for exterior wall, by following heavy
The raw material composition of amount part：
White portland cement 20-25 parts, precipitated calcium carbonate powder 25-30 parts, Pulvis Talci 20-30 parts, sierozem power 10-15
Part, silica flour 5-10 parts, GN-1008 glue powder 1.0-1.5 parts, efficient general dispersant P-30A 0.5-2.0 parts, polyacrylamide
Amine 0.3-0.6 parts, organic silicon solid defoaming agent 0.4-0.8 parts, antifungus agent BJ-750.3-1.0 parts, easily dispersion fiber 1-2 parts, receive
Rice zinc oxide 1-2 parts.
The white portland cement, precipitated calcium carbonate powder, sierozem power, talcous particle diameter are 10-15 microns.
The specification of the silica flour is 400 mesh.
The polyacrylamide is anion surfactant.
Beneficial effects of the present invention：The putty powder for exterior wall of the present invention, with waterproof, water-fast, viscosity is strong, cracking resistance, hardness
The advantages of high, environmental protection；Each composition is interpenetrated, and with the addition of nano zine oxide, silica flour, is had sterilization anti-ultraviolet, is strengthened firmly
The effect such as degree；The present invention putty powder for exterior wall make moist do not fall off, non-foaming；Dry run contractility is little, filling capacity is good.
Specific embodiment
Hereinafter the specific embodiment of the present invention is described in detail.It should be appreciated that described herein concrete
Embodiment is merely to illustrate and explains the present invention, is not limited to the present invention.In embodiment, white portland cement, light
Matter Paris white, Pulvis Talci, sierozem power, silica flour, efficient general dispersant P-30A, polyacrylamide, organic silicon solid defoaming
Agent, nano zine oxide, easily dispersion fiber are Gaede chemical industry net commercially available product, and GN-1008 glue powders are the sensible great achievement waterproof in Harbin
Materials Co., Ltd's product, antifungus agent BJ-75 are Li Yuan Chemical Co., Ltd.s of Foshan City product.
Embodiment 1
A kind of putty powder for exterior wall, is made up of the raw material of following weight portion：
22 parts of white portland cement, 28 parts of precipitated calcium carbonate powder, 23 parts of Pulvis Talci, 12 parts of sierozem power, silica flour 8.2
Part, 1.2 parts of GN-1008 glue powders, 1.0 parts of efficient general dispersant P-30A, 0.4 part of polyacrylamide, organic silicon solid disappear
0.6 part of infusion, easily 0.6 part of antifungus agent BJ-75,1.5 parts of fiber of dispersion, 1.5 parts of nano zine oxide.
Embodiment 2
A kind of putty powder for exterior wall, is made up of the raw material of following weight portion：
23 parts of white portland cement, 27 parts of precipitated calcium carbonate powder, 23 parts of Pulvis Talci, 12.2 parts of sierozem power, silica flour 7.5
Part, 1.3 parts of GN-1008 glue powders, 1.2 parts of efficient general dispersant P-30A, 0.4 part of polyacrylamide, organic silicon solid disappear
0.6 part of infusion, easily 0.8 part of antifungus agent BJ-75,1.5 parts of fiber of dispersion, 1.5 parts of nano zine oxide.
Measure of merit
Water Resistance Test and using effect
Powder of lacquer putty for use on obtained in embodiment 1,2 is criticized respectively and is scraped on three face interior walls, powder of lacquer putty for use on thickness about 3mm treats that putty is done
After dry, to metope water drenching, metope humidity in 7 days, is kept, wall surface putty powder is without exception.
When preparing powder of lacquer putty for use on of the invention, each raw material stirring mix homogeneously.During use, plus suitable quantity of water, it is evenly stirred until slurry
Shape.
The adhesion strength of powder of lacquer putty for use on obtained in embodiment 1 is 2.8Mpa, and obtained in embodiment 2, the adhesion strength of powder of lacquer putty for use on is
2.9Mpa；Obtained in embodiment 1,2, powder of lacquer putty for use on attachment is uniform, after construction 3 years without delamination, have no any crackle, have no and send out
Mould.
Claims (4)
1. a kind of putty powder for exterior wall, it is characterised in that be made up of the raw material of following weight portion：
White portland cement 20-25 parts, precipitated calcium carbonate powder 25-30 parts, Pulvis Talci 20-30 parts, sierozem power 10-15 parts, stone
English powder 5-10 parts, GN-1008 glue powder 1.0-1.5 parts, efficient general dispersant P-30A 0.5-2.0 parts, polyacrylamide
0.3-0.6 parts, organic silicon solid defoaming agent 0.4-0.8 parts, antifungus agent BJ-75 0.3-1.0 parts, easily dispersion fiber 1-2 parts, receive
Rice zinc oxide 1-2 parts.
2. a kind of putty powder for exterior wall according to claim 1, it is characterised in that：The white portland cement, lightweight carbon
Sour calcium powder, sierozem power, talcous particle diameter are 10-15 microns.
3. a kind of putty powder for exterior wall according to claim 1, it is characterised in that：The specification of the silica flour is 400 mesh.
4. a kind of putty powder for exterior wall according to claim 1, it is characterised in that：The polyacrylamide is anionic surface
Activating agent.